CN116675963A - 一种rpet发泡帽舌 - Google Patents
一种rpet发泡帽舌 Download PDFInfo
- Publication number
- CN116675963A CN116675963A CN202310861989.4A CN202310861989A CN116675963A CN 116675963 A CN116675963 A CN 116675963A CN 202310861989 A CN202310861989 A CN 202310861989A CN 116675963 A CN116675963 A CN 116675963A
- Authority
- CN
- China
- Prior art keywords
- rpet
- parts
- foaming
- resin
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种RPET发泡帽舌，包括RPET发泡帽舌片材，所述RPET发泡帽舌片材包括RPET树脂和添加剂，所述添加剂包括有机成核剂、增韧剂和发泡剂，按重量份数计，所述RPET树脂80‑90份，有机成核剂0.5‑5份，增韧剂1‑4份，发泡剂0.5‑5份；其中，所述RPET树脂的加工工艺为：将与添加剂混合后的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3‑5min内快速反应，本发明通过团相缩聚，原住共聚和扩链改造，本产品根据生产需求采用扩链改性，将RPET树脂加入挤出机中，添加多种能团扩链剂与之熔融、共混；使之二者在短时内快速反应，从而提高PET分子量。扩链改性法工艺流程短、生产效率高、改性效果好，特有利RPET生产，并且环保安全。
Description
技术领域
本发明涉及RPET发泡帽舌技术领域，具体为一种RPET发泡帽舌。
背景技术
RPET为再生的，为高聚合物，由酯发生脱水缩合反应而来。对苯二甲酸乙二醇酯是由对苯二甲酸和乙二醇发生酯化反应所得。
PRET分子链为规则的线型结构，高温下表现出较低的熔体强度和熔体黏弹性，发泡时PRET熔体无法承受泡孔生长造成剧烈拉伸，易出现泡孔破裂、并聚，导致泡孔成型困难；
且目前对生产的低发泡片还存在发泡信率低的问题，生产出的密度在0.9g/cm3，离需要在0.6g/cm3的目的存在一定困难，因此我们需要提出一种RPET发泡帽舌。
发明内容
本发明的目的在于提供一种RPET发泡帽舌，通过团相缩聚，原住共聚和扩链改造，本产品根据生产需求采用扩链改性，将RPET树脂加入挤出机中，添加多种能团扩链剂与之熔融、共混；使之二者在短时内快速反应，从而提高PET分子量。扩链改性法工艺流程短、生产效率高、改性效果好，特有利RPET生产，并且环保安全，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种RPET发泡帽舌，包括RPET发泡帽舌片材，所述RPET发泡帽舌片材包括RPET树脂和添加剂，所述添加剂包括有机成核剂、增韧剂和发泡剂，按重量份数计，所述RPET树脂80-90份，有机成核剂0.5-5份，增韧剂1-4份，发泡剂0.5-5份；
其中，所述RPET树脂的加工工艺为：将与添加剂混合后的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3-5min内快速反应，提高RPET的分子量。生产出的RPET发泡帽舌片的密度可达到0.6g/cm3。
采用扩链方法后，RPET的熔体强度高，且采用百分之二百二氧化碳气体，产品的泡孔细；
优选的，按重量份数计，所述RPET发泡帽舌片材包括RPET树脂80份，有机成核剂0.5份，增韧剂1份，发泡剂0.5份。
优选的，按重量份数计，所述RPET发泡帽舌片材包括RPET树脂83份，有机成核剂2份，增韧剂2份，发泡剂2份。
优选的，按重量份数计，所述RPET发泡帽舌片材包括RPET树脂87份，有机成核剂3.5份，增韧剂3份，发泡剂3.5份。
优选的，按重量份数计，所述RPET发泡帽舌片材包括RPET树脂90份，有机成核剂5份，增韧剂4份，发泡剂5份。
优选的，所述扩链剂用于提高RPET发泡帽舌片材的特性粘度、分子量和熔体强度，所述扩链剂包括噁唑啉类、易氰酸酯类、酸酐类、环氧类中的任意一种。
优选的，所述发泡剂为超临界二氧化碳，所述超临界二氧化碳的质量为发泡剂总质量的100％；
所述有机成核剂用于提高RPET发泡帽舌片材的透明性和光泽度，所述有机成核剂为脂肪羧酸金属化合物、山梨醇苄叉衍生物、芳香族羧酸金属化合物、有机磷酸盐和木质酸及其衍生物类、以及双羧基铝中的任意一种或多种的组合；
所述增韧剂用于增加RPET发泡帽舌片材的柔韧性，所述增韧剂为、液体丙烯酸酯橡胶、橡胶、丁腈橡胶、乙丙橡胶及丁苯橡胶中的任意一种或多种的组合。
优选的，所述RPET发泡帽舌片材在挤出机中挤出成型时的挤出温度为225℃-255℃。
