CN115701977A - 包含烷基烯酮化合物的毛发或纤维处理用组合物 - Google Patents
包含烷基烯酮化合物的毛发或纤维处理用组合物 Download PDFInfo
- Publication number
- CN115701977A CN115701977A CN202180044511.1A CN202180044511A CN115701977A CN 115701977 A CN115701977 A CN 115701977A CN 202180044511 A CN202180044511 A CN 202180044511A CN 115701977 A CN115701977 A CN 115701977A
- Authority
- CN
- China
- Prior art keywords
- hair
- fiber
- acid
- composition
- alkyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种包含烷基烯酮化合物的毛发或纤维处理用组合物。本发明的组合物包含能够与毛发或纤维表面的蛋白质残基共价结合的烷基烯酮化合物,并且上述烷基烯酮化合物在毛发或纤维上形成共价键,从而可以提供长时间持续的调理等有益的效果。
Description
技术领域
本发明涉及一种包含烷基烯酮化合物的毛发或纤维处理用组合物。
背景技术
通常,毛发化妆品的目的在于为了通过赋予毛发光滑、柔软、容易梳理、丰盈感、顺滑、造型等有益的特性来美化毛发、增加魅力、改变容貌并且保持毛发健康,以对毛发进行涂布、散布和其他与之类似的方法使用。
毛发的调理必须是持续的过程。头发基本上可以说是从深存于皮肤表面的少数活细胞衍生出来的基本死亡的细胞。因此,毛发调理成分对实质的细胞的生长没有任何影响,并且不会影响根源细胞的修复。因此,毛发的调理暂时提高受损的毛发的特性,一旦去除上述调理,就必须重新应用。
物理化学处理引起的毛发的损伤会诱发毛发的物理结构变更。调理成分虽然无法从根本上治愈毛发,但在利用清洗剂清洗并去除调理剂之前,可以暂时提高毛发的化妆学价值和功能。因此,调理成分的非常重要的特性是,即使使用清洗剂也不会被去除,在毛发上残留更长时间并使其效果持续。
大部分的毛发损伤是由以美容为目的的洗发、干燥、梳理、造型、调理、烫发等毛发打理的习惯、对化学物质的暴露以及阳光、大气污染、风、海水和氯化游泳池等环境因素引起的。调理剂可以通过减少静电、提高毛发强度、保护免受紫外线辐射以及增加光泽等多种形式的机理来提高风化的毛发的化妆学价值。
在本发明中,毛发处理包括通过减少毛发的断裂和多孔性并增加强度和光泽来缓解或防止、恢复因热、染发、烫发、清洗、紫外线等的多种损伤因素造成的毛发的损伤。使用阳离子表面活性剂或阳离子聚合物成分的调理剂由于具有直接参与表面活性剂或聚合物与毛发表面的相反电荷之间的电相互作用的亲和性,因此是非常有效的调理成分。调理剂通常残留在发丝的表面,从而减少对梳理的摩擦力和毛发翘起现象,并使毛发的触感变得柔顺和柔软。在其他一部分系统中,调理剂赋予强化丰盈、保持卷曲、毛发的浓密感、容易梳理性等,并且这些特性也包括在本发明的毛发处理中。
另外,最近的调理剂被设计成提供以下功能中的一种以上的功能:对湿和干燥状态的毛发提供容易梳理性、通过填补并重新整理毛发损伤部分来提供柔顺感、使多孔性最小化、通过赋予头发光泽来赋予丝滑(Silky)的触感、提供对热和机械损伤的保护功能、保湿、赋予丰盈和厚重的感觉、去除静电,并且这些特性也包括在本发明的毛发处理中。
通常,人的毛发表皮(cuticle)由平坦重叠的细胞(鳞片)构成。表皮细胞像屋顶的瓦片一样附着于毛发纤维的根部至尾部。各表皮层的厚度为约0.3~0.5μm,其中看得见的表皮的部分为约5~10μm左右。人的毛发的表皮一般层叠有5~10层。毛发的各表皮细胞由上表皮(epicuticle)、A-层(A-layer)、外表皮(exocuticle)、内表皮(endocuticle)、内层(inner layer)等多种亚层(sublamella)和细胞膜复合体(cell membrane complex)构成。最外层的上表皮层由共价结合的脂质(脂肪酸)覆盖,脂质中包含最多的成分是18-甲基二十烷酸(18-Methyl Eicosanoic Acid,18-MEA)。该层构成表皮细胞膜复合体(cellmembrane complex)的外层β-层(β-layer),起到润滑、减少摩擦、形成疏水性表面等作用。
在毛发中,露出头皮之外的部分称为毛干,该部分根据毛发的寿命和长度而变化。另外,剪发时、使用洗发液、吹风机时、梳理时或使用烫发剂、染发剂等时,或根据干燥、紫外线、海水、游泳池的石灰粉等的环境压力而变化。特别是,包围毛干外部的毛小皮,即使不直接受到这种压力的影响,但综合累积时还是会受到损伤。对于受损的毛发,毛小皮的尾部会凸出或部分剥离而脱落一层。这种毛发由于散射光,因此失去光泽,且不光滑。如果毛发的损伤进一步加剧,则毛小皮层会完全脱落,从而露出内部的毛皮质,最终导致毛发劈叉或易断。
为了改善像这样18-MEA丢失而受损的毛发的表面,正在尝试多种处理。特别是,使用有机硅涂覆毛发表面的头发美容或护发精华等提供毛发调理效果的产品正在销售或者通过美容院实施。但是,当将这种调理成分用于毛发时,仅提供暂时的、短期的效果至处理后的下一次清洗之前,始终存在清洗后还需再次处理的不便。
专利文献1涉及皮肤或毛发用非水系个人护理产品,公开了一种具有选自由碳酸酯(carbonate)、乙醛(aldehyde)、丙醛(propionaldehyde)、丁醛(butylaldehyde)、硝基苯基碳酸酯(nitrophenyl carbonate)、氮丙啶(aziridine)、异氰酸酯(isocyanate)、硫氰酸酯(thiocyanate)、环氧化合物(epoxide)、三氟乙基磺酸酯(tresylate)、琥珀酰亚胺(succinimide)、羟基琥珀酰亚胺酯(hydroxysuccinimidyl ester)、咪唑(imidazole)、氧羰基咪唑(oxycarbonylamidazole)、亚胺(imine)、硫醇(thiol)、马来酰亚胺(maleimide)、乙烯基砜(vinylsulfone)、乙撑亚胺(ethyleneimine)、硫醚(thioether)、丙烯腈(acrylonitrile)、丙烯酸或甲基丙烯酸酯(acrylic acid or methacrylic ester)、二硫化物(disulfide)、酮(ketone)以及RX表示的官能团(R是选自由烷基、芳基、芳烷基、环和不饱和环组成的组中的任何一种,X是I、Br或Cl)组成的组中的任何一种以上作为能够与毛发或皮肤表面的蛋白质残基共价结合的官能团的调理成分。并且毛发或皮肤用个人护理产品的特征在于,包含上述调理成分,并且分为非水系部分和水系部分,在即将使用之前混合而使用。对于上述提出的多种官能团,对人体有害,或者以在构成毛发或皮肤的蛋白质的氨基酸中含量低的赖氨酸(毛发1.9~3.1%,皮肤角蛋白3.1~6.9%)或半胱氨酸(毛发16.6~18%,皮肤角蛋白2.3~3.8%)作为靶进行反应,因此,反应效率降低,存在需要将每个物质分别单独合成的问题。
在本发明中,纤维处理剂的功能是指赋予纤维柔软效果;防止光引起的损伤;抑制纤维的褶皱形成或者使得容易去除已形成的褶皱;使纤维固有颜色鲜明;使固有颜色长时间保持;使表面的污染容易去除;赋予香气;去除异味;抗菌或驱虫;防止洗涤引起的损伤;防止雨水等的渗透等的功能。
在本发明中,纤维处理用组合物通常可以包括用于为了护理纤维的清洗、整理、点缀(point)用等的组合物以及染色、漂白、柔软、杀菌紫外线阻断、芳香、香气等对纤维具有有益功能的组合物。
作为将这种组合物剂型化的产品,可以例举洗剂、柔软剂、纤维漂洗液(rinse)、修护剂(treatment)或部分处理剂等。
作为用于构成这种纤维护理用组合物的一般原料,有油脂、蜡、烃、高级脂肪酸、高级醇、酯油以及硅油等油性原料、阴离子、阳离子、两性、非离子表面活性剂、用作保湿剂、增稠剂和成膜剂的高分子化合物、紫外线吸收和阻断剂、抗氧化剂、金属离子封锁剂、离子交换剂、助洗剂(builder)、漂白剂、酶、气泡调节剂、荧光增白剂、移染防止剂、包括染料和颜料的色材、香料和防腐剂等。
