CN113213833B - 一种粉煤灰基泡沫地聚合物及其制备方法和应用 - Google Patents
一种粉煤灰基泡沫地聚合物及其制备方法和应用 Download PDFInfo
- Publication number
- CN113213833B CN113213833B CN202110662284.0A CN202110662284A CN113213833B CN 113213833 B CN113213833 B CN 113213833B CN 202110662284 A CN202110662284 A CN 202110662284A CN 113213833 B CN113213833 B CN 113213833B
- Authority
- CN
- China
- Prior art keywords
- fly ash
- based foamed
- foamed geopolymer
- parts
- geopolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种粉煤灰基泡沫地聚合物及其制备方法和应用，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：粉煤灰基材料900‑1000份；复合碱溶液600‑700份；增稠剂0‑10份；稳泡剂A 2‑6份；减水剂5‑10份；发泡剂20‑40份。本发明的制备方法简单，不需要对原材料进行球磨、水洗、煅烧等工艺，减少了粉磨设备、水洗设备、污水处理设备及煅烧设备的投入，降低了能耗及碳排放。本发明利用粉煤灰基材料作为主要原材料制备的粉煤灰基泡沫地聚合物具有较低的表观密度和较高的早期强度，可用于装配式建筑领域。
Description
技术领域
本发明属于建筑材料技术领域，涉及到工业固体废弃物再利用、低碳胶凝材料、绿色建筑技术，具体涉及一种粉煤灰基泡沫地聚合物及其制备方法和应用，尤其涉及一种早强超轻的粉煤灰基泡沫地聚合物及其制备方法和应用。
背景技术
近年来，在国家大力推动装配式建筑发展的政策下，对于预制构件提出了新的需求，即用于构件的混凝土制品早期能快速形成强度，有助于装配式构件场内模具的周转，成品构件的出厂运输，减少构件场内堆放。泡沫混凝土作为一种多孔轻质的材料，具有良好的隔热、隔音等特点，是制备非结构预制构件的理想材料。然而，混凝土制品生产原料-水泥的生产需要消耗大量的天然资源和能源，同时排放大量二氧化碳，与我国低碳节能、绿色发展的主题及本世纪三十年代的“碳达峰”目标相悖。另一方面，我国在经济高速发展，工业化进程不断提升的过程中，产生了大量的工业固体废弃物。近年数据显示，作为工业固体废弃物之一的粉煤灰年产生量保持在5.6亿吨左右，综合利用率约为75.96％，其中中西部地区粉煤灰综合利用率仅为50％。大量粉煤灰堆存，既占用了大量的土地，其所含的重金属元素也给环境带来极大威胁。
目前，通过强碱性溶液对富含活性硅铝质的粉煤灰进行化学激发制备地聚合物是实现粉煤灰建筑制品化的新兴技术。同时，地聚合技术对重金属的高效固化是实现固废资源无害化的重要保障。利用过氧化氢在碱性条件下分解产生氧气的特性，在地聚合物中加入过氧化氢溶液能够制备泡沫地聚合物，实现替代传统泡沫混凝土的目的。然而，以粉煤灰为原料的地聚合物在反应初期生成的胶体以富铝凝胶(GEL I)为主，此类产物为主的地聚合物抗压强度非常低，需要通过后期反应，将富铝凝胶转变成富硅凝胶(GEL Ⅱ)，强度才会提升，因此无法满足装配式预制构件的脱模强度需求。强碱性溶液控制粉煤灰中硅、铝等元素浸出，促进地聚合反应进行；但过高的pH值会加剧过氧化氢分解，给形成稳定的泡沫骨架结构带来极大困难。对于超轻泡沫地聚合物，过量的过氧化氢在强碱性环境下发泡效果更易失控。因此，地聚合物早期强度形成所依赖的强碱性条件，与过氧化氢在高碱性条件下的剧烈反应这一矛盾构成了制备早强超轻粉煤灰基泡沫地聚合物所需克服的难点。
CN108975795A公开了一种泡沫地聚合物及其制备方法和应用。该泡沫地聚合物包括以下组分：偏高岭土30～50重量份、碱激发剂40～50重量份、粉煤灰1～4重量份、发泡剂2～5重量份、稳泡剂0.3～0.7重量份、改性剑麻纤维0.3～0.8重量份、石蜡乳液1～4重量份、水5～10重量份、无水乙醇0.3～0.7重量份。该发明的泡沫地聚合物与传统的抗渗防水水泥基材料及水泥基防护材料相比，材料抗裂性好、防水性能优异，具有优良的耐久性能，能较长时间保持良好的使用性能，具有耐酸、碱腐蚀、抗冻融、抗碳化等性能，能广泛应用于隧道复合式衬砌等基础工程领域。但该发明的泡沫地聚合物不具有早强超轻的特点，并且所用到的固体废弃物粉煤灰的量也较少。
