CN114411301A - 一种丝柔骨感有形混纺交织的针织面料及其制备方法 - Google Patents
一种丝柔骨感有形混纺交织的针织面料及其制备方法 Download PDFInfo
- Publication number
- CN114411301A CN114411301A CN202111494343.4A CN202111494343A CN114411301A CN 114411301 A CN114411301 A CN 114411301A CN 202111494343 A CN202111494343 A CN 202111494343A CN 114411301 A CN114411301 A CN 114411301A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- liquid ammonia
- knitted fabric
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种丝柔骨感有形混纺交织的针织面料的制备方法，步骤包括：S1、将第一纱线、第二纱线、第三纱线以及第四纱线通过编织机交织织造得到面料；S2、将步骤S1中的面料进行煮漂和染色处理；S3、将步骤S2中的面料进行液氨整理处理；S4、将步骤S3中的面料进行拉幅定形处理；液氨整理处理包括：将面料放入预烘干装置烘干、冷却后，直接进入连续多个冲满液氨的金属罐中进行液氨处理，经过多个蒸发罐加热后，通过汽蒸去除布面残余液氨、蒸汽烘干、出布。本发明的丝柔骨感有形混纺交织的针织面料，原料上采用高支数、高粘度、毛羽少的优质精梳合股棉纱，配合染色之后的液氨整理技术，使面料丝滑的同时，缩率稳定、不易变形。
Description
技术领域
本发明涉及面料加工技术领域，尤其涉及一种丝柔骨感有形混纺交织的针织面料及其制备方法。
背景技术
随着人类时代的进步、生活水平的逐渐提高，人们对服装的要求也相应提高，单一穿着功能的服装已渐渐被市场所淘汰，而新颖、上档次的面料俨然成为了消费者的宠儿。根据国际市场流行趋势，通过自主创新，研究开发纺织新材料、新技术、新工艺和新产品是企业创新能力的综合体现。
然而，现在很多厂商还是沿用面料在后整理过程中多加柔软剂或骨干整理剂等常规处理方式，导致现有的面料不够丝滑、缩率不稳定、易变形发黄等问题。
因此，亟需一种丝柔骨感有形混纺交织的针织面料及其制备方法。
发明内容
本发明的目的是针对现有技术中的不足，提供一种丝柔骨感有形混纺交织的针织面料及其制备方法。
为实现上述目的，本发明采取的技术方案是：
本发明的第一方面是提供一种丝柔骨感有形混纺交织的针织面料的制备方法，步骤包括：
S1、将第一纱线、第二纱线、第三纱线以及第四纱线通过编织机交织织造得到面料；
S2、将步骤S1中的面料进行煮漂和染色处理；
S3、将步骤S2中的面料进行液氨整理处理；
S4、将步骤S3中的面料进行拉幅定形处理；
其中，所述染色处理包括：将所述面料放入染料中，50-60℃棉纤维上色，10-40分钟后，升温至100-120℃锦纶纤维上色，保温20-50分钟后，降温至80-100℃固色10-20分钟；
所述液氨整理处理包括：将所述面料放入预烘干装置烘干、冷却后，直接进入连续多个冲满液氨的金属罐中进行液氨处理，所述液氨处理的工作速度5-40m/min，最大工作幅宽2200mm，液氨浸渍槽轧车压力0.5-10ton。所述液氨浸轧后，经过多个蒸发罐加热达到液氨整理效果后，通过汽蒸去除布面残余液氨、蒸汽烘干、出布。
优选地，所述液氨整理处理工序可在染色处理前，也可在染色后进行。
优选地，所述拉幅定形处理包括：将所述液氨整理的面料放入定型机烘箱内，110-160℃条件下进行烘干定形。
本发明的第二方面是提供一种如上所述制备方法所制得的丝柔骨感有形混纺交织的针织面料，包括：第一表层和第二表层；
其中，若干所述第一纱线在第一平面的X方向上形成若干第一纱线组，若干所述第二纱线在第一平面的Y方向上形成若干第二纱线组，若干所述第一纱线组与若干所述第二纱线组在所述第一平面形成所述第一表层，且若干所述第一纱线与若干所述第二纱线交替编织；
若干所述第三纱线在第二平面的X方向上形成若干第三纱线组，若干所述第四纱线在第二平面的Y方向上形成若干第四纱线组，若干所述第三纱线组与若干所述第四纱线组在所述第二平面形成所述第二表层，且若干所述第三纱线与若干所述第四纱线交替编织；
所述第一表层和所述第二表层在Z方向上由软性材料连接；所述X方向、所述Y方向与所述Z方向互相垂直。
优选地，所述第一纱线由30-40D的绵纶纤维材料制得。
优选地，所述第二纱线由30-40D的绵纶纤维材料制得。
优选地，所述第三纱线由70-80D的锦纶材料制得。
优选地，所述第四纱线由70-80D的锦纶材料制得。
优选地，所述软性材料为32-60S的棉纤维纱线。
优选地，所述第一表层和所述第二表层之间形成有空气层。
本发明采用以上技术方案，与现有技术相比，具有如下技术效果：
本发明的丝柔骨感有形混纺交织的针织面料，原料上采用高支数、高捻度、毛羽少的优质精梳单纱或合股棉纱，配合染色之后的液氨整理技术，使面料丝滑的同时，缩率稳定、不易变形。
附图说明
图1是本发明中丝柔骨感有形混纺交织的针织面料的结构示意图；
