CN113999619B - 一种热封胶带及其制备方法 - Google Patents
一种热封胶带及其制备方法 Download PDFInfo
- Publication number
- CN113999619B CN113999619B CN202111407050.8A CN202111407050A CN113999619B CN 113999619 B CN113999619 B CN 113999619B CN 202111407050 A CN202111407050 A CN 202111407050A CN 113999619 B CN113999619 B CN 113999619B
- Authority
- CN
- China
- Prior art keywords
- heat
- density polyethylene
- styrene
- butadiene
- block copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种热封胶带及其制备方法，属于热封胶带领域。该热封胶带包括底层和胶粘层，所述底层为高密度聚乙烯膜，所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯30‑65份、苯乙烯‑丁二烯‑苯乙烯嵌段共聚物25‑45份、松香树脂10‑25份、抗氧化剂0.1‑0.5份。本发明通过选择胶粘层的原料，将胶粘层和高密度聚乙烯膜形成双层结构的热封胶带，显著提高了热封胶带的耐酸碱性和粘接性能。
Description
技术领域
本发明涉及一种热封胶带及其制备方法，属于热封胶带领域。
背景技术
对于防护工作者来讲，由于可能接触到有毒有害物质，需要防护口罩、防护服装、防护眼镜、防护手套等，然而，防护服在生产的过程中，在面料与面料之间存在接缝，车缝加工后留下车针的孔隙，这样就需要用到胶带进行封死孔隙。
热封胶带是利用压胶机或者热压机加热，粘贴在面料的车缝位处，达到较好密封效果的一种防水胶带，被广泛地应用于冲锋衣、滑雪衣、帐篷、防寒服、登山服、雨衣、潜水服等防水系列产品及其他的体育运动服。但是，由于受技术和材料的影响，现有普通的热封胶带难以达到防化服的耐酸碱性、防腐蚀性的标准，具有一定的局限性，使得热封胶带在防化服的应用上受到限制。
发明内容
本发明的目的在于克服现有技术的不足，提供一种热封胶带，该热封胶带具有优异的耐酸碱性和粘接性能。
为实现上述目的，本发明采取的技术方案为：一种热封胶带，所述热封胶带包括底层和胶粘层，所述底层为高密度聚乙烯膜，所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯30-65份、苯乙烯-丁二烯-苯乙烯嵌段共聚物25-45份、松香树脂10-25份、抗氧化剂0.1-0.5份。
本发明通过将线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物、松香树脂和抗氧化剂作为胶粘层的原料，制备的胶粘层与高密度聚乙烯膜制备成热封胶带，能够提高热封胶带的耐酸碱性和粘接性。线性低密度聚乙烯(LLDPE)是乙烯与少量α-烯烃共聚形成在线性乙烯的主链上，带有非常短小的共聚单体支链的分子结构。线性低密度聚乙烯具有较高的软化温度和熔融温度，有强度大、韧性好、刚性大、耐热、耐寒性好等优点，还具有良好的耐环境应力开裂性，耐冲击强度、耐撕裂强度等性能。苯乙烯-丁二烯-苯乙烯嵌段共聚物可以和水、弱酸、弱碱等接触，具有优良的拉伸强度，表面摩擦系数大，低温性能好，电性能优良，加工性能好等特性。松香树脂含有双链和羧基活性基因，具有共轭双键和典型羧基反应，具有高软化点、高粘性，和更好的抗氧化性。抗氧化剂的作用是增加胶粘层的抗老化性能。
优选地，所述线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:5-9:2-5。
发明人经过研究发现，线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比会影响热封胶带的耐酸碱性和粘接性能，当线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:5-9:2-5时，热封胶带的耐酸碱性和粘接性能更好。
优选地，所述线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:7-9:2-5。
优选地，所述线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:7-9:3-4。
优选地，所述热封胶带的厚度为0.08-0.25mm。
优选地，所述胶粘层的厚度为热封胶带厚度的40-55％。
