CN114574269A - 一种耐氧化长寿命的针织机油组合物 - Google Patents
一种耐氧化长寿命的针织机油组合物 Download PDFInfo
- Publication number
- CN114574269A CN114574269A CN202011402342.8A CN202011402342A CN114574269A CN 114574269 A CN114574269 A CN 114574269A CN 202011402342 A CN202011402342 A CN 202011402342A CN 114574269 A CN114574269 A CN 114574269A
- Authority
- CN
- China
- Prior art keywords
- oxidation
- life
- knitting machine
- oil composition
- machine oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐氧化长寿命的针织机油组合物，包括抗氧剂、极压抗磨剂、乳化剂和基础油，其中以所述耐氧化长寿命的针织机油组合物的总重量计，所含组分如下：抗氧剂0.1‑4.0％，极压抗磨剂0.2‑2.0％，乳化剂0.5‑5.0％。本发明提供的耐氧化长寿命的针织机油组合物，其具有优良的抗氧化性能、抗腐蚀性能和防锈性能。
Description
技术领域
本发明涉及一种耐氧化长寿命的针织机油组合物。
背景技术
纺织行业是轻工业中的主要产业之一，在工业现代化的推动下，纺织业在技术更新、设备升级等各个方面迅速发展，对于纺织机械润滑油的选用，也提出了更高的要求。正确地选用纺织机械润滑油，可最大程度减少机件磨损、降低摩擦阻力、延长设备使用寿命以及提高生产效率。
圆筒针织机广泛应用于纺织行业，该设备制造精密，设计为高转速以达到快速编织能力，设备零配件价格较高，因此对设备所用的针织机油的性能要求比较高，油品必须具备适宜的黏度、良好的氧化安定性和热稳定性、抗磨性等。
针织机进行生产时，在织物编织过程中设备的一些部位在高速运行时产生高热，可能会造成针织机的关键润滑部位如凸轮、织针及针筒处形成沉积，影响到设备的正常运转。
因此，有必要开发一种新的针织机油组合物。
发明内容
本发明提供一种耐氧化长寿命的针织机油组合物，其具有优良的抗氧化性能、抗腐蚀性能和防锈性能。
本发明提供一种耐氧化长寿命的针织机油组合物，包括抗氧剂、极压抗磨剂、乳化剂和基础油，其中以所述耐氧化长寿命的针织机油组合物的总重量计，所含组分如下：
抗氧剂 0.1-4.0％
极压抗磨剂 0.2-2.0％
乳化剂 0.5-5.0％。
根据本发明实施例，以所述耐氧化长寿命的针织机油组合物的总重量计，所述抗氧剂的含量为0.1-2.0％，可选为0.3-1.0％，进一步可选为0.3-0.5％。
根据本发明实施例，以所述耐氧化长寿命的针织机油组合物的总重量计，所述极压抗磨剂的含量为0.2-0.4％。
根据本发明实施例，以所述耐氧化长寿命的针织机油组合物的总重量计，所述乳化剂的含量为0.5-2％，可选为0.5-1％。
根据本发明实施例，以所述耐氧化长寿命的针织机油组合物的总重量计，所述基础油的含量为91-99％，可选为88-89％。
根据本发明实施例，所述耐氧化长寿命的针织机油组合物即是由抗氧剂、极压抗磨剂、乳化剂和基础油组成，可以基础油调整至总量为100％。
根据本发明实施例，所述基础油由不同种类的基础油组成，选择合适调合比例，以获得相应的黏度产品。
根据本发明实施例，所述基础油采用抗氧化能力强的Ⅱ类加氢基础油或Ⅲ类加氢基础油中的至少一种。
根据本发明实施例，所述基础油为中石化公司Ⅲ类加氢基础油III4和/或III6。
