CN114525065A - 一种节能抗甲醛净味涂料及制备方法 - Google Patents
一种节能抗甲醛净味涂料及制备方法 Download PDFInfo
- Publication number
- CN114525065A CN114525065A CN202111604245.1A CN202111604245A CN114525065A CN 114525065 A CN114525065 A CN 114525065A CN 202111604245 A CN202111604245 A CN 202111604245A CN 114525065 A CN114525065 A CN 114525065A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy
- emulsion
- formaldehyde
- saving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于装饰涂料技术领域，公开了一种节能抗甲醛净味涂料及制备方法。该涂料包括分散相装饰彩点和连续相乳液；分散相装饰彩点包括以重量份计的以下组分：保护胶溶液30‑48份；自交联硅丙乳液20‑30份；羟乙基纤维素0.8‑2份；pH调节剂0.05‑0.3份；成膜助剂1‑1.5份；颜填料6‑8份；其他助剂0.1‑3份；水20‑45份；连续相乳液包括以重量份计的以下组分：丙烯酸乳液20‑90份；绒毛触感树脂20‑30份；相变微胶囊27‑45份；其他助剂0.1‑15份；水2‑5份；pH调节剂0.05‑0.3份；成膜助剂2‑4份。本发明提供的涂料是一种环保节能、抗甲醛净味、具备绒毛触感的内墙艺术多彩涂料。
Description
技术领域
本发明属于装饰涂料技术领域，更具体地，涉及一种节能抗甲醛净味涂料及制备方法。
背景技术
现有的微晶石涂料可用于任何场所的室内环境，赋予墙面各种各样的装饰效果，如：仿石类装饰效果，艺术涂料类装饰效果，并能提供优异的耐洗刷性能。但是，现有的微晶石涂料普通涂料装饰性单一、不具备抗甲醛功能、气味大、VOC高、环保性差、触感差，因此，目前亟待提出一种节能抗甲醛净味涂料及其制备方法，进而得到一款集个性化装饰和环保性一体的涂料。
发明内容
本发明的目的是针对现有技术的不足，提供一种节能抗甲醛净味涂料及制备方法。本发明提供的涂料是一种环保节能、抗甲醛净味、具备绒毛触感的内墙艺术多彩涂料。
为了实现上述目的，本发明一方面提供了一种节能抗甲醛净味涂料，该涂料包括分散相装饰彩点和连续相乳液；
所述分散相装饰彩点包括以重量份计的以下组分：
所述连续相乳液包括以重量份计的以下组分：
根据本发明，优选地，本发明的节能抗甲醛净味涂料包括分散相装饰彩点和连续相乳液；
所述分散相装饰彩点包括以重量份计的以下组分：
所述连续相乳液包括以重量份计的以下组分：
根据本发明，优选地，所述保护胶溶液包括以重量份计的以下组分：保护胶粉8-10份、水90-92份和杀菌防腐剂0.1-0.5份；优选地，所述保护胶粉为RD粉、RT粉、GS粉、GTS粉和S482粉中的至少一种。
在本发明中，所述保护胶溶液和羟乙基纤维素反应产生凝胶，使得本发明所得到的涂料为凝胶型材料。
根据本发明，优选地，所述分散相装饰彩点中的其他助剂包括以重量份计的以下组分：分散剂0.1-5份、消泡剂0.1-5份和杀菌防腐剂0.1-4份。
