CN115155575B - 一种高效催化硝基苯加氢制苯胺的双原子催化剂及其制备方法 - Google Patents
一种高效催化硝基苯加氢制苯胺的双原子催化剂及其制备方法 Download PDFInfo
- Publication number
- CN115155575B CN115155575B CN202210930850.6A CN202210930850A CN115155575B CN 115155575 B CN115155575 B CN 115155575B CN 202210930850 A CN202210930850 A CN 202210930850A CN 115155575 B CN115155575 B CN 115155575B
- Authority
- CN
- China
- Prior art keywords
- ball milling
- catalyst
- diatomic
- hours
- finished
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种高效催化硝基苯加氢制苯胺的双原子催化剂及其制备方法；其结构式为Z1Pd1/MxOy双原子催化剂；该双原子催化剂通过两步简单球磨，之后通过煅烧得到双金属原子负载于载体表面，实现双原子催化剂的制备；所述双原子催化剂包括两种金属，即Pd和其他一种金属，均以单原子形式存在于载体表面；将本发明所述双原子催化剂用于硝基苯加氢制苯胺反应中，实现了苯胺的高效合成，显著提高了苯胺产率。本发明不仅提供了一种简单制备双原子催化剂的方法，并将其应用到硝基苯及其衍生物加氢反应中，所得产率高，反应条件温和，具有安全、绿色环保、成本低的优点。
Description
技术领域
本发明涉及属于精细化工技术领域，具体地说，涉及一种高效催化硝基苯加氢制苯胺的双原子催化剂，本发明还涉及该催化剂的制备方法与应用。
背景技术
硝基苯加氢制苯胺是一个非常重要的反应，苯胺作为化学工业中染料和制药所需的重要中间体，广泛应用于合成农药、染料、橡胶化学品、有机颜料、氨基树脂、环己胺等具有高附加值的产品。目前，苯胺的商业化生产主要依赖于在氢氧化铵中使用亚硫酸钠、铁、锡或锌等化学计量还原剂对硝基芳烃的非催化还原。然而，这种工艺存在严重的环境问题，而且选择性差。因此，开发更高效、选择性和环境友好的苯胺生产工艺对于基础研究和工业应用都具有重要意义。近年来，研究人员开发了多种催化剂用于加氢反应中，包括单原子催化剂、合金催化剂、非贵金属催化剂等，它们硝基芳烃的选择性加氢反应中取得了良好的催化性能。正因为如此，单原子催化剂在各种加氢反应中得到了广泛的应用，但对于硝基苯加氢反应，还需要反应性能更好、反应条件更温和的催化剂。
单原子催化剂的配位环境严重影响着催化剂性能，通过加入第二金属是调控单原子催化剂配位环境的有效方法。两种金属均以单原子形式负载于载体上，通过金属间的电子转移改善催化剂性能，可表现为协同效应或助催化效应。这种双原子催化剂往往展现出优于单金属原子催化剂的催化活性。将该催化剂用于硝基苯加氢制苯胺反应中，有望解决目前高温高压的生产条件及反应耗时长等问题。
发明内容
本发明目的在于提供一种高效催化硝基苯加氢制苯胺的双原子催化剂及其制备方法，该催化剂活性中心包括两种金属，其中一种金属为Pd，以单原子的形式存在；另一种金属元素为K、Ca、Na、Ba、Sr、Rb、Cs中的一种，以单原子形式存在。
为了实现上述目的，本发明采用如下技术方案：
一种高效催化硝基苯加氢制苯胺的双原子催化剂，其结构式为：Z1Pd1/MxOy双原子催化剂，
所述辅助金属元素为K、Ca、Na、Ba、Sr、Rb、Cs中的一种；
所述MxOy为Ti，Al，Fe，Si，Cu，Zn，Mg所对应氧化物；
所述辅助金属Z与金属Pd均以单原子的形式存在；
所述辅助金属Z与金属Pd均占Z1Pd1/MxOy双原子催化剂质量分数万分之到百分之五。上述高效催化硝基苯加氢制苯胺的双原子催化剂及其制备方法，依次包括下述步骤：
1)按一定的质量比例分别称取辅助金属前驱体与载体，加入球磨罐中室温下球磨5-24小时；
2)将步骤1)中所得样品置于马弗炉中空气气氛下以5℃/min的升温速率由室温升至600℃并保温2小时，降至室温后得到Z1/MxOy单原子催化剂；
3)将Pd金属前驱体与步骤2)中Z1/MxOy单原子催化剂按一定比例分别加入球磨罐中室温下球磨5-24小时；
4)将步骤3)中所得样品置于马弗炉中空气气氛下以5℃/min的升温速率由室温升至600℃并保温2小时，降至室温后得到Z1Pd1/MxOy双原子催化剂；