因此，在本领域中，期待开发一种可充分利用固体废弃物，并且早强超轻的粉煤灰基泡沫地聚合物。
发明内容
针对现有技术的不足，本发明的目的在于提供一种粉煤灰基泡沫地聚合物及其制备方法和应用，特别提供一种早强超轻的粉煤灰基泡沫地聚合物及其制备方法和应用。本发明的粉煤灰基泡沫地聚合物同时具有早期强度高、孔隙率高的优点，特别适宜于装配式非结构预制构件的生产。同时，粉煤灰基泡沫地聚合物的规模化生产不仅可节约原材料成本，还可缓解固体废弃物堆积对土壤及地下水环境的污染。本发明的粉煤灰基泡沫地聚合物主要用于装配式建筑材料领域。
为达到此发明目的，本发明采用以下技术方案：
第一方面，本发明提供一种粉煤灰基泡沫地聚合物，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：
本发明的粉煤灰基泡沫地聚合物利用粉煤灰基材料作为主要原材料，降低了生产成本，适用于大规模生产，同时，有效解决了工业废渣处置的问题，节约了自然资源，保护了生态环境。本发明的粉煤灰基泡沫地聚合物具有较低表观密度的同时，具有较高的早期强度。
与传统水泥基泡沫材料相比，本发明的粉煤灰基泡沫地聚合物实现了粉煤灰等工业固废的大规模资源化利用，具有制备能耗低、碳排放量小的特点。与现有地聚物基泡沫材料相比，本发明通过复合碱溶液调节发泡剂发泡速度、稳泡剂A调节泡沫破裂时间、增稠剂锁定泡沫空间分布的方式，能够使粉煤灰基泡沫地聚合物具备大量均匀、细密孔隙的同时，获得较高的早期强度。
本发明的粉煤灰基泡沫地聚合物在粉煤灰利用率可达到90％以上的同时，能够实现行业标准JGT266-2011《泡沫混凝土》规定的A05级别干密度，并在1天蒸汽养护、7天标准养护后即可达到C3级别的强度等级，克服了传统制备手段的粉煤灰基发泡混凝土在高粉煤灰利用率、低密度、高强度三者无法同时协调实现的问题，满足了装配式工厂轻质构件尽早脱模、加快模具周转的生产需求。
在本发明中，所述粉煤灰基泡沫地聚合物的制备原料中，粉煤灰基材料的用量可以为900份、910份、920份、930份、940份、950份、960份、970份、980份、990份或1000份等。
在本发明中，所述粉煤灰基泡沫地聚合物的制备原料中，复合碱溶液的用量可以为600份、610份、620份、630份、640份、650份、660份、670份、680份、690份或700份等。
若复合碱溶液的用量低于600份，其无法充分激发粉煤灰基材料的活性，影响最终产品的强度，若复合碱溶液的用量高于700份，容易引起产品表面泛碱发白，影响产品表面质量。
在本发明中，所述粉煤灰基泡沫地聚合物的制备原料中，增稠剂的用量可以为0份、1份、2份、3份、4份、5份、6份、7份、8份、9份或10份等。
在本发明中，所述粉煤灰基泡沫地聚合物的制备原料中，稳泡剂A的用量可以为2份、3份、4份、5份或6份等。
在本发明中，所述粉煤灰基泡沫地聚合物的制备原料中，减水剂的用量可以为5份、6份、7份、8份、9份或10份等。
在本发明中，所述粉煤灰基泡沫地聚合物的制备原料中，发泡剂的用量可以为20份、23份、25份、28份、30份、33份、35份、38份或40份等。
若发泡剂的用量低于20份，会使得最终产品达不到发泡效果，表观密度高于预期，无法实现产品轻质的目的，若发泡剂的用量高于40份，会使得最终产品发泡过量，产品表观密度低于预期，但是产品强度无法达到要求。
优选地，所述粉煤灰基材料通过以下制备方法制备得到：
将粉煤灰和钙质材料混合，得到所述粉煤灰基材料。
本发明中的粉煤灰为火力发电厂煤粉燃烧后的残余产物。
优选地，以所述粉煤灰基材料的质量为100％计，粉煤灰的含量为90％-100％，例如90％、91％、92％、93％、94％、95％、96％、97％、98％、99％或100％等，钙质材料的含量为0％-10％，例如0％、1％、2％、3％、4％、5％、6％、7％、8％、9％或10％等。
优选地，所述钙质材料包括水泥、矿渣、石膏或偏高岭土中的任意一种或至少两种的组合。
优选地，所述复合碱溶液通过以下制备方法制备得到：
将复合碱激发剂、金属络合剂和稳泡剂B混合，得到所述复合碱溶液。
优选地，以所述复合碱溶液的质量为100％计，复合碱激发剂的含量为95％-98％，例如95％、95.5％、96％、96.5％、97％、97.5％或98％等，金属络合剂的含量为0.05％-0.5％，例如0.05％、0.1％、0.2％、0.3％、0.4％或0.5％等，稳泡剂B的含量为1.95％-4.5％，例如1.95％、2％、2.5％、3％、3.5％、4％或4.5％等。