优选的，还包括RPET发泡帽舌片材的成型工艺，包括如下步骤：
S1、将RPET树脂加入到容器中进行加热至熔融状态，并向熔融的RPET树脂中加入有机成核剂、增韧剂和发泡剂，并通过搅拌机构使有机成核剂、增韧剂和发泡剂与RPET树脂充分混合；
S2、将混合有添加剂的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3-5min内快速反应，然后RPET树脂通过挤出机挤出成型有RPET发泡帽舌片材。
优选的，所述搅拌机构包括转动安装在容器内部的转轴，所述转轴的外壁上安装有多组搅拌杆，且容器的底部安装有驱动转轴转动的电机，所述电机的转速设为200-300r/min。
与现有技术相比，本发明的有益效果是：
本发明通过团相缩聚，原住共聚和扩链改造，本产品根据生产需求采用扩链改性，将RPET树脂加入挤出机中，添加多种能团扩链剂与之熔融、共混；使之二者在短时内快速反应，从而提高PET分子量；扩链改性法工艺流程短、生产效率高、改性效果好，特有利RPET生产，并且环保安全。
附图说明
图1为本发明RPET发泡帽舌片材的成型工艺流程图。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
请参阅图1本发明提供一种技术方案：一种RPET发泡帽舌，包括RPET发泡帽舌片材，所述RPET发泡帽舌片材包括RPET树脂和添加剂，所述添加剂包括有机成核剂、增韧剂和发泡剂，按重量份数计，所述RPET树脂80-90份，有机成核剂0.5-5份，增韧剂1-4份，发泡剂0.5-5份；
其中，所述RPET树脂的加工工艺为：将与添加剂混合后的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3-5min内快速反应，提高RPET的分子量。
具体的，按重量份数计，所述RPET发泡帽舌片材包括RPET树脂80份，有机成核剂0.5份，增韧剂1份，发泡剂0.5份。
所述扩链剂用于提高RPET发泡帽舌片材的特性粘度、分子量和熔体强度，所述扩链剂包括噁唑啉类、易氰酸酯类、酸酐类、环氧类中的任意一种。
噁唑啉是一类含有一个双键的五元杂环化合物，该双键可以位于环中的三个不同位置，噁唑啉类扩链剂主要是2-噁唑啉，噁唑啉环的活性较强，可以和多种官能团发生开环反应；对于噁唑啉类化合物(PBO)的阔怜原理是PBO可与两个PET端羧基发生大分子封端偶联反应，使PET分子质量增加，端羧基含量值下降，特性粘度上升。
易氰酸酯类扩链剂主要适用于如PET等含末端羟基的聚合物扩链，易氰酸酯类化合物中，二异氰酸酯是一类常见的扩链剂；
酸酐类化合物可以和PET的端羟基发生缩聚偶联反应。为了满足PET扩链剂耐高温的性质，通常用作PET扩链的酸酐类化合物主要为均苯四甲酸酐(PMDA)。单独添加PMDA可以提高PET的熔体强度，但是添加PMDA和季戊四醇复配扩链剂，能够实现扩链协效作用。
环氧扩链剂一般含有两个或两个以上的环氧基团，同时还可能含有其他活性基团，如氨基、羟基、琉球、羧基等，环氧官能团与PET链端羧基发生亲电加成反应的活性，比与PET链端羟基发生缩聚反应生成醚键的活性强，因此PET环氧扩链反应主要是环氧基与羧基间发生的加成反应。环氧化合物扩链反应可分为两步进行，即封端和偶联。当一个PET端羧基反应后与环氧基反应后，即得到封端的PET分子。当两个或多个PET的端羧基与多个环氧基反应时，即得到多分子PET偶联产物，从而使分子量增加。用环氧化合物进行扩链反应时，由于偶联作用可能使体系形成凝胶，因此需要控制反应工艺和扩链剂种类与用量，阻止在反应过程中发生过量偶联导致交联。
所述发泡剂为超临界二氧化碳，所述超临界二氧化碳的质量为发泡剂总质量的100％；
所述有机成核剂用于提高RPET发泡帽舌片材的透明性和光泽度，所述有机成核剂为脂肪羧酸金属化合物、山梨醇苄叉衍生物、芳香族羧酸金属化合物、有机磷酸盐和木质酸及其衍生物类、以及双羧基铝中的任意一种或多种的组合；
所述增韧剂用于增加RPET发泡帽舌片材的柔韧性，所述增韧剂为、液体丙烯酸酯橡胶、橡胶、丁腈橡胶、乙丙橡胶及丁苯橡胶中的任意一种或多种的组合。
所述RPET发泡帽舌片材在挤出机中挤出成型时的挤出温度为225℃-255℃。
还包括RPET发泡帽舌片材的成型工艺，包括如下步骤：
S1、将RPET树脂加入到容器中进行加热至熔融状态，并向熔融的RPET树脂中加入有机成核剂、增韧剂和发泡剂，并通过搅拌机构使有机成核剂、增韧剂和发泡剂与RPET树脂充分混合；
S2、将混合有添加剂的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3-5min内快速反应，然后RPET树脂通过挤出机挤出成型有RPET发泡帽舌片材。
所述搅拌机构包括转动安装在容器内部的转轴，所述转轴的外壁上安装有多组搅拌杆，且容器的底部安装有驱动转轴转动的电机，所述电机的转速设为200-300r/min。RPET树脂与添加剂的搅拌时间为15-30min。