胶粘层的厚度需要适宜，过薄或过厚都会使热封胶带的耐酸碱性和粘接性能下降。
优选地，所述抗氧化剂为受阻酚类抗氧剂。
在可选的实施方式中，所述受阻酚类抗氧剂为四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯、β-(3，5-二叔丁基-4-羟基苯基)丙酸辛酯中的一种。
第二方面本发明还提供了一种热封胶带的制备方法，包括以下步骤：
(1)将线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物、松香树脂和抗氧化剂按比例混合均匀后得到胶粘剂；
(2)将胶粘剂和高密度聚乙烯分别通过两根螺杆挤出机熔融、塑化、同时挤出、涂布即得热封胶带。
可选的，所述胶粘剂的挤出温度为160-200℃，所述高密度聚乙烯的挤出温度为190-230℃。
与现有技术相比，本发明的有益效果为：本发明通过选择胶粘层的原料，将胶粘层和高密度聚乙烯膜形成双层结构的热封胶带，显著提高了热封胶带的耐酸碱性和粘接性能。
附图说明
图1为本发明热封胶带的结构示意图。
具体实施方式
为更好的说明本发明的目的、技术方案和优点，下面将结合具体实施例和附图对本发明作进一步的说明。
实施例1
本实施例提供了一种热封胶带，所述热封胶带包括底层和胶粘层，所述底层为高密度聚乙烯膜，所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯30份、苯乙烯-丁二烯-苯乙烯嵌段共聚物45份、松香树脂25份、抗氧化剂0.1份；所述抗氧化剂为四[β-(3，5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯。
本实施例还提供了一种热封胶带的制备方法，包括以下步骤：
(1)将线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物、松香树脂和抗氧化剂按比例混合均匀后得到胶粘剂；
(2)将胶粘剂和高密度聚乙烯分别通过两根螺杆挤出机熔融、塑化、同时挤出、实现二层共挤在一起，涂布即得热封胶带；其中所述胶粘剂的挤出温度为160℃，所述高密度聚乙烯的挤出温度为190℃；所述热封胶带的厚度为0.25mm，胶粘层的厚度为热封胶带厚度的40％，制备的热封胶带的结构示意图如图1所示。
实施例2
本实施例提供了一种热封胶带，所述热封胶带包括底层和胶粘层，所述底层为高密度聚乙烯膜，所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯40份、苯乙烯-丁二烯-苯乙烯嵌段共聚物40份、松香树脂20份、抗氧化剂0.3份；所述抗氧化剂为β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯。
本实施例还提供了一种热封胶带的制备方法，包括以下步骤：
(1)将线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物、松香树脂和抗氧化剂按比例混合均匀后得到胶粘剂；
(2)将胶粘剂和高密度聚乙烯分别通过两根螺杆挤出机熔融、塑化、同时挤出、实现二层共挤在一起，涂布即得热封胶带；其中所述胶粘剂的挤出温度为180℃，所述高密度聚乙烯的挤出温度为210℃；所述热封胶带的厚度为0.15mm，胶粘层的厚度为热封胶带厚度的50％。
实施例3
本实施例提供了一种热封胶带，所述热封胶带包括底层和胶粘层，所述底层为高密度聚乙烯膜，所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯65份、苯乙烯-丁二烯-苯乙烯嵌段共聚物25份、松香树脂10份、抗氧化剂0.5份；所述抗氧化剂为-(3，5-二叔丁基-4-羟基苯基)丙酸辛酯。
本实施例还提供了一种热封胶带的制备方法，包括以下步骤：
(1)将线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物、松香树脂和抗氧化剂按比例混合均匀后得到胶粘剂；
(2)将胶粘剂和高密度聚乙烯分别通过两根螺杆挤出机熔融、塑化、同时挤出、实现二层共挤在一起，涂布即得热封胶带；其中所述胶粘剂的挤出温度为200℃，所述高密度聚乙烯的挤出温度为230℃；所述热封胶带的厚度为0.08mm，胶粘层的厚度为热封胶带厚度的55％。
对比例1
作为本发明一种热封胶带的对比例，本对比例与实施例2的唯一区别在于：所述底层为TPU薄膜。
对比例2
作为本发明一种热封胶带的对比例，本对比例与实施例2的唯一区别在于：所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯25份、苯乙烯-丁二烯-苯乙烯嵌段共聚物50份、松香树脂25份、抗氧化剂0.3份；所述抗氧化剂为β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯。
