CN113186721B - 一种免烫裤子的整理工艺 - Google Patents
一种免烫裤子的整理工艺 Download PDFInfo
- Publication number
- CN113186721B CN113186721B CN202110503934.7A CN202110503934A CN113186721B CN 113186721 B CN113186721 B CN 113186721B CN 202110503934 A CN202110503934 A CN 202110503934A CN 113186721 B CN113186721 B CN 113186721B
- Authority
- CN
- China
- Prior art keywords
- trousers
- parts
- finishing
- finishing liquid
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本申请涉及整理工艺领域，具体公开了一种免烫裤子的整理工艺，包括如下步骤：S1，浸轧整理液：将裤子浸轧整理液，二浸二轧；S2，烘焙：将经过S1步骤的裤子先在70‑90℃下预烘5‑10min，再在120‑130℃下烘焙3‑5min；S3，水洗，将经过S2步骤的裤子采用热水、冷水交替清洗三次；S4，烘干，将经过S3步骤的裤子在40‑50℃下烘干。采用明胶水解后的小分子明胶蛋白对裤子面料进行接枝，显著提高裤子羊毛面料的抗皱性能，且通过在整理液中添加鱼胶原蛋白肽，提高裤子的抗皱性能、柔韧性。维生素E的乙醇溶液对羊毛和鱼胶原蛋白肽进行养护，提高裤子羊毛面料的抗皱性能与断裂强力。
Description
技术领域
本申请涉及整理工艺领域，更具体地说，它涉及一种免烫裤子的整理工艺。
背景技术
西裤常配上严肃的樽领衬衫在上班时穿着，既方便在上班途中奔波，又可树立严谨、精干的工作形象。
西裤的通常采用羊毛纤维制得，西裤长用于庄严、严肃的场合，因此西裤的平整度尤为重要，但是羊毛的抗皱性较差，导致在穿着过程中，西裤容易出现褶皱，影响西裤的平整性。通常需要将西裤重新熨烫后才能使其恢复平整，但是出门在外出差时，不足以满足熨烫的条件，因此研发一种免熨烫的西裤是尤为重要。
发明内容
为了提高羊毛裤子的抗皱性，本申请提供一种免烫裤子的整理工艺。
本申请提供的一种免烫裤子的整理工艺，采用如下的技术方案：
一种免烫裤子的整理工艺，包括如下步骤：
S1，浸轧整理液：将裤子浸轧整理液，二浸二轧，裤子浸泡整理液时间为大于10min，轧余率90-100%；
S2，烘焙：将经过S1步骤的裤子先在70-90℃下预烘5-10min，再在120-130℃下烘焙3-5min；
S3，水洗，将经过S2步骤的裤子采用热水、冷水交替清洗三次，热水温度为45-55℃，冷水温度为10-25℃；
S4，烘干，将经过S3步骤的裤子在40-50℃下烘干；
所述整理液包括如下重量份的原料：
15-20g/L的水解明胶的水溶液30-40份；
乙二醛100-120份；
硫酸铝30-50份。
通过采用上述技术方案，明胶的相对分子质量较大，明胶大分子只能附着在裤子羊毛面料表面，不能形成很好的交联。明胶通过水解后变成小分子明胶蛋白，小分子明胶蛋白方便侵入至裤子羊毛面料的内部，并且通过交联剂乙二醛、催化剂硫酸铝使小分子明胶蛋白与裤子羊毛面料发生交联反应，小分子明胶蛋白接枝羊毛上，在裤子面料上形成网状结构，显著提高裤子面料的抗皱性能。
可选的，所述整理液还包括重量份为的0.1-30份的鱼胶原蛋白肽。
通过采用上述技术方案，羊毛主要成分为蛋白质，在高温烘焙条件下，裤子羊毛面料容易损伤。鱼胶原蛋白肽的主要成分为蛋白质，采用鱼胶原蛋白肽对裤子羊毛面料处理，在高温烘焙过程中，鱼胶原蛋白肽通过乙二醛在裤子羊毛面料表面接枝，并且对受损的羊毛纤维表面进行修补，提高裤子的抗皱性能、柔韧性。