另外,作为用于提供特殊性能的纤维护理成分,可以包括具有以下功能的成分:赋予纤维柔软效果;防止光引起的损伤;抑制纤维的褶皱形成或者使得容易去除已形成的褶皱;使纤维固有颜色鲜明;使固有颜色长时间保持;使表面的污染容易去除;赋予香气;去除异味;抗菌或驱虫;防止洗涤引起的损伤;防止雨水等的渗透,具体地,可以包括皂(香皂)、烷基苯磺酸盐(alkyl benzene sulfonate)、链烷磺酸盐(alkane sulfonate)、α-烯烃磺酸盐(alpha olefin sulfonate)、α-磺基脂肪酸酯(alpha sulfofatty acid ester)、烷基硫酸盐(alkyl sulfate)、烷基醚硫酸盐(alkyl ether sulfate)、醇乙氧基化物(alcoholethoxylate)、烷基酚乙氧基化物(alkylphenol ethoxylate)、脂肪酸烷醇酰胺(fattyacid alkanolamide)、烷基胺氧化物(alkyl amine oxide)、甲基葡糖酰胺(methylglucamide)、烷基聚葡萄糖苷(alkyl polyglucoside)、二硬脂基二甲基氯化铵(distearyldimethyl ammonium chloride)、咪唑啉鎓衍生物(imidazolinium derivative)、烷基二甲基苯氯化铵(alkyl dimethyl benzene ammonium chloride)、酯季铵盐(esterquat)、氨基酯盐(amino ester salt)、烷基甜菜碱(alkyl betaine)、烷基磺基甜菜碱(alkyl sulfobetaine)、碳酸钠、碳酸钙、硅酸钠、三磷酸钠(sodium triphosphate)、硝基三乙酸(nitrotriacetic acid)、聚羧酸盐(polycarboxylate)、沸石(zeolite)、聚羧酸钠(sodiumpolycarboxylate)、聚丙烯酸钠(sodium polyacrylate)、羟基乙烷二磷酸钠(sodiumhydroxy ethane diphosphate)、过硼酸钠(sodium perborate)、过碳酸钠(sodiumpercarbonate)、过氧化物(peroxide)、次氯酸盐(hypochlorite)、四乙酰乙二胺(tetraacetyl ethylenediamine)、对壬酰氧基苯磺酸钠(sodium para nonanoyloxybenzene sulfonate)、过碳酸钠、过硼酸钠、蛋白酶、脂肪酶、淀粉酶、果胶酶、纤维素酶、羧甲基纤维素(carboxymethyl cellulose)、羧甲基淀粉(carboxymethyl starch)、纤维素醚(cellulose ether)、聚乙烯对苯二甲酸/聚氧乙烯对苯二甲酸共聚物、脂肪酸酰胺(fatty acid amide)、脂肪酸烷醇酰胺(fatty acid alkanol amide)、胺氧化物(amineoxide)、二苯乙烯(stilbene)、香豆素(coumarin)、双吲哚(bisbenzazole)、二苯乙烯基联苯(distyryl biphenyl)、聚乙烯吡咯烷酮(polyvinylpyrrolidone)、聚乙烯吡啶氧化物(polyvinylpyridine oxide)、香料、环糊精(cyclodextrin)、硫酸钠、有机硅及衍生物、烷基胺(alkyl amine)、脂肪醇、脂肪酸、聚乙烯(polyethylene)、氯化镁、氯化钙、氯化钠和醋酸钠等。
但是,当将这种纤维护理成分用于纤维时,仅提供暂时的效果至处理后的下一次清洗之前,始终存在清洗后还需再次处理的不便。
专利文献2公开了一种在具有与羊毛纤维相似的构成成分的毛发上使化妆特性长时间持续的化妆处理方法。在上述技术中,在毛发化妆处理前,需要通过热、电磁波、电场、声波和等离子体等的物理方法或者除还原方法以外的化学方法进行使毛发第一次活化的过程,以使毛发的表面产生变化。但是,这种毛发活化过程需要将热、电磁波、电场、声波和等离子体等高能量施加于毛发,而且作为除还原方法以外的化学非活性物质使用的过氧化氢、溴酸盐(bromate)等的氧化剂对毛发造成严重的损伤。此外,在聚胺或多糖类聚合物的情况下,虽然可以活化,但并不是这些聚合物与毛发进行共价结合的活化状态,因此存在通过清洗容易去除的问题。
另外,在专利文献3中,除了纤维的柔软效果之外,为了使香气的持久性优异且赋予纤维抗菌性,还考虑了使用作为抗菌成分的壳聚糖(chitosan)且将香料微胶囊化而添加的方案。如果如此地将香料处理为微胶囊,则胶囊从外部环境保护作为内部物质(corematerial)的香料,从而提高存储稳定性,因此具有在纤维中的香气持久性优异的优点。相反,由于该香气胶囊也在洗涤过程中大部分被洗掉而不能残留于纤维表面,因此对于仅靠残留在纤维的部分胶囊成分提供其效果,则存在限制,并且经济上也存在所使用的胶囊大部分未能发挥其功能而被漂洗水洗掉的问题。
现有技术文献
专利文献
1.专利文献1.韩国公开专利第2008-0064467号
2.专利文献2.日本公开专利第2004-182731号
3.专利文献3.韩国公开专利第2002-0068427号
发明内容
技术课题
本发明的一个目的是提供一种能够使调理等有益的效果长时间持续而不损伤毛发或纤维的毛发或纤维处理用组合物。
本发明的另一个目的是提供一种能够使毛发或纤维保持余香并强化柔软性、柔顺、疏水性和/或防缩力的毛发或纤维处理用组合物。
技术方案
作为用于解决上述课题的手段,本发明提供了一种毛发或纤维处理用组合物,其包含由下述化学式1表示的烷基烯酮化合物。
<化学式1>
在上述化学式1中,
R1和R2各自独立地是具有1至40个碳原子的饱和或不饱和烷基、或具有1至40个碳原子的饱和或不饱和脂肪酸。
另外,本发明提供了一种毛发或纤维的调理方法,其包括用上述毛发或纤维处理用组合物处理毛发或纤维的步骤。上述方法可以进一步包括热处理步骤。
另外,本发明提供了一种用于防止或改善热损伤的毛发或纤维处理用产品,其包含上述毛发或纤维处理用组合物。
另外,本发明提供了一种包含由上述化学式1表示的烷基烯酮化合物的组合物在制备毛发或纤维处理用产品中的用途。
发明效果
本发明的毛发或纤维处理用组合物含有能够与毛发或纤维的蛋白质残基共价结合的烷基烯酮化合物,因此上述烷基烯酮化合物与上述蛋白质残基形成共价键而不损伤毛发或纤维,并且通过赋予永久性疏水性可以提供长时间持续的调理等有益的效果。
另外,本发明的毛发或纤维处理用组合物可以防止和/或改善热(heat)引起的毛发或纤维的损伤。
另外,本发明的毛发或纤维处理用组合物可以使毛发或纤维保持余香,并且可以强化柔软性、柔顺、疏水性或防缩力。
具体实施方式
本发明涉及一种包含由下述化学式1表示的烷基烯酮化合物的毛发或纤维处理用组合物。
另外,本发明涉及一种包含由下述化学式1表示的烷基烯酮化合物的组合物在制备毛发或纤维处理用产品中的用途。
[化学式1]
在下文中,将具体描述本发明的构成。
本发明的毛发或纤维处理用组合物含有上述烷基烯酮化合物,并且这些烷基烯酮化合物与毛发或纤维形成共价键,从而可以使调理效果最大化并使上述效果长时间持续。另外,可以防止热(heat)引起的毛发或纤维的损伤。即,本发明的毛发或纤维处理用组合物可以用作毛发或纤维的调理组合物。
在本发明中,“调理”效果是指为了通过赋予毛发或纤维容易梳理性、光滑、柔顺、顺滑、润泽和丰盈感等有益的特性来美化毛发或纤维、增加魅力、改变容貌并且保持毛发或纤维健康,以对身体(毛发)或纤维进行涂布、散布、其他与之类似的方法使用,并且作为调理效果,例如,可以例举赋予光泽和润泽、减少静电等。另外,通过使毛发或纤维的表面变为疏水性,防止水分从外部环境渗透到毛发中,而且防止毛发或纤维内部的水分逸出到外部,从而有助于毛发或纤维保持水分。同时,还可以防止毛发或纤维内部的蛋白质成分由于毛发和蛋白质系纤维(羊毛、丝等)的损伤通过清洗而洗脱的现象。因此,还可以期待不仅可以缓解乃至恢复受损的毛发或受损的纤维的症状,而且最终可以预防毛发或纤维的损伤的效果。
