CN113062025A - 一种玉锌冰爽保健面料及其制备方法 - Google Patents
一种玉锌冰爽保健面料及其制备方法 Download PDFInfo
- Publication number
- CN113062025A CN113062025A CN202110235644.9A CN202110235644A CN113062025A CN 113062025 A CN113062025 A CN 113062025A CN 202110235644 A CN202110235644 A CN 202110235644A CN 113062025 A CN113062025 A CN 113062025A
- Authority
- CN
- China
- Prior art keywords
- jade
- zinc
- fabric
- ice
- release particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种玉锌冰爽保健面料及其制备方法，由经纱和纬纱编织而成，经纱和纬纱由玉锌纤维和棉纤维混纺制成；玉锌纤维中负载有功能粉末，功能粉末包括玉石粉、电气石粉及纳米氧化锌；面料上负载有包括芳香缓释粒子的涂层，芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层。本发明使用玉锌纤维与棉纤维混纺制成具有冰爽、释放负离子、抗菌、防臭等功效的功能性面料，并且在面料表面负载芳香缓释粒子，使面料可以在不同温度下实现香气的控释，适用于制备内衣裤、塑身衣、袜子、睡衣、T恤、衬衣等各种贴身穿着的衣物。
Description
技术领域
本发明涉及功能性面料技术领域，尤其是涉及一种玉锌冰爽保健面料及其制备方法。
背景技术
随着生活水平的不断提高，人们对贴身衣物的品质要求也日益增高，具有各种功能的贴身衣物应运而生，如抗菌、防辐射、保暖等等。在炎热的夏天，人们急需一种具有降温功效的贴身衣物，高温天气下穿一件冰爽透气的衣服，能够极大的提升人体舒适度，有利于工作和生活。
目前，一般通过在面料中添加玉石纤维制成具有凉爽功能的面料，例如，一种在中国专利文献上公开的“玉石纤维混纺面料”，其公开号CN105544051A，由经纱和纬纱编织而成，所述的经纱由玉石纤维与麻纤维混纺，玉石纤维所占的重量百分比为45-60％，麻纤维所占的重量百分比为40-55％；所述的纬纱由玉石纤维和薄荷纤维混纺，玉石纤维所占的重量百分比为38-64％，薄荷纤维所占的重量百分比为36-62％。
但现有技术中使用玉石纤维制成的冰爽面料功能性较为单一，难以满足人们对贴身衣物日益增长的功能需求。
发明内容
本发明是为了克服现有技术中使用玉石纤维制成的冰爽面料功能性较为单一，难以满足人们对贴身衣物日益增长的功能需求的问题，提供一种玉锌冰爽保健面料及其制备方法，使用玉锌纤维与棉纤维混纺制成具有冰爽、释放负离子、抗菌、防臭等功效的功能性面料，并且在面料表面负载芳香缓释粒子，使面料可以在不同温度下实现香气的控释，适用于制备内衣裤、塑身衣、袜子、睡衣、T恤、衬衣等各种贴身穿着的衣物，满足人们对贴身衣物保健功能的多样化需求。
为了实现上述目的，本发明采用以下技术方案：
