CN114015384A - 纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶 - Google Patents
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶 Download PDFInfo
- Publication number
- CN114015384A CN114015384A CN202111455862.XA CN202111455862A CN114015384A CN 114015384 A CN114015384 A CN 114015384A CN 202111455862 A CN202111455862 A CN 202111455862A CN 114015384 A CN114015384 A CN 114015384A
- Authority
- CN
- China
- Prior art keywords
- styrene
- parts
- filler
- mixture
- acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶。包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液50‑150份、填料1‑10份、偶联剂5‑20份、消泡剂1‑10份、天然树脂10‑50份、增塑剂1‑10份，所述填料为纳米硅，所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油，所述偶联剂为N‑氨乙基‑3‑氨丙基甲基二甲氧基硅烷(KH‑602)，所述增塑剂为磷酸三丁酯，该纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，能够有效的在1.45/mpa拉力下，拉伸率能够达到225‑256，与现有的方案制备出的密封胶对比，拉伸率以及拉伸强度增加50%以上。
Description
技术领域
本发明涉及密封胶技术领域，具体为纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶。
背景技术
密封胶是指随密封面形状而变形，不易流淌，有一定粘结性的密封材料。是用来填充构形间隙、以起到密封作用的胶粘剂。具有防泄漏、防水、防振动及隔音、隔热等作用。
通常以沥青物、天然树脂或合成树脂、天然橡胶或合成橡胶等干性或非干性的粘稠物为基料，配合滑石粉、白土、炭黑、钛白粉和石棉等惰性填料，再加入增塑剂、溶剂、固化剂、促进剂等制成。可分为弹性密封胶、液体密封垫料和密封腻子三大类。广泛用于建筑、交通运输、电子仪器仪表及零部件的密封，但是现有的密封胶在干燥完成之后，但是拉伸强度交底，通常在1/mpa拉伸强度下，拉伸率为140-150左右，这样就导致了现有的密封胶无法满足更多其他需求，为此我们提出了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶。
发明内容
针对现有技术的不足，本发明提供了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶。
为实现上述目的，本发明提供如下技术方案：纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液50-150份、填料1-10份、偶联剂5-20份、消泡剂1-10份、天然树脂10-50份、增塑剂1-10份。
天然树脂是指由植物、动物、天然矿物获得的树脂。植物性树脂主要是树木（如松树、桃树）的分泌物，或者已枯死树木的分泌物埋没土壤中所化成的物质。动物性树脂主要是昆虫的分泌物——虫胶，天然树脂种类很多，可根据特性、来源、输出地点等分类，如分为化石树脂和近代树脂，或分为Copal树脂和达玛树脂等。天然树脂特点是受热时变软，可熔化，在应力作用下有流动倾向，一般不溶于水，而能溶于醇、醚、酮及其他有机溶剂。
优选的，按照如下重量份原料：苯丙乳液100份、填料5份、偶联剂13份、泡剂5份、天然树脂30份、增塑剂5份。
优选的，所述填料为纳米硅，纳米硅指的是直径小于5纳米（10亿（1G）分之一米）的晶体硅颗粒。纳米硅粉具有纯度高，粒径小，分布均匀等特点。具有表面积大，高表面活性，松装密度低的特点，该产品具有无毒，无味。纳米硅粉是新一代光电半导体材料，具有较宽的间隙能半导体，也是高功率光源材料。
优选的，所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
优选的，所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
优选的，所述增塑剂为磷酸三丁酯。
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在30-32度的温度下，以320-380rmp速度搅拌50-80min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以350-400rmp速度搅拌50-80min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以320-380rmp速度搅拌50-80min，用盐酸调至PH为7-7.5，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋。
与现有技术相比，本发明提供了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，具备以下优点：本发明纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，由苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料组成，其制备出的密封胶，能够有效的在1.45/mpa拉力下，拉伸率能够达到225-256，与现有的方案制备出的密封胶对比，拉伸率以及拉伸强度增加50%以上。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
天然树脂是指由植物、动物、天然矿物获得的树脂。植物性树脂主要是树木（如松树、桃树）的分泌物，或者已枯死树木的分泌物埋没土壤中所化成的物质。动物性树脂主要是昆虫的分泌物——虫胶，天然树脂种类很多，可根据特性、来源、输出地点等分类，如分为化石树脂和近代树脂，或分为Copal树脂和达玛树脂等。天然树脂特点是受热时变软，可熔化，在应力作用下有流动倾向，一般不溶于水，而能溶于醇、醚、酮及其他有机溶剂。
所述填料为纳米硅，纳米硅指的是直径小于5纳米（10亿（1G）分之一米）的晶体硅颗粒。纳米硅粉具有纯度高，粒径小，分布均匀等特点。具有表面积大，高表面活性，松装密度低的特点，该产品具有无毒，无味。纳米硅粉是新一代光电半导体材料，具有较宽的间隙能半导体，也是高功率光源材料。
实施例一：纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液70份、填料3份、偶联剂8份、消泡剂6份、天然树脂20份、增塑剂4份。
所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
所述增塑剂为磷酸三丁酯。