在本发明中,调理组合物是指为了毛发或纤维的调理效果而使用的组合物。
本发明中使用的烷基烯酮化合物可以由下述化学式1表示。
[化学式1]
在上述化学式1中,R1和R2可以各自独立地是具有1至40个碳原子的饱和或不饱和烷基、或具有1至40个碳原子的饱和或不饱和脂肪酸。
在本发明中,除非另有说明,“烷基”是指具有指定数量的碳原子的直链、支链或环状烃。
在本发明中,除非另有说明,“脂肪酸”是指具有指定数量的碳原子的羧酸。此时,上述指定数量的碳原子可以具有直链或支链的结构。
在一个具体例中,R1和R2可以各自独立地是具有8至22个碳原子的直链或支链的饱和或不饱和烷基、或具有8至22个碳原子的直链或支链的饱和或不饱和脂肪酸。优选地,可以选自由具有16至18个碳原子的直链的饱和或不饱和烷基和18-MEA(18-甲基二十烷酸)组成的组,最优选地,可以是18-MEA(18-甲基二十烷酸)。
另外,上述R1和/或R2除了上述烷基或脂肪酸之外,还可以包括2-氧杂环丁酮二聚体(2-oxetanone dimer)末端的醇(alcohol)等亲核基团,并且这些醇的烷基可以包括酯(esters)、醚(ethers)等功能性基团。另外,可以包括醇的乙氧基化物(EO/PO加成)或氢化等。
在一个具体例中,烷基烯酮化合物例如可以使用选自由烷基(R1,R2;C12-16)烯酮、氢化牛脂脂肪酸(R1,R2;C12-16)双烯酮(R1,R2;脂肪酸(Fatty acids),牛脂(tallow),氢化的(hydrogenated),二聚体(dimers),双烯酮衍生物(diketene derivatives))、烷基(R1,R2;C14-16)烯酮、烷基(R1,R2;C16-18)烯酮、烷基(R1,R2;C20-22)烯酮、烷基(R1,R2;C14)烯酮、烷基(R1,R2;C16)烯酮、烷基(R1,R2;C18)烯酮、烷基(R1,R2;C22)烯酮、烷基(R1;C14,R2;C16)烯酮、烷基(R1;C16,R2;C14)烯酮、烷基(R1;C16,R2;C18)烯酮、烷基(R1;C18,R2;C16)烯酮、烷基(R1,R2;C18-MEA)烯酮、烷基(R1;C16,R2;C18-MEA)烯酮、烷基(R1;C18,R2;C18-MEA)烯酮、烷基(R1;C22,R2;C18-MEA)烯酮、烷基(R1;C18-MEA,R2;C16)烯酮、烷基(R1;C18-MEA,R2;C18)烯酮和烷基(R1;C18-MEA,R2;C22)烯酮组成的组中的一种以上,但不限于此,并且可以使用多种类型的烷基烯酮化合物。此时,例如,“C12”是指具有12个碳原子的饱和或不饱和烷基,“C12-16”是指由具有12至16个碳原子的饱和或不饱和烷基组成的混合物,“C18-MEA”是指18-MEA(18-甲基二十烷酸)。另外,“烷基(R1;C18,R2;C16)烯酮”是指化学式1的化合物中R1为具有18个碳原子的饱和或不饱和烷基,R2为具有16个碳原子的饱和或不饱和烷基。“烷基(R1,R2;C14)烯酮”是指化学式1的化合物中R1和R2各自为具有14个碳原子的饱和或不饱和烷基。
在一个具体例中,烷基烯酮化合物的含量没有特别限制,并且相对于全部组合物100重量份,其含量可以为0.0001至10重量份、0.01至7重量份或0.1至5重量份。如果上述含量小于0.0001重量份,则难以出现持续的调理效果,而如果超过10重量份,则存在以下问题:上述化合物多于毛发或纤维中存在的反应位置而过度存在,导致与毛发或纤维发生反应后剩余状态的烷基烯酮化合物损失。
这种烷基烯酮化合物应用于毛发或纤维,从而可以与上述毛发或纤维的蛋白质残基形成共价键。由此可以使毛发或纤维的调理效果最大化。
在本发明中,由上述化学式1表示的烷基烯酮化合物可以预先以分散、乳化的形式或胶囊化的形式包含在毛发或纤维处理用组合物中。
当以分散和乳化的形式使用时,组合物可以包含分散剂和乳化剂,并且上述分散剂和乳化剂可以使用常规使用的那些。例如,可以使用月桂基硫酸钠、棕榈酸(palmiticacid)、硬脂酸(stearic acid)等的脂肪酸皂等阴离子表面活性剂、乙氧基化脂肪醇、甘油酯、脂肪酸的脱水山梨糖醇酯等非离子表面活性剂、季铵盐等阳离子表面活性剂以及阳离子淀粉、阳离子纤维素等阳离子聚合物。具体地,作为非离子表面活性剂(乳化剂),可以使用选自由甘油脂肪酸酯、聚氧乙烯脂肪酸酯、聚氧乙烯脱水山梨糖醇脂肪酸酯和聚氧乙烯烷基苯基醚等组成的组中的一种以上,但不限于此。
另外,当以胶囊化的形式使用时,可以通过将烷基烯酮化合物用液态烃、酯油、硅油等稀释,并用明胶、角叉菜胶、琼脂(Agar)、二氧化硅等胶囊化来使用。胶囊化技术不限于所列示例,并且可以应用化妆品中通常使用的剂型化技术。
本发明的组合物可以进一步包含选自由阳离子表面活性剂和阴离子表面活性剂组成的组中的一种以上。通过进一步包含上述成分,可以进一步提高调理效果。
本发明的组合物中,作为阳离子表面活性剂,可以没有限制地使用通常可用于毛发或纤维处理用组合物中的那些,例如,可以使用选自由烷基三甲基铵盐、二烷基二甲基铵盐、烷基二甲基苄基铵盐、酯季铵盐、烷基吡啶鎓盐、烷基咪唑啉鎓盐、烷基胺盐和脂肪酸酰胺基胺盐等组成的组中的一种以上,优选地,可以使用二烷基二甲基铵盐、烷基咪唑啉鎓盐、酯季铵盐,更优选地,可以使用酯季铵盐。
在本发明中,通过将烷基烯酮化合物和阳离子表面活性剂组合而使用,可以帮助使得上述烷基烯酮化合物因烷基烯酮化合物与阳离子表面活性剂的疏水性部分之间的相互作用而更容易地作用于基质。由此预见与各自单独处方而使用时相比可以表现出更加优异的效果,但本发明不限于上述理论。
另外,本发明的组合物中,作为上述阴离子表面活性剂,可以没有限制地使用通常可用于毛发或纤维处理用组合物中的那些,例如,可以使用选自由皂(soap)、烷基硫酸盐、烷基醚硫酸盐、烷基苯磺酸盐、链烷磺酸盐、α-烯烃磺酸盐、α-磺基脂肪酸酯盐、烷基磺基乙酸盐(alkyl sulfoacetate)、烷基磺基琥珀酸盐(alkyl sulfosuccinate)、烷基醚磺基琥珀酸盐(alkyl ether sulfosuccinate)、烷基磷酸盐、烷基醚磷酸盐、烷基醚羧酸盐、酰基乳酸盐(acyl lactate)、酰基牛磺酸盐(acyl taurate)、酰基谷氨酸盐(acyl glutamate)、酰基丙氨酸盐(acyl alaninate)、酰基羟乙基磺酸盐(acyl isethionate)和酰基肌氨酸盐(acyl sarcosinate)等组成的组中的一种以上。优选地,可以使用皂(soap)、烷基醚硫酸盐、烷基苯磺酸盐,更优选地,可以使用烷基苯磺酸盐。
在本发明中,通过将烷基烯酮化合物和阴离子表面活性剂组合而使用,可以帮助阴离子表面活性剂去除基质的脂质等而使得烷基烯酮化合物更容易地作用于基质。由此预见与各自单独处方而使用时相比可以表现出更加优异的效果,但本发明不限于上述理论。
在一个具体例中,阳离子表面活性剂和/或阴离子表面活性剂的含量没有特别限制,并且相对于全部组合物100重量份,其含量可以为0.01至50重量份、1至30重量份或10至20重量份。在上述含量范围内可以赋予更加优异的调理效果。
本发明的组合物可以进一步包括羟乙基-、羟丙基-、羧甲基纤维素等水溶性纤维素衍生物以及淀粉、黄原胶、聚乙烯醇、丙烯酸酯聚合物和羧乙烯基聚合物等分散和乳化稳定剂。
本发明的组合物可以进一步包括香料。上述香料的种类没有特别限制,只要其通常可用于毛发或纤维处理用组合物中即可,并且可以使用log P值为-1.0至4.5的香料。
上述P是分馏系数,表示化合物对两个溶剂的溶解度。例如,P可以是化合物对辛醇的溶解度与化合物对水的溶解度之比。当化合物是亲油性时,P值可能非常大,因此可以用log P值表示。优选地,香的log P值可以为0.5至4.5、0.7至4.5、1.0至4.4或2.0至4.4。