一种玉锌冰爽保健面料，由经纱和纬纱编织而成，所述的经纱和纬纱由玉锌纤维和棉纤维混纺制成；所述玉锌纤维中负载有功能粉末，所述功能粉末包括玉石粉、电气石粉及纳米氧化锌；所述面料上负载有包括芳香缓释粒子的涂层，所述的芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层。
本发明的面料由负载了玉石粉、电气石粉和纳米氧化锌的玉锌纤维和棉纤维混纺编织而成。棉纤维具有良好的吸湿性和亲肤性，可以提高面料的穿着舒适性；玉锌纤维中，玉是热的良导体，因此用添加了玉石粉的玉锌纤维制成的织物可以使人体有较好的冰爽感，特别适合在炎热的夏天或运动的时候穿着；并且玉石中含有丰富的对人体有益的矿物质和微量元素，长期贴附在人体的皮肤上，进行释放，能改善血液微循环，促进新陈代谢，从而达到预防疾病、消除疲劳的作用。电气石能够自动和永久地释放负氧离子，是天然的负离子发生器，在面料中添加负载了电气石粉的玉锌纤维，使面料可以释放负离子，制成贴身衣物穿着时，可以净化血液，复活细胞，提高人体的免疫力，有助于改善头疼、失眠、神经衰弱等现象。玉锌纤维中的纳米氧化锌同样具有良好的导热性能，加入面料中有利于散热形成冰爽触感；并且纳米氧化锌具有良好的抗红外线、紫外线辐射及杀菌功能，可以使面料具有防辐射和抗菌功效，满足贴身衣物的穿着健康性。
为了使面料可以长效的释放香味，以起到舒缓压力、愉悦心情、杀菌除臭的功效，本发明还在面料上负载了芳香缓释粒子。本发明中的芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层。内核的介孔二氧化硅用于将植物精油吸附负载在其孔道内，实现易挥发的植物精油的初步缓释，延长纤维的释香时间；外层的无定形二氧化硅层起到对相变材料层的赋形和保护作用；中间的相变材料层用于实现植物精油在不同温度下的控释：由十六酸和十四醇混合形成的相变材料层相变温度为32℃左右，芳香缓释粒子随纤维制成贴身衣物后，当衣物穿着接触人体时，温度升高，芳香缓释粒子中间的相变材料层变为液态，壳层的致密性降低，内核中负载的植物精油释放速率加快，香味释放量增大；而当衣物离开人体后，温度降低，相变材料层凝固为固态，壳层致密性增大，内核中负载的植物精油释放量降低，香味减弱。
因此本发明中的玉锌冰爽保健面料不但具有冰爽、释放负离子、抗菌等保健功效，同时还可以在穿着时通过挥发植物精油释放香气，起到杀菌除臭、愉悦心情等功能。并且香味的释放可以通过温度进行控释，实现衣物穿着时香味释放多而不穿时则释放较少，有效减少了植物精油的损失，延长了纤维的释香时间。本发明中的面料可用于制备内衣裤、塑身衣、运动内衣、袜子、睡衣、T恤、衬衣等各种贴身穿着的衣物，有利于人体舒适和健康。
作为优选，所述芳香缓释粒子的制备方法为：
A)将正硅酸乙酯加入乙醇和水的混合溶剂中，65～75℃下搅拌1～2h后用氨水调节溶液pH至8～9，继续保温搅拌1～2h得到凝胶，然后在空气中陈化1～3d，得到陈化后的凝胶；
B)将陈化后的凝胶置于pH为9～11的4-叠氮苯胺盐酸盐水溶液中浸泡5～8h，过滤后将产物置于紫外光下照射15～20min；然后在100～120℃下真空干燥10～12h，再在700～800℃下煅烧2～3h后得到介孔二氧化硅；
C)将介孔二氧化硅置于植物精油溶液中，搅拌吸附12～24h，得到负载植物精油的二氧化硅；
D)将十六酸、十四醇、正硅酸乙酯混合，再依次加入十六烷基三甲基溴化铵、水和乙醇，剪切均质40～60min得到乳化液；