根据本发明，优选地，所述分散相装饰彩点还包括至少一种颜色的色浆，优选地，所述色浆的颜色选用黄色、红色、黑色、咖啡色、蓝色、绿色、橙色、紫色或上述颜色的衍生色。
根据本发明，优选地，所述连续相乳液中的其他助剂包括以重量份计的以下组分：防冻剂2-4份、消泡剂0.3-0.5份、增稠剂0.1-2份和杀菌防腐剂0.1-4份。
根据本发明，优选地，所述分散相装饰彩点与所述连续相乳液的重量比为(1.25-1.75):1。
根据本发明，优选地，所述消泡剂为矿物油类消泡剂和/或有机硅类消泡剂，优选为富含C10的乙氧基化异C9-C11醇与表氯醇的交联聚合物复合的矿物油类消泡剂。
根据本发明，优选地，所述分散剂为钠盐类阴离子表面活性剂。
根据本发明，优选地，所述增稠剂为疏水改性碱溶胀增稠剂。
根据本发明，优选地，所述杀菌防腐剂为吡啶硫酮锌、甲基异噻唑啉酮类和苯并异噻唑啉酮类中的至少一种。
根据本发明，优选地，所述自交联硅丙乳液是以二氧化硅为内核，以聚合丙烯酸为外壳的硅杂化核壳结构聚合丙烯酸乳液，具有很好的抗渗色性，在制作分散相装饰彩点时可以和羟乙基纤维素进行交联，加强彩点的韧性，优选为巴德富RS-8098、RS-8366和RS-5938中的至少一种。
根据本发明，优选地，所述颜填料为4000目高岭土和/或金红石型钛白粉。
根据本发明，优选地，所述丙烯酸乳液为包括氨基和/或重氮基的改性丙烯酸乳液，优选为罗门哈斯SF-105和/或SF-508。
根据本发明，优选地，所述绒毛触感树脂选自万华化学
T8552和/或广东罗斯夫新材料有限公司ROSF-5055。
根据本发明，优选地，所述相变微胶囊为直链烷烃被丙烯酸共聚体包裹形成的微型胶囊，优选地，所述直链烷烃为C9-C16的直链烷烃。
根据本发明，优选地，所述成膜助剂包括己二酸二异丁酯、戊二酸二异丁酯和琥珀酸二异丁酯中的至少一种；优选地，所述成膜助剂为生兴行Loca DA和/或Loca TS中的至少一种。
根据本发明，优选地，所述pH调节剂为伊士曼VANTEXT和/或NaOH水溶液中的至少一种。
在本发明中，所述羟乙基纤维素为亚跨龙250HBR、亚跨龙250HHBR、亚跨龙HE10K、信越HS30000-YP2、诺力昂EBS351FQ、诺力昂EBS481FQ、诺力昂EBS451FQ和诺力昂EHM500中的至少一种。
本发明另一方面提供了所述的节能抗甲醛净味涂料的制备方法，该方法包括如下步骤：
S1：将所述自交联硅丙乳液、羟乙基纤维素、pH调节剂、成膜助剂、颜填料、其他助剂、水和部分保护胶溶液混合均匀，得到基础漆；将所述基础漆与所述保护胶溶液的剩余部分混合均匀，得到凝胶固体物；对所述凝胶固体物进行剪切和分散处理，得到分散相装饰彩点；
S2：将所述丙烯酸乳液、绒毛触感树脂、相变微胶囊、其他助剂、水、pH调节剂和成膜助剂混合均匀，得到所述连续相乳液；
S3：将步骤S2制得的连续相乳液与将步骤S1制得的分散相装饰彩点混合搅拌均匀，得到所述节能抗甲醛净味涂料。
根据本发明，优选地，所述保护胶溶液的制备方法包括：将所述保护胶粉、水和杀菌防腐剂混合并在分散釜中在转速1000-1300rpm下分散均匀0.5-1.5h，进而得到所述保护胶溶液。
根据本发明，优选地，所述步骤S1还包括：将所述基础漆与所述至少一种颜色的色浆混合，得到至少一种颜色的着色基础漆，并将所述至少一种颜色的着色基础漆与所述保护胶溶液的剩余部分混合，得到着色凝胶固体物；对所述着色凝胶固体物进行剪切和分散处理，得到分散相装饰彩点；
