CN114958220A - 一种树脂镜片的封装胶带 - Google Patents
一种树脂镜片的封装胶带 Download PDFInfo
- Publication number
- CN114958220A CN114958220A CN202110206263.8A CN202110206263A CN114958220A CN 114958220 A CN114958220 A CN 114958220A CN 202110206263 A CN202110206263 A CN 202110206263A CN 114958220 A CN114958220 A CN 114958220A
- Authority
- CN
- China
- Prior art keywords
- layer
- weight
- adhesive
- parts
- base layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种树脂镜片的封装胶带，包括一基层，一胶黏剂层和一离型层，其中，该基层为聚脂薄膜材料层，该基层的一面涂布有该胶黏剂层，该基层的另一面涂布有该离型层。该胶黏剂层由耐高温丙烯酸胶黏剂、固化剂、醋酸乙酯按一定重量配比混合均匀组成，各组分的重量配比为耐高温丙烯酸胶黏剂100份、固化剂5‑12份、醋酸乙酯80‑120份。本发明改善了胶带的高温保持力和密封透水性能，提高了胶带与普通树脂镜片和防蓝光树脂镜片的树脂液匹配性，使两种不同树脂眼镜片的生产可以共用同一款封装胶带。
Description
技术领域
本发明涉及胶带领域，具体为一种树脂镜片的封装胶带。
背景技术
在树脂眼镜片制作过程中，需使用到树脂眼镜片模具，在树脂眼镜片模具中填满树脂眼镜液料后，用胶带密封上下树脂眼镜片模具，然后经过20小时高温烘烤使树脂眼镜液料固化，即生产出成品树脂眼镜片；在密封上下树脂眼镜片模具时，胶带的质量关系到所生产出树脂眼镜片的质量，当胶带质量较差时，树脂眼镜片模具在高温烘烤时，上下树脂眼镜片模具之间易开裂、树脂眼镜片起雾和残胶等不良现象，导致生产出不良树脂眼镜片。目前市场上树脂眼镜片分普通树脂眼镜片和防蓝光树脂眼镜片，在制作两种不同的树脂眼镜片时，使用的是两种不同的胶带，两种不同的树脂眼镜片不能共用同一款胶带，这样无形的增加了成本和降低了效率。
发明内容
为解决上述技术问题，本发明提供了一种树脂镜片的封装胶带，改善了胶带的高温保持力和密封透水性能，及其与两种不同的镜片树脂液匹配性，使两种不同的树脂眼镜片共用同一款封装胶带。
为达到上述目的，本发明的技术方案如下：
一种树脂镜片的封装胶带，包括一基层，一胶黏剂层和一离型层，其中，该基层为聚脂薄膜材料层，该基层的一面涂布有该胶黏剂层，该基层的另一面涂布有该离型层。
进一步的，该胶黏剂层由耐高温丙烯酸胶黏剂、固化剂、醋酸乙酯按一定重量配比混合均匀组成，各组分的重量配比为耐高温丙烯酸胶黏剂100份、固化剂5-12份、醋酸乙酯80-120份。
进一步的，该耐高温丙烯酸胶黏剂由丙烯酸酯类共聚物、甲苯、乙酸乙酯按一定重量配比组成，各组分的重量配比为丙烯酸酯类共聚物50-70份、甲苯15-30份、乙酸乙酯20-30份，所述丙烯酸酯类共聚物主要由丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸2-乙基己酯组成。
进一步的，该胶黏剂层采用逗号刮刀涂布的方式涂布于基层的一面上，涂布量为45-60g/㎡，涂布速度为18±2m/min。
进一步的，该离型层采用微凹涂布的方式涂布于该基层另一面上，涂布量为0.5g/㎡，涂布速度为20±2m/min。
进一步的，该固化剂为异氰酸酯类固化剂，包括55％重量比的异氰酸酯和45％重量比的醋酸乙酯。
本发明通过以上的技术方案，封装胶带的质量好，具有良好的高温保持力和密封透水性能，与镜片树脂液的匹配性好，能够大大降低树脂眼镜片的不良率，且能够同时适用于普通树脂镜片和防蓝光树脂镜片的生产。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍。
图1为本发明的结构示意图。
具体元件符号如下：
1基层2胶黏剂层3离型层
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述。
请参考图1所示，一种树脂镜片的封装胶带，包括一基层1、一胶黏剂层2和一离型层3。
该基层1为聚酯薄膜材料层，对基层1进行清洁和电晕处理，去除表面的油污和杂志。
称取耐高温丙烯酸胶黏剂100份、固化剂5-12份、醋酸乙酯80-120份搅拌混合均匀，用600目过滤布将混合后的材料进行充分过滤，将混合过滤后的材料采用逗号刮刀涂布的方式涂布于该基层1的上表面，形成胶黏剂层2，涂布量为45-60g/㎡，涂布速度为18±2m/min。
该离型层3为有机硅离型剂层，涂布于该基层1的下表面，采用微凹涂布的方式，涂布量为0.5g/㎡，涂布速度为20±2m/min。
上述耐高温丙烯酸胶黏剂由丙烯酸酯类共聚物、甲苯、乙酸乙酯按一定重量配比组成，各组分的重量配比为丙烯酸酯类共聚物50-70份、甲苯15-30份、乙酸乙酯20-30份，所述丙烯酸酯类共聚物主要由丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸2-乙基己酯组成。
上述固化剂为异氰酸酯类固化剂，包括55％重量比的异氰酸酯和45％重量比的醋酸乙酯。
上述实施案例，仅例示性说明本发明的原理及其功效，而非用于限制本发明。任何熟悉此技术的人士皆可在不违背本发明的精神及范畴下，对上述实施例进行修饰或改变。因此，举凡所属技术领域中具有通常知识者在未脱离本发明所揭示的精神与技术思想下所完的一切等效修饰或改变，仍应由发明的权利要求所涵盖。
Claims (6)
1.一种树脂镜片的封装胶带，包括一基层，一胶黏剂层和一离型层，其中，该基层为聚脂薄膜材料层，该基层的一面涂布有该胶黏剂层，该基层的另一面涂布有该离型层。
2.如权利要求1所述的一种树脂镜片的封装胶带，其特征在于，该胶黏剂层由耐高温丙烯酸胶黏剂、固化剂、醋酸乙酯按一定重量配比混合均匀组成，各组分的重量配比为耐高温丙烯酸胶黏剂100份、固化剂5-12份、醋酸乙酯80-120份。
3.如权利要求2所述的一种树脂镜片的封装胶带，其特征在于，该耐高温丙烯酸胶黏剂由丙烯酸酯类共聚物、甲苯、乙酸乙酯按一定重量配比组成，各组分的重量配比为丙烯酸酯类共聚物50-70份、甲苯15-30份、乙酸乙酯20-30份，所述丙烯酸酯类共聚物由丙烯酸乙酯、丙烯酸丁酯、甲基丙烯酸2-乙基己酯组成。
4.如权利要求1-3任一项所述的一种树脂镜片的封装胶带，其特征在于，该胶黏剂层采用逗号刮刀涂布的方式涂布于基层的一面上，涂布量为45-60g/㎡，涂布速度为18±2m/min。
5.如权利要求1-3任一项所述的一种树脂镜片的封装胶带，其特征在于，该离型层采用微凹涂布的方式涂布于该基层另一面上，涂布量为0.5g/㎡，涂布速度为20±2m/min。
6.如权利要求2或3所述的一种树脂镜片的封装胶带，其特征在于，该固化剂为异氰酸酯类固化剂，包括55％重量比的异氰酸酯和45％重量比的醋酸乙酯。