可选的，所述整理液还包括重量份为6-8份的次亚磷酸钠。
通过采用上述技术方案，次亚磷酸钠作为防腐剂，抑制微生物的繁殖，从而保护鱼胶原蛋白肽、羊毛不易被微生物分解。
可选的，所述整理液的制备方法如下：称取15-20g/L的水解明胶的水溶液30-40份加入30-50份硫酸铝、100-120份乙二醛、6-8份的次亚磷酸钠以及0.1-30份的鱼胶原蛋白肽，混合均匀得到整理液。
通过上述技术方案，制备得到整理液。
可选的，所述鱼胶原蛋白肽的重量份为18-22份。
通过采用上述技术方案，鱼胶原蛋白肽价格较为昂贵，添加量较少，使羊毛的修复效果较差，添加量过多，使鱼胶原蛋白肽不能有效利用，造成浪费，因而有效控制鱼胶原蛋白肽的添加量尤为关键。
可选的，S1步骤中，浸轧整理液时整理液的温度为50-60℃。
通过上述技术方案，将整理液温度设置为50-60℃，使整理液流动性好，同时使裤子羊毛面料软化后方便露出纤维间的空隙，整理液方便浸入裤子羊毛面料的内部，使得整理液与裤子交联均匀，减小交联不均引起应力集中导致的断裂强力损失。
可选的，还包括S5，将S4烘干的裤子浸泡在浓度为0.7-1.0g/L的维生素E的乙醇溶液中，浸泡时间4-5h，取出，烘干。
通过上述技术方案，维生素E具有滋润、养护鱼胶原蛋白肽、羊毛的效果，鱼胶原蛋白肽、羊毛吸收维生素E后，能够保持韧性、弹性，提高裤子羊毛面料的抗皱性能与断裂强力。
可选的，所述维生素E的乙醇溶液的温度为50-60℃。
通过上述技术方案，在50-60℃下采用维生素E的乙醇溶液对裤子进行浸泡，使羊毛以及鱼胶原蛋白肽对维生素E的吸收效果较好，使维生素E对羊毛和胶原蛋白肽的吸收效果较好，从而进一步提高裤子羊毛面料的抗皱性能与断裂强力。
综上所述，本申请具有以下有益效果：
1、由于本申请采用明胶水解后的小分子明胶蛋白对裤子面料进行接枝，显著提高裤子羊毛面料的抗皱性能。
2、本申请中通过在整理液中添加鱼胶原蛋白肽，提高裤子的抗皱性。
3、通过采用维生素E的乙醇溶液对羊毛和鱼胶原蛋白肽进行浸泡养护，进一步提高裤子羊毛面料的抗皱性能与断裂强力。
具体实施方式
以下结合实施例对本申请作进一步详细说明。
| 原料名称 | 种类或来源 |
| 明胶 | 科彩牌工业明胶颗粒，工业级 |
| 鱼胶原蛋白肽 | 佳源诚牌鳕鱼胶原蛋白肽粉，食品级 |
| 维生素E | 健川牌维生素E油，食品级 |
制备例
制备例1
水解明胶的水溶液的制备
称取36kg明胶、8kg柠檬酸加入至2L溶剂水搅拌混合，75℃下加热水解1h，得到18g/L的水解明胶的水溶液。
制备例2
整理液的制备：
称取制备例1得到的水解明胶的水溶液30kg，加入30kg硫酸铝以及100kg的乙二醛，搅拌混合均匀得到整理液。
制备例3
整理液的制备：
称取制备例1得到的水解明胶的水溶液40kg，加入50kg硫酸铝以及120kg的乙二醛，搅拌混合均匀得到整理液。
制备例4
整理液的制备：
称取制备例1得到的水解明胶的水溶液35kg，加入40kg硫酸铝以及110kg的乙二醛，搅拌混合均匀得到整理液。
制备例5
整理液的制备：
与制备例4的区别在于，还添加有7kg的次亚磷酸钠。
制备例6
整理液的制备：
与制备例5的区别在于，还添加有10kg的鱼胶原蛋白肽。
制备例7
整理液的制备
与制备例6的区别在于，鱼胶原蛋白肽的添加量为18kg。
制备例8
整理液的制备：
与制备例6的区别在于，鱼胶原蛋白肽的添加量为22kg。
制备例9
整理液的制备：
与制备例6的区别在于，鱼胶原蛋白肽的添加量为30kg。
制备例10
维生素E的乙醇溶液制备：
称取10kg维生素E溶解于10000L乙醇中，得到1g/L的维生素E的乙醇溶液。
实施例
实施例1
一种免烫裤子的整理工艺，包括如下步骤：
S1，浸轧由制备例2得到的25℃的整理液：将裤子浸轧整理液，二浸二轧，裤子浸泡整理液时间为10min，轧余率90%；
S2，烘焙：将经过S1步骤的裤子先在70℃下预烘5min，再在120℃下烘焙3min；
