CN116355443A - 一种隔热保温的环保涂料 - Google Patents
一种隔热保温的环保涂料 Download PDFInfo
- Publication number
- CN116355443A CN116355443A CN202310278653.5A CN202310278653A CN116355443A CN 116355443 A CN116355443 A CN 116355443A CN 202310278653 A CN202310278653 A CN 202310278653A CN 116355443 A CN116355443 A CN 116355443A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- environment
- insulating
- friendly paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及环保涂料技术领域，且公开了一种隔热保温的环保涂料，所述环保涂料由以下成分组成：珍珠岩20‑40份、石棉绒10‑20份、胶粘剂2‑8份、海泡石2‑12份、玻璃微珠1‑4份、硅酸铝10‑18份、多孔粉石英4‑8份、渗透剂2‑8份、漂珠和聚乙烯醇缩甲醛水溶液3‑5份。该隔热保温的环保涂料，生产工艺简单，操作方便，制作不受季节的限制，且无污染；导热系数小，保温隔热性能好，还可具有防水性能，因而用量明显减少，所需保温厚度为传统保温材料的1/3‑1/5，图层的减薄还易于探伤，可准确地发现保温层内设备故障的位置，该环保涂料适用面较广，能够通过多种方式来进行使用，操作起来比较简单。
Description
技术领域
本发明涉及环保涂料技术领域，具体为一种隔热保温的环保涂料。
背景技术
环保涂料是指涂料产品的性能指标，安全指标在符合各自产品标准的前提下，符合国家环境标志产品提出的技术要求的涂料产品，称为环保涂料的涂料产品亦称为绿色产品。
目前的一些环保涂料在制备时，其工艺比较复杂，容易受到季节的限制，且制得的涂料中含有一定的污染，环保性能不佳，且隔热性能也不是很好，为此我们提出了一种隔热保温的环保涂料。
发明内容
针对现有技术的不足，本发明提供了一种隔热保温的环保涂料，解决了目前的一些环保涂料环保隔热性能不是很好的问题。
为实现上述目的，本发明提供如下技术方案：一种隔热保温的环保涂料，所述环保涂料由以下成分组成：珍珠岩20-40份、石棉绒10-20份、胶粘剂2-8份、海泡石2-12份、玻璃微珠1-4份、硅酸铝10-18份、多孔粉石英4-8份、渗透剂2-8份、漂珠和聚乙烯醇缩甲醛水溶液3-5份。
优选的，所述多孔粉石英是一种火烧毁沉积岩，该产品自然粒径细，为0.5μm左右，颗粒分布均匀，外形结构近似球型无棱角状，其表面全是纳米级的介孔。
优选的，所述玻璃微珠由碱石灰硼硅玻璃制成，强度高、密度低，它们是无孔的，具有化学稳定性、出色的防水性和防油性。
优选的，所述环保涂料的使用方式为刷涂、滚涂、浸涂或者喷涂，该环保涂料对于物面的细孔很容易渗透，可以加强对物面的附着力。
优选的，所述环保涂料有高温下隔热保温效果好，防水防裂、防火隔音、阻燃绝缘、耐磨抗酸碱、重量轻、施工方便、使用寿命长的特点。
优选的，所述环保涂料可涂覆于化工、冶金、建筑、石油等介质温度为-40-700℃任何形状、尺寸的设备用于保温，在涂覆时，先用自来水浸泡1-2h并搅拌均匀。
优选的，所述制备方法如下：
S1、将聚乙烯醇甲醛水溶液、胶粘剂同时投入蒸馏釜中进行搅拌；
S2、将石棉绒、硅酸铝同时投入到烘干箱的内部进行烘干，烘干时的温度控制在100-150℃；