根据本发明实施例，为进一步提高油品在使用时抗氧化变质能力，所述抗氧剂为高温酚类抗氧剂、胺类抗氧剂、胺酚混合物中的一种或多种。
根据本发明实施例，所述高温酚类抗氧剂可选自IRGANOX L101、IRGANOX L115，可购自BASF(巴斯夫)公司；或选自Vanlube 81，可购自范德比尔特公司。
根据本发明实施例，所述胺类抗氧剂可选自IRGANOX L57、IRGANOX L06，可购自BASF(巴斯夫)公司。
根据本发明实施例，所述胺酚混合物可选自IRGANOX L64，可购自BASF(巴斯夫)公司。
根据本发明实施例，本发明所述抗氧剂的加入量控制在0.1-4.0％，优选为0.1-2.0％，最优选的加入量控制在0.3-1.0％，当加入量过小时，会影响油品的抗氧化变质能力；当加入量过大时，高温下分解产生黑色颗粒沉淀物甚至可能形成沉积，影响油品的正常使用。
根据本发明实施例，为进一步在金属表面上形成保护膜，以达成降低摩擦系数、提高抗磨损能力的效果，同时具有良好的金属附着力，有效降低机械设备零部件的磨损，延长使用寿命，所述极压抗磨剂选自磷酸胺盐、亚磷酸三月桂基酯、亚磷酸二正丁酯、磷酸三甲苯基酯中的至少一种。
根据本发明实施例，所述极压抗磨剂为BASF(巴斯夫)公司的Irgalube 349。
根据本发明实施例，为进一步降低油、水之间的界面张力，具有良好的助洗效果，实现易清洗油污的目的，所述乳化剂选自蓖麻油磷酸酯、脂肪酸聚氧乙烯酯、烷基酚聚氧乙烯醚中的一种。
根据本发明实施例，所述乳化剂为天津市助剂厂的C-125。
整体而言，本发明所述耐氧化长寿命的针织机油组合物，优选所述基础油为III类加氢基础油；所述的抗氧剂优选为Irganox L64(BASF(巴斯夫)公司)；所述的极压抗磨剂为Irgalube 349(BASF(巴斯夫)公司)；所述的乳化剂为天津市助剂厂的C-125。
本发明所述耐氧化长寿命的针织机油组合物可采用常规的润滑油品调和方法制备，具体地说，将各成分按配比加入调合容器中，在50-65℃搅拌2-3小时而成。
本发明选择具有适宜烃类结构的基础油，加入抗氧剂、极压抗磨剂、乳化剂等添加剂复配而成，对各添加剂组分种类及配比进行选择，各组分合理配比，达成协同作用，尤其是抗氧化性能有了很大的提高，得到耐氧化长寿命的针织机油组合物。通过测定酸值、黏度、乳化状态、旋转氧弹、磨斑直径等理化指标，全面评定产品性能满足并高于现有其他对比产品。本发明耐氧化长寿命的针织机油组合物，其具备极佳的热氧化安定性，能够耐受织机在高速运行时产生的高热，不会出现油品过度增稠现象，延长油品的使用寿命。
本发明一种耐氧化长寿命的针织机油组合物，具有耐氧化性能好、抗磨防锈、成本低、制备方法简单、易于工业化生产等特点。
具体实施方式
以下实施例用于说明本发明，但不用来限制本发明的范围。实施例中未注明具体技术或条件者，按照本领域内的文献所描述的技术或条件，或者按照产品说明书进行。所用试剂或仪器未注明生产厂商者，均为可通过正规渠道商购买得到的常规产品。
以下实施例中，Irganox L64和Irgalube 349购自BASF(巴斯夫)公司，C-125为天津市助剂厂生产的乳化剂，III4和III6为中石化公司生产的基础油。
实施例1-3
实施例1-3中的耐氧化长寿命的针织机油组合物的组分见表1。
表1实施例1各组分含量
| 原料 | 含量(％) |
| Irganox L64 | 0.3 |
| Irgalube 349 | 0.2 |
| C-125 | 0.5 |
| III4 | 10 |
| III6 | 89 |
表2实施例2各组分含量
| 原料 | 含量(％) |
| Irganox L64 | 0.4 |
| Irgalube 349 | 0.4 |
| C-125 | 0.5 |
| III4 | 10 |