所述剪切处理包括：利用调漆刀将所述凝胶固体物或所述着色凝胶固体物切为2-5cm3的凝胶块；
所述分散处理包括：利用分散机将所述凝胶块分散成片状彩点，进而得到分散相装饰彩点。
根据本发明，优选地，制备所述基础漆的保护胶溶液的用量占所述保护胶溶液总重量的20-30％。
根据本发明，优选地，在步骤S2中，所述连续相乳液的pH为7-10，粘度为70-80ku。
本发明的技术方案具有如下有益效果：
1)本发明提供的涂料产品采用的是复合涂层，分散相装饰彩点和连续相乳液搭配可以得到多种类型的装饰效果，即可仿制大理石的石材效果，也可制作出多种艺术涂料效果，具备很强的装饰性。
2)本发明提供的涂料产品使用的自交联硅丙乳液可形成耐水、耐候、耐污等理化性能优异的涂层，可保证本发明的涂料产品寿命在10年之久或更久。
3)本发明提供的涂料产品使用的丙烯酸乳液在干燥成膜后，漆膜中的分子结构中氨基和/或重氮基可以和空气中的游离甲醛反应，将游离甲醛吸附在该官能团中，达到除醛的效果。本发明的涂料产品在制备过程中采用了大量的环保型材料，具备优异的环保性，产品游离甲醛第三方检测结果为未检出，VOC第三方检测结果很低，气味低，为净味体系，可满足快速入住要求，空气净化性能可到达II类要求，可应用于卧室、儿童卧室、会议室等场所。
4)本发明提供的涂料产品使用了绒毛触感树脂，在涂料产品干燥成膜后，膜中会有粒径大小不同的乳胶颗粒，膜表面就会变得粗糙柔软，形成绒感效果，不会感受到混泥土墙体的冰冷质感。可以很好的提升室内使用的舒适性。
5)本发明提供的涂料产品使用了相变微胶囊，相变微胶囊可使得涂料产品进行固-液、液-固之间的转换，当温度高于相变点时，涂料产品中的相变微胶囊会固-液相变吸收热量；当温度低于相变点时，涂层中的相变微胶囊会液-固的相变而释放热量。相变微胶囊可使得涂料产品起到适当的控制室内的温度，降低能耗的作用。
本发明的其它特征和优点将在随后具体实施方式部分予以详细说明。
具体实施方式
下面将更详细地描述本发明的优选实施方式。虽然以下描述了本发明的优选实施方式，然而应该理解，可以以各种形式实现本发明而不应被这里阐述的实施方式所限制。相反，提供这些实施方式是为了使本发明更加透彻和完整，并且能够将本发明的范围完整地传达给本领域的技术人员。
以下各个实施例中，
所述自交联硅丙乳液为巴德富RS-8098、RS-8366和RS-5938中的至少一种。
所述羟乙基纤维素为亚跨龙250HBR、亚跨龙250HHBR、亚跨龙HE10K、信越HS30000-YP2、诺力昂EBS351FQ、诺力昂EBS481FQ、诺力昂EBS451FQ和诺力昂EHM500中的至少一种。
所述颜填料为4000目高岭土和/或金红石型钛白粉。
所述丙烯酸乳液为罗门哈斯SF-105和/或SF-508。
所述绒毛触感树脂选自万华化学
T8552和/或广东罗斯夫新材料有限公司ROSF-5055。
消泡剂为富含C10的乙氧基化异C9-C11醇与表氯醇的交联聚合物复合的矿物油类消泡剂。
杀菌防腐剂为吡啶硫酮锌、甲基异噻唑啉酮类和苯并异噻唑啉酮类中的至少一种。
分散剂为钠盐类阴离子表面活性剂。
增稠剂为疏水改性碱溶胀增稠剂。
所述pH调节剂为伊士曼VANTEXT和/或NaOH水溶液中的至少一种。
所述成膜助剂为生兴行Loca DA和/或Loca TS中的至少一种。
实施例1