S3、将加热烘干的石棉绒、硅酸铝投入到双向搅拌机中进行双向搅拌，再将聚乙烯醇甲醛水溶液、胶粘剂混合液一次投入到搅拌机中，先低速搅拌，再高速搅拌；
S4、最后将珍珠棉、海泡石、多孔粉石英、渗透剂、玻璃微珠、漂珠依次分别加入到搅拌机的内部进行搅拌。
有益效果如下：
该隔热保温的环保涂料，生产工艺简单，操作方便，制作不受季节的限制，且无污染；导热系数小，保温隔热性能好，还可具有防水性能，因而用量明显减少，所需保温厚度为传统保温材料的1/3-1/5，图层的减薄还易于探伤，可准确地发现保温层内设备故障的位置，该环保涂料适用面较广，能够通过多种方式来进行使用，操作起来比较简单。
具体实施方式
基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明提供一种技术方案：一种隔热保温的环保涂料，所述环保涂料由以下成分组成：珍珠岩20份、石棉绒10份、胶粘剂2份、海泡石2份、玻璃微珠1份、硅酸铝10份、多孔粉石英4份、渗透剂2份、漂珠和聚乙烯醇缩甲醛水溶液3份。
所述多孔粉石英是一种火烧毁沉积岩，该产品自然粒径细，为0.5μm左右，颗粒分布均匀，外形结构近似球型无棱角状，其表面全是纳米级的介孔，所述玻璃微珠由碱石灰硼硅玻璃制成，强度高、密度低，它们是无孔的，具有化学稳定性、出色的防水性和防油性，所述环保涂料的使用方式为刷涂、滚涂、浸涂或者喷涂，该环保涂料对于物面的细孔很容易渗透，可以加强对物面的附着力，所述环保涂料有高温下隔热保温效果好，防水防裂、防火隔音、阻燃绝缘、耐磨抗酸碱、重量轻、施工方便、使用寿命长的特点，所述环保涂料可涂覆于化工、冶金、建筑、石油等介质温度为-40-700℃任何形状、尺寸的设备用于保温，在涂覆时，先用自来水浸泡1-2h并搅拌均匀，所述制备方法如下：
S1、将聚乙烯醇甲醛水溶液、胶粘剂同时投入蒸馏釜中进行搅拌；
S2、将石棉绒、硅酸铝同时投入到烘干箱的内部进行烘干，烘干时的温度控制在100-150℃；
S3、将加热烘干的石棉绒、硅酸铝投入到双向搅拌机中进行双向搅拌，再将聚乙烯醇甲醛水溶液、胶粘剂混合液一次投入到搅拌机中，先低速搅拌，再高速搅拌；
S4、最后将珍珠棉、海泡石、多孔粉石英、渗透剂、玻璃微珠、漂珠依次分别加入到搅拌机的内部进行搅拌。
实施例2
本发明提供一种技术方案：一种隔热保温的环保涂料，所述环保涂料由以下成分组成：珍珠岩30份、石棉绒15份、胶粘剂5份、海泡石7份、玻璃微珠2.5份、硅酸铝14份、多孔粉石英6份、渗透剂5份、漂珠和聚乙烯醇缩甲醛水溶液4份。
所述多孔粉石英是一种火烧毁沉积岩，该产品自然粒径细，为0.5μm左右，颗粒分布均匀，外形结构近似球型无棱角状，其表面全是纳米级的介孔，所述玻璃微珠由碱石灰硼硅玻璃制成，强度高、密度低，它们是无孔的，具有化学稳定性、出色的防水性和防油性，所述环保涂料的使用方式为刷涂、滚涂、浸涂或者喷涂，该环保涂料对于物面的细孔很容易渗透，可以加强对物面的附着力，所述环保涂料有高温下隔热保温效果好，防水防裂、防火隔音、阻燃绝缘、耐磨抗酸碱、重量轻、施工方便、使用寿命长的特点，所述环保涂料可涂覆于化工、冶金、建筑、石油等介质温度为-40-700℃任何形状、尺寸的设备用于保温，在涂覆时，先用自来水浸泡1-2h并搅拌均匀，所述制备方法如下：
S1、将聚乙烯醇甲醛水溶液、胶粘剂同时投入蒸馏釜中进行搅拌；
S2、将石棉绒、硅酸铝同时投入到烘干箱的内部进行烘干，烘干时的温度控制在100-150℃；
S3、将加热烘干的石棉绒、硅酸铝投入到双向搅拌机中进行双向搅拌，再将聚乙烯醇甲醛水溶液、胶粘剂混合液一次投入到搅拌机中，先低速搅拌，再高速搅拌；
