CN1131701A - 泡沫镍钛记忆合金 - Google Patents
泡沫镍钛记忆合金 Download PDFInfo
- Publication number
- CN1131701A CN1131701A CN 95110120 CN95110120A CN1131701A CN 1131701 A CN1131701 A CN 1131701A CN 95110120 CN95110120 CN 95110120 CN 95110120 A CN95110120 A CN 95110120A CN 1131701 A CN1131701 A CN 1131701A
- Authority
- CN
- China
- Prior art keywords
- memory alloy
- foam
- powder
- alloy
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种泡沫NiTi记忆合金，合金成分范围在：(原子百分比)Ni：49.2～50.8，余Ti，其特征在于：合金内有许多微孔，孔隙度在20～80％之间。本发明可用作生物材料，与肌体组织结合完美。
Description
本发明涉及记忆合金领域，特别提供了一种泡沫态的NiTi记忆合金。
形状记忆合金是集感知和功能为一体的新型智能材料，具有广阔的应用前景，目前，实际应用的NiTi记忆合金都是块体材料，它在医学临床应用时，记忆合金器件和肌体组织不能形成完整的结合，便其医疗效果受到限制。
本发明目的是提供一种与肌体组织结合更完美的记忆合金。
本发明提供了一种泡沫NiTi记忆合金，合金成份范围在：(原子百分比)
Ni Ti49.2～50.8 余
其特征在于：合金内有许多微孔，孔隙度在20～80％之间。
本发明所提供的泡沬记忆合金，其孔洞可以是连通的，也可以是不连通的。它不仅具有块体材料的记忆效应和超弹性性能，而且具有重量轻易变形的特点，用它来制作医疗器件，置入前体积可以变化到更小，使手术过程更加方便，简单，由于它具有一定的孔隙度，肌体组织可生长到该孔洞内，使其结合更紧密，医疗效果更佳，这种材料特别适合于人体，尤其是脸部损坏部位的修补。
本发明提供了上述泡沫NiTi记忆合金的制备方法，其特征在于：该材料系将钛粉，镍粉及钛氢粉混合均匀后，经压型，烧结及退火工艺制得，反应式为：
工艺参数为：
①成型压力 1-2GPa
②真空烧结温度 1000～1300℃ 时间20～80分钟
迅速冷致室温
③800℃～900℃ 真空退火30～60分钟
通过控制TiH2的含量，可制备出密度为1/3～1/6d(d为块体材料的密度)的泡沫记忆合金，其记忆应变：4～6％，超弹性：3.5～6.5％。
下面通过实施例详述本发明。
实施例1：Ni50Ti50泡沫合金
用TiH2粉替代10％的钛粉，混匀压成型后采用下列工艺：
1)1100℃块结30分钟(真空)，速冷至室温。
2)850℃保温30分钟(真空)
所得材料：孔隙度为30％，记忆应变大于4.5％，起弹性3.8％。
实施例2：泡沫Ti50.5Ni49.5合金
将30％的Ti粉用TiH2替代，混匀后压型。制备工艺：
1)1050℃烧结40分钟(真空)，速冷至室温
2)900℃保温40分钟(真空)
所得材料：孔隙度为54％，记忆应变接近5％，超弹性3.6％，
实施例3：泡沫Ti49.5Ni50.5合金
TiH2粉与Ni粉直接压型后制备：
1)1250℃烧结30分钟(真空)
2)880℃保温60分钟(真空)
所得材料：孔隙度大于65％，记忆应度5.3％，超弹性5％。
Claims (2)
1.一种泡沫NiTi记忆合金，合金成份范围在：(原子百分比)
Ni Ti49.2～50.8 余
其特征在于：合金内有许多微孔，孔隙度在20～80％之间。
2.一种权利要求1所述泡沫NiTi记忆合金的制备方法，其特征在于：
该材料系将钛粉，镍粉及钛氢粉混合均匀后，经压型，烧结及退火工艺制得，反应式为：
工艺参数为：
①成型压力 1-2GPa
②真空烧结温度 1000～1300℃时间20～80分钟
迅速冷致室温
③800℃～900℃ 真空退火30～60分钟