本实施例提供一种节能抗甲醛净味涂料，该涂料包括分散相装饰彩点和连续相乳液；所述分散相装饰彩点与所述连续相乳液的重量比为1.5:1；
所述分散相装饰彩点包括以重量份计的以下组分：
保护胶溶液38份；自交联硅丙乳液25份；羟乙基纤维素1.5份；
pH调节剂0.1份；成膜助剂1.2份；颜填料7份；
分散剂0.5份；消泡剂0.7份；杀菌防腐剂0.4份；
水29.6份；适量的红色、黄色、黑色色浆；
所述连续相乳液包括以重量份计的以下组分：
丙烯酸乳液23份；绒毛触感树脂27份；相变微胶囊40份；
防冻剂3份；消泡剂0.4份；增稠剂0.5份；杀菌防腐剂0.3份；
水2.7份；pH调节剂0.1份；成膜助剂3份。
所述保护胶溶液包括以重量份计的以下组分：保护胶粉5份、水94.9份和杀菌防腐剂0.1份；所述保护胶粉为GS粉。
实施例2
本实施例提供一种节能抗甲醛净味涂料，本实施例与实施例1的区别仅在于：
在所述分散相装饰彩点中，水为31.6份；
在所述连续相乳液中，丙烯酸乳液33份；绒毛触感树脂20份；相变微胶囊27份；水12.7份；
实施例3
本实施例提供一种实施例1-2所述的节能抗甲醛净味涂料的制备方法，该方法包括如下步骤：
S1：将所述保护胶粉、水和杀菌防腐剂混合并在分散釜中在转速1250rpm下分散均匀1h，进而得到所述保护胶溶液。
S2：将所述自交联硅丙乳液、羟乙基纤维素、pH调节剂、成膜助剂、颜填料、其他助剂、水和部分保护胶溶液混合均匀，得到基础漆；将所述基础漆分成三份并分别加入红色、黄色、黑色色浆，调制成红色基础漆、黄色基础漆、黑色基础漆，并将三种颜色的基础漆与所述保护胶溶液的剩余部分混合，得到着色凝胶固体物；利用调漆刀将所述着色凝胶固体物切为2-5cm2的凝胶块；再利用分散机将所述凝胶块分散成片状彩点，进而得到分散相装饰彩点。制备所述基础漆的保护胶溶液的用量占所述保护胶溶液总重量的25％。
S3：将所述丙烯酸乳液、绒毛触感树脂、相变微胶囊、其他助剂、水、pH调节剂和成膜助剂混合均匀，得到所述连续相乳液；所述连续相乳液的pH为7-10，粘度为70-80ku。
S4：将步骤S3制得的连续相乳液与将步骤S2制得的分散相装饰彩点混合搅拌均匀，得到所述节能抗甲醛净味涂料。
对比例1
本对比例提供一种节能抗甲醛净味涂料，本对比例的涂料与实施例1的区别在于：本对比例的涂料中不含有绒毛触感树脂和相变微胶囊；
具体地：
本对比例的涂料中的分散相装饰彩点包括以重量份计的以下组分：
保护胶溶液30份；自交联硅丙乳液20份；羟乙基纤维素0.8份；
pH调节剂0.1份；成膜助剂1份；颜填料7份；
分散剂0.5份；消泡剂0.7份；杀菌防腐剂0.4份；
水39.5份；适量的红色、黄色、黑色色浆；
本对比例的涂料中的连续相乳液包括以重量份计的以下组分：
丙烯酸乳液80份；
防冻剂3份；消泡剂0.4份；增稠剂0.5份；杀菌防腐剂0.3份；
水12.7份；pH调节剂0.1份；成膜助剂3份。
所述保护胶溶液包括以重量份计的以下组分：保护胶粉5份、水94.9份和杀菌防腐剂0.1份；所述保护胶粉为GS粉。
对比例2
本对比例提供一种节能抗甲醛净味涂料，本对比例的涂料与实施例1的区别在于：本对比例的涂料中的所述连续相乳液中的绒绒毛触感树脂为10份，相变微胶囊为10份；
具体地：
本对比例的涂料中的分散相装饰彩点包括以重量份计的以下组分：
保护胶溶液32份；自交联硅丙乳液23份；羟乙基纤维素1份；
