CN116589657B - 一种透气透水可水洗慢回弹海绵 - Google Patents
一种透气透水可水洗慢回弹海绵 Download PDFInfo
- Publication number
- CN116589657B CN116589657B CN202310569224.3A CN202310569224A CN116589657B CN 116589657 B CN116589657 B CN 116589657B CN 202310569224 A CN202310569224 A CN 202310569224A CN 116589657 B CN116589657 B CN 116589657B
- Authority
- CN
- China
- Prior art keywords
- parts
- polyol
- slow rebound
- modified
- sponge
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及海绵技术领域，具体是一种透气透水可水洗慢回弹海绵，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇60～85份、改性慢回弹聚醚多元醇10～35份、改性聚合物多元醇10～30份、链扩展剂0.5～1.2份、扩链交联剂0.3～1份、催化剂0.8～1.5份、发泡剂1.5～3份、匀泡剂0.5～2份、硅油0.8～1.6份、改性异氰酸酯40～65份。本发明通过一定质量份数的特种聚酯醚多元醇、改性慢回弹聚醚多元醇、改性聚合物多元醇、链扩展剂、扩链交联剂、催化剂、发泡剂、匀泡剂、硅油和改性异氰酸酯发泡制备得到具有矢量纤维效果的海绵，保证舒适度的同时还具有透气、透水且能够水洗的特性，具有绿色环保、健康功能，有很好的实用性和市场前景。
Description
技术领域
本发明涉及海绵技术领域，具体是一种透气透水可水洗慢回弹海绵。
背景技术
慢回弹海绵又称记忆绵具有良好的温感性，能够根据人体的不同部位的温度提供适合的软硬程度，当受压而下陷时，不会表现出强烈的反弹力，而是当压力移除后慢慢恢复原状，这样可以很好的将人体与其接触点的压力均衡分散，达到最舒适的状态，但是传统慢回弹海绵的透气及透水性能较差，导致产品容易滋生各类细菌，并且不能水洗。
然而随着生活水平的提高，人们也日益注重生活质量，因此，研发既能保持记忆绵材料的柔软舒适，又具有绿色环保、健康功能的替代材料，将具有很好的实用性和市场前景。
发明内容
本发明的目的是提供一种透气透水可水洗慢回弹海绵，通过一定质量份数的特种聚酯醚多元醇、改性慢回弹聚醚多元醇、改性聚合物多元醇、链扩展剂、扩链交联剂、催化剂、发泡剂、匀泡剂、硅油和改性异氰酸酯发泡制备得到具有矢量纤维效果的海绵，保证舒适度的同时还具有透气、透水且能够水洗的特性。
为解决上述技术问题，本发明提供了一种透气透水可水洗慢回弹海绵，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇60～85份、改性慢回弹聚醚多元醇10～35份、改性聚合物多元醇10～30份、链扩展剂0.5～1.2份、扩链交联剂0.3～1份、催化剂0.8～1.5份、发泡剂1.5～3份、匀泡剂0.5～2份、硅油0.8～1.6份、改性异氰酸酯40～65份。
进一步的，所述特种聚酯醚多元醇以官能度3，分子量为3000的聚酯醚多元醇为基础聚醚，通过调整接枝不同比例的环氧乙烷和环氧丙烷聚合而成。
进一步的，所述环氧乙烷与所述环氧丙烷的质量比为35∶55～45∶65。
进一步的，所述环氧乙烷与所述环氧丙烷的质量比为40∶60。
进一步的，所述改性慢回弹聚醚多元醇通过调整不同慢回弹聚醚组分制备，并同步改变玻璃化转变温度，玻璃化转变温度范围为20～33℃。
进一步的，所述不同慢回弹聚醚组分包括质量分数为20～40%的分子量为1000的聚醚多元醇、质量分数为20～40%的分子量为700的聚醚多元醇和剩余质量分数的分子量为1200的聚醚多元醇。
进一步的，所述改性聚合物多元醇为苯乙烯、丙烯腈与聚醚多元醇的接枝共聚物。
进一步的，所述改性异氰酸酯为质量份数10～20的甲苯二异氰酸酯和质量份数40～60的亚甲基二苯基异氰酸酯的混合物。
本发明的有益效果是：
本发明通过一定质量份数的特种聚酯醚多元醇、改性慢回弹聚醚多元醇、改性聚合物多元醇、链扩展剂、扩链交联剂、催化剂、发泡剂、匀泡剂、硅油和改性异氰酸酯发泡制备得到具有矢量纤维效果的海绵，且该海绵具有透气、透水且能够水洗的特性，回弹性好、舒适度强，压缩变形损失小，另外应用机洗时，能至少机洗10次以上，强度能满足使用者的需求。
实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例
一种透气透水可水洗慢回弹海绵，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇75份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；