在一个具体例中,香料例如可以包括选自由(2-叔丁基环己基)乙酸酯((2-tert-butylcyclohexyl)acetate)、(3-氧代-2-戊基环戊基)乙酸((3-oxo-2-pentylcyclopentyl)acetic acid)、(E)-4-癸醛((E)-4-decanal)、1-(1,2,3,4,5,6,7,8-八氢-2,3,8,8-四甲基-2-萘基)乙酮(1-(1,2,3,4,5,6,7,8-Octahydro-2,3,8,8-tetramethyl-2-naphthalenyl)ethanone)、(1-(2,6,6-三甲基-1-环己-3-烯基)2-丁烯-1-酮((1-(2,6,6-trimethyl-1-cyclohex-3-enyl)but-2-en1-one)、1-(2,6,6-三甲基-2-环己烯-1-基)戊烯-3-酮(1-(2,6,6-trimethyl-2-cyclohexen-1-yl)penten-3-one)、1,2-二氯乙烷(1,2-Dichloroethane)、1,3,3-三甲基-2-氧杂二环[2.2,2]辛烷(1,3,3-trimethyl-2-oxabicyclo[2,2,2]octane)、1,4-二噁烷(1,4-Dioxane)、1,6己二醇二缩水甘油醚(1,6Hexanediol diglycidyl ether)、1,7,7-三甲基二环[2.2.1]庚-2-基乙酸酯(1,7,7-Trimethylbicyclo[2.2.1]hept-2-yl acetate)、10-十一烯醛(10-undecenal)、17a-羟孕酮(17a-Hydroxyprogesterone)、1-溴乙烷(1-bromoethane)、1-溴戊烷(1-bromopentane)、1-丁醇(1-butanol)、1-丁烯(1-butene)、1-氯己烷(1-chlorohexane)、1-氟辛烷(1-fluorooctane)、1-庚醇(1-heptanol)、1-庚烯(1-heptene)、1-己醇(1-hexanol)、1-己烯(1-hexene)、1-碘丁烷(1-iodobutane)、1-甲氧基-2-丙醇(1-Methoxypropan-2-ol)、1-萘酚(1-Naphthol)、1-壬醇(1-nonanol)、1-辛醇(1-octanol)、1-辛炔(1-octyne)、1-戊醇(1-pentanol)(1.56)、1-戊烯(1-pentene)(2.80)、1-丙醇(1-propanol)(0.25)、2-(2-丁氧基乙氧基)乙醇(2-(2-Butoxyethoxy)ethanol)(0.65)、2-(二甲基氨基)-5,6-二甲基嘧啶-4-醇(2-(dimethylamino)-5,6-dimethylpyrimidin-4-ol)(1.63)、2-(乙氧羰基)苯甲酸(2-(ethoxycarbonyl)benzoic acid)(1.80)、2,2,2-三氯-1-苯基乙醇(2,2,2-trichloro-1-phenylethanol)、2,3-丁二醇(2,3-Butanediol)、2,4,6-三氯苯酚(2,4,6-Trichlorophenol)、2,4-二氯苯酚(2,4-Dichlorophenol)、2,4-二氯苯氧基乙酸(2,4-Dichlorophenoxyacetic acid)、2,4-二羟基-3,6-二甲基苯甲酸(2,4-dihydroxy-3,6-dimethylbenzoic acid)、2,4-二甲基环己-3-烯-1-甲醛(2,4-dimethylcyclohex-3-ene-1-carbaldehyde)、2,6-二甲基-2-庚醇(2,6-dimethyl-2-heptanol)、2-丁醇(2-butanol)、2-丁酮(2-butanone)、2-丁氧基乙醇(2-Butoxyethanol)、2-丁炔(2-butyne)、2-氯苯酚(2-Chlorophenol)、2-甲酚(2-Cresol)、2-癸酮(2-decanone)、2-乙氧基乙醇(2-Ethoxy ethanol)、2-乙基-1-己醇(2-Ethyl-1-hexanol)、2-乙基己烯(2-ethylhexene)、2-庚酮(2-heptanone)、2-己醇(2-hexanol)、2-己酮(2-hexanone)、2-己烯-1-醇(2-hexen-1-ol)、2-羟基苯甲酸(2-Hydroxybenzoic acid)、2-碘丁烷(2-iodobutane)、2-异丙氧基乙醇(2-Isopropoxyethanol)、2-异丙氧基苯酚(2-isopropoxyphenol)、2-MeTHF、2-甲氧基-4-(2-丙烯基)-苯酚(2-methoxy-4-(2-propenyl)-phenol)、2-甲氧基-4-丙基苯酚(2-Methoxy-4-propylphenol)、2-甲氧基-4-乙烯基苯酚(2-Methoxy-4-vinylphenol)、2-甲氧基乙醇(2-Methoxyethanol)、2-甲氧基乙基乙酸酯(2-Methoxyethyl acetate)、2-甲基-1-丁醇(2-methyl-1-butanol)、2-甲基-1-丙醛(2-methyl-1-propanal)、2-甲基-2-丁醇(2-methyl-2-butanol)、2-甲基-2-戊醇(2-methyl-2-pentanol)、2-甲基-2-丙醇(2-methyl-2-propanol)、2-甲基丁基乙酸酯(2-methylbutyl acetate)、2-甲基丁酸(2-methylbutyric acid)、2-甲基丙烷(2-methylpropane)、2-甲基丙酸(2-methylpropionic acid)、2-萘酚(2-Naphthol)、2-萘胺(2-Naphthylamine)、2-硝基-4-苯二胺(2-Nitro-4-Phenylenediamine)、2-壬酮(2-nonanone)、2-辛酮(2-octanone)、2-辛炔(2-octyne)、2-戊酮(2-pentanone)、2-苯氧基乙醇(2-Phenoxyethanol)、2-苯基-1-乙醇(2-phenyl-1-ethanol)、2-苯基苯酚(2-phenylphenol)、2-丙醇(2-propanol)、2-十一酮(2-undecanone)、3(4)-(4-羟基-4-甲基戊基)-3-环己烯-1-甲醛(3and4-(4-Hydroxy-4-methylpentyl)-3-cyclohexene-1-carboxaldehyde)、3-(4-叔丁基苯基)-2-甲基丙醛(3-(4-tert-butylphenyl)-2-methylpropanal(Lilial))、3,4-二甲苯酚(3,4-Xylenol)、3,7-二甲基辛-6-烯-1-醇(3,7-Dimethyloct-6-en-1-ol)、3,7-二甲基辛-2,6-二烯醛(3,7-dimethylocta-2,6-dienal)、3,7-二甲基辛-3-醇(3,7-dimethyloctan-3-ol)、3-甲酚(3-Cresol)、3-己醇(3-hexanol)、3-己酮(3-hexanone)、3-甲基-1-丁醇(3-methyl-1-butanol)、3-甲基-3-戊醇(3-methyl-3-pentanol)、3-甲基丁基乙酸酯(3-methylbutyl acetate)、3-甲基丁酸(3-methylbutyric acid)、3-硝基苯酚(3-Nitrophenol)、3-苯基丁醛(3-phenyl butanal)、3-苯基-1-丙醇(3-Phenyl-1-propanol)、4-(2,6,6-三甲基-1-环己烯-1-基)-3-丁烯-2-酮(4-(2,6,6-trimethyl-1-cyclohexene-1-yl)-3-butene-2-one)、4-(甲硫基)-3,5-二甲苯酚(4-(methylthio)-3,5-xylenol)、4-乙酰氨基苯酚(4-Acetamidophenol)、4-氨基-2-硝基苯酚(4-Amino-2-nitrophenol)、4-氨基苯甲酸(4-Aminobenzoic acid)、4-氨基苯酚(4-Aminophenol)、4-溴苯酚(4-Bromophenol)、4-氯-3-二甲苯酚(4-Chloro-3-xylenol)、4-氯甲酚(4-Chlorocresol)、4-氯苯酚(4-Chlorophenol)、4-甲酚(4-Cresol)、4-氰基苯酚(4-Cyanophenol)、4-乙氧基-4-氧代丁烯酸(4-ethoxy-4-oxobut-2-enoic