pH调节剂0.1份；成膜助剂1.2份；颜填料7份；
分散剂0.5份；消泡剂0.7份；杀菌防腐剂0.4份；
水36.1份；适量的红色、黄色、黑色色浆；
本对比例的涂料中的连续相乳液包括以重量份计的以下组分：
丙烯酸乳液60份；绒毛触感树脂10份；相变微胶囊10份；
防冻剂3份；消泡剂0.4份；增稠剂0.5份；杀菌防腐剂0.3份；
水12.7份；pH调节剂0.1份；成膜助剂3份。
所述保护胶溶液包括以重量份计的以下组分：保护胶粉5份、水94.9份和杀菌防腐剂0.1份；所述保护胶粉为GS粉。
测试例
本测试例将实施例1-2的节能抗甲醛净味涂料喷涂在基材表面，涂料的彩点颗粒均匀分布，并全覆盖基材表面，取得了微晶石的装饰效果。
本测试例将实施例1-2和对比例1-2的节能抗甲醛净味涂料喷涂在透明塑料板上，并使得喷有相同涂料的塑料板拼接成一个密闭空间，在同一环境下分别测试4个密闭空间的温度，进而测试涂层对室内温度的调节性能，结果如表1所示。
本测试例根据HG/T 4343-2012和JC/T1074-2008对实施例1-2和对比例1-2的节能抗甲醛净味涂料进行检测，结果如表1所示。
表1
| 性能测试 | 对比例1 | 对比例2 | 实施例2 | 实施例1 |
| 容器中状态 | 正常 | 正常 | 正常 | 正常 |
| 气味 | 轻微气味 | 基本无气味 | 基本无气味 | 基本无气味 |
| 空气净化性能 | I类 | I类 | I类 | I类 |
| VOC | 18 | 18 | 19 | 17 |
| 渗色情况 | 渗色严重 | 轻微渗色 | 不渗色 | 不渗色 |
| 绒毛触感 | 无 | 轻微触感 | 触感一般 | 触感柔软 |
| 低温稳定性 | 通过 | 通过 | 通过 | 通过 |
| 热储稳定性 | 彩点变糊 | 通过 | 通过 | 通过 |
| 耐洗刷性(≥1000次) | 1500 | 1500 | 1500 | 3000 |
| 洗刷后绒感效果 | 无 | 轻微触感 | 触感一般 | 触感较好 |
| 耐水性(48h) | 通过 | 通过 | 通过 | 通过 |
| 耐碱性(24h) | 通过 | 通过 | 通过 | 通过 |
| 空间温度(高温环境)/℃ | 30 | 29 | 28 | 26 |
| 空间温度(低温环境)/℃ | 10 | 11 | 12 | 13 |
以上已经描述了本发明的各实施例，上述说明是示例性的，并非穷尽性的，并且也不限于所披露的各实施例。在不偏离所说明的各实施例的范围和精神的情况下，对于本技术领域的普通技术人员来说许多修改和变更都是显而易见的。
Claims (10)
1.一种节能抗甲醛净味涂料，其特征在于，该涂料包括分散相装饰彩点和连续相乳液；
所述分散相装饰彩点包括以重量份计的以下组分：
所述连续相乳液包括以重量份计的以下组分：
2.根据权利要求1所述的节能抗甲醛净味涂料，其中，
所述保护胶溶液包括以重量份计的以下组分：保护胶粉3-25份、水75-97份和杀菌防腐剂0.1-0.5份；优选地，所述保护胶粉为RD粉、RT粉、GS粉、GTS粉和S482粉中的至少一种；
所述分散相装饰彩点中的其他助剂包括以重量份计的以下组分：分散剂0.1-5份、消泡剂0.1-5份和杀菌防腐剂0.1-4份；
所述分散相装饰彩点还包括至少一种颜色的色浆，优选地，所述色浆的颜色选用黄色、红色、黑色、咖啡色、蓝色、绿色、橙色、紫色或上述颜色的衍生色；