优选地，步骤1)中所述辅助金属前驱体与载体比例为1∶20-1∶800；
优选地，步骤1)所述辅助金属元素为K、Ca、Na、Ba、Sr、Rb、Cs中的一种；
优选地，步骤1)所述辅助金属Z前驱体为相应的氯化盐、碳酸盐、硫酸盐；具体为KCl，K2CO3，K2SO4，CaCl2，CaCO3，CaSO4，NaCl，Na2CO3，Na2SO4，BaCl2，BaCO3，BaSO4，SrCl2，SrCO3，SrSO4，RbCl2，RbCO3，RbSO4，CsCl，Cs2CO3，Cs2SO4。
优选地，步骤1)所述载体MxOy为Ti，Al，Fe，Si，Cu，Zn，Mg所对应氧化物；
优选地，步骤2)中所述煅烧温度为300-700℃。
优选地，步骤3)所述金属Pd前驱体为相应的[Pd(NH3)4](NO3)2，[Pd(NH3)4]SO4，(NH4)2PdCl6，K2PdCl4，Na2PdCl4，Pd(acac)2，Pd(OAc)2，PdCl2，Pd(NO3)2中的一种。
优选地，步骤4)中所述Z1Pd1/MxOy双原子催化剂，辅助金属Z与Pd均以单原子形式存在。
本发明提供的一种硝基苯加氢制苯胺的方法，采用高压反应釜作为反应器，往含有硝基苯的醇溶液中加入上述双原子催化剂，在0.1-2MPa的H2氛围下，10℃-80℃下反应5min-5h制取苯胺。
更进一步地，上述的醇为甲醇、乙醇、异丙醇、正丁醇中的一种。
与现有技术相比，本发明具有如下优势：
(1)本发明提供的技术方案制备方法通过两步球磨法将两种金属原子孤立地锚定在载体上，实现了双原子催化剂的可控制备，在硝基苯加氢制苯胺反应中展现出优越的选择性及产率，制备简单，自动化程度高，污染性小，环境友好；
(2)本发明制备的双原子催化剂应用于硝基苯加氢制苯胺反应中，实现了活性组分的高效利用以及苯胺的绿色合成；所得苯胺选择性高，产率高；
(3)本发明制备的双原子催化剂应用于硝基苯加氢制苯胺反应中，实现了苯胺的低温低压合成，安全性高，经济效益好；
(4)本发明所制备双原子催化剂，在同等效益下金属含量低，所加入的辅助金属能极大地提高苯胺产率，具有一定成本优势。
(5)本发明所制备双原子催化剂，不仅适用于硝基苯加氢制苯胺，还对硝基苯衍生物具有较高的活性与选择性，具有极好的底物普适性。
附图说明：
图1为Ba1Pd1/Al2O3双原子催化剂XRD图；
图2为Ba1Pd1/Al2O3双原子催化剂球差校正透射电镜及元素分布图；
图3为反应前硝基苯含量GC图；
图4为反应后硝基苯及苯胺含量GC图。
具体实施方式
下面结合实施例对本发明做进一步的说明，但本发明的保护范围并不局限于实施例表示的范围。
实施例1
Ba1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和26.8mg BaCl2·2H2O，加入100mL玛瑙球磨罐中，加入的球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1/Al2O3单原子催化剂。
双原子催化剂Pd1Ba1/Al2O3的制备：分别称取1.5g制备好的Ba1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1Pd1/Al2O3双原子催化剂。图1为Ba1Pd1/Al2O3双原子催化剂XRD图；图2为Ba1Pd1/Al2O3双原子催化剂球差校正透射电镜及元素分布图，可观察到单个的Pd、Ba原子均匀分散在载体上，说明Ba1Pd1/Al2O3双原子催化剂的成功制备。
硝基苯加氢制苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应30分钟后取出，排出气体。利用GC进行物质定量分析。硝基苯转化率为100％，选择性为100％，质量比活性为3100h-1。
实施例2
Ba1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和26.8mg BaCl2·2H2O，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1/Al2O3单原子催化剂。
双原子催化剂Pd1Ba1/Al2O3的制备：分别称取1.5g制备好的Ba1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1Pd1/Al2O3双原子催化剂。
硝基苯加氢制苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应15分钟后取出，排出气体。利用GC进行物质定量分析。硝基苯转化率为55％，选择性为100％，质量比活性为2300h-1。