若不添加金属络合剂会导致泡沫形成的孔隙粗大，产品强度下降，若金属络合剂的含量高于0.5％，会导致产品流动性差，入模困难。
优选地，所述复合碱激发剂的模数为1.0-1.5，例如1.0、1.1、1.2、1.3、1.4或1.5等。
优选地，所述金属络合剂包括三乙醇胺、甲基二乙醇胺、二异丙醇胺、二乙醇单异丙醇胺、三乙醇胺或三异丙醇胺中的任意一种或至少两种的组合。
优选地，所述金属络合剂的固含量不低于78％，例如78％、80％、83％、85％、88％或90％等。
优选地，所述稳泡剂B包括十二烷基苯磺酸钠粉末、十二烷基硫酸钠粉末、磷酸三钠粉末或十二烷基硫酸钙粉末中的任意一种或至少两种的组合。
优选地，所述稳泡剂B的纯度不低于88％。
优选地，所述复合碱激发剂通过以下制备方法制备得到：
将氢氧化钠粉末和水倒入水玻璃中，搅拌，得到所述复合碱激发剂。
优选地，以所述复合碱激发剂的质量为100％计，氢氧化钠粉末的含量为8.5％-9％，例如8.5％、8.6％、8.7％、8.8％、8.9％或9％等，水的含量为4.5％-7％，例如4.5％、5％、5.5％、6％、6.5％或7％等，水玻璃的含量为84％-87％，例如84％、84.5％、85％、85.5％、86％、86.5％或87％等。
优选地，所述氢氧化钠粉末的纯度不低于96％。
优选地，所述水为自来水。
优选地，所述水玻璃的模数为1.0-3.8，例如1.0、1.5、2.0、2.5、3.0、3.5或3.8等，波美度为34.0-42.0，例如34.0、35.0、36.0、37.0、38.0、39.0、40.0、41.0或42.0等。
优选地，所述增稠剂包括甲基纤维素醚和/或羧甲基纤维素醚，优选甲基纤维素醚和羧甲基纤维素醚。
优选地，所述增稠剂的纯度不低于96％。
优选地，所述增稠剂的粘度不低于30000厘泊，例如30000厘泊、35000厘泊、40000厘泊、45000厘泊或50000厘泊等。
优选地，所述稳泡剂A包括磷酸三钠和/或硬脂酸钙粉末。
优选地，所述磷酸三钠的纯度不低于98％。
优选地，所述硬脂酸钙粉末的纯度不低于99％。
优选地，所述减水剂包括聚羧酸减水剂、萘磺酸盐系减水剂、脂肪系减水剂、木质素磺酸盐类减水剂或氨基磺酸盐系减水剂中的任意一种或至少两种的组合。
优选地，所述发泡剂包括过氧化氢溶液。
优选地，所述过氧化氢溶液的含量不低于30％，例如30％、33％、35％、38％或40％等。在本发明中，过氧化氢溶液的含量不低于30％指的是在过氧化氢溶液中，过氧化氢溶质的质量含量不低于30％。
第二方面，本发明提供一种第一方面所述的粉煤灰基泡沫地聚合物的制备方法，所述制备方法包括以下步骤：
(1)将配方量的粉煤灰基材料、复合碱溶液、增稠剂、稳泡剂A和减水剂搅拌，得到料浆；
(2)将发泡剂加入步骤(1)得到的料浆中，搅拌，得到混合物，而后将混合物注入模具中；
(3)将步骤(2)的混合物及模具放入养护舱内养护，脱模，而后将脱模后的样品放置于标准养护环境下养护，得到所述粉煤灰基泡沫地聚合物。
优选地，步骤(1)所述搅拌在搅拌锅中进行。
优选地，步骤(1)所述搅拌的搅拌叶公转转速为115-135r/min，例如115r/min、120r/min、125r/min、130r/min或135r/min等，自转转速为275-295r/min，例如275r/min、280r/min、285r/min、290r/min或295r/min等。
优选地，步骤(1)所述搅拌的时间为4-6min，例如4min、4.5min、5min、5.5min或6min等。
优选地，步骤(2)所述搅拌的搅拌叶公转转速为57-67r/min，例如57r/min、60r/min、63r/min、65r/min或67r/min等，自转转速为135-145r/min，例如135r/min、138r/min、140r/min、143r/min或145r/min等。
优选地，步骤(2)所述搅拌的时间为20-40s，例如20s、23s、25s、28s、30s、33s、35s、38s或40s等。
优选地，步骤(2)所述将混合物注入模具中为将混合物注入至模具的1/2深度处。
优选地，将混合物注入模具中之后，在模具上覆盖聚乙烯薄膜，避免水分蒸发。
优选地，步骤(3)所述养护舱内的温度为65-75℃，例如65℃、68℃、70℃、73℃或75℃等。