对比例3
作为本发明一种热封胶带的对比例，本对比例与实施例2的唯一区别在于：所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯70份、苯乙烯-丁二烯-苯乙烯嵌段共聚物22份、松香树脂8份、抗氧化剂0.3份；所述抗氧化剂为β-(3,5-二叔丁基-4-羟基苯基)丙酸十八碳醇酯。
性能测试
剥离强度：实施例1-3和对比例1-3的热封胶带分别在350℃、450℃，以速度：10m/min，压力：1kg，压在橡胶布(布面)，测试剥离强度，单位为(N/cm)。
静水压：实施例1-3和对比例1-3的热封胶带分别在350℃、450℃，以速度：10m/min，压力：1kg，压在防护服面料，测试静水压，单位为mmH2O水柱。
耐酸碱性：实施例1-3和对比例1-3的热封胶带上分别滴加浓度为85％H2SO4、70％HNO3、35％HCl、6.8mol/L NaOH中，观察热封胶带发生渗透的时间，单位为h。性能测试结果如表1和表2所示。
表1
表2
从表1和表2的试验数据可知，本发明的热封胶带相比与市售热封胶带，具有较好的耐酸碱性和粘接性能，当组分含量不在本发明范围内时，热封胶带的性能显著下降。
效果例1
本效果例进一步研究了线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比对本发明热封胶带性能的影响。本效果例按照实施例2所述热封胶带的制备方法，制备了试验组1-11热封胶带。试验组1-11热封胶带的组成组分除了线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比不同之外，其他均与实施例2相同；试验组1-11热封胶带中线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比如表3所示。按照性能测试的方法测试本效果例制得的热封胶带的性能，结果如表3和表4所示。
表3
表4
从表3和表4的数据可知，当线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的总质量相同，改变三者之间的质量比，会影响热封胶带的性能，当线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:5-9:2-5时，热封胶带的性能较好，当线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:7-9:2-5时，热封胶带的性能更佳，当线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:7-9:3-4时，热封胶带的性能最好。
最后所应当说明的是，以上实施例用以说明本发明的技术方案而非对本发明保护范围的限制，尽管参照较佳实施例对本发明作了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者同等替换，而不脱离本发明技术方案的实质和范围。
Claims (7)
1.一种热封胶带，其特征在于，所述热封胶带包括底层和胶粘层，所述底层为高密度聚乙烯膜，所述胶粘层由以下重量份的组分组成：线性低密度聚乙烯30-65份、苯乙烯-丁二烯-苯乙烯嵌段共聚物25-45份、松香树脂10-25份、抗氧化剂0.1-0.5份；
所述线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:5-9:2-5。
2.如权利要求1所述的热封胶带，其特征在于，所述线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:7-9:2-5。
3.如权利要求2所述的热封胶带，其特征在于，所述线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物和松香树脂的质量比为线性低密度聚乙烯：苯乙烯-丁二烯-苯乙烯嵌段共聚物：松香树脂＝7-11:7-9:3-4。
4.如权利要求1所述的热封胶带，其特征在于，所述热封胶带的厚度为0.08-0.25mm。
5.如权利要求1所述的热封胶带，其特征在于，所述胶粘层的厚度为热封胶带厚度的40-55％。
6.如权利要求1所述的热封胶带，其特征在于，所述抗氧化剂为受阻酚类抗氧剂。
7.一种如权利要求1-6任一项所述热封胶带的制备方法，其特征在于，包括以下步骤：
(1)将线性低密度聚乙烯、苯乙烯-丁二烯-苯乙烯嵌段共聚物、松香树脂和抗氧化剂按比例混合均匀后得到胶粘剂；
(2)将胶粘剂和高密度聚乙烯分别通过两根螺杆挤出机熔融、塑化、同时挤出、涂布即得热封胶带。