实施例3
Na1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和26.8mg NaCl，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Na1/Al2O3单原子催化剂。
双原子催化剂Pd1Na1/Al2O3的制备：分别称取1.5g制备好的Na1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Na1Pd1/Al2O3双原子催化剂。
硝基苯加氢制苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应30分钟后取出，排出气体。利用GC进行物质定量分析。硝基苯转化率为61％，选择性为100％，质量比活性为2500h-1。
实施例4
Sr1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和18.5mg氯化锶，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Sr1/Al2O3单原子催化剂。
双原子催化剂Sr1Pd/Al2O3的制备：分别称取1.5g制备好的Sr1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Sr1Pd1/Al2O3双原子催化剂。
硝基苯加氢制苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应30分钟后取出，排出气体。利用GC进行物质定量分析。硝基苯转化率为73％，选择性为100％，质量比活性为2610h-1。
实施例5
Ba1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和26.8mg BaCl2·2H2O，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1/Al2O3单原子催化剂。
双原子催化剂Pd1Ba1/Al2O3的制备：分别称取1.5g制备好的Ba1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1Pd1/Al2O3双原子催化剂。
对甲基硝基苯加氢制对甲基苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol对甲基硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应50分钟后取出，排出气体。利用GC进行物质定量分析。对甲基硝基苯转化率为100％，选择性为100％，质量比活性为1860h-1。
实施例6
Ba1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和26.8mg BaCl2·2H2O，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1/Al2O3单原子催化剂。
双原子催化剂Pd1Ba1/Al2O3的制备：分别称取1.5g制备好的Ba1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1Pd1/Al2O3双原子催化剂。
对氟硝基苯加氢制对甲基苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol对甲基硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应50分钟后取出，排出气体。利用GC进行物质定量分析。对氟硝基苯转化率为100％，选择性为100％，质量比活性为1860h-1。
实施例7
Ba1/Al2O3单原子催化剂的制备：分别称取3g Al2O3和26.8mg BaCl2·2H2O，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1/Al2O3单原子催化剂。
双原子催化剂Pd1Ba1/Al2O3的制备：分别称取1.5g制备好的Ba1/Al2O3单原子催化剂，并称取21.6mg二(乙酰丙酮)钯(Pd(acac)2)，加入100mL玛瑙球磨罐中，加入球磨珠。将球磨罐放入行星式球磨机，设置转速为500rpm，球磨10小时。球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5℃/min的升温速率程序升温至600℃保持2小时。结束后自然冷却至室温，得到Ba1Pd1/Al2O3双原子催化剂。
