CN113150552A - 门窗的磁吸消音闭合密封条生产方法 - Google Patents
门窗的磁吸消音闭合密封条生产方法 Download PDFInfo
- Publication number
- CN113150552A CN113150552A CN202110491497.1A CN202110491497A CN113150552A CN 113150552 A CN113150552 A CN 113150552A CN 202110491497 A CN202110491497 A CN 202110491497A CN 113150552 A CN113150552 A CN 113150552A
- Authority
- CN
- China
- Prior art keywords
- sealing strip
- doors
- weight parts
- magnetic
- noise reduction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明门窗的磁吸消音闭合密封条生产方法涉及密封条技术领域。以“磁性与发泡”关键技术，将液态硅胶90%重量份、偶氮二甲酰胺3%重量份、三溴苯酚4%重量份、双二四铂金硫化剂3%重量份搅拌混合制成滴液备用；将硅胶覆膜的磁性密封条放入模具中，对模具在温度110℃、负压60KPa条件下滴入滴液，使滴液在模具内发泡以填充模具腔体且使磁性密封条定型，将定型的磁性密封条脱出模具，制成门窗的磁吸消音闭合密封条成品。用于门窗的密封。构思科学合理、方法简单实用、使用方便快捷、效果稳定可靠、制作成本低、利于推广应用。
Description
技术领域
本发明门窗的磁吸消音闭合密封条生产方法，涉及密封条技术领域。
背景技术
目前，已有公知技术的门窗的密封条,存在着防尘差、保温差、隔音差、防虫差、防潮差、耐磨差、易老化、欠耐用、对适用环境要求高、适用范围有局限等诸多不足、缺陷与弊端。基于发明人的专业知识和丰富的工作经验以及对事业精益求精的不懈追求，特采取“磁性与发泡”关键技术，研制成功了“门窗的磁吸消音闭合密封条生产方法”，且生产出了“门窗的磁吸消音闭合密封条”新产品。有效的提高了本行业的技术水平。
发明内容
本发明采取“磁性与发泡”关键技术、提供了“门窗的磁吸消音闭合密封条生产方法”，且生产出了“门窗的磁吸消音闭合密封条”新产品。本发明将液态硅胶90%重量份、偶氮二甲酰胺3%重量份、三溴苯酚4%重量份、双二四铂金硫化剂3%重量份搅拌混合制成滴液备用；将硅胶覆膜的磁性密封条放入模具中，对模具在温度110℃、负压60KPa条件下滴入滴液，使滴液在模具内发泡以填充模具腔体且使磁性密封条定型，将定型的磁性密封条脱出模具，制成门窗的磁吸消音闭合密封条成品。
通过本发明达到的目的是：①、采取“磁性与发泡”关键技术、提供了“门窗的磁吸消音闭合密封条生产方法”，且生产出了“门窗的磁吸消音闭合密封条”新产品。②、本发明设置有磁性密封条，从而获得了具有磁吸功能、且经久耐用的有益效果。③、本发明设置有滴液在模具内发泡且使磁性密封条定型的工艺生产过程，从而获得了使密封条成品具有防尘、保温、隔音、消音、防虫、防潮、不易老化、经久耐用的有益效果。④、由于本发明的产品具有适应各种环境要求的有益效果。⑤、由于本发明的产品可应用于金属门、木门、车门、柜门、箱体门等各个方面，具有适用范围广的有益效果。⑥、本发明的构思科学合理、方法简单实用、产品使用方便、效果稳定可靠、制作成本低、利于广泛推广应用的有益效果。⑦、本发明的研制成功，有效的提高了本行业的技术水平。
为实现上述目的，本发明提供的技术方案为：
一种门窗的磁吸消音闭合密封条生产方法：
①滴液的制备：将液态硅胶90%重量份的主用剂、偶氮二甲酰胺3%重量份的发泡剂、三溴苯酚4%重量份的阻燃剂、双二四铂金硫化剂3%重量份的促进剂搅拌混合制备成滴液备用；
②、将硅胶覆膜的磁性密封条放入模具中，对所述模具在温度110℃、负压60KPa条件下滴入所述滴液，使所述滴液在所述模具内发泡以填充所述模具的腔体且使所述磁性密封条定型，将所述定型的磁性密封条脱出所述模具，制成门窗的磁吸消音闭合密封条成品。
所述门窗的磁吸消音闭合密封条生产方法，所述三溴苯酚选择替换为三聚氰胺氰尿酸盐、三聚磷酸铝、四溴双酚A、四溴苯酐中的一种。
所述门窗的磁吸消音闭合密封条生产方法，所述温度110℃替换为80℃-160℃，所述负压60KPa替换为40KPa-87KPa。