其中，附图标记包括：第一表层1、第二表层2。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
需要说明的是，在不冲突的情况下，本发明中的实施例及实施例中的特征可以相互组合。
下面结合附图和具体实施例对本发明作进一步说明，但不作为本发明的限定。
实施例1
如图1所示，本实施例提供一种丝柔骨感有形混纺交织的针织面料的制备方法，步骤包括：
S1、将第一纱线、第二纱线、第三纱线以及第四纱线通过编织机交织织造得到面料；
S2、将步骤S1中的面料进行煮漂染色处理；
S3、将步骤S2中的面料进行液氨整理处理；
S4、将步骤S3中的面料进行拉幅定形处理；
其中，所述染色处理包括：将所述面料放入染料中，60℃染色30分钟后，升温至100℃保温40分钟后，降温至80℃固色10分钟；
所述液氨整理处理包括：将所述面料放入预烘干装置烘干、冷却后，直接进入连续多个冲满液氨的金属罐中进行液氨处理，所述液氨处理的工作速度5-40m/min，最大工作幅宽2200mm，液氨浸渍槽轧车压力0.5-10ton。所述液氨浸轧后，经过多个蒸发罐加热达到液氨整理效果后，通过汽蒸去除布面残余液氨、蒸汽烘干、出布。
实施例2
本实施例提供一种如实施例1所述的制备方法所制得的丝柔骨感有形混纺交织的针织面料，包括：第一表层1和第二表层2；
其中，若干所述第一纱线在第一平面的X方向上形成若干第一纱线组，若干所述第二纱线在第一平面的Y方向上形成若干第二纱线组，若干所述第一纱线组与若干所述第二纱线组在所述第一平面形成所述第一表层1，且若干所述第一纱线与若干所述第二纱线交替编织；
若干所述第三纱线在第二平面的X方向上形成若干第三纱线组，若干所述第四纱线在第二平面的Y方向上形成若干第四纱线组，若干所述第三纱线组与若干所述第四纱线组在所述第二平面形成所述第二表层2，且若干所述第三纱线与若干所述第四纱线交替编织；
所述第一表层1和所述第二表层2在Z方向上由软性材料连接；所述X方向、所述Y方向与所述Z方向互相垂直。
优选地，所述第一纱线由36D的绵纶纤维材料制得。
优选地，所述第二纱线由36D的绵纶纤维材料制得。
优选地，所述第三纱线由70D的锦纶材料制得。
优选地，所述第四纱线由70D的锦纶材料制得。
优选地，所述软性材料为40S的棉纤维纱线。
优选地，所述第一表层1和所述第二表层2之间形成有空气层。
综上所述，本发明的丝柔骨感有形混纺交织的针织面料，原料上采用高支数、高粘度、毛羽少的优质精梳合股棉纱，配合染色之后的液氨整理技术，使面料丝滑的同时，缩率稳定、不易变形。
以上所述仅为本发明较佳的实施例，并非因此限制本发明的实施方式及保护范围，对于本领域技术人员而言，应当能够意识到凡运用本发明说明书及图示内容所作出的等同替换和显而易见的变化所得到的方案，均应当包含在本发明的保护范围内。
Claims (9)
1.一种丝柔骨感有形混纺交织的针织面料的制备方法，其特征在于，步骤包括：
S1、将第一纱线、第二纱线、第三纱线以及第四纱线通过编织机交织织造得到面料；
S2、将步骤S1中的面料进行煮漂和染色处理；
S3、将步骤S2中的面料进行液氨整理处理；
S4、将步骤S3中的面料进行拉幅定形处理；
其中，所述染色处理包括：将所述面料放入染料中，50-60℃棉纤维染色10-40后，升温至100-120℃锦纶纤维上色，保温20-50分钟后，降温至80-100℃固色10-20分钟；
所述液氨整理处理包括：将所述面料放入预烘干装置烘干、冷却后，直接进入连续多个冲满液氨的金属罐中进行液氨处理，所述液氨处理的工作速度为5-40m/min，最大工作幅宽为2200mm，液氨浸渍槽轧车压力0.5-10ton；液氨浸轧后，经过多个蒸发罐加热达到液氨整理效果后，通过汽蒸去除布面残余液氨、蒸汽烘、出布、拉幅定型。
2.根据权利要求1所述的制备方法，其特征在于，所述拉幅定形处理包括：将所述液氨整理的面料放入定型机烘箱内，110-160℃条件下进行烘干定形。
3.一种如权利要求1-2任一项所述制备方法所制得的丝柔骨感有形混纺交织的针织面料，其特征在于，包括：第一表层(1)和第二表层(2)；
其中，若干所述第一纱线在第一平面的X方向上形成若干第一纱线组，若干所述第二纱线在第一平面的Y方向上形成若干第二纱线组，若干所述第一纱线组与若干所述第二纱线组在所述第一平面形成所述第一表层(1)，且若干所述第一纱线与若干所述第二纱线交替编织；
若干所述第三纱线在第二平面的X方向上形成若干第三纱线组，若干所述第四纱线在第二平面的Y方向上形成若干第四纱线组，若干所述第三纱线组与若干所述第四纱线组在所述第二平面形成所述第二表层(2)，且若干所述第三纱线与若干所述第四纱线交替编织；
所述第一表层(1)和所述第二表层(2)在Z方向上由软性材料连接；所述X方向、所述Y方向与所述Z方向互相垂直。
4.根据权利要求3所述的针织面料，其特征在于，所述第一纱线由30-40D的绵纶纤维材料制得。
5.根据权利要求3所述的针织面料，其特征在于，所述第二纱线由30-40D的绵纶纤维材料制得。
6.根据权利要求3所述的针织面料，其特征在于，所述第三纱线由70-80D的锦纶材料制得。
7.根据权利要求3所述的针织面料，其特征在于，所述第四纱线由70-80D的锦纶材料制得。
8.根据权利要求3所述的针织面料，其特征在于，所述软性材料为32-60S的棉纤维纱线。
9.根据权利要求3所述的针织面料，其特征在于，所述第一表层(1)和所述第二表层(2)之间形成有空气层。