E)将负载植物精油的二氧化硅置于乳化液中，搅拌20～30min后加入氨水，调节体系pH至8～9，持续搅拌12～24h，过滤、洗涤、干燥后得到所述芳香缓释粒子。
本发明利用溶胶凝胶法，以4-叠氮苯胺盐酸盐为造孔剂制得了介孔二氧化硅。由于正硅酸乙酯在碱催化下水解形成的二氧化硅凝胶表面带负电，本发明利用造孔剂4-叠氮苯胺盐酸盐中带正电的季铵盐基团与带负电的二氧化硅凝胶之间的静电吸引作用，使造孔剂吸附和富集在二氧化硅凝胶内，然后通过紫外光照射使造孔剂中的苯基叠氮基团分解为氮气逸出，从而在二氧化硅凝胶中初步形成孔道，最后通过高温烧结，使造孔剂中的其他有机基团分解，进一步扩大孔道，得到具有较大比表面积和良好负载性能的介孔二氧化硅载体。
作为优选，所述的经纱在面料中的质量分数为48～52％，其余为纬纱。
作为优选，所述经纱中玉锌纤维的质量分数为50～55％，所述纬纱中玉锌纤维的质量分数为30～35％。
本发明还提供了一种上述玉锌冰爽保健面料的制备方法，包括如下步骤：
S1：原料准备：制备玉锌纤维；
S2：混纺：将玉锌纤维与棉纤维按比例混纺，制成经纱和纬纱；
S3：织造：将经纱和纬纱编织成面料；
S4：涂覆：将编织好的面料水洗后用包含芳香缓释粒子的涂层剂进行涂覆，烘干后得到所述玉锌冰爽保健面料。
作为优选，S1中玉锌纤维的制备方法为：
(1)将功能粉末与聚丙烯酸酯乳液混合，搅拌得到喷涂浆料；
(2)将聚酯切片熔融后喷丝冷却得到单丝；
(3)用喷涂浆料对所得单丝进行喷涂；
(4)喷涂后的单丝经集束上油后进入纺丝甬道纺丝；
(5)纺丝后经拉伸、卷绕得到所述玉锌纤维。
本发明中的玉锌纤维制备时，是在纺丝前将功能粉末喷涂在单丝上，然后再对单丝进行集束纺丝，使各种功能粉末均匀分布在纤维内部和表面，有效避免了将功能粉末加入聚酯熔体中进行纺丝时对纤维可纺性的影响。
作为优选，步骤(1)所述喷涂浆料的成分以质量分数计包括40～60％的功能粉末及60～40％的聚丙烯酸酯乳液，所述聚丙烯酸酯乳液的固含量为40～45wt％；步骤(3)中喷涂浆料的喷涂质量为步骤(2)中熔融物单位时间输送质量的10～20％。
作为优选，步骤(1)中所述的功能性粉末中玉石粉、电气石粉和纳米氧化锌的质量比为：4～6:1～2:1。
作为优选，S4中所述的涂层剂以质量分数计包括15～25％的芳香缓释粒子及75～85％的聚丙烯酸酯乳液，所述聚丙烯酸酯乳液的固含量为40～45wt％。
作为优选，S4中芳香缓释粒子的涂覆量为基布质量的3～5％。
因此，本发明具有如下有益效果：
(1)面料由负载了玉石粉、电气石粉和纳米氧化锌的玉锌纤维和棉纤维混纺编织而成。棉纤维具有良好的吸湿性和亲肤性，可以提高面料的穿着舒适性；玉锌纤维中的功能粉末使面料具有冰爽、释放负离子、抗菌等保健功效，有利于人体舒适和健康；
(2)在面料上负载芳香缓释粒子，使面料可以通过挥发植物精油释放香气，起到杀菌除臭、愉悦心情等功能；并且香味的释放可以通过温度进行控释，实现衣物穿着时香味释放多而不穿时则释放较少，有效减少了植物精油的损失，延长了纤维的释香时间。
具体实施方式
下面结合具体实施方式对本发明做进一步的描述。
在本发明中，若非特指，所有原料均可从市场购得或是本行业常用的，下述实施例中的方法，如无特别说明，均为本领域常规方法。
实施例1：
一种玉锌冰爽保健面料的制备方法，包括如下步骤：