优选地，步骤(3)所述放入养护舱内养护的时间为12-24h，例如12h、14h、15h、16h、18h、20h、22h或24h等。
优选地，步骤(3)所述标准养护环境的温度为18-22℃，例如18℃、19℃、20℃、21℃或22℃等，湿度为95％以上，例如95％、96％、97％或98％等。
优选地，步骤(3)所述放置于标准养护环境下养护的时间为7天。
第三方面，本发明提供第一方面所述的粉煤灰基泡沫地聚合物在建筑材料中的应用。
优选地，所述建筑材料包括装配式建筑材料。
相对于现有技术，本发明具有以下有益效果：
(1)本发明利用粉煤灰基材料作为主要原材料制备粉煤灰基泡沫地聚合物，降低了生产成本，适用于大规模生产，同时，本发明有效解决了工业废渣处置的问题，节约了自然资源，保护了生态环境；
(2)本发明的粉煤灰基泡沫地聚合物具有较低表观密度(421.7-521.4kg/m3)的同时，具有较高的早期强度(7天抗压强度：1.56-3.60MPa)，且构件脱模后强度仍快速发展，可避免构件吊运等过程造成的损耗，有助于装配式构件场内模具的周转，成品构件的出厂运输，减少构件场内堆放带来的仓储成本压力；
(3)本发明的粉煤灰基泡沫地聚合物的制备方法，不需要对原材料进行球磨、水洗、煅烧等工艺，减少了粉磨设备、水洗设备、污水处理设备及煅烧设备的投入，降低能耗及碳排放，且无重化学试剂气味，成本低，对大气环境无污染。
附图说明
图1为本发明实施例中粉煤灰基泡沫地聚合物所用原料示意图。
图2为实施例1制备的粉煤灰基泡沫地聚合物的成品外观图。
图3为实施例1制备的粉煤灰基泡沫地聚合物的X射线断层扫描重构投影图。
图4为实施例1制备的粉煤灰基泡沫地聚合物的X射线断层扫描重构后的孔隙分布图。
图5为实施例2制备的粉煤灰基泡沫地聚合物的成品外观图。
图6为实施例2制备的粉煤灰基泡沫地聚合物的X射线断层扫描重构投影图。
图7为实施例2制备的粉煤灰基泡沫地聚合物的X射线断层扫描重构后的孔隙分布图。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。本领域技术人员应该明了，所述实施例仅仅是帮助理解本发明，不应视为对本发明的具体限制。
除非另有定义，本发明所使用的所有的技术和科学术语与属于本发明的技术领域的技术人员通常理解的含义相同。本发明在说明书中所使用的术语只是为了描述具体的实施例，不是旨在于限制本发明。
本发明实施例中用到的粉煤灰为国标GB/T 1596-2017《用于水泥和混凝土的粉煤灰》规定的II级或以上的粉煤灰，SO3≤3.0；本发明实施例中用到的矿渣为不低于国标GB/T18046-2017《用于水泥、砂浆和混凝土中的粒化高炉矿渣粉》规定的S95级别粒化高炉矿渣粉。
实施例1
在本实施例中提供一种粉煤灰基泡沫地聚合物，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：
其中，稳泡剂A为纯度不低于99％的硬脂酸钙粉末；减水剂为聚羧酸减水剂；发泡剂为过氧化氢溶液，其含量为30％；粉煤灰基材料为100％的粉煤灰。
复合碱溶液通过以下制备方法制备得到：
将复合碱激发剂、金属络合剂和稳泡剂B充分搅拌混合，得到所述复合碱溶液。
以复合碱溶液的质量为100％计，复合碱激发剂的含量为96％，金属络合剂的含量为0.3％，稳泡剂B的含量为3.7％；复合碱激发剂的模数为1.0；金属络合剂为三乙醇胺，其固含量不低于78％；稳泡剂B为十二烷基苯磺酸钠粉末，其纯度不低于88％。
复合碱激发剂通过以下制备方法制备得到：
将氢氧化钠粉末和水倒入水玻璃中，充分搅拌后密封，静置备用，得到所述复合碱激发剂；
以所述复合碱激发剂的质量为100％计，氢氧化钠粉末的含量为9％，水的含量为5.8％，水玻璃的含量为85.2％；氢氧化钠粉末的纯度不低于96％；水为自来水；水玻璃的模数为1.0，波美度为34.0。
粉煤灰基泡沫地聚合物的制备方法包括以下步骤：
(1)将配方量的粉煤灰基材料、复合碱溶液、稳泡剂A和减水剂放入搅拌锅中，以搅拌叶公转115r/min、自转275r/min的转速，快速搅拌6min，确保净浆均匀，无固体粉体下沉，得到料浆；
(2)将发泡剂迅速加入步骤(1)得到的料浆中，以搅拌叶公转57r/min、自转135r/min的转速，慢速搅拌40s后，得到混合物，而后将混合物快速注入至模具的1/2深度处，然后在模具上覆盖聚乙烯薄膜，避免水分流失；
(3)将步骤(2)的混合物及模具放入温度为65℃的养护舱内养护24h后脱模，而后将脱模后的样品放置于温度为20℃，湿度为95％的标准养护环境下养护7天，得到所述粉煤灰基泡沫地聚合物。