其中，特种聚酯醚多元醇以官能度3，分子量为3000的聚酯醚多元醇为基础聚醚，通过调整接枝不同比例的环氧乙烷和环氧丙烷聚合而成，本实施例中环氧乙烷与环氧丙烷的质量比为40∶60；
改性慢回弹聚醚多元醇通过调整不同慢回弹聚醚组分制备，并同步改变玻璃化转变温度为20～33℃；其中，不同慢回弹聚醚组分包括质量分数为30%的分子量为1000的聚醚多元醇、质量分数为30%的分子量为700的聚醚多元醇和剩余质量分数的分子量为1200的聚醚多元醇；
其中，改性聚合物多元醇为苯乙烯、丙烯腈与聚醚多元醇的接枝共聚物；
其中，改性异氰酸酯为质量份数18的甲苯二异氰酸酯和质量份数55的亚甲基二苯基异氰酸酯的混合物；
本发明的透气透水可水洗慢回弹海绵通过发泡、整形、切割等工序的配合来制备，其中，在对海绵进行整形时，通过侧面板、输送带的输送速度、原料的输入量控制、降落板的升降高度以及降落板的板型等多方面的控制来实现对海绵的宽度、密度、高度、顶面形状的多方面的控制，确保海绵整形后能够满足多项需求，减少后续的二次整形。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇75.2份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇75.4份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇75.6份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇75.8份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇76份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇76.2份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇76.4份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇76.6份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
实施例
一种透气透水可水洗慢回弹海绵，与实施例1不同在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇76.8份、改性慢回弹聚醚多元醇20份、改性聚合物多元醇20份、链扩展剂0.7份、扩链交联剂0.8份、催化剂1份、发泡剂2份、匀泡剂1.2份、硅油1.2份、改性异氰酸酯55份；其余各原料制备方法与实施例1相同，故此不再赘述。
针对上述实施例1-实施例10，制备得到的透气透水可水洗慢回弹海绵的基本物理性能测试结果如表1所示：
表1
针对上述实施例1-实施例10，制备得到的透气透水可水洗慢回弹海绵的透气透水性能的测试结果如表2所示：
表2
结合表1和表2可知，本实施例1至实施例10的海绵的物理性能不仅符合目标市场应用的物理性能要求，还能实现透气、透水、水洗的特性，且水洗后物理性能的损失达到最小；其中，海绵密度均大于40，回弹性好、舒适度强，压缩变形损失小，另外应用机洗时，能至少机洗10次以上，强度能满足使用者的需求。
本发明的透气透水可水洗慢回弹海绵具有湿张度高、矢量纤维的效果，具有透气、透水、可水洗的功能，本发明既能保持记忆绵材料的柔软舒适，又具有绿色环保、健康功能，有很好的实用性和市场前景。
以上所揭露的仅为本发明的几种实施例而已，当然不能以此来限定本发明之权利范围，因此依本发明权利要求所作的等同变化，仍属本发明所涵盖的范围。
Claims (3)
1.一种透气透水可水洗慢回弹海绵，其特征在于，由以下质量份数原料发泡而成，包括特种聚酯醚多元醇60～85份、改性慢回弹聚醚多元醇10～35份、改性聚合物多元醇10～30份、链扩展剂0.5～1.2份、扩链交联剂0.3～1份、催化剂0.8～1.5份、发泡剂1.5～3份、匀泡剂0.5～2份、硅油0.8～1.6份、改性异氰酸酯40～65份；
所述特种聚酯醚多元醇以官能度3，分子量为3000的聚酯醚多元醇为基础聚醚，通过调整接枝不同比例的环氧乙烷和环氧丙烷聚合而成；所述改性异氰酸酯为质量份数10～20的甲苯二异氰酸酯和质量份数40～60的亚甲基二苯基异氰酸酯的混合物；
所述改性慢回弹聚醚多元醇通过调整不同慢回弹聚醚组分制备，并同步改变玻璃化转变温度，所述不同慢回弹聚醚组分包括质量分数为20～40%的分子量为1000的聚醚多元醇、质量分数为20～40%的分子量为700的聚醚多元醇和剩余质量分数的分子量为1200的聚醚多元醇；
所述改性聚合物多元醇为苯乙烯、丙烯腈与聚醚多元醇的接枝共聚物。
2.根据权利要求1所述的一种透气透水可水洗慢回弹海绵，其特征在于，所述环氧乙烷与所述环氧丙烷的质量比为35∶55～45∶65。
3.根据权利要求2所述的一种透气透水可水洗慢回弹海绵，其特征在于，所述环氧乙烷与所述环氧丙烷的质量比为40∶60。