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在30度的温度下，以350rmp速度搅拌60min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以380rmp速度搅拌60min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以350rmp速度搅拌60min，用盐酸调至PH为7.2，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋，每袋定额20ML。
实施例二：纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液80份、填料4份、偶联剂11份、消泡剂7份、天然树脂30份、增塑剂6份。
所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
所述增塑剂为磷酸三丁酯。
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在32度的温度下，以330rmp速度搅拌70min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以370rmp速度搅拌60min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以330rmp速度搅拌80min，用盐酸调至PH为7，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋，每袋定额20ML。
实施例三：纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液90份、填料6份、偶联剂13份、消泡剂8份、天然树脂40份、增塑剂7份。
所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
所述增塑剂为磷酸三丁酯。
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在30度的温度下，以370rmp速度搅拌70min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以400rmp速度搅拌60min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以360rmp速度搅拌65min，用盐酸调至PH为7.5，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋，每袋定额20ML。
实施例四：纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液110份、填料7份、偶联剂15份、消泡剂9份、天然树脂45份、增塑剂8份。
所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
所述增塑剂为磷酸三丁酯。
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在32度的温度下，以360rmp速度搅拌80min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以390rmp速度搅拌55min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以370rmp速度搅拌60min，用盐酸调至PH为7.5，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋，每袋定额20ML。
实施例五：纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液100份、填料5份、偶联剂13份、泡剂5份、天然树脂30份、增塑剂5份。
所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
所述增塑剂为磷酸三丁酯。
纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在30度的温度下，以370rmp速度搅拌70min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以400rmp速度搅拌50min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以350rmp速度搅拌65min，用盐酸调至PH为7.3，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋，每袋定额20ML。
结合以上的五个实施例，得到以下测定数据：
Claims (7)
1.纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于，包括：苯丙乳液、填料、偶联剂、消泡剂、增塑剂、天然树脂、苯丙乳液和填料，包含如下重量份原料：苯丙乳液50-150份、填料1-10份、偶联剂5-20份、消泡剂1-10份、天然树脂10-50份、增塑剂1-10份。
2.根据权利要求1所述的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于，按照如下重量份原料：苯丙乳液100份、填料5份、偶联剂13份、泡剂5份、天然树脂30份、增塑剂5份。
3.根据权利要求1所述的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于：所述填料为纳米硅。
4.根据权利要求1所述的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于：所述消泡剂为邻苯二甲酸二辛酯或者聚醚改性硅油。
5.根据权利要求1所述的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于：所述偶联剂为N-氨乙基-3-氨丙基甲基二甲氧基硅烷(KH-602)。
6.根据权利要求1所述的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于：所述增塑剂为磷酸三丁酯。
7.纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶，其特征在于，包括以下步骤：
S1：准备材料，苯丙乳液，填料，偶联剂，消泡剂，增塑剂，苯丙乳液和填料加入三口瓶中，在30-32度的温度下，以320-380rmp速度搅拌50-80min，使填料与苯丙乳液充分融合在一起，得混合物1；
S2：制备混合物2，向S2所得混合物1中加入偶联剂，加入装有温度计、搅拌器并且有干燥氮气保护的反应釜中，将混合物1进行加热，直至温度加热到65以上的时候，以350-400rmp速度搅拌50-80min，冷却至常温，得混合物2；
S3：制备苯丙硅酮密封胶，向将S2中所述的混合物2中加入消泡剂和增塑剂，以320-380rmp速度搅拌50-80min，用盐酸调至PH为7-7.5，最终得到了纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶；
S4：进行装袋，将制备出的纳米SiO2有机硅弹性体改性单组分苯丙硅酮密封胶装入到装袋机中的储料箱中，在装载前需要检查箱体内壁，需要保持箱体内壁整洁，无杂物，然后进行装袋。