acid)、4-乙基苯酚(4-Ethyl phenol)、4-庚氧基苯酚(4-Heptyloxyphenol)、4-碘苯酚(4-Iodophenol)、4-甲氧基苯乙酮(4-Methoxy acetophenone)、4-甲氧基苄醇(4-Methoxybenzyl alcohol)、4-甲基戊酸(4-methylpentanoic acid)、4-硝基苯胺(4-Nitroaniline)、4-硝基苯酚(4-Nitrophenol)、4-戊氧基苯酚(4-Pentyloxyphenol)、5-氟尿嘧啶(5-Fluorouracil)、5-己基氧杂环戊烷-2-酮(5-Hexyloxolan-2-one)、乙醛(acetaldehyde)、乙酸(Acetic acid)、丙酮(Acetone)、乙腈(Acetonitrile)、苯乙酮(acetophenone)、乙酰基雪松烯(Acetylcedrene)、乙酰半胱氨酸(Acetylcysteine)、乙酰水杨酸(Acetylsalicylic acid)、烯丙醇(allyl alcohol)、庚酸烯丙酯(allylheptanoate)、α松油醇(alpha terpineol)、异戊巴比妥(Amobarbital)、戊醇(Amyl alcohol)、水杨酸戊酯(Amyl salicylate)、雄烯二酮(Androstenedione)、茴香烯USP(anethole USP)、苯胺(Aniline)、α-松油醇(α-terpineol)、莠去津(Atrazine)、阿托品(Atropine)、久效磷(Azodrin)、巴比妥(Barbital)、苯甲醛(benzaldehyde)、苯(Benzene)、苯佐卡因(Benzocaine)、苯甲酸(Benzoic acid)、2-氨基苯甲酸二盐酸盐(Benzoic acid,2-amino-,dihydrochloride)、二苯甲酮(Benzophenone)、乙酸苄酯(Benzyl acetate)、苄醇(Benzyl alcohol)、苯甲酸苄酯(Benzyl benzoate)、烟酸苄酯(Benzyl nicotinate)、水杨酸苄酯(Benzyl salicylate)、β-松油醇(beta terpineol)、β-雌二醇(Beta-estradiol)、硼酸(Boric Acid)、丁草胺(Butachlor)、丁巴比妥(Butobarbital)、4-羟基苯甲酸丁酯(Butyl4-hydroxybenzoate)、乙酸丁酯(butyl acetate)、丁醇(Butyl alcohol)、烟酸丁酯(Butyl nicotinate)、丁醛(butyraldehyde)、丁酸(Butyric acid)、咖啡因(Caffeine)、二甲基氨基甲酸乙酯(Carbamic acid,dimethyl-,ethylester)、西维因(Carbaryl)、香芹酮(Carvone)、儿茶酚(Catechol)、氯霉素(Chloramphenicol)、氯甲酚(Chlorocresol)、氯仿(Chloroform)、对氯间二甲苯酚(Chloroxylenol)、氯苯那敏(Chlorpheniramine)、肉桂酸(Cinnamic acid)、肉桂醛(Cinnamic aldehyde)、肉桂醇(Cinnamic alcohol)、肉桂基醇(Cinnamyl alcohol)、邻氨基苯甲酸肉桂酯(Cinnamyl anthranilate)、顺式-1,3-二氯丙烯(cis-1,3-Dichloropropene)、顺式-3-己烯基乙酸酯(cis-3-Hexenyl acetate)、顺式-6-壬烯醛(cis-6-nonenal)、顺式-茉莉酮(cis-jasmone)、可待因(Codeine)、脱氧皮质酮(Cortexone)、香豆素(Coumarin)、枯烯(Cumene)、环十二酮(cyclododecanone)、环己烷(cyclohexane)、环己酮(cyclohexanone)、环戊酮(cyclopentanone)、环十一酮(cycloundecanone)、癸醛(decanal)、癸酸(decanoic acid)、去氧皮质酮(Deoxycorticosterone)、氟磷酸二异丙酯(DFP)、脱氢表雄酮(DHEA)、二嗪农(Diazinon)、二氯甲烷(Dichloromethane)、双氯芬酸(Diclofenac)、二乙基醚(Diethyl ether)、马来酸二乙酯(Diethyl maleate)、丙二酸二乙酯(Diethyl malonate)、邻苯二甲酸二乙酯(Diethyl phthalate)、二乙二醇单丁醚(Diethylene glycol monobutyl ether)、二乙二醇单丁醚乙酸酯(Diethylene glycol monobutyl ether acetate)、二乙醚(Diethylether)、二氢芳樟醇(dihydro linalool)、二氢月桂烯醇(Dihydromyrcenol)、二氢-α-松油醇(Dihydro-α-terpineol)、乐果(Dimethoate)、乙酸二甲基苄基原酯(Dimethylbenzyl carbinyl acetate)、碳酸二甲酯(Dimethyl carbonate)、二甲基环己醇(dimethylcyclohexanol)、二甲基乙胺(Dimethylethylamine)、二甲基甲酰胺(Dimethylformamide)、二甲基亚硝胺(Dimethylnitrosamine)、二硝基氯苯(Dinitrochlorobenzene)、二苯醚(diphenyl ether)、二丙二醇甲醚(Dipropylene glycolmethyl ether)、dl-香茅醇(dl-Citronellol)、d-柠檬烯(d-Limonene)、邻苯二甲酸二甲酯(DMP)、E-2-丁烯醛(E-2-butenal)、E-2-己烯醛(E-2-hexenal)、E-2-辛烯(E-2-octene)、乙二醇(Ethylene glycol)、麻黄碱(Ephedrine)、雌二醇(Estradiol)、草蒿脑(Estragole)、雌三醇(Estriol)、雌酮(Estrone)、乙烷(ethane)、乙醇(Ethanol)、乙酸乙酯(Ethylacetate)、乙苯(Ethyl benzene)、乙醚(Ethyl ether)、丙二酸氢乙酯(Ethyl hydrogenmalonate)、烟酸乙酯(Ethyl nicotinate)、乙基香兰素(ethyl Vanillin)、乙苯(ethylbenzene)、乙二醇甲醚(Ethylene glycol methyl ether)、乙炔苯(ethynylbenzene)、桉叶油醇(Eucalyptol)、丁香酚(Eugenol)、丁子香基甲基醚(Eugenylmethyl ether)、flor乙酸酯(flor acetate)、氟他胺(Flutamide)、香叶醇(geraniol)、香叶腈(Geranyl nitrile)、甘油缩甲醛(Glycerol formal)、希蒂莺(Hedione)、庚醛(heptanal)、庚烷(Heptane)、庚酸(Heptanoic acid)、庚醇(Heptanol)、己醛(hexanal)、己酸(Hexanoic acid)、己醇(Hexanol)、马尿酸(Hippuric acid)、盐酸(Hydrochloricacid)、羟基香茅醛(hydroxycitronellal)、布洛芬(Ibuprofen)、吲哚(Indole)、碘甲烷(iodomethane)、异丁香酚(iso eugenol)、异丁酸异丁酯(isobutyl isobutyrate)、水杨酸异丁酯(isobutyl salicylate)、异丁香酚(Isoeugenol)、异戊酸异戊酯(isopentylisovalerate)、异喹啉(Isoquinoline)、乙酰基二聚异常戊烯(koavone)、乳酸(Lacticacid)、绿花芬(LIFFAROME)、芳樟醇(Linalool)、林丹(Lindane)、马拉硫磷(Malathion)、马来酸(Maleic