CN1142319C - 一种环保型微晶合金镀液 - Google Patents
一种环保型微晶合金镀液 Download PDFInfo
- Publication number
- CN1142319C CN1142319C CNB00107217XA CN00107217A CN1142319C CN 1142319 C CN1142319 C CN 1142319C CN B00107217X A CNB00107217X A CN B00107217XA CN 00107217 A CN00107217 A CN 00107217A CN 1142319 C CN1142319 C CN 1142319C
- Authority
- CN
- China
- Prior art keywords
- portions
- environment
- plating solution
- alloy plating
- protecting type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种环保型微晶合金镀液，该镀液由下述化工原料按其重量份数配制而成：其中硫酸镍20-30；次磷酸钠15-20；柠檬酸6；乙酸钾12；乙酸铅0.001；硫脲3；α-α’联吡啶0.0005；水950-1000。
Description
本发明涉及一种环保型微晶合金镀液，将金属零件放入该镀液中进行处理，即可在其表面形成一层微晶颗粒的金属合金保护层。
在已有技术中，对金属表面的防腐处理及装饰处理常采用涂料或电镀方式，涂料处理的工序较多且易脱落，因此多采用电镀工艺，电镀工艺具有装饰性好，表面光洁度高并能提高零件表面硬度的特点，但是，电镀工艺的耗电量较大，而且电镀生成过程中将产生大量有毒的污染物质，将给环境造成严重污染，为此，有人在申请号为99126063.5的专利文件中提出了一种合金镀液，该技术方案可以解决上述缺陷，但是，该镀液形成的镀层比较粗糙，光洁度低。
本发明的目的在于提供一种环保型微晶合金镀液，该镀液可以在被镀物体的表面上形成金属合金镀层，并且镀层的表面光洁度较高。
本发明的目的是由下述技术方案实现的：一种环保型微晶合金镀液，该镀液由下述化工原料按其重量份数配制而成：
硫酸镍 20-30
次磷酸钠 15-20
柠檬酸 6
乙酸钾 12
乙酸铅 0.001
硫脲 3
α-α’联吡啶 0.0005
水 950-1000。
本发明与已有技术相比具有在镀件表面形成的镀层均匀度好，镀层光洁度高的优点。
以下结合实施例对本发明作进一步说明
实施例一：环保型微晶合金镀液，由下述原料按重量份数配制而成：
硫酸镍 20 克
次磷酸钠 15 克
柠檬酸 6 克
乙酸钾 12 克
乙酸铅 0.001 克
硫脲 3 克
α-α’联吡啶 0.0005克
水 950克。
该合金镀液配成后其PH值应为4-6，可以使用20％的硫酸溶液和25％的氨水调整其PH值。该合金镀液使用时用加热器将其温度保持在85℃，将被镀零件放入镀池中30-50分钟即可在被镀零件的表面生成一层镍合金镀层，镀层厚度可控制在12微米左右。
实施例二：环保型微晶合金镀液，由下述原料按重量份数配制而成：
硫酸镍 25克
次磷酸钠 18克
柠檬酸 6克
乙酸钾 12克
乙酸铅 0.001克
硫脲 3克
α-α’联吡啶 0.0005克
水 1000克。
该合金镀液配成后其PH值应为4-6。
实施例三：环保型微晶合金镀液，由下述原料按重量份数配制而成：
硫酸镍 30克
次磷酸钠 20克
柠檬酸 6克
乙酸钾 12克
乙酸铅 0.001克
硫脲 3克
α-α’联吡啶 0.0005克
水 1000克。
该合金镀液配成后其PH值应为4-6。
Claims (2)
1、一种环保型微晶合金镀液，其特征在于：由下述化工原料按其重量份数配制而成：
硫酸镍 20-30
次磷酸钠 15-20
柠檬酸 6
乙酸钾 12
乙酸铅 0.001
硫脲 3
α-α’联吡啶 0.0005
水 950-1000。
2、根据权利要求1所述的环保型微晶合金镀液，其特征在于：由下述化工原料按其重量份数配制而成：
硫酸镍 20
次磷酸钠 15
柠檬酸 6
乙酸钾 12
乙酸铅 0.001
硫脲 3
α-α’联吡啶 0.0005
水 950。