所述门窗的磁吸消音闭合密封条生产方法，所述模具为L形的腔体，所述磁性密封条的形状与所述模具的腔体相吻合。
本发明的工作原理及工作过程是：本发明采取“磁性与发泡”关键技术，提供了“门窗的磁吸消音闭合密封条生产方法”，且生产出了“门窗的磁吸消音闭合密封条”新产品。本发明如说明书附图1所示，本发明将液态硅胶90%重量份、偶氮二甲酰胺3%重量份、三溴苯酚4%重量份、双二四铂金硫化剂3%重量份搅拌混合制成滴液备用；将硅胶覆膜的磁性密封条放入模具中，对模具在温度110℃、负压60KPa条件下滴入滴液，使滴液在模具内发泡以填充模具腔体且使磁性密封条定型，将定型的磁性密封条脱出模具，制成门窗的磁吸消音闭合密封条成品。----本发明具有构思科学合理、方法简单实用、产品使用方便、效果稳定可靠、制作成本低、利于推广应用的突出有益效果与特点。
由于采用了本发明所提供的技术方案；由于本发明采取“磁性与发泡”关键技术；由于本发明的工作原理及工作过程所述；由于本发明将液态硅胶90%重量份、偶氮二甲酰胺3%重量份、三溴苯酚4%重量份、双二四铂金硫化剂3%重量份搅拌混合制成滴液备用；将硅胶覆膜的磁性密封条放入模具中，对模具在温度110℃、负压60KPa条件下滴入滴液，使滴液在模具内发泡以填充模具腔体且使磁性密封条定型，将定型的磁性密封条脱出模具，制成门窗的磁吸消音闭合密封条成品。使得本发明与已有公知技术相比，获得的有益效果是：
1、本发明采取了“磁性与发泡”关键技术，提供了“门窗的磁吸消音闭合密封条生产方法”，且生产出了“门窗的磁吸消音闭合密封条”新产品。
2、本发明设置有磁性密封条，从而获得了具有磁吸功能、且经久耐用的有益效果。
3、本发明设置有滴液在模具内发泡且使磁性密封条定型的工艺生产过程，从而获得了使密封条成品具有防尘、保温、隔音、消音、防虫、防潮、不易老化、经久耐用的有益效果。
4、由于本发明的产品具有适应各种环境要求的有益效果。
5、由于本发明的产品可应用于金属门、木门、车门、柜门、箱体门等各个方面，具有适用范围广的有益效果。
6、本发明的构思科学合理、方法简单实用、产品使用方便、效果稳定可靠、制作成本低、利于广泛推广应用的有益效果。
7、本发明的研制成功，有效的提高了本行业的技术水平。
附图说明
图1为本发明具体实施方式的工艺流程窗框示意图。
具体实施方式
下面结合说明书附图，对本发明作详细描述。正如说明书附图1所示：
一种门窗的磁吸消音闭合密封条生产方法：
①滴液的制备：将液态硅胶90%重量份的主用剂、偶氮二甲酰胺3%重量份的发泡剂、三溴苯酚4%重量份的阻燃剂、双二四铂金硫化剂3%重量份的促进剂搅拌混合制备成滴液备用；
②、将硅胶覆膜的磁性密封条放入模具中，对所述模具在温度110℃、负压60KPa条件下滴入所述滴液，使所述滴液在所述模具内发泡以填充所述模具的腔体且使所述磁性密封条定型，将所述定型的磁性密封条脱出所述模具，制成门窗的磁吸消音闭合密封条成品。
所述门窗的磁吸消音闭合密封条生产方法，所述三溴苯酚选择替换为三聚氰胺氰尿酸盐、三聚磷酸铝、四溴双酚A、四溴苯酐中的一种。
所述门窗的磁吸消音闭合密封条生产方法，所述温度110℃替换为80℃-160℃，所述负压60KPa替换为40KPa-87KPa。
所述门窗的磁吸消音闭合密封条生产方法，所述模具为L形的腔体，所述磁性密封条的形状与所述模具的腔体相吻合。
以上仅为本发明的较佳实施例，并非对本发明作任何形式上的限制；凡本行业技术人员均可顺畅实施；但在不脱离本发明技术方案作出修饰与演变的等同变化，均为本发明的技术方案。
Claims (4)
1.一种门窗的磁吸消音闭合密封条生产方法，其特征在于：
①滴液的制备：将液态硅胶90%重量份的主用剂、偶氮二甲酰胺3%重量份的发泡剂、三溴苯酚4%重量份的阻燃剂、双二四铂金硫化剂3%重量份的促进剂搅拌混合制备成滴液备用；
②、将硅胶覆膜的磁性密封条放入模具中，对所述模具在温度110℃、负压60KPa条件下滴入所述滴液，使所述滴液在所述模具内发泡以填充所述模具的腔体且使所述磁性密封条定型，将所述定型的磁性密封条脱出所述模具，制成门窗的磁吸消音闭合密封条成品。
2.根据权利要求1所述门窗的磁吸消音闭合密封条生产方法，其特征在于：所述三溴苯酚选择替换为三聚氰胺氰尿酸盐、三聚磷酸铝、四溴双酚A、四溴苯酐中的一种。
3.根据权利要求1所述门窗的磁吸消音闭合密封条生产方法，其特征在于：所述温度110℃替换为80℃-160℃，所述负压60KPa替换为40KPa-87KPa。
4.根据权利要求1所述门窗的磁吸消音闭合密封条生产方法，其特征在于：所述模具为L形的腔体，所述磁性密封条的形状与所述模具的腔体相吻合。