CN113355944A - 一种新型环保卡纸的防腐剂制造方法 - Google Patents
一种新型环保卡纸的防腐剂制造方法 Download PDFInfo
- Publication number
- CN113355944A CN113355944A CN202110692389.0A CN202110692389A CN113355944A CN 113355944 A CN113355944 A CN 113355944A CN 202110692389 A CN202110692389 A CN 202110692389A CN 113355944 A CN113355944 A CN 113355944A
- Authority
- CN
- China
- Prior art keywords
- stirring
- mixing
- parts
- preservative
- preparing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种新型环保卡纸的防腐剂制造方法，包括以下步骤：S1：准备：准备硼酸锌：5～25份、盐酸：1～10份、卡松：3～15份、硅胶溶液：2～12份、柠檬酸铜：2～8份、四硼酸钠：5～12份、山仓子精油：3～16、苯甲酸钠：6～18、纳米二氧化硅:10～25；S2：配料一：首先取一定量的硼酸锌、盐酸、卡松，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液。该新型环保卡纸的防腐剂制造方法，通过由硼酸锌、盐酸、卡松制成的防霉液使防腐剂具有防腐的性能，加强了防腐剂的使用性能，通过纳米二氧化硅不仅可以提高防腐剂的防腐性能，也可以加强防腐剂的抗老化性。
Description
技术领域
本发明涉及防腐剂制造技术领域，具体为一种新型环保卡纸的防腐剂制造方法。
背景技术
卡纸(card paper)是介于纸和纸板之间的一类厚纸的总称，每平方米重约120克以上，用于明信片、卡片、画册衬纸等，现有的环保卡纸上都会加入防腐剂成分，防腐剂是能抑制微生物活动，防止食品腐败变质的一类食品添加剂。要使食品有一定的保藏期，就必须采用一定的措施来防止微生物的感染和繁殖。实践证明，采用防腐剂是达到上述目的的最经济、最有效和最简捷的办法之一，但是现有的防腐剂的防腐效果仍存在一些不足和缺陷。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种新型环保卡纸的防腐剂制造方法，解决了上述背景所提出的问题。
(二)技术方案
为实现上述目的，本发明提供如下技术方案：一种新型环保卡纸的防腐剂制造方法，包括以下步骤：
S1：准备：
准备硼酸锌：5～25份、盐酸：1～10份、卡松：3～15份、硅胶溶液：2～12份、柠檬酸铜：2～8份、四硼酸钠：5～12份、山仓子精油：3～16、苯甲酸钠：6～18、纳米二氧化硅:10～25。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂。
优选的，S2步骤中的第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟。
优选的，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的。
优选的，S3步骤中的混合搅拌的转速为300r/min，且混合搅拌时间为45分钟。
优选的，S4步骤中的第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟。
优选的，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的。
优选的，S5步骤中的混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。
(三)有益效果
与现有技术相比，本发明提供了一种新型环保卡纸的防腐剂制造方法，具备以下有益效果：
该新型环保卡纸的防腐剂制造方法，通过由硼酸锌、盐酸、卡松制成的防霉液使防腐剂具有防腐的性能，加强了防腐剂的使用性能，通过加入的纳米二氧化硅不仅可以提高防腐剂的防腐性能，也可以加强防腐剂的抗老化性。
具体实施方式
下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一：
一种新型环保卡纸的防腐剂制造方法，包括以下步骤：
S1：准备：
准备硼酸锌：5份、盐酸：1份、卡松：3份、硅胶溶液：2份、柠檬酸铜：2份、四硼酸钠：5份、山仓子精油：3、苯甲酸钠：6、纳米二氧化硅:10。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液，第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一，混合搅拌的转速为300r/min，且混合搅拌时间为45分钟；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二，第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂，混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。
实施例二：
一种新型环保卡纸的防腐剂制造方法，包括以下步骤：
S1：准备：