acid)、丙二酸(Malonic acid)、4,4'-亚甲基双(2-氯苯胺)(MbOCA)、间甲酚(m-Cresol)、MDA、哌替啶(Meperidine)、均三甲苯(mesitylene)、甲醇(Methanol)、甲硫威(Methiocarb)、2-(3-氧代-2-戊基环戊基)乙酸甲酯(methyl2-(3-oxo-2-pentylcyclopentyl)acetate)、2-壬炔酸甲酯(Methyl 2-nonynoate)、乙酸甲酯(methylacetate)、邻氨基苯甲酸甲酯(methyl anthranilate)、橡苔(Methyl atrarate)、苯甲酸甲酯(methyl benzoate)、甲基β萘基酮(methyl beta naphthyl ketone)、二氢茉莉酮酸甲酯(Methyl dihydrojasmonate)、甲基异丁基酮(Methyl isobutyl ketone)、N甲基邻氨基苯甲酸甲酯(Methyl N methylanthranilate)、烟酸甲酯(Methyl nicotinate)、丙酸甲酯(methyl propionate)、水杨酸甲酯(Methyl salicylate)、甲基叔丁基醚(Methyl tert-butyl ether)、甲基-4-羟基苯甲酸酯(Methyl-4-hydroxy benzoate)、甲基-4-OH苯甲酸酯(Methyl-4-OH benzoate)、甲基-对硫磷(Methyl-Parathion)、水杨酸甲酯(Methylsalicylate)、吗啡(Morphine)、麝香酮(Musk ketone)、间二甲苯(m-xylene)、N,N-二乙基-间甲苯甲酰胺(N,N-Diethyl-m-toluamide)、萘普生(Naproxen)、正丁烷(n-butane)、正丁醇(n-Butanol)、正癸醇(n-Decanol)、橙花醇(Nerol)、正庚烷(n-heptane)、正庚醇(n-Heptanol)、正己烷(n-Hexane)、正己醇(n-Hexanol)、烟酸正己酯(N-Hexylnicotinate)、烟酰胺(Nicotinamide)、尼古丁(Nicotine)、烟酸(Nicotinic acid)、硝基苯(Nitrobenzene)、硝化甘油(Nitroglycerine)、N-甲基吡咯烷酮(N-Methyl pyrrolidone)、N-甲基氨基甲酸酯(N-methylcarbamate)、正壬醇(n-Nonanol)、正辛醇(n-Octanol)、壬内酯(nonalactone)、壬酸(nonanoic acid)、正戊烷(n-pentane)、正戊醇(n-Pentanol)、N-苯基-2-萘胺(N-Phenyl-2-naphthylamine)、正丙醇(n-Propanol)、正丙氧基乙醇(n-Propoxyethanol)、邻氯甲苯(o-chlorotoluene)、邻甲酚(o-Cresol)、邻甲苯缩水甘油醚(o-cresyl glycidyl ether)、辛醛(octanal)、辛酸(Octanoic acid)、辛醇(Octanol)、橙花醚苯基乙酸乙酯(orange flower ether phenyl ethyl acetate)、邻甲苯胺(o-toluidine)、邻二甲苯(o-xylene)、对氧磷(Paraoxon)、对硫磷(Parathion)、对甲酚(p-Cresol)、戊酸(Pentanoic acid)、戊醇(Pentanol)、苯乙醇(Phenethyl alcohol)、苯巴比妥(Phenobarbital)、苯酚(Phenol)、苯基异己醇(Phenoxanol)、异丁酸苯氧乙酯(phenoxyethyl isobutyrate)、苯乙醇(phenyl ethyl alcohol)、苯丙醇(phenyl propylalcohol)、苯乙醇(Phenylethyl alcohol)、亚胺硫磷(Phosmet)、辛硫磷(Phoxim)、邻苯二甲酸(phthalic acid)、抗蚜威(Pirimicarb)、孕烯醇酮(Pregnenolone)、黄体酮(Progesterone)、庚酸2-丙烯酯(prop-2-enyl heptanoate)、丙烷(propane)、丙烯醛(propenal)、丙烯(propene)、丙醛(propionaldehyde)、丙酸(propionic acid)、残杀威(Propoxur)、普萘洛尔(Propranolol)、乙酸丙酯(propyl acetate)、丁酸丙酯(propylbutyrate)、甲酸丙酯(propyl formate)、碳酸亚丙酯(Propylene carbonate)、丙二醇(Propylene glycol)、对叔丁基-α-甲基氢化肉桂醛(p-t-Butyl-α-methylhydrocinnamicaldehyde)、对二甲苯(p-Xylene)、吡啶(Pyridine)、间苯二酚(Resorcinol)、黄樟素(Safrole)、水杨酸(Salicylic acid)、东莨菪碱(Scopolamine)、苯乙烯(Styrene)、松油烯-4-醇(terpinen-4-ol)、叔丁醇(tert-Butanol)、睾酮(Testosterone)、四氢呋喃(Tetrahydrofuran)、四氢芳樟醇(Tetrahydrolinalool)、茶碱(Theophylline)、百里酚(Thymol)、甲苯(Toluene)、三乙酸甘油酯(Triacetin)、三氯甲烷(Trichloromethane)、乙酸三氯甲基苯基原酯(Trichloromethyl phenyl carbinyl acetate)、三氯吡氧乙酸(Triclopyr)、乙酸三环十二烯酯(Tricyclododecenyl Acetate)、三乙醇胺(Triethanolamine)、三氟乙酸(Trifluoroacetic acid)、三甲胺(Trimethylamine)、十一酸(undecanoic acid)、戊酸(valeric acid)、香兰素(vanillin)和α-甲基-1,3-苯并二氧杂环戊烯-5-丙醛(α-Methyl-1,3-benzodioxole-5-propionaldehyde)组成的组中的一种以上的化合物。
在一个具体例中,香料的含量没有特别限制,并且相对于全部组合物100重量份,可以为0.0001至30重量份。
另外,为了附带地增加稳定和调理效果,本发明的组合物可以进一步包括脂肪酸、脂肪醇、阳离子淀粉、阳离子纤维素、阳离子瓜尔胶、阳离子丙烯酸酯和丙烯酰胺、聚乙烯吡咯烷酮等的阳离子聚合物和有机硅等。另外,为了剂型化,可以进一步包括溶剂、表面活性剂、增稠剂、稳定剂、防腐剂、着色剂、pH调节剂、金属离子封锁剂、珠光剂、外观改善剂、颜料和粉体颗粒等用于制剂化的成分。
当本发明的组合物用作毛发处理用组合物、即毛发调理化妆品组合物时,剂型没有特别限制,并且可以包括洗发液、润发液(rinse)、修护液(treatment)、发膜、护发精华、蜡、凝胶和喷剂等的所有剂型。
另外,当本发明的组合物用作纤维处理用组合物时,通常可以包括赋予用于护理纤维的清洗、整理、点缀(point)用等的功能的成分以及染色、漂白、柔软、杀菌紫外线阻断、芳香、香气等的对纤维赋予有益功能的成分。上述纤维处理用组合物的剂型没有特别限制,并且作为应用例,可以例举洗剂、柔软剂、纤维漂洗液、修护剂和部分处理剂等产品。
本发明的组合物中包含的上述提及的成分各自优选地可以在不超过各国政府规定的规范中明示的最大使用量的范围内包含在本发明的组合物中。例如,在提供药学组合物的情况下,可以在韩国、美国、欧洲、德国、日本、中国等中规定的药典(Pharmacopoeia)或医药品集中明示的制备方法、性状、使用量等的范围内包含在本发明中。另外,在提供化妆料组合物的情况下,可以在不超过各国政府规定的化妆品安全相关的法律或中国政府规定的《化妆品安全技术规范》中明示的最大使用量的范围内包含在本发明的化妆料组合物中。
另外,本发明涉及一种用上述毛发或纤维处理用组合物处理毛发或纤维的调理方法。