本实施例中粉煤灰基泡沫地聚合物所用原料示意图如图1所示。
本实施例制备的粉煤灰基泡沫地聚合物的成品外观图如图2所示，X射线断层扫描重构投影图如图3所示，X射线断层扫描重构后的孔隙分布图如图4所示。从图中可以看出，本实施例制备的粉煤灰基泡沫地聚合物样品孔隙致密均匀，孔隙独立性好，孔隙连通性限制高，样品骨架无可见缺陷，为孔隙提供的结构性支撑强。图2中的粉煤灰基泡沫地聚合物样品的大小并不表示本实施例制备的样品大小，这只是为了做测试所截取出来的尺寸。
实施例2
在本实施例中提供一种粉煤灰基泡沫地聚合物，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：
其中，增稠剂为纯度不低于96％、粘度为30000厘泊的甲基纤维素醚；稳泡剂A为纯度不低于99％的硬脂酸钙粉末；减水剂为聚羧酸减水剂；发泡剂为过氧化氢溶液，其含量为30％。
粉煤灰基材料通过以下制备方法制备得到：
将粉煤灰和钙质材料放入搅拌锅中，充分搅拌混合，得到所述粉煤灰基材料。
以粉煤灰基材料的质量为100％计，粉煤灰的含量为90％，钙质材料的含量为10％；钙质材料为矿渣。
复合碱溶液通过以下制备方法制备得到：
将复合碱激发剂、金属络合剂和稳泡剂B充分搅拌混合，得到所述复合碱溶液。
以复合碱溶液的质量为100％计，复合碱激发剂的含量为95％，金属络合剂的含量为0.5％，稳泡剂B的含量为4.5％；复合碱激发剂的模数为1.5；金属络合剂为三乙醇胺，其固含量不低于78％；稳泡剂B为十二烷基苯磺酸钠粉末，其纯度不低于88％。
复合碱激发剂通过以下制备方法制备得到：
将氢氧化钠粉末和水倒入水玻璃中，充分搅拌后密封，静置备用，得到所述复合碱激发剂；
以所述复合碱激发剂的质量为100％计，氢氧化钠粉末的含量为8.5％，水的含量为4.5％，水玻璃的含量为87％；氢氧化钠粉末的纯度不低于96％；水为自来水；水玻璃的模数为3.8，波美度为42.0。
粉煤灰基泡沫地聚合物的制备方法包括以下步骤：
(1)将配方量的粉煤灰基材料、复合碱溶液、增稠剂、稳泡剂A和减水剂放入搅拌锅中，以搅拌叶公转135r/min、自转295r/min的转速，快速搅拌4min，确保净浆均匀，无固体粉体下沉，得到料浆；
(2)将发泡剂迅速加入步骤(1)得到的料浆中，以搅拌叶公转67r/min、自转145r/min的转速，慢速搅拌20s后，得到混合物，而后将混合物快速注入至模具的1/2深度处，然后在模具上覆盖聚乙烯薄膜，避免水分流失；
(3)将步骤(2)的混合物及模具放入温度为75℃的养护舱内养护24h后脱模，而后将脱模后的样品放置于温度为20℃，湿度为96％的标准养护环境下养护7天，得到所述粉煤灰基泡沫地聚合物。
本实施例中粉煤灰基泡沫地聚合物所用原料示意图如图1所示。
本实施例制备的粉煤灰基泡沫地聚合物的成品外观图如图5所示，X射线断层扫描重构投影图如图6所示，X射线断层扫描重构后的孔隙分布图如图7所示。从图中可以看出，本实施例制备的粉煤灰基泡沫地聚合物样品孔隙致密均匀，孔隙独立性好，孔隙连通性限制高，样品骨架无可见缺陷，为孔隙提供的结构性支撑强。图5中的粉煤灰基泡沫地聚合物样品的大小并不表示本实施例制备的样品大小，这只是为了做测试所截取出来的尺寸。
实施例3
在本实施例中提供一种粉煤灰基泡沫地聚合物，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：
其中，增稠剂为纯度不低于96％、粘度为35000厘泊的羧甲基纤维素醚；稳泡剂A为纯度不低于98％的磷酸三钠；减水剂为聚羧酸减水剂；发泡剂为过氧化氢溶液，其含量为30％。
粉煤灰基材料通过以下制备方法制备得到：
将粉煤灰和钙质材料放入搅拌锅中，充分搅拌混合，得到所述粉煤灰基材料。
以粉煤灰基材料的质量为100％计，粉煤灰的含量为92％，钙质材料的含量为8％；钙质材料为矿渣。
复合碱溶液通过以下制备方法制备得到：
将复合碱激发剂、金属络合剂和稳泡剂B充分搅拌混合，得到所述复合碱溶液。
以复合碱溶液的质量为100％计，复合碱激发剂的含量为98％，金属络合剂的含量为0.05％，稳泡剂B的含量为1.95％；复合碱激发剂的模数为1.3；金属络合剂为三乙醇胺，其固含量不低于78％；稳泡剂B为十二烷基苯磺酸钠粉末，其纯度不低于88％。
复合碱激发剂通过以下制备方法制备得到：
将氢氧化钠粉末和水倒入水玻璃中，充分搅拌后密封，静置备用，得到所述复合碱激发剂；
