CN103741448B - 一种抗收缩防菌的棉服处理液及其制备方法 - Google Patents
一种抗收缩防菌的棉服处理液及其制备方法 Download PDFInfo
- Publication number
- CN103741448B CN103741448B CN201310688858.7A CN201310688858A CN103741448B CN 103741448 B CN103741448 B CN 103741448B CN 201310688858 A CN201310688858 A CN 201310688858A CN 103741448 B CN103741448 B CN 103741448B
- Authority
- CN
- China
- Prior art keywords
- parts
- treatment fluid
- cotton clothes
- fungi
- clothes treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种抗收缩防菌的棉服处理液及其制备方法,棉服处理液由以下成分按照重量比组成:氧化锌粉末为2~4份、玫瑰精油为3~5份、油酸聚氧乙烯酯为1~2份、丙二醇为6~9份、羟乙基纤维素为3~6份、水150~170份。上述原料组成通过混合、搅拌等方式制备得到棉服处理液、制备得到的棉服处理液具有抗收缩和防菌的功能。
Description
技术领域
本发明涉及一种棉服处理液及其制备方法,特别是涉及一种具有抗收缩、防菌功能的棉服处理液。
背景技术
棉质衣服是人们经常穿着的一种衣服,棉质衣服在经过多次洗涤后,会出现一定的收缩现象,收缩后衣服的尺寸变小,影响了人们的正常穿着,降低棉质衣服在多次洗涤后的收缩率是非常有必要的。同时,随着人们生活水平的提高,人们对棉质衣服的抗菌性能也越来越关注,提高棉质衣服的抗菌性能,可以降低细菌的污染,提高衣服的洁净程度。进而扩大棉服的应用领域。
发明内容
要解决的技术问题:普通棉服抗菌能力差、收缩率高的问题。
技术方案:本发明公开了一种抗收缩防菌的棉服处理液及其制备方法,棉服处理液由以下成分按照重量比组成:氧化锌粉末为2~4份、玫瑰精油为3~5份、油酸聚氧乙烯酯为1~2份、丙二醇为6~9份、羟乙基纤维素为3~6份、水150~170份。
一种抗收缩防菌的棉服处理液的制备方法,制备方法包括以下步骤:(1)打开搅拌罐,向其中加入水为150~170份,加热水至50℃~60℃;(2)水温稳定后向水中加入氧化锌粉末为2~4份、玫瑰精油为3~5份,用搅拌桨进行搅拌,搅拌转速为140rpm~160rpm,搅拌时间为5min~10min;(3)再向搅拌罐中加入油酸聚氧乙烯酯为1~2份、丙二醇为6~9份、羟乙基纤维素为3~6份,再次进行搅拌,搅拌转速为120rpm~130rpm,搅拌时间为10min~15min;(4)搅拌结束后,将处理液冷却至室温,封装保存。
其中,氧化锌粉末的目数优选为400目~500目。加入的玫瑰精油优选为5份。加入的羟乙基纤维素优选为3份。
有益效果:经过本处理液处理过的棉服具有抗收缩和防菌的功能,对黒曲霉的抑制率为94.8%至97.2%,洗涤30次后收缩率只有0.4%至0.9%。
具体实施方式
实施例1
(1)打开搅拌罐,向其中加入水为150kg,加热水至60℃;(2)水温稳定后向水中加入氧化锌粉末为4kg、玫瑰精油为3kg,用搅拌桨进行搅拌,搅拌转速为160rpm,搅拌时间为5min;(3)再向搅拌罐中加入油酸聚氧乙烯酯为2kg、丙二醇为6kg、羟乙基纤维素为6kg,再次进行搅拌,搅拌转速为130rpm,搅拌时间为10min;(4)搅拌结束后,将处理液冷却至室温,封装保存。
实施例2
(1)打开搅拌罐,向其中加入水为160kg,加热水至50℃;(2)水温稳定后向水中加入氧化锌粉末为2kg、玫瑰精油为5kg,用搅拌桨进行搅拌,搅拌转速为150rpm,搅拌时间为8min;(3)再向搅拌罐中加入油酸聚氧乙烯酯为1kg、丙二醇为7kg、羟乙基纤维素为4kg,再次进行搅拌,搅拌转速为120rpm,搅拌时间为15min;(4)搅拌结束后,将处理液冷却至室温,封装保存。
实施例3
(1)打开搅拌罐,向其中加入水为170kg,加热水至55℃;(2)水温稳定后向水中加入氧化锌粉末为3kg、玫瑰精油为4kg,用搅拌桨进行搅拌,搅拌转速为140rpm,搅拌时间为10min;(3)再向搅拌罐中加入油酸聚氧乙烯酯为2kg、丙二醇为9kg、羟乙基纤维素为3kg,再次进行搅拌,搅拌转速为130rpm,搅拌时间为10min;(4)搅拌结束后,将处理液冷却至室温,封装保存。
取纯棉质棉服,用实施例1、实施例2、实施例3的处理液常温下浸泡1h后甩干。甩干后用洗衣机在标准洗涤模式下清洗30次。之后棉服的收缩率。将被实施例1、实施例2、实施例3浸泡过甩干后的棉服进行防菌试验。菌种为黒曲霉,防菌实验测试标准为AATCC30,测试结果如下表。
实施例1 | 实施例2 | 实施例3 | |
收缩率 | 0.9% | 0.4% | 0.7% |
黒曲霉抑制率 | 94.8% | 96.3% | 97.2% |
经过本发明的处理液处理过的棉服具有优良的抗收缩和防菌的功能。
Claims (4)
1.一种抗收缩防菌的棉服处理液,其特征在于棉服处理液由以下成分按照重量比组成:氧化锌粉末为2~4份、玫瑰精油为3~5份、油酸聚氧乙烯酯为1~2份、丙二醇为6~9份、羟乙基纤维素为3~6份、水150~170份;
所述的一种抗收缩防菌的棉服处理液的制备方法,包括以下步骤:(1)打开搅拌罐,向其中加入水为150~170份,加热水至50℃~60℃;(2)水温稳定后向水中加入氧化锌粉末为2~4份、玫瑰精油为3~5份,用搅拌桨进行搅拌,搅拌转速为140rpm~160rpm,搅拌时间为5min~10min;(3)再向搅拌罐中加入油酸聚氧乙烯酯为1~2份、丙二醇为6~9份、羟乙基纤维素为3~6份,再次进行搅拌,搅拌转速为120rpm~130rpm,搅拌时间为10min~15min;(4)搅拌结束后,将处理液冷却至室温,封装保存。
2.根据权利要求1所述的一种抗收缩防菌的棉服处理液,其特征在于氧化锌粉末的目数为400目~500目。
3.根据权利要求1所述的一种抗收缩防菌的棉服处理液,其特征在于加入的玫瑰精油为5份。
4.根据权利要求1所述的一种抗收缩防菌的棉服处理液,其特征在于加入的羟乙基纤维素为3份。