S1：制备玉锌纤维：
(1)将包括质量比为5:1:1的亚微米级玉石粉、亚微米级电气石粉及纳米氧化锌的功能粉末与固含量为42wt％的聚丙烯酸酯乳液混合，搅拌得到喷涂浆料，喷涂浆料中功能粉末和聚丙烯酸酯乳液的质量分数分别为50％和50％；
(2)将聚酯切片熔融后经十字形喷丝板喷丝冷却得到截面呈十字形的单丝；
(3)用喷涂浆料对所得单丝进行喷涂，喷涂浆料的喷涂质量为步骤(2)中聚酯熔融物单位时间输送质量的15％；
(4)喷涂后的单丝经集束上油后进入纺丝甬道，90℃下纺丝；
(5)纺丝后经拉伸、卷绕得到所述玉锌纤维；
S2：混纺：将上述制得的玉锌纤维与棉纤维按比例混纺，制成经纱和纬纱，经纱中玉锌纤维的质量分数为53％，纬纱中玉锌纤维的质量分数为32％；
S3：织造：将经纱和纬纱编织成厚度为0.5mm的面料，经纱在面料中的质量分数为50％；
S4：涂覆：将编织好的面料水洗并烘干后用包含芳香缓释粒子的涂层剂进行涂覆，涂层剂以质量分数计包括20％的芳香缓释粒子及80％的聚丙烯酸酯乳液，聚丙烯酸酯乳液的固含量为42wt％，芳香缓释粒子的涂覆量为基布质量的4％，烘干后得到所述玉锌冰爽保健面料。
其中，芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层，其制备方法为：
A)将正硅酸乙酯加入乙醇和水的混合溶剂中，使正硅酸乙酯、乙醇和水的体积比为1:2.5:2.5，70℃下搅拌1.5h后用氨水调节溶液pH至8.6，继续保温搅拌1.5h得到凝胶，然后在空气中陈化2d，得到陈化后的凝胶；
B)将陈化后的凝胶置于pH为10、浓度为12mg/mL的4-叠氮苯胺盐酸盐水溶液中浸泡6h，过滤后将产物置于功率为1500mW/cm2的紫外光下照射18min；然后在110℃下真空干燥11h，再在750℃下煅烧2.5h，将产物研磨后得到介孔二氧化硅；
C)将介孔二氧化硅置于质量分数为4％的玫瑰精油溶液中，搅拌吸附18h，得到负载玫瑰精油的二氧化硅；
D)将十六酸、十四醇、正硅酸乙酯混合，再依次加入十六烷基三甲基溴化铵、水和乙醇，1000rpm转速下剪切均质50min得到乳化液，十六酸、十四醇、正硅酸乙酯、十六烷基三甲基溴化铵、水和乙醇的添加比例为20g:80g:100mL:32g:2.8L:1.2L；
E)将负载玫瑰精油的二氧化硅置于乳化液中，负载玫瑰精油的二氧化硅与乳化液的质量体积比为：0.15g：5mL，搅拌25min后加入氨水，调节体系pH至8.5，持续搅拌18h，过滤、洗涤、干燥后得到所述芳香缓释粒子。
实施例2：
一种玉锌冰爽保健面料的制备方法，包括如下步骤：
S1：制备玉锌纤维：
(1)将包括质量比为4:2:1的亚微米级玉石粉、亚微米级电气石粉及纳米氧化锌的功能粉末与固含量为42wt％的聚丙烯酸酯乳液混合，搅拌得到喷涂浆料，喷涂浆料中功能粉末和聚丙烯酸酯乳液的质量分数分别为40％和60％；
(2)将聚酯切片熔融后经米字形喷丝板喷丝冷却得到截面呈米字形的单丝；
(3)用喷涂浆料对所得单丝进行喷涂，喷涂浆料的喷涂质量为步骤(2)中聚酯熔融物单位时间输送质量的20％；
(4)喷涂后的单丝经集束上油后进入纺丝甬道，80℃下纺丝；
(5)纺丝后经拉伸、卷绕得到所述玉锌纤维；
S2：混纺：将上述制得的玉锌纤维与棉纤维按比例混纺，制成经纱和纬纱，经纱中玉锌纤维的质量分数为50％，纬纱中玉锌纤维的质量分数为35％；