S4、最后将珍珠棉、海泡石、多孔粉石英、渗透剂、玻璃微珠、漂珠依次分别加入到搅拌机的内部进行搅拌。
实施例3
本发明提供一种技术方案：一种隔热保温的环保涂料，所述环保涂料由以下成分组成：珍珠岩40份、石棉绒20份、胶粘剂8份、海泡石12份、玻璃微珠4份、硅酸铝18份、多孔粉石英8份、渗透剂8份、漂珠和聚乙烯醇缩甲醛水溶液5份。
所述多孔粉石英是一种火烧毁沉积岩，该产品自然粒径细，为0.5μm左右，颗粒分布均匀，外形结构近似球型无棱角状，其表面全是纳米级的介孔，所述玻璃微珠由碱石灰硼硅玻璃制成，强度高、密度低，它们是无孔的，具有化学稳定性、出色的防水性和防油性，所述环保涂料的使用方式为刷涂、滚涂、浸涂或者喷涂，该环保涂料对于物面的细孔很容易渗透，可以加强对物面的附着力，所述环保涂料有高温下隔热保温效果好，防水防裂、防火隔音、阻燃绝缘、耐磨抗酸碱、重量轻、施工方便、使用寿命长的特点，所述环保涂料可涂覆于化工、冶金、建筑、石油等介质温度为-40-700℃任何形状、尺寸的设备用于保温，在涂覆时，先用自来水浸泡1-2h并搅拌均匀，所述制备方法如下：
S1、将聚乙烯醇甲醛水溶液、胶粘剂同时投入蒸馏釜中进行搅拌；
S2、将石棉绒、硅酸铝同时投入到烘干箱的内部进行烘干，烘干时的温度控制在100-150℃；
S3、将加热烘干的石棉绒、硅酸铝投入到双向搅拌机中进行双向搅拌，再将聚乙烯醇甲醛水溶液、胶粘剂混合液一次投入到搅拌机中，先低速搅拌，再高速搅拌；
S4、最后将珍珠棉、海泡石、多孔粉石英、渗透剂、玻璃微珠、漂珠依次分别加入到搅拌机的内部进行搅拌。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种隔热保温的环保涂料，其特征在于：所述环保涂料由以下成分组成：珍珠岩20-40份、石棉绒10-20份、胶粘剂2-8份、海泡石2-12份、玻璃微珠1-4份、硅酸铝10-18份、多孔粉石英4-8份、渗透剂2-8份、漂珠和聚乙烯醇缩甲醛水溶液3-5份。
2.根据权利要求1所述的一种隔热保温的环保涂料，其特征在于：所述多孔粉石英是一种火烧毁沉积岩，该产品自然粒径细，为0.5μm左右，颗粒分布均匀，外形结构近似球型无棱角状，其表面全是纳米级的介孔。
3.根据权利要求1所述的一种隔热保温的环保涂料，其特征在于：所述玻璃微珠由碱石灰硼硅玻璃制成，强度高、密度低，它们是无孔的，具有化学稳定性、出色的防水性和防油性。
4.根据权利要求1所述的一种隔热保温的环保涂料，其特征在于：所述环保涂料的使用方式为刷涂、滚涂、浸涂或者喷涂，该环保涂料对于物面的细孔很容易渗透，可以加强对物面的附着力。
5.根据权利要求1所述的一种隔热保温的环保涂料，其特征在于：所述环保涂料有高温下隔热保温效果好，防水防裂、防火隔音、阻燃绝缘、耐磨抗酸碱、重量轻、施工方便、使用寿命长的特点。
6.根据权利要求1所述的一种隔热保温的环保涂料，其特征在于：所述环保涂料可涂覆于化工、冶金、建筑、石油等介质温度为-40-700℃任何形状、尺寸的设备用于保温，在涂覆时，先用自来水浸泡1-2h并搅拌均匀。
7.一种根据权利要求1所述的隔热保温的环保涂料的制备方法，其特征在于：所述制备方法如下：
S1、将聚乙烯醇甲醛水溶液、胶粘剂同时投入蒸馏釜中进行搅拌；
S2、将石棉绒、硅酸铝同时投入到烘干箱的内部进行烘干，烘干时的温度控制在100-150℃；
S3、将加热烘干的石棉绒、硅酸铝投入到双向搅拌机中进行双向搅拌，再将聚乙烯醇甲醛水溶液、胶粘剂混合液一次投入到搅拌机中，先低速搅拌，再高速搅拌；
S4、最后将珍珠棉、海泡石、多孔粉石英、渗透剂、玻璃微珠、漂珠依次分别加入到搅拌机的内部进行搅拌。