| III6 | 88.7 |
表3实施例3各组分含量
| 原料 | 含量(％) |
| Irganox L64 | 0.5 |
| Irgalube 349 | 0.35 |
| C-125 | 0.5 |
| III4 | 10 |
| III6 | 88.65 |
实验例1
本实验例提供了实施例1-3所述组合物的制备方法，具体如下：先将基础油加热到70℃，随后加入其余各组分搅拌至均匀透明即可制成。
将实施例1-3进行各项性能评定，结果如下：
表4理化分析
对照样1为某市售针织机油产品性能数据。
以上数据表明，本发明提出的一种耐氧化长寿命的针织机油组合物，具有优良的氧化安定性、极压抗磨性等优点，不易与弹性织物纤维反应，长期使用亦不会生产油泥及酸性特质，防止机械磨损及动力损耗，延缓恶化，促进延长油品寿命，并且具有良好的可清洗性。
虽然，上文中已经用一般性说明及具体实施方案对本发明作了详尽的描述，但在本发明基础上，可以对之作一些修改或改进，这对本领域技术人员而言是显而易见的。因此，在不偏离本发明精神的基础上所做的这些修改或改进，均属于本发明要求保护的范围。
Claims (10)
1.一种耐氧化长寿命的针织机油组合物，其特征在于，包括抗氧剂、极压抗磨剂、乳化剂和基础油，其中以所述耐氧化长寿命的针织机油组合物的总重量计，所含组分如下：
抗氧剂 0.1-4.0％
极压抗磨剂 0.2-2.0％
乳化剂 0.5-5.0％。
2.根据权利要求1所述耐氧化长寿命的针织机油组合物，其特征在于，以所述耐氧化长寿命的针织机油组合物的总重量计，所述抗氧剂的含量为0.1-2.0％，可选为0.3-1.0％，进一步可选为0.3-0.5％。
3.根据权利要求1或2所述耐氧化长寿命的针织机油组合物，其特征在于，以所述耐氧化长寿命的针织机油组合物的总重量计，所述极压抗磨剂的含量为0.2-0.4％；和/或，
以所述耐氧化长寿命的针织机油组合物的总重量计，所述乳化剂的含量为0.5-2％，可选为0.5-1％。
4.根据权利要求1-3任一项所述耐氧化长寿命的针织机油组合物，其特征在于，以所述耐氧化长寿命的针织机油组合物的总重量计，所述基础油的含量为91-99％，可选为88-89％。
5.根据权利要求1-4任一项所述耐氧化长寿命的针织机油组合物，其特征在于，所述基础油采用抗氧化能力强的Ⅱ类加氢基础油或Ⅲ类加氢基础油中的至少一种；可选地，所述基础油为Ⅲ类加氢基础油III4和/或III6。
6.根据权利要求1-5任一项所述耐氧化长寿命的针织机油组合物，其特征在于，所述抗氧剂为高温酚类抗氧剂、胺类抗氧剂、胺酚混合物中的一种或多种；
其中，所述高温酚类抗氧剂可选自IRGANOX L101、IRGANOX L115、Vanlube 81；
所述胺类抗氧剂可选自IRGANOX L57、IRGANOX L06；
所述胺酚混合物可选自IRGANOX L64。
7.根据权利要求1-6任一项所述耐氧化长寿命的针织机油组合物，其特征在于，所述极压抗磨剂选自磷酸胺盐、亚磷酸三月桂基酯、亚磷酸二正丁酯、磷酸三甲苯基酯中的至少一种；
可选地，所述极压抗磨剂为Irgalube 349。
8.根据权利要求1-7任一项所述耐氧化长寿命的针织机油组合物，其特征在于，所述乳化剂选自蓖麻油磷酸酯、脂肪酸聚氧乙烯酯、烷基酚聚氧乙烯醚中的一种；
可选地，所述乳化剂为C-125(天津市助剂厂)。
9.根据权利要求1-4任一项所述耐氧化长寿命的针织机油组合物，其特征在于，所述基础油为III类加氢基础油；所述抗氧剂优选为Irganox L64；所述极压抗磨剂为Irgalube349；所述乳化剂为C-125(天津市助剂厂)。
10.权利要求1-9任一项所述耐氧化长寿命的针织机油组合物的制备方法，包括将各成分按配比加入调合容器中，在50-65℃搅拌2-3小时而成。