S3：织造：将经纱和纬纱编织成厚度为0.5mm的面料，经纱在面料中的质量分数为52％；
S4：涂覆：将编织好的面料水洗并烘干后用包含芳香缓释粒子的涂层剂进行涂覆，涂层剂以质量分数计包括15％的芳香缓释粒子及85％的聚丙烯酸酯乳液，聚丙烯酸酯乳液的固含量为42wt％，芳香缓释粒子的涂覆量为基布质量的3％，烘干后得到所述玉锌冰爽保健面料。
其中，芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层，其制备方法为：
A)将正硅酸乙酯加入乙醇和水的混合溶剂中，使正硅酸乙酯、乙醇和水的体积比为1:2:3，65℃下搅拌2h后用氨水调节溶液pH至8，继续保温搅拌2h得到凝胶，然后在空气中陈化1d，得到陈化后的凝胶；
B)将陈化后的凝胶置于pH为9、浓度为10mg/mL的4-叠氮苯胺盐酸盐水溶液中浸泡5h，过滤后将产物置于功率为1000mW/cm2的紫外光下照射20min；然后在100℃下真空干燥12h，再在700℃下煅烧3h，将产物研磨后得到介孔二氧化硅；
C)将介孔二氧化硅置于质量分数为3％的薰衣草精油溶液中，搅拌吸附12h，得到负载薰衣草精油的二氧化硅；
D)将十六酸、十四醇、正硅酸乙酯混合，再依次加入十六烷基三甲基溴化铵、水和乙醇，2000rpm转速下剪切均质40min得到乳化液，十六酸、十四醇、正硅酸乙酯、十六烷基三甲基溴化铵、水和乙醇的添加比例为18g:82g:100mL:30g:2.5L:1.5L；
E)将负载薰衣草精油的二氧化硅置于乳化液中，负载薰衣草精油的二氧化硅与乳化液的质量体积比为：0.1g：5mL，搅拌20min后加入氨水，调节体系pH至8.1，持续搅拌12h，过滤、洗涤、干燥后得到所述芳香缓释粒子。
实施例3：
一种玉锌冰爽保健面料的制备方法，包括如下步骤：
S1：制备玉锌纤维：
(1)将包括质量比为6:1:1的亚微米级玉石粉、亚微米级电气石粉及纳米氧化锌的功能粉末与固含量为42wt％的聚丙烯酸酯乳液混合，搅拌得到喷涂浆料，喷涂浆料中功能粉末和聚丙烯酸酯乳液的质量分数分别为60％和40％；
(2)将聚酯切片熔融后经双十字形喷丝板喷丝冷却得到截面呈双十字形的单丝；
(3)用喷涂浆料对所得单丝进行喷涂，喷涂浆料的喷涂质量为步骤(2)中聚酯熔融物单位时间输送质量的10％；
(4)喷涂后的单丝经集束上油后进入纺丝甬道，100℃下纺丝；
(5)纺丝后经拉伸、卷绕得到所述玉锌纤维；
S2：混纺：将上述制得的玉锌纤维与棉纤维按比例混纺，制成经纱和纬纱，经纱中玉锌纤维的质量分数为55％，纬纱中玉锌纤维的质量分数为30％；
S3：织造：将经纱和纬纱编织成厚度为0.5mm的面料，经纱在面料中的质量分数为48％；
S4：涂覆：将编织好的面料水洗并烘干后用包含芳香缓释粒子的涂层剂进行涂覆，涂层剂以质量分数计包括25％的芳香缓释粒子及75％的聚丙烯酸酯乳液，聚丙烯酸酯乳液的固含量为42wt％，芳香缓释粒子的涂覆量为基布质量的5％，烘干后得到所述玉锌冰爽保健面料。
其中，芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层，其制备方法为：
A)将正硅酸乙酯加入乙醇和水的混合溶剂中，使正硅酸乙酯、乙醇和水的体积比为1:3:2，75℃下搅拌1h后用氨水调节溶液pH至9，继续保温搅拌1h得到凝胶，然后在空气中陈化3d，得到陈化后的凝胶；