对硝基苯乙酮加氢制对甲基苯胺具体步骤如下：准确称取30mg催化剂，0.2mmol对甲基硝基苯，0.125mmol十三烷(作为内标)，3mL无水乙醇(作为溶剂)，依次加入10mL高压反应釜中。向釜中充入0.5MPa H2。将反应釜放入35℃油浴锅中，搅拌反应50分钟后取出，排出气体。利用GC进行物质定量分析。对硝基苯乙酮转化率为100％，选择性为100％，质量比活性为1860h-1。
Claims (5)
1.一种催化硝基苯加氢制苯胺的双原子催化剂，其特征在于，通过下述方法制备的：
Ba1/Al2O3单原子催化剂的制备
分别称取3 g Al2O3和26.8 mg BaCl2·2H2O，加入100 mL玛瑙球磨罐中，加入球磨珠；将球磨罐放入行星式球磨机，设置转速为500 rpm，球磨10小时；球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5 °C/min的升温速率程序升温至600 °C保持2小时；结束后自然冷却至室温，得到Ba1/Al2O3单原子催化剂；
2）双原子催化剂Pd1Ba1/Al2O3的制备
称取1.5 g步骤1）制备好的Ba1/Al2O3单原子催化剂，并称取21.6 mg二（乙酰丙酮）钯Pd(acac)2，加入100 mL玛瑙球磨罐中，加入球磨珠；将球磨罐放入行星式球磨机，设置转速为500 rpm，球磨10小时；球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5°C/min的升温速率程序升温至600 °C保持2小时；结束后自然冷却至室温，得到Ba1Pd1/Al2O3双原子催化剂。
2.一种催化硝基苯加氢制苯胺的双原子催化剂，其特征在于，通过下述方法制备的：
1)Na1/Al2O3单原子催化剂的制备
分别称取3 g Al2O3和26.8 mg NaCl，加入100 mL玛瑙球磨罐中，加入球磨珠；将球磨罐放入行星式球磨机，设置转速为500 rpm，球磨10小时；球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5 °C/min的升温速率程序升温至600 °C保持2小时；结束后自然冷却至室温，得到Na1/Al2O3单原子催化剂；
双原子催化剂Pd1Na1/Al2O3的制备
称取1.5 g步骤1）制备好的Na1/Al2O3单原子催化剂，并称取21.6 mg二（乙酰丙酮）钯Pd(acac)2，加入100 mL玛瑙球磨罐中，加入球磨珠；将球磨罐放入行星式球磨机，设置转速为500 rpm，球磨10小时；球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5°C/min的升温速率程序升温至600 °C保持2小时；结束后自然冷却至室温，得到Na1Pd1/Al2O3双原子催化剂。
3.一种催化硝基苯加氢制苯胺的双原子催化剂，其特征在于，通过下述方法制备的：
1）Sr1/Al2O3单原子催化剂的制备
分别称取3 g Al2O3和18.5 mg 氯化锶，加入100 mL玛瑙球磨罐中，加入球磨珠；将球磨罐放入行星式球磨机，设置转速为500 rpm，球磨10小时；球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5 °C/min的升温速率程序升温至600 °C保持2小时；结束后自然冷却至室温，得到Sr1/Al2O3单原子催化剂；
2）双原子催化剂Sr1Pd1/Al2O3的制备
称取1.5 g步骤1）制备好的Sr1/Al2O3单原子催化剂，并称取21.6 mg二（乙酰丙酮）钯Pd(acac)2，加入100 mL玛瑙球磨罐中，加入球磨珠；将球磨罐放入行星式球磨机，设置转速为500 rpm，球磨10小时；球磨结束后，将球磨罐中的粉末转移至瓷方舟，并置于马弗炉中以5°C/min的升温速率程序升温至600 °C保持2小时；结束后自然冷却至室温，得到Sr1Pd1/Al2O3双原子催化剂。
4.一种硝基苯加氢制苯胺的方法，其特征在于，采用高压反应釜作为反应器，往含有硝基苯的醇溶液中加入权利要求1-3任一所述的双原子催化剂，在0.1-2 MPa的H2氛围下，10℃-80℃下反应5 min-5 h制取苯胺。
5.根据权利要求4所述的硝基苯加氢制苯胺的方法，其特征在于，所述的醇为甲醇、乙醇、异丙醇、正丁醇中的一种。