准备硼酸锌：25份、盐酸：10份、卡松：15份、硅胶溶液：12份、柠檬酸铜：8份、四硼酸钠：12份、山仓子精油：16、苯甲酸钠：18、纳米二氧化硅:25。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液，第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一，混合搅拌的转速为300r/min，且混合搅拌时间为45分钟；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二，第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂，混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。
实施例三：
一种新型环保卡纸的防腐剂制造方法，包括以下步骤：
S1：准备：
准备硼酸锌：6份、盐酸：2份、卡松：4份、硅胶溶液：3份、柠檬酸铜：3份、四硼酸钠：6份、山仓子精油：5、苯甲酸钠：7、纳米二氧化硅:11。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液，第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一，混合搅拌的转速为300r/min，且混合搅拌时间为45分钟；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二，第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂，混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。
实施例四：
一种新型环保卡纸的防腐剂制造方法，包括以下步骤：
S1：准备：
准备硼酸锌：8份、盐酸：5份、卡松：6份、硅胶溶液：5份、柠檬酸铜：4份、四硼酸钠：8份、山仓子精油：7、苯甲酸钠：10、纳米二氧化硅:15。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液，第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一，混合搅拌的转速为300r/min，且混合搅拌时间为45分钟；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二，第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂，混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。
实施例五：
一种新型环保卡纸的防腐剂制造方法，包括以下步骤：
S1：准备：
准备硼酸锌：20份、盐酸：8份、卡松：13份、硅胶溶液：10份、柠檬酸铜：6份、四硼酸钠：10份、山仓子精油：15、苯甲酸钠：16、纳米二氧化硅:22。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液，第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一，混合搅拌的转速为300r/min，且混合搅拌时间为45分钟；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二，第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂，混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。
本发明的有益效果是：通过由硼酸锌、盐酸、卡松制成的防霉液使防腐剂具有防腐的性能，加强了防腐剂的使用性能，通过加入的纳米二氧化硅不仅可以提高防腐剂的防腐性能，也可以加强防腐剂的抗老化性。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (7)
1.一种新型环保卡纸的防腐剂制造方法，其特征在于，包括以下步骤：
S1：准备：
准备硼酸锌：5～25份、盐酸：1～10份、卡松：3～15份、硅胶溶液：2～12份、柠檬酸铜：2～8份、四硼酸钠：5～12份、山仓子精油：3～16、苯甲酸钠：6～18、纳米二氧化硅:10～25。
S2：配料一：
首先取一定量的硼酸锌、盐酸、卡松，然后将备好量的硼酸锌与盐酸进行第一次搅拌混合处理，搅拌结束后，再加入已备好量的卡松，进行第二次混合搅拌处理，最后便可以得到防霉液；
S3：配料二：
取一定量的柠檬酸铜、四硼酸钠进行混合搅拌处理，得到混合物料一；
S4：配料三：
取出一定量的山仓子精油与由S3步骤得到的混合物料一进行第一次混合搅拌处理，再加入一定量的苯甲酸钠，进行第二次混合搅拌处理，最后得到混合物料二；
S5：制备：
将由S2步骤得到的防霉液、S4步骤得到的混合物料二混合，然后加入一定量的硅胶溶液、纳米二氧化硅，进行混合搅拌处理，最后再静置一段时间，便可以得到防腐剂。
2.根据权利要求1所述的一种新型环保卡纸的防腐剂制造方法，其特征在于，S2步骤中的第一次混合搅拌处理的转速为350r/min，且搅拌的时间为25分钟，第二次混合混合搅拌的转速与第一次混合搅拌处理的转速一致，且第二混合搅拌的时间为75分钟。
3.根据权利要求1所述的一种新型环保卡纸的防腐剂制造方法，其特征在于，硼酸锌是由氧化锌、壳聚糖、海藻酸钠经过恒温水浴、混合搅拌制成的。
4.根据权利要求1所述的一种新型环保卡纸的防腐剂制造方法，其特征在于，S3步骤中的混合搅拌的转速为300r/min，且混合搅拌时间为45分钟。
5.根据权利要求1所述的一种新型环保卡纸的防腐剂制造方法，其特征在于，S4步骤中的第一次混合搅拌与第二次混合搅拌的转速、时间一致，转速为280r/min，时间为60分钟。
6.根据权利要求1所述的一种新型环保卡纸的防腐剂制造方法，其特征在于，山苍子精油经山苍子经过氯化钠溶液浸泡，再粉碎，得山苍子浆料，最后加热、冷凝、静置分层得到的。
7.根据权利要求1所述的一种新型环保卡纸的防腐剂制造方法，其特征在于，S5步骤中的混合搅拌的转速为250r/min，搅拌时间为120分钟，且静置时间为7天。