B)将陈化后的凝胶置于pH为11、浓度为15mg/mL的4-叠氮苯胺盐酸盐水溶液中浸泡8h，过滤后将产物置于功率为2000mW/cm2的紫外光下照射15min；然后在120℃下真空干燥10h，再在800℃下煅烧2h，将产物研磨后得到介孔二氧化硅；
C)将介孔二氧化硅置于质量分数为5％的柠檬精油溶液中，搅拌吸附24h，得到负载薰衣草精油的二氧化硅；
D)将十六酸、十四醇、正硅酸乙酯混合，再依次加入十六烷基三甲基溴化铵、水和乙醇，1000rpm转速下剪切均质60min得到乳化液，十六酸、十四醇、正硅酸乙酯、十六烷基三甲基溴化铵、水和乙醇的添加比例为22g:78g:100mL:35g:3.0L:1.0L；
E)将负载薰衣草精油的二氧化硅置于乳化液中，负载薰衣草精油的二氧化硅与乳化液的质量体积比为：0.2g：5mL，搅拌30min后加入氨水，调节体系pH至9.0，持续搅拌24h，过滤、洗涤、干燥后得到所述芳香缓释粒子。
对比例1(芳香缓释粒子不包覆相变材料层和无定形二氧化硅层)：
对比例1中使用的芳香缓释粒子的制备方法为：
A)将正硅酸乙酯加入乙醇和水的混合溶剂中，使正硅酸乙酯、乙醇和水的体积比为1:2.5:2.5，70℃下搅拌1.5h后用氨水调节溶液pH至8.6，继续保温搅拌1.5h得到凝胶，然后在空气中陈化2d，得到陈化后的凝胶；
B)将陈化后的凝胶置于pH为10、浓度为12mg/mL的4-叠氮苯胺盐酸盐水溶液中浸泡6h，过滤后将产物置于功率为1500mW/cm2的紫外光下照射18min；然后在110℃下真空干燥11h，再在750℃下煅烧2.5h，将产物研磨后得到介孔二氧化硅；
C)将介孔二氧化硅置于质量分数为4％的玫瑰精油溶液中，搅拌吸附18h，得到所述芳香缓释粒子。
其余均与实施例1中相同。
对比例2(芳香缓释粒子中无定型二氧化硅层过厚)：
对比例2中使用的芳香缓释粒子的制备方法为：
A)将正硅酸乙酯加入乙醇和水的混合溶剂中，使正硅酸乙酯、乙醇和水的体积比为1:2.5:2.5，70℃下搅拌1.5h后用氨水调节溶液pH至8.6，继续保温搅拌1.5h得到凝胶，然后在空气中陈化2d，得到陈化后的凝胶；
B)将陈化后的凝胶置于pH为10、浓度为12mg/mL的4-叠氮苯胺盐酸盐水溶液中浸泡6h，过滤后将产物置于功率为1500mW/cm2的紫外光下照射18min；然后在110℃下真空干燥11h，再在750℃下煅烧2.5h，将产物研磨后得到介孔二氧化硅；
C)将介孔二氧化硅置于质量分数为4％的玫瑰精油溶液中，搅拌吸附18h，得到负载玫瑰精油的二氧化硅；
D)将十六酸、十四醇、正硅酸乙酯混合，再依次加入十六烷基三甲基溴化铵、水和乙醇，1000rpm转速下剪切均质50min得到乳化液，十六酸、十四醇、正硅酸乙酯、十六烷基三甲基溴化铵、水和乙醇的添加比例为20g:80g:300mL:32g:2.8L:1.2L；
E)将负载玫瑰精油的二氧化硅置于乳化液中，负载玫瑰精油的二氧化硅与乳化液的质量体积比为：0.15g：5mL，搅拌25min后加入氨水，调节体系pH至8.5，持续搅拌18h，过滤、洗涤、干燥后得到所述芳香缓释粒子。
其余均与实施例1中相同。
对上述实施例和对比例中制得的面料的凉感、抗菌性及负离子发生量进行测定，结果如表1中所示。
其中，接触凉感系数的测定参照GB/T 35263-2017中的方法；