实施例2
与实施例1不同的是
按重量份数计，所述RPET发泡帽舌片材包括RPET树脂83份，有机成核剂2份，增韧剂2份，发泡剂2份。
实施例3
与实施例1不同的是
按重量份数计，所述RPET发泡帽舌片材包括RPET树脂87份，有机成核剂3.5份，增韧剂3份，发泡剂3.5份。
实施例4
与实施例1不同的是
按重量份数计，所述RPET发泡帽舌片材包括RPET树脂90份，有机成核剂5份，增韧剂4份，发泡剂5份。
本发明四组实施例的具体配方数据如下表：
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | |
| RPET树脂 | 80份 | 0.5份 | 1份 | 0.5份 |
| 有机成核剂 | 83份 | 2份 | 2份 | 2份 |
| 增韧剂 | 87份 | 3.5份 | 3份 | 3.5份 |
| 发泡剂 | 90份 | 5份 | 4份 | 5份 |
本发明通过团相缩聚，原住共聚和扩链改造，本产品根据生产需求采用扩链改性，将RPET树脂加入挤出机中，添加多种能团扩链剂与之熔融、共混；使之二者在短时内快速反应，从而提高PET分子量；扩链改性法工艺流程短、生产效率高、改性效果好，特有利RPET生产，并且环保安全。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种RPET发泡帽舌，其特征在于：包括RPET发泡帽舌片材，所述RPET发泡帽舌片材包括RPET树脂和添加剂，所述添加剂包括有机成核剂、增韧剂和发泡剂，按重量份数计，所述RPET树脂80-90份，有机成核剂0.5-5份，增韧剂1-4份，发泡剂0.5-5份；
其中，所述RPET树脂的加工工艺为：将与添加剂混合后的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3-5min内快速反应，提高RPET的分子量。
2.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：按重量份数计，所述RPET发泡帽舌片材包括RPET树脂80份，有机成核剂0.5份，增韧剂1份，发泡剂0.5份。
3.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：按重量份数计，所述RPET发泡帽舌片材包括RPET树脂83份，有机成核剂2份，增韧剂2份，发泡剂2份。
4.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：按重量份数计，所述RPET发泡帽舌片材包括RPET树脂87份，有机成核剂3.5份，增韧剂3份，发泡剂3.5份。
5.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：按重量份数计，所述RPET发泡帽舌片材包括RPET树脂90份，有机成核剂5份，增韧剂4份，发泡剂5份。
6.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：所述扩链剂用于提高RPET发泡帽舌片材的特性粘度、分子量和熔体强度，所述扩链剂包括噁唑啉类、易氰酸酯类、酸酐类、环氧类中的任意一种。
7.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：所述发泡剂为超临界二氧化碳，所述超临界二氧化碳的质量为发泡剂总质量的100％；
所述有机成核剂用于提高RPET发泡帽舌片材的透明性和光泽度，所述有机成核剂为脂肪羧酸金属化合物、山梨醇苄叉衍生物、芳香族羧酸金属化合物、有机磷酸盐和木质酸及其衍生物类、以及双羧基铝中的任意一种或多种的组合；
所述增韧剂用于增加RPET发泡帽舌片材的柔韧性，所述增韧剂为、液体丙烯酸酯橡胶、橡胶、丁腈橡胶、乙丙橡胶及丁苯橡胶中的任意一种或多种的组合。
8.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：所述RPET发泡帽舌片材在挤出机中挤出成型时的挤出温度为225℃-255℃。
9.根据权利要求1所述的一种RPET发泡帽舌，其特征在于：还包括RPET发泡帽舌片材的成型工艺，包括如下步骤：
S1、将RPET树脂加入到容器中进行加热至熔融状态，并向熔融的RPET树脂中加入有机成核剂、增韧剂和发泡剂，并通过搅拌机构使有机成核剂、增韧剂和发泡剂与RPET树脂充分混合；
S2、将混合有添加剂的RPET树脂加入到挤出机中，并添加多功能团扩链剂，RPET树脂与扩链剂熔融、共混，且RPET树脂与扩链剂在3-5min内快速反应，然后RPET树脂通过挤出机挤出成型有RPET发泡帽舌片材。
10.根据权利要求9所述的一种RPET发泡帽舌，其特征在于：所述搅拌机构包括转动安装在容器内部的转轴，所述转轴的外壁上安装有多组搅拌杆，且容器的底部安装有驱动转轴转动的电机，所述电机的转速设为200-300r/min。