CN114406260B - 一种高可靠性cpc复合材料的生产工艺 - Google Patents
一种高可靠性cpc复合材料的生产工艺 Download PDFInfo
- Publication number
- CN114406260B CN114406260B CN202111599178.9A CN202111599178A CN114406260B CN 114406260 B CN114406260 B CN 114406260B CN 202111599178 A CN202111599178 A CN 202111599178A CN 114406260 B CN114406260 B CN 114406260B
- Authority
- CN
- China
- Prior art keywords
- copper
- molybdenum
- cpc
- plate blank
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (8)