S3，水洗，将经过S2步骤的裤子采用热水、冷水交替清洗三次，热水温度为45℃，冷水温度为10℃；
S4，烘干，将经过S3步骤的裤子在40℃下烘干。
实施例2
一种免烫裤子的整理工艺，包括如下步骤：
S1，浸轧由制备例3得到的25℃的整理液：将裤子浸轧整理液，二浸二轧，裤子浸泡整理液时间为20min，轧余率90%；
S2，烘焙：将经过S1步骤的裤子先在90℃下预烘10min，再在130℃下烘焙5min；
S3，水洗，将经过S2步骤的裤子采用热水、冷水交替清洗三次，热水温度为55℃，冷水温度为25℃；
S4，烘干，将经过S3步骤的裤子在50℃下烘干。
实施例3
一种免烫裤子的整理工艺，包括如下步骤：
S1，浸轧由制备例4得到的25℃的整理液：将裤子浸轧整理液，二浸二轧，裤子浸泡整理液时间为10min，轧余率90%；
S2，烘焙：将经过S1步骤的裤子先在80℃下预烘8min，再在126℃下烘焙4min；
S3，水洗，将经过S2步骤的裤子采用热水、冷水交替清洗三次，热水温度为50℃，冷水温度为20℃；
S4，烘干，将经过S3步骤的裤子在45℃下烘干。
实施例4
与实施例3的区别在于，整理剂由制备例5得到。
实施例5
与实施例3的区别在于，整理剂由制备例6得到。
实施例6
与实施例3的区别在于，整理剂由制备例7得到。
实施例7
与实施例3的区别在于，整理剂由制备例6得到。
实施例8
与实施例3的区别在于，整理剂由制备例8得到。
实施例9
与实施例7的区别在于，整理剂的温度为50℃。
实施例10
与实施例7的区别在于，整理剂的温度为60℃。
实施例11
与实施例7的区别在于，整理剂的温度为55℃。
实施例12
与实施例7的区别在于，整理剂的温度为70℃。
实施例13
与实施例11的区别在于，还包括S5，将S4烘干的裤子浸泡在由制备例10得到的25℃的维生素E的乙醇溶液中，浸泡时间5h，取出，40℃下烘干，25℃冷水清洗，再于40℃下烘干。
实施例14
与实施例4的区别在于，还包括S5，将S4烘干的裤子浸泡在由制备例10得到的25℃的维生素E的乙醇溶液中，浸泡时间5h，取出，40℃下烘干，25℃冷水清洗，再于40℃下烘干。
实施例15
与实施例13的区别在于，维生素E的乙醇溶液的温度为50℃。
实施例16
与实施例13的区别在于，维生素E的乙醇溶液的温度为60℃。
实施例17
与实施例13的区别在于，维生素E的乙醇溶液的温度为55℃。
实施例18
与实施例13的区别在于，维生素E的乙醇溶液的温度为70℃。
对比例
对比例1
与实施例3的区别在于，整理液中不添加水解明胶的水溶液。
性能检测试验
纯羊毛精纺面料，100%羊毛，河北日伊丰达绒毛加工有限公司出售，规格为单面450G，斜纹。
纯羊毛精纺面料通过实施例1-17与对比例1的整理工艺进行整理后得到试样件。对试样件以及未经过整理的试样件采用如下测试方法进行测试：
抗皱性能测试：参照按GB/T 3819—1997《纺织品 织物折痕回复性的测定 回复角法》测定试样件的折皱回复角。并通过如下公式计算折皱回复角提升值，实验数据详见表1。
折皱回复角提升值=A1-A0
A1--整理后试样件折皱回复角；
A0--整理前试样件折皱回复角。
断裂强力测试：参照GB/T3923.1-2013《纺织品 织物拉伸性能 第1部分：断裂强力和断裂伸长率的测定（条样法）》进行测定断裂强力。并通过如下公式计算断裂强力保留率，实验数据详见表1。
断裂强力保留率=N1/N0*100%
N1--整理后试样件断裂强力；
N0--整理前试样件断裂强力。
表1
| 折皱回复角提升值/° | 断裂强力保留率/% | |
| 实施例1 | 126 | 71 |
| 实施例2 | 127 | 72 |
| 实施例3 | 129 | 73 |
| 实施例4 | 130 | 73 |
| 实施例5 | 137 | 81 |
| 实施例6 | 145 | 84 |
| 实施例7 | 146 | 85 |