以所述复合碱激发剂的质量为100％计，氢氧化钠粉末的含量为9％，水的含量为7％，水玻璃的含量为84％；氢氧化钠粉末的纯度不低于96％；水为自来水；水玻璃的模数为2.0，波美度为36.0。
粉煤灰基泡沫地聚合物的制备方法包括以下步骤：
(1)将配方量的粉煤灰基材料、复合碱溶液、增稠剂、稳泡剂A和减水剂放入搅拌锅中，以搅拌叶公转120r/min、自转280r/min的转速，快速搅拌5min，确保净浆均匀，无固体粉体下沉，得到料浆；
(2)将发泡剂迅速加入步骤(1)得到的料浆中，以搅拌叶公转60r/min、自转140r/min的转速，慢速搅拌30s后，得到混合物，而后将混合物快速注入至模具的1/2深度处，然后在模具上覆盖聚乙烯薄膜，避免水分流失；
(3)将步骤(2)的混合物及模具放入温度为70℃的养护舱内养护24h后脱模，而后将脱模后的样品放置于温度为20℃，湿度为97％的标准养护环境下养护7天，得到所述粉煤灰基泡沫地聚合物。
本实施例中粉煤灰基泡沫地聚合物所用原料示意图如图1所示。
实施例4
在本实施例中提供一种粉煤灰基泡沫地聚合物，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：
其中，增稠剂为纯度不低于96％、粘度为40000厘泊的羧甲基纤维素醚；稳泡剂A为纯度不低于98％的磷酸三钠；减水剂为聚羧酸减水剂；发泡剂为过氧化氢溶液，其含量为30％。
粉煤灰基材料通过以下制备方法制备得到：
将粉煤灰和钙质材料放入搅拌锅中，充分搅拌混合，得到所述粉煤灰基材料。
以粉煤灰基材料的质量为100％计，粉煤灰的含量为95％，钙质材料的含量为5％；钙质材料为矿渣。
复合碱溶液通过以下制备方法制备得到：
将复合碱激发剂、金属络合剂和稳泡剂B充分搅拌混合，得到所述复合碱溶液。
以复合碱溶液的质量为100％计，复合碱激发剂的含量为97％，金属络合剂的含量为0.1％，稳泡剂B的含量为2.9％；复合碱激发剂的模数为1.2；金属络合剂为三乙醇胺，其固含量不低于78％；稳泡剂B为十二烷基苯磺酸钠粉末，其纯度不低于88％。
复合碱激发剂通过以下制备方法制备得到：
将氢氧化钠粉末和水倒入水玻璃中，充分搅拌后密封，静置备用，得到所述复合碱激发剂；
以所述复合碱激发剂的质量为100％计，氢氧化钠粉末的含量为8.8％，水的含量为5％，水玻璃的含量为86.2％；氢氧化钠粉末的纯度不低于96％；水为自来水；水玻璃的模数为3.0，波美度为40.0。
粉煤灰基泡沫地聚合物的制备方法包括以下步骤：
(1)将配方量的粉煤灰基材料、复合碱溶液、增稠剂、稳泡剂A和减水剂放入搅拌锅中，以搅拌叶公转130r/min、自转285r/min的转速，快速搅拌5min，确保净浆均匀，无固体粉体下沉，得到料浆；
(2)将发泡剂迅速加入步骤(1)得到的料浆中，以搅拌叶公转65r/min、自转140r/min的转速，慢速搅拌30s后，得到混合物，而后将混合物快速注入至模具的1/2深度处，然后在模具上覆盖聚乙烯薄膜，避免水分流失；
(3)将步骤(2)的混合物及模具放入温度为70℃的养护舱内养护24h后脱模，而后将脱模后的样品放置于温度为20℃，湿度为95％的标准养护环境下养护7天，得到所述粉煤灰基泡沫地聚合物。
本实施例中粉煤灰基泡沫地聚合物所用原料示意图如图1所示。
实施例5
在本实施例中提供一种粉煤灰基泡沫地聚合物，所述粉煤灰基泡沫地聚合物的制备原料包括如下重量份的组分：
其中，增稠剂为纯度不低于96％、粘度不低于30000厘泊的羧甲基纤维素醚；稳泡剂A为纯度不低于98％的磷酸三钠；减水剂为聚羧酸减水剂；发泡剂为过氧化氢溶液，其含量为30％。
粉煤灰基材料通过以下制备方法制备得到：
将粉煤灰和钙质材料放入搅拌锅中，充分搅拌混合，得到所述粉煤灰基材料。
以粉煤灰基材料的质量为100％计，粉煤灰的含量为98％，钙质材料的含量为2％；钙质材料为矿渣。
复合碱溶液的制备方法及原料组成与实施例1相同。
复合碱激发剂的制备方法及原料组成与实施例1相同。
粉煤灰基泡沫地聚合物的制备方法包括以下步骤：
(1)将配方量的粉煤灰基材料、复合碱溶液、增稠剂、稳泡剂A和减水剂放入搅拌锅中，以搅拌叶公转125r/min、自转280r/min的转速，快速搅拌6min，确保净浆均匀，无固体粉体下沉，得到料浆；
(2)将发泡剂迅速加入步骤(1)得到的料浆中，以搅拌叶公转60r/min、自转135r/min的转速，慢速搅拌40s后，得到混合物，而后将混合物快速注入至模具的1/2深度处，然后在模具上覆盖聚乙烯薄膜，避免水分流失；