所述连续相乳液中的其他助剂包括以重量份计的以下组分：防冻剂2-4份、消泡剂0.3-0.5份、增稠剂0.1-2份和杀菌防腐剂0.1-4份；
所述分散相装饰彩点与所述连续相乳液的重量比为(1.25-1.75):1。
3.根据权利要求2所述的节能抗甲醛净味涂料，其中，
所述消泡剂为矿物油类消泡剂和/或有机硅类消泡剂，优选为富含C10的乙氧基化异C9-C11醇与表氯醇的交联聚合物复合的矿物油类消泡剂；
所述分散剂为钠盐类阴离子表面活性剂；
所述增稠剂为疏水改性碱溶胀增稠剂；
所述杀菌防腐剂为吡啶硫酮锌、甲基异噻唑啉酮类和苯并异噻唑啉酮类中的至少一种。
4.根据权利要求1所述的节能抗甲醛净味涂料，其中，
所述自交联硅丙乳液是以二氧化硅为内核，以聚合丙烯酸为外壳的硅杂化核壳结构聚合丙烯酸乳液，优选为巴德富RS-8098、RS-8366和RS-5938中的至少一种；
所述颜填料为4000目高岭土和/或金红石型钛白粉。
5.根据权利要求1所述的节能抗甲醛净味涂料，其中，
所述丙烯酸乳液为包括氨基和/或重氮基的改性丙烯酸乳液，优选为罗门哈斯SF-105和/或SF-508；
所述绒毛触感树脂选自万华化学
T8552和/或广东罗斯夫新材料有限公司ROSF-5055；
所述相变微胶囊为直链烷烃被丙烯酸共聚体包裹形成的微型胶囊，优选地，所述直链烷烃为C9-C16的直链烷烃。
6.根据权利要求1所述的节能抗甲醛净味涂料，其中，
所述成膜助剂包括己二酸二异丁酯、戊二酸二异丁酯和琥珀酸二异丁酯中的至少一种；优选地，所述成膜助剂为生兴行Loca DA和/或Loca TS中的至少一种；
所述pH调节剂为伊士曼VANTEXT和/或NaOH水溶液中的至少一种。
7.根据权利要求1-6中任意一项所述的节能抗甲醛净味涂料的制备方法，其特征在于，该方法包括如下步骤：
S1：将所述自交联硅丙乳液、羟乙基纤维素、pH调节剂、成膜助剂、颜填料、其他助剂、水和部分保护胶溶液混合均匀，得到基础漆；将所述基础漆与所述保护胶溶液的剩余部分混合均匀，得到凝胶固体物；对所述凝胶固体物进行剪切和分散处理，得到分散相装饰彩点；
S2：将所述丙烯酸乳液、绒毛触感树脂、相变微胶囊、其他助剂、水、pH调节剂和成膜助剂混合均匀，得到所述连续相乳液；
S3：将步骤S2制得的连续相乳液与将步骤S1制得的分散相装饰彩点混合搅拌均匀，得到所述节能抗甲醛净味涂料。
8.根据权利要求7所述的节能抗甲醛净味涂料的制备方法，其中，所述保护胶溶液的制备方法包括：将所述保护胶粉、水和杀菌防腐剂混合并在分散釜中在转速1000-1300rpm下分散均匀，进而得到所述保护胶溶液。
9.根据权利要求7或8所述的节能抗甲醛净味涂料的制备方法，其中，所述步骤S1还包括：将所述基础漆与所述至少一种颜色的色浆混合，得到至少一种颜色的着色基础漆，并将所述至少一种颜色的着色基础漆与所述保护胶溶液的剩余部分混合，得到着色凝胶固体物；对所述着色凝胶固体物进行剪切和分散处理，得到分散相装饰彩点；
所述剪切处理包括：利用调漆刀将所述凝胶固体物或所述着色凝胶固体物切为2-5cm3的凝胶块；
所述分散处理包括：利用分散机将所述凝胶块分散成片状彩点，进而得到分散相装饰彩点；
制备所述基础漆的保护胶溶液的用量占所述保护胶溶液总重量的20-30％。
10.根据权利要求7所述的节能抗甲醛净味涂料的制备方法，其中，在步骤S2中，所述连续相乳液的pH为7-10，粘度为70-80ku。