在本发明中,处理可以使用涂布、散布、其他与之类似的方法。
当用本发明的毛发或纤维处理用组合物处理毛发或纤维时,由化学式1表示的烷基烯酮化合物与毛发或纤维的蛋白质残基形成共价键。由此可以赋予毛发或纤维永久性疏水性并使调理效果持续。
上述烷基烯酮化合物的活性基团(内酯环)可以以通过与毛发或纤维中的羟基发生酯化反应而固定的共价键的形式结合至毛发或纤维。具体地,烷基烯酮化合物与羟基形成共价键,从而可以赋予表面疏水性,增强刚性并且不损害柔软性。
在本发明中,处理温度、即用本发明的毛发或纤维处理用组合物处理毛发或纤维时的温度没有特别限制,并且可以在20至250℃下处理,优选地可以在30至230℃下处理,更优选地可以在80至120℃下处理。在上述温度范围内,可以通过提高化合物与毛发或纤维之间的永久性结合效率来提供持续的调理效果。
作为一例,本发明的组合物可以防止和/或改善热(heat)引起的毛发或纤维的损伤。
另外,作为一例,本发明的组合物使毛发或纤维保持余香,另外,可以强化毛发或纤维的柔软性、柔顺、疏水性和/或防缩力。
实施方式
在下文中,通过实施例详细描述本发明。以下实施例仅用于例示本发明,并且本发明的范围不限于以下实施例。本发明的实施例是为了使本发明的公开完全并且向本发明所属技术领域的普通技术人员完整地描述本发明的范畴而提供的,并且本发明仅由权利要求的范畴来限定。
在下文中,本发明的实施例和比较例中使用的物质从常规原料采购处购买并使用。
实施例
制备例1.制备毛发处理用组合物(实施例1至8和比较例1至6)
制备了包含下表1和表2的成分的毛发处理用组合物(实施例1至8和比较例1至6)。在下表2中,烷基烯酮化合物是具有化学式1的结构的化合物,记载了R1和R2。
首先,将脂肪酸或烷基烯酮化合物和非离子乳化剂和增稠剂投入纯净水中,加热至70℃,充分搅拌,然后冷却至常温(25℃),从而制备组合物。
[表1]
[表2]
实验例1.比较毛发处理用组合物的调理效果
(1)方法
将上述制备的实施例1至8和比较例1至6的毛发处理组合物各1g均匀涂抹于4g左右的发束(tress),在常温下放置30分钟以诱导反应,并且第一次用流动的水和洗发液洗掉,从而比较初始调理效果(刚使用后毛发光滑满意度_满意度1)。
之后每天洗发一次,10天后比较毛发的调理效果(10次洗发后毛发光滑满意度_满意度2)。
上述调理效果以5分尺度(5非常优异,4稍微优异,3没有差异,2没有效果,1非常没有效果)的官能进行评价比较。
(2)结果
上述满意度评价结果示于下表3。
如表3所示,可以确认,与不包含烷基烯酮化合物的比较例1至6相比,使用烷基烯酮化合物的实施例1至8表现出更加优异的调理效果和调理持续效果。
[表3]
实验例2.比较根据处理温度的毛发处理用组合物的调理效果
(1)方法
使用实施例1至8的组合物,将上述组合物各1g均匀涂抹于4g左右的发束,用80至100℃的温度条件的吹风机干燥5分钟,以施加热的方式处理。
处理后,第一次用流动的水和洗发液洗掉,从而比较初始调理效果(刚使用后毛发光滑满意度_满意度1)。
之后每天洗发一次,10天后比较毛发的调理效果(10次洗发后毛发光滑满意度_满意度2)。
上述调理效果以5分尺度(5非常优异,4稍微优异,3没有差异,2没有效果,1非常没有效果)的官能进行评价比较。
(2)结果
上述满意度评价结果示于下表4。
如表4所示,可以确认,包含实施例的烷基烯酮化合物并且利用吹风机以80至100℃处理5分钟的发束与使用相同的组合物并且在常温下干燥的情况相比,具有相对优异的调理效果和持久性。
因此,当添加热处理条件时,可以确认,烷基烯酮化合物与毛发形成共价键的效率更加优异,其结果表现出更加优异的调理效果和持续效果。即,当使用本发明的组合物时,显示出毛发不会因热而受损,而是调理效果得到进一步改善的惊人的效果。
[表4]
制备例2.制备纤维处理用组合物(实施例9至16和比较例7至12)
制备了包含下表5和表6的成分的纤维处理用组合物(实施例9至16和比较例7至12)。在下表6中,烷基烯酮化合物是具有化学式1的结构的化合物,记载了R1和R2。
首先,将脂肪酸或烷基烯酮化合物和非离子乳化剂和乙醇投入纯净水中,加热至70℃,充分搅拌,然后冷却至常温(25℃),从而制备组合物。
[表5]
[表6]
实验例3.比较纤维处理用组合物的调理效果
(1)方法
用上述制备的实施例8至16和比较例7至12的纤维处理用组合物各1g均匀处理宽度x长度为20cm x 20cm的标准羊毛(Wool)布,在常温下放置30分钟以诱导反应,并且第一次用流动的水和洗剂洗掉并干燥,从而比较初始纤维柔软效果(刚使用后纤维柔软力满意度_满意度1)。
之后利用洗涤洗剂洗涤3次,然后干燥,从而比较纤维柔软效果(3次洗涤后纤维柔软力满意度_满意度2)。
上述纤维柔软效果以5分尺度(5非常优异,4稍微优异,3没有差异,2没有效果,1非常没有效果)的官能进行评价比较。
(2)结果
上述满意度评价结果示于下表7。
如表7所示,可以确认,与不包含烷基烯酮化合物的比较例7至12相比,使用烷基烯酮化合物的实施例9至16的情况表现出更加优异的纤维柔软效果和纤维柔软持续效果。
[表7]
实验例4.比较根据处理温度的纤维处理用组合物的调理效果
(1)方法
使用实施例9至16的组合物,用其各1g均匀处理宽度x长度为20cm x 20cm的标准羊毛(Wool)布,用150至170℃温度条件的熨斗熨烫1分钟,从而诱导热引起的反应。
之后,第一次用流动的水和洗剂洗掉并干燥,从而比较初始纤维柔软效果(刚使用后纤维柔软力满意度_满意度1)。
之后利用洗涤洗剂洗涤3次,然后干燥,从而比较纤维柔软效果(3次洗涤后纤维柔软力满意度_满意度2)。
上述纤维柔软效果以5分尺度(5非常优异,4稍微优异,3没有差异,2没有效果,1非常没有效果)的官能进行评价比较。
(2)结果
上述满意度评价结果示于下表8。
如表8所示,可以确认,包含烷基烯酮化合物并且利用熨斗以150至170℃处理1分钟的羊毛布与使用相同的组合物并且在常温下干燥的情况相比,具有更加优异的纤维柔软效果和持久性。
因此,当添加热处理条件时,可以确认,烷基烯酮化合物与羊毛纤维形成共价键的效率更加优异,其结果表现出更加优异的纤维柔软效果和持续效果。即,当使用本发明的组合物时,显示出纤维不会因热而受损,而是调理效果得到进一步改善的惊人的效果。
[表8]
附加地,实施例的组合物即使使用衣物烘干机(LG电子-RH16VS)进行热处理,也表现出相似的效果。
制备例3.制备纤维处理用组合物(实施例17至23和比较例13至18)
制备了包含下表9和表10的成分的纤维处理用组合物(实施例17至23和比较例13至18)。
烷基醚硫酸盐、烷基苯磺酸盐和皂(Soap)是阴离子表面活性剂,二烷基二甲基铵盐、烷基咪唑啉鎓盐和酯季铵盐是阳离子表面活性剂,聚氧乙烯脱水山梨糖醇脂肪酸酯是非离子表面活性剂。
另外,使用C12-16烷基烯酮二聚体(C12-16 alkyl ketene dimer)作为烷基烯酮化合物。
首先,将阴离子表面活性剂或阳离子表面活性剂、非离子表面活性剂和烷基烯酮化合物投入纯净水中,加热至70℃,充分搅拌。之后,将温度降至40℃,投入香料,充分搅拌,然后冷却至常温(25℃),从而制备组合物。
[表9]
[表10]
实验例5.评价根据烷基烯酮化合物和表面活性剂的组合的纤维物性改善效果
对于实施例17至23的组合物,评价了官能评价(余香强度、柔软性)、刚度(Stiffness)、摩擦系数、接触角和收缩率。
试料处理如下进行。
首先,将上述纤维处理用组合物稀释10倍。
将宽度x长度为8cm x 8cm的标准棉布(E-211,Center For Testmaterials BV,Netherlands)浸入上述稀释的纤维处理用组合物中,并用磁棒在400rpm的速度和35℃下搅拌1小时。之后,取出棉布,在流动的自来水中漂洗3分钟,然后用洗碗巾擦拭表面的水分,投入60℃的干燥炉中,干燥2小时。在25℃、50%RH条件下保管24小时,然后进行各评价项目试验。
(1)官能评价
①方法
(A)试料处理后,对棉布上残留的香气的强度和柔软程度进行官能评价,并给出1分至5分的分数。评价由熟练的专门小组成员进行,并重复10次来求得平均值。