抗菌性能的测试参照FZ/T 73023-2006中的方法；
负离子发生量的测定参照GB/T 30128-2013中的方法。
表1：织物性能测试结果。
将上述面料分别置于25℃和35℃恒温箱中测试其释香性能，结果如表2中所示。其中
表2：释香性能测试结果。
从表1和表2中可以看出，本发明制得的面料具有良好的冰爽感、抗菌性及负离子产生量，制作成贴身衣物可以有较好的保健效果。并且实施例1～3中负载了本发明中的芳香缓释粒子的面料可以长效释放香气，香气的释放量随温度进行变化，室温下香气释放较少，接近人体温度时香气释放较多，35℃下的释香时间可达21个月。而对比文件1中的芳香缓释粒子表面不包覆相变材料层，面料不能根据温度对香气进行控释，面料的释香持久性明显降低；对比例2中芳香缓释粒子表面包覆的无定形二氧化硅层过厚，导致香气不能有效释放，释香效果不佳。
Claims (9)
1.一种玉锌冰爽保健面料，其特征是，由经纱和纬纱编织而成，所述的经纱和纬纱由玉锌纤维和棉纤维混纺制成；所述玉锌纤维中负载有功能粉末，所述功能粉末包括玉石粉、电气石粉及纳米氧化锌；所述面料上负载有包括芳香缓释粒子的涂层，所述的芳香缓释粒子具有三层核壳结构，由内至外依次为负载了植物精油的介孔二氧化硅内核、由十六酸和十四醇组成的相变材料层及相变层外侧的无定形二氧化硅保护层。
2.根据权利要求1所述的一种玉锌冰爽保健面料，其特征是，所述的经纱在面料中的质量分数为48~52%，其余为纬纱。
3.根据权利要求1或2所述的一种玉锌冰爽保健面料，其特征是，所述经纱中玉锌纤维的质量分数为50~55%，所述纬纱中玉锌纤维的质量分数为30~35%。
4.根据权利要求1~3任意一项所述的一种玉锌冰爽保健面料的制备方法，其特征是，包括如下步骤：
S1：原料准备：制备玉锌纤维；
S2：混纺：将玉锌纤维与棉纤维按比例混纺，制成经纱和纬纱；
S3：织造：将经纱和纬纱编织成面料；
S4：涂覆：将编织好的面料水洗后用包含芳香缓释粒子的涂层剂进行涂覆，烘干后得到所述玉锌冰爽保健面料。
5.根据权利要求4所述的一种玉锌冰爽保健面料的制备方法，其特征是，S1中玉锌纤维的制备方法为：
（1）将功能粉末与聚丙烯酸酯乳液混合，搅拌得到喷涂浆料；
（2）将聚酯切片熔融后喷丝冷却得到单丝；
（3）用喷涂浆料对所得单丝进行喷涂；
（4）喷涂后的单丝经集束上油后进入纺丝甬道纺丝；
（5）纺丝后经拉伸、卷绕得到所述玉锌纤维。
6.根据权利要求5所述的一种玉锌冰爽保健面料的制备方法，其特征是，步骤（1）所述喷涂浆料的成分以质量分数计包括40~60%的功能粉末及60~40%的聚丙烯酸酯乳液，所述聚丙烯酸酯乳液的固含量为40~45wt%；步骤（3）中喷涂浆料的喷涂质量为步骤（2）中熔融物单位时间输送质量的10~20%。
7.根据权利要求5或6所述的一种玉锌冰爽保健面料的制备方法，其特征是，步骤（1）中所述的功能性粉末中玉石粉、电气石粉和纳米氧化锌的质量比为：4~6:1~2:1。
8.根据权利要求4所述的一种玉锌冰爽保健面料的制备方法，其特征是，S4中所述的涂层剂以质量分数计包括15~25%的芳香缓释粒子及75~85%的聚丙烯酸酯乳液，所述聚丙烯酸酯乳液的固含量为40~45wt%。
9.根据权利要求4所述的一种玉锌冰爽保健面料的制备方法，其特征是，S4中芳香缓释粒子的涂覆量为基布质量的3~5%。