(3)将步骤(2)的混合物及模具放入温度为75℃的养护舱内养护24h后脱模，而后将脱模后的样品放置于温度为20℃，湿度为95％的标准养护环境下养护7天，得到所述粉煤灰基泡沫地聚合物。
本实施例中粉煤灰基泡沫地聚合物所用原料示意图如图1所示。
实施例6
本实施例与实施例1不同之处仅在于，制备复合碱溶液时不添加金属络合剂，复合碱激发剂的含量为96.3％，稳泡剂B的含量为3.7％，其他条件均与实施例1相同。
实施例7
本实施例与实施例1不同之处仅在于，制备复合碱溶液时金属络合剂的含量为0.7％，复合碱激发剂的含量为95.6％，稳泡剂B的含量为3.7％，其他条件均与实施例1相同。
对比例1
本对比例与实施例1不同之处仅在于，粉煤灰基泡沫地聚合物的制备原料中，复合碱溶液的添加量为500份，其他条件均与实施例1相同。
对比例2
本对比例与实施例1不同之处仅在于，粉煤灰基泡沫地聚合物的制备原料中，复合碱溶液的添加量为800份，其他条件均与实施例1相同。
对比例3
本对比例与实施例1不同之处仅在于，粉煤灰基泡沫地聚合物的制备原料中，发泡剂的添加量为45份，其他条件均与实施例1相同。
对实施例1-7以及对比例1-3制备的粉煤灰基泡沫地聚合物进行性能测试，测试方法如下：
(1)抗压强度和表观密度按照《GBT 11969-2008蒸压加气混凝土性能实验方法》规定的方法进行测试；7天抗压强度指的是将脱模后的样品放置于标准养护环境下养护7天得到粉煤灰基泡沫地聚合物，对其进行抗压强度测试；
(2)孔隙率及孔隙圆度、等效球直径采用微米X射线断层扫描技术进行测试。
性能测试结果如表1所示。
表1
由表1可以看出，实施例1-5通过大掺量的利用粉煤灰(粉煤灰利用率：90％-100％)制备的粉煤灰基泡沫地聚合物样品具有表观密度低(421.7-521.4kg/m3)和早期强度高(1.56-3.60MPa)的特点，可用作轻质多孔建筑材料，另外，通过增加钙质材料能够有效的在小范围内增加样品表观密度的情况下，极大增强样品的早期抗压强度，实现样品强度、表观密度在实际使用过程中的可调可控，适应各种使用场景需求。
与实施例1相比，实施例6和实施例7制备的粉煤灰基泡沫地聚合物样品的表观密度均稍微上升，抗压强度均明显下降，这说明金属络合剂的添加量过少或过多均会影响样品的性能。
与实施例1相比，对比例1制备的粉煤灰基泡沫地聚合物样品的抗压强度明显下降，对比例2制备的粉煤灰基泡沫地聚合物样品的抗压强度虽稍微上升，但其表面泛碱发白，影响产品表面质量。
与实施例1相比，对比例3制备的粉煤灰基泡沫地聚合物样品的抗压强度明显下降。
申请人声明，本发明通过上述实施例来说明本发明的粉煤灰基泡沫地聚合物及其制备方法和应用，但本发明并不局限于上述实施例，即不意味着本发明必须依赖上述实施例才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明所选用原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
Claims (32)
1.一种粉煤灰基泡沫地聚合物，其特征在于，所述粉煤灰基泡沫地聚合物的制备原料由如下重量份的组分组成：
粉煤灰基材料 900-1000份；
复合碱溶液 600-700份；
增稠剂 2-10份；
稳泡剂A 2-6份；
减水剂 5-10份；
发泡剂 20-40份；
所述粉煤灰基材料通过以下制备方法制备得到：
将粉煤灰和钙质材料混合，得到所述粉煤灰基材料；
以所述粉煤灰基材料的质量为100%计，粉煤灰的含量为90%-100%，钙质材料的含量为0%-10%；
所述钙质材料包括水泥、矿渣、石膏或偏高岭土中的任意一种或至少两种的组合；
所述复合碱溶液通过以下制备方法制备得到：
将复合碱激发剂、金属络合剂和稳泡剂B混合，得到所述复合碱溶液；
以所述复合碱溶液的质量为100%计，复合碱激发剂的含量为95%-98%，金属络合剂的含量为0.05%-0.5%，稳泡剂B的含量为1.95%-4.5%；
所述稳泡剂A包括磷酸三钠和/或硬脂酸钙粉末；
所述稳泡剂B包括十二烷基苯磺酸钠粉末、十二烷基硫酸钠粉末、磷酸三钠粉末或十二烷基硫酸钙粉末中的任意一种或至少两种的组合。
2.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述复合碱激发剂的模数为1.0-1.5。
3.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述金属络合剂包括三乙醇胺、甲基二乙醇胺、二异丙醇胺、二乙醇单异丙醇胺、三乙醇胺或三异丙醇胺中的任意一种或至少两种的组合。