(B)另外,与上述试料处理方法相同地,用SLES 15%溶液处理棉布共3次,重复洗涤和干燥3次,然后以与(A)相同的方法进行官能评价。
-余香强度:1几乎没有香气,2香气较弱,3香气适中,4香气较强,5香气非常强
-柔软性:1非常坚硬,2稍微坚硬,3普通,4稍微柔软,5非常柔软
②结果
上述官能评价结果示于下表11和表12。
如表所示,可以确认,与比较例相比,单独使用烷基烯酮化合物的实施例23和同时使用烷基烯酮化合物和表面活性剂的实施例17至22被评价为具有高的余香强度和柔软性分数。特别是,当同时使用烷基烯酮化合物和表面活性剂时,可以确认具有更加优异的余香强度和柔软性。
这种结果即使在洗涤后也保持了倾向。
[表11]
[表12]
(2)刚度评价
①方法
(A)试料处理后,将棉布的相对的两侧平铺并固定在装置(Pure Bending Tester(KES-FB2-S,Kato Tech,Japan))的两个轴上,一轴在固定状态下旋转另一轴,并且根据棉布的曲率K(cm-1)记录(旋转范围:K=±2.5cm-1,旋转速度:0.5cm-1/sec)棉布弯曲时产生的力矩M(gf cm/cm)。
(B)对在曲率K=0~2.5cm-1的范围内力矩变化量一定的区间通过线性拟合(linear fitting)获得斜率值_1。
(C)将棉布旋转90度,重复(A)和(B)过程,并获得斜率值_2。
(D)将斜率值_1和2进行几何平均,并表示为刚度(gf cm2/cm)(重复10次取平均)。
(E)另外,与上述试料处理方法相同地,用SLES 15%溶液处理棉布共3次,重复洗涤和干燥3次,然后以与(A)至(D)相同的方法进行刚度评价(重复10次取平均)。
本实验在25℃、50%RH下进行。
②结果
上述刚度评价结果示于下表13和表14。
如表所示,可以确认,与比较例相比,单独使用烷基烯酮化合物的实施例23和同时使用烷基烯酮化合物和表面活性剂的实施例17至22具有较低的刚度,因此更加柔软,特别是,当同时使用烷基烯酮化合物和表面活性剂时,可以确认其效果更加优异。
这种结果即使在洗涤后也保持了倾向。上述结果类似于上述柔软性官能评价结果。
[表13]
[表14]
(3)评价摩擦系数
①方法
(A)在摩擦试验机(MTT175,Dia-stron,UK)上安装专用橡胶探针(Probe)和施加200g的法向力的砝码,并将经试料处理的棉布平铺并固定在装置的移动板上。将橡胶探针与棉布的一端接触,并且在以200mm/min速度移动移动板的同时根据棉布的位置记录橡胶探针和棉布之间产生的摩擦力。从棉布的特定范围内的摩擦力的平均值和法向力获得摩擦系数(重复10次取平均)。
(B)另外,与上述试料处理方法相同地,用SLES 15%溶液处理棉布共3次,重复洗涤和干燥3次,然后以与(A)相同的方法进行摩擦系数评价(重复10次取平均)。
本实验在25℃、50%RH下进行。
②结果
上述摩擦系数评价结果示于下表15和表16。
如表所示,可以确认,与比较例相比,单独使用烷基烯酮化合物的实施例23和同时使用烷基烯酮化合物和表面活性剂的实施例17至22具有较低的摩擦系数,因此纤维表面的损伤更少且柔顺,特别是,当同时使用烷基烯酮化合物和表面活性剂时,可以确认其效果更加优异。
这种结果即使在洗涤后也保持了倾向。
[表15]
[表16]
(4)接触角
①方法
(A)试料处理后,将棉布平铺并放在平行板上,然后在5个任意位置处分别滴10μL蒸馏水,使用液滴形状分析仪(DSA100,Kruss,Germany)对生成的液滴(droplet)的形象进行拍摄,并测量接触角(重复10次取平均)。
(B)另外,与上述试料处理方法相同地,用SLES 15%溶液处理棉布共3次,重复洗涤和干燥3次,然后以与(A)相同的方法进行接触角评价(重复10次取平均)。
本实验在25℃、50%RH下进行。
②结果
上述接触角评价结果示于下表17。
对于仅处理表面活性剂的比较例13至18,液滴被棉布完全吸收,因此无法测量接触角。
然而,单独使用烷基烯酮化合物的实施例23和同时使用烷基烯酮化合物和表面活性剂的实施例17至22示出30°以上的接触角,由此可以确认纤维表面呈疏水性。另外,可以确认即使在洗涤后也能保持一定程度的表面疏水性。
特别是,同时使用烷基烯酮化合物和表面活性剂的实施例17至22示出接近90°的接触角并且即使在洗涤后也示出较高的接触角,因此可以通过赋予本发明所目的的疏水性而赋予长时间持续的调理效果。
[表17]
(5)收缩率
①方法
(A)用实施例17至23和比较例13至18中制备的纤维处理用组合物处理标准羊毛布(537,Testfabrics,Inc.,USA)。
处理方法与实验例5中前述的处理方法相同。
(B)展开羊毛布,将一边角末端用装置(Volume Tester(Bolero Lite,BOSSA NOVAVISION,USA))内的夹子夹住并悬挂,然后用相机拍照,测量羊毛布的面积,并将相对于原始面积(8cm x 8cm)收缩的程度表示为收缩率(%)(重复10次取平均)。
(C)另外,与上述试料处理方法相同地,用SLES 15%溶液处理羊毛布共3次,重复洗涤和干燥3次,然后以与(B)相同的方法进行收缩率评价(重复10次取平均)。
②结果
上述收缩率评价结果示于下表18和表19。
如表所示,可以确认,与比较例相比,单独使用烷基烯酮化合物的实施例23和同时使用烷基烯酮化合物和表面活性剂的实施例17至22具有较低的收缩率,因此纤维防缩力高,特别是,当同时使用烷基烯酮化合物和表面活性剂时,可以确认其效果更加优异。
这种结果即使在洗涤后也保持了倾向。
[表18]
[表19]
工业可用性
本发明的毛发或纤维处理用组合物含有能够与毛发或纤维的蛋白质残基共价结合的烷基烯酮化合物,因此上述烷基烯酮化合物与上述蛋白质残基形成共价键而不损伤毛发或纤维,并且通过赋予永久性疏水性可以提供长时间持续的调理等有益的效果。
另外,本发明的毛发或纤维处理用组合物可以防止和/或改善热(heat)引起的毛发或纤维的损伤。
另外,本发明的毛发或纤维处理用组合物可以使毛发或纤维保持余香,并且可以强化柔软性、柔顺、疏水性或防缩力。
Claims (16)
2.根据权利要求1所述的毛发或纤维处理用组合物,其中,R1和R2各自独立地是具有8至22个碳原子的直链或支链的饱和或不饱和烷基、或具有8至22个碳原子的直链或支链的饱和或不饱和脂肪酸。
3.根据权利要求1所述的毛发或纤维处理用组合物,其中,R1和R2各自独立地是具有16至18个碳原子的直链的饱和或不饱和烷基、或18-MEA(18-甲基二十烷酸)。
4.根据权利要求1所述的毛发或纤维处理用组合物,其中,相对于毛发或纤维处理用组合物总重量,烷基烯酮化合物的含量为0.0001至10重量份。
5.根据权利要求1所述的毛发或纤维处理用组合物,其中,烷基烯酮化合物应用于毛发或纤维,从而与上述毛发或纤维形成共价键。
6.根据权利要求1所述的毛发或纤维处理用组合物,其中,该毛发或纤维处理用组合物还包含选自由阳离子表面活性剂和阴离子表面活性剂组成的组中的一种以上。
7.一种毛发或纤维的调理方法,其包括用权利要求1所述的毛发或纤维处理用组合物处理毛发或纤维的步骤。
8.根据权利要求7所述的毛发或纤维的调理方法,其中,毛发或纤维处理用组合物中的烷基烯酮化合物与毛发或纤维形成共价键。
9.根据权利要求7所述的毛发或纤维的调理方法,其中,对毛发或纤维的处理在20至250℃下进行。
10.一种用于防止或改善热损伤的毛发或纤维处理用产品,其包含权利要求1所述的毛发或纤维处理用组合物。
12.根据权利要求11所述的用途,其中,R1和R2各自独立地是具有8至22个碳原子的直链或支链的饱和或不饱和烷基、或具有8至22个碳原子的直链或支链的饱和或不饱和脂肪酸。
13.根据权利要求11所述的用途,其中,R1和R2各自独立地是具有16至18个碳原子的直链的饱和或不饱和烷基、或18-MEA(18-甲基二十烷酸)。
14.根据权利要求11所述的用途,其中,相对于组合物总重量,烷基烯酮化合物的含量为0.0001至10重量份。
15.根据权利要求11所述的用途,其中,烷基烯酮化合物应用于毛发或纤维,从而与上述毛发或纤维形成共价键。
16.根据权利要求11所述的用途,其中,组合物还包含选自由阳离子表面活性剂和阴离子表面活性剂组成的组中的一种以上。