| 实施例8 | 148 | 85 |
| 实施例9 | 147 | 88 |
| 实施例10 | 147 | 89 |
| 实施例11 | 147 | 90 |
| 实施例12 | 146 | 84 |
| 实施例13 | 155 | 91 |
| 实施例14 | 132 | 75 |
| 实施例15 | 158 | 95 |
| 实施例16 | 158 | 95 |
| 实施例17 | 159 | 95 |
| 实施例18 | 154 | 92 |
| 对比例1 | 78 | 64 |
结合实施例1-3和对比例1并结合表1可以看出，水解明胶的水溶液在整理液中的添加，能显著提高试样件的折皱回复角提升值与断裂强力保留率。
结合实施例3和实施例4并结合表1可以看出，次亚磷酸钠的添加对试样件的折皱回复角提升值与断裂强力保留率影响不明显。
结合实施例3和实施例5并结合表1可以看出，鱼胶原蛋白肽的添加，对羊毛限位进行修补后，显著提高试样件的折皱回复角提升值与断裂强力保留率。
结合实施例5-8并结合表1可以看出，当鱼胶原蛋白肽的添加量达到18和22g时，试样件的折皱回复角提升值与断裂强力保留率提高效果较好。鱼胶原蛋白肽添加量较小时，使其对羊毛纤维的修补作用不足；当鱼胶原蛋白肽添加量过量时，使鱼胶原蛋白肽浪费，造成工艺成本上不必要的损失。
结合实施例7以及实施例9-12并结合表1可以看出，整理剂的温度在50-60℃使较为适宜，能较好的提高整理剂对试样件的浸润程度以及分散均匀度，使整理液与试样件交联均匀，从而使提高试样件的断裂强力保留率。
结合实施例11以及实施例13并结合表1可以看出，将试样件通过维生素E的乙醇溶液浸泡后，维生素E对羊毛以及鱼胶原蛋白肽进行滋润养护，显著提高试样件的折皱回复角提升值与断裂强力保留率。
结合实施例11、实施例13以及实施例14并结合表1可以看出，维生素E对羊毛的养护效果不明显，说明维生素E的主要养护对象为鱼胶原蛋白肽，使鱼胶原蛋白肽韧性提高，从而提高试样件的折皱回复角提升值与断裂强力保留率。
结合实施例13以及实施例15-18并结合表1可以看出，维生素E的乙醇溶液在50-60℃下进行浸泡，使试样件的折皱回复角提升值与断裂强力保留率的效大。当温度过高时，酒精挥发速度快，使维生素E的乙醇溶液的浓度提升，容易使维生素E的乙醇溶液不易浸透试样件。当温度较低时，羊毛以及鱼胶原蛋白肽对维生素E的吸收较差，使裤子羊毛面料的抗皱性能与断裂强力提升较小。
本具体实施例仅仅是对本申请的解释，其并不是对本申请的限制，本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改，但只要在本申请的权利要求范围内都受到专利法的保护。
Claims (2)
1.一种免烫裤子的整理工艺，其特征在于，包括如下步骤：
S1，浸轧整理液：将裤子浸轧整理液，二浸二轧，裤子浸泡整理液时间为大于10min，轧余率90-100％，温度为50-60℃；
S2，烘焙：将经过S1步骤的裤子先在70-90℃下预烘5-10min，再在120-130℃下烘焙3-5min；
S3，水洗，将经过S2步骤的裤子采用热水、冷水交替清洗三次，热水温度为45-55℃，冷水温度为10-25℃；
S4，烘干，将经过S3步骤的裤子在40-50℃下烘干；
S5，将S4烘干的裤子浸泡在浓度为0.7-1.0g/L的维生素E的乙醇溶液中，温度为50-60℃，浸泡时间4-5h，取出，烘干；
所述整理液包括如下重量份的原料：
15-20g/L的水解明胶的水溶液30-40份；
乙二醛100-120份；
硫酸铝30-50份；
鱼胶原蛋白肽18-22份；
次亚磷酸钠6-8份。
2.根据权利要求1所述的一种免烫裤子的整理工艺，其特征在于：所述整理液的制备方法如下：称取15-20g/L的水解明胶的水溶液30-40份加入30-50份硫酸铝、100-120份乙二醛、6-8份的次亚磷酸钠以及0.1-30份的鱼胶原蛋白肽，混合均匀得到整理液。