4.根据权利要求3所述的粉煤灰基泡沫地聚合物，其特征在于，所述金属络合剂的固含量不低于78%。
5.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述稳泡剂B的纯度不低于88%。
6.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述复合碱激发剂通过以下制备方法制备得到：
将氢氧化钠粉末和水倒入水玻璃中，搅拌，得到所述复合碱激发剂。
7.根据权利要求6所述的粉煤灰基泡沫地聚合物，其特征在于，以所述复合碱激发剂的质量为100%计，氢氧化钠粉末的含量为8.5%-9%，水的含量为4.5%-7%，水玻璃的含量为84%-87%。
8.根据权利要求6所述的粉煤灰基泡沫地聚合物，其特征在于，所述氢氧化钠粉末的纯度不低于96%。
9.根据权利要求6所述的粉煤灰基泡沫地聚合物，其特征在于，所述水为自来水。
10.根据权利要求6所述的粉煤灰基泡沫地聚合物，其特征在于，所述水玻璃的模数为1.0-3.8，波美度为34.0-42.0。
11.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述增稠剂包括甲基纤维素醚和/或羧甲基纤维素醚。
12.根据权利要求11所述的粉煤灰基泡沫地聚合物，其特征在于，所述增稠剂包括甲基纤维素醚和羧甲基纤维素醚。
13.根据权利要求11所述的粉煤灰基泡沫地聚合物，其特征在于，所述增稠剂的纯度不低于96%。
14.根据权利要求11所述的粉煤灰基泡沫地聚合物，其特征在于，所述增稠剂的粘度不低于30000厘泊。
15.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述磷酸三钠的纯度不低于98%。
16.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述硬脂酸钙粉末的纯度不低于99%。
17.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述减水剂包括聚羧酸减水剂、萘磺酸盐系减水剂、脂肪系减水剂、木质素磺酸盐类减水剂或氨基磺酸盐系减水剂中的任意一种或至少两种的组合。
18.根据权利要求1所述的粉煤灰基泡沫地聚合物，其特征在于，所述发泡剂包括过氧化氢溶液。
19.根据权利要求18所述的粉煤灰基泡沫地聚合物，其特征在于，所述过氧化氢溶液中，过氧化氢溶质的质量含量不低于30%。
20.根据权利要求1-19中任一项所述的粉煤灰基泡沫地聚合物的制备方法，其特征在于，所述制备方法包括以下步骤：
（1）将配方量的粉煤灰基材料、复合碱溶液、增稠剂、稳泡剂A和减水剂搅拌，得到料浆；
（2）将发泡剂加入步骤（1）得到的料浆中，搅拌，得到混合物，而后将混合物注入模具中；
（3）将步骤（2）的混合物及模具放入养护舱内养护，脱模，而后将脱模后的样品放置于标准养护环境下养护，得到所述粉煤灰基泡沫地聚合物。
21.根据权利要求20所述的制备方法，其特征在于，步骤（1）所述搅拌在搅拌锅中进行。
22.根据权利要求20所述的制备方法，其特征在于，步骤（1）所述搅拌的搅拌叶公转转速为115-135 r/min，自转转速为275-295 r/min。
23.根据权利要求20所述的制备方法，其特征在于，步骤（1）所述搅拌的时间为4-6min。
24.根据权利要求20所述的制备方法，其特征在于，步骤（2）所述搅拌的搅拌叶公转转速为57-67 r/min，自转转速为135-145 r/min。
25.根据权利要求20所述的制备方法，其特征在于，步骤（2）所述搅拌的时间为20-40s。
26.根据权利要求20所述的制备方法，其特征在于，步骤（2）所述将混合物注入模具中为将混合物注入至模具的1/2深度处。
27.根据权利要求20所述的制备方法，其特征在于，步骤（3）所述养护舱内的温度为65-75℃。
28.根据权利要求20所述的制备方法，其特征在于，步骤（3）所述放入养护舱内养护的时间为12-24 h。
29.根据权利要求20所述的制备方法，其特征在于，步骤（3）所述标准养护环境的温度为18-22℃，湿度为95%以上。
30.根据权利要求20所述的制备方法，其特征在于，步骤（3）所述放置于标准养护环境下养护的时间为7天。
31.根据权利要求1-19中任一项所述的粉煤灰基泡沫地聚合物在建筑材料中的应用。
32.根据权利要求31所述的应用，其特征在于，所述建筑材料包括装配式建筑材料。