CN112940371A - 一种聚烯烃全降解母料的制作方法 - Google Patents
一种聚烯烃全降解母料的制作方法 Download PDFInfo
- Publication number
- CN112940371A CN112940371A CN202110148482.5A CN202110148482A CN112940371A CN 112940371 A CN112940371 A CN 112940371A CN 202110148482 A CN202110148482 A CN 202110148482A CN 112940371 A CN112940371 A CN 112940371A
- Authority
- CN
- China
- Prior art keywords
- biological
- master batch
- fully
- steps
- polyolefin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种聚烯烃全降解母料的制作方法，具体包括以下步骤：1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。本发明优点在于：原料配比设计合理，制作简单，使用时添加量少，成本低，且使用方便，不改变原有的设备及工艺，方便控制光、热氧化降解，具有降解速度快，降解彻底的优点，具备很好的推广前景和市场价值。
Description
技术领域
本发明涉及一种聚烯烃全降解母料的制作方法。
背景技术
目前市场上常见的降解母料为：光氧降解母料、热氧化降解母料、光氧/生物双降解母料等，均存在一定的缺陷。其中，光氧降解、热氧化降解只能在特定条件下将聚合物降解为碎片或颗粒，光氧/生物双降解母料中的生物降解物质多为玉米淀粉，自身不能降解聚合物，只能通过引起环境中的细菌、真菌等的聚集而引发生物降解，降解速度慢且大量使用玉米淀粉，不利于国家的粮食安全。生物酶、生物菌只能降解数均分子量不超过28000的聚合物，而聚合物的数均分子量一般为十万及以上，即生物酶与生物菌不能直接降解聚合物。
发明内容
本发明的目的在于提供一种聚烯烃全降解母料的制作方法，以解决上述背景技术中提出的问题。
为解决上述技术问题，本发明提供的技术方案为：一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为一种优选方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中的至少一种。
作为一种优选方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中的至少一种。
作为一种优选方案，所述的热敏剂为硬脂酸锰。
作为一种优选方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的至少一种。
作为一种优选方案，所述的树脂为聚烯烃树脂。
作为一种优选方案，所述的加工助剂为聚乙烯蜡、石蜡中的一种。
作为一种优选方案，所述的生物剂包括生物培养基和生物降解剂。
作为一种优选方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中的至少一种。
作为一种优选方案，所述的生物降解剂包括生物酶和生物菌。
本发明优点在于：原料配比设计合理，制作简单，使用时添加量少，成本低，且使用方便，不改变原有的设备及工艺，方便控制光、热氧化降解，具有降解速度快，降解彻底的优点，具备很好的推广前景和市场价值。
具体实施方式
下面用具体实施例说明本发明，并不是对本发明的限制。
实施例1
一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为本实施例的优选实施方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中的一种。
作为本实施例的优选实施方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中一种。
作为本实施例的优选实施方案，所述的热敏剂为硬脂酸锰。
作为本实施例的优选实施方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的一种。
作为本实施例的优选实施方案，所述的树脂为聚烯烃树脂。
作为本实施例的优选实施方案，所述的加工助剂为聚乙烯蜡。
作为本实施例的优选实施方案，所述的生物剂包括生物培养基和生物降解剂。
作为本实施例的优选实施方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中的一种。
作为本实施例的优选实施方案，所述的生物降解剂包括生物酶和生物菌。
实施例2
一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为本实施例的优选实施方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中的两种。
作为本实施例的优选实施方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中的两种。
作为本实施例的优选实施方案，所述的热敏剂为硬脂酸锰。
作为本实施例的优选实施方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的两一种。
作为本实施例的优选实施方案，所述的树脂为聚烯烃树脂。
作为本实施例的优选实施方案，所述的加工助剂为聚乙烯蜡。
作为本实施例的优选实施方案，所述的生物剂包括生物培养基和生物降解剂。
作为本实施例的优选实施方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中的两种。
作为本实施例的优选实施方案，所述的生物降解剂包括生物酶和生物菌。
实施例3
一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为本实施例的优选实施方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中三种。
作为本实施例的优选实施方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中的三种。
作为本实施例的优选实施方案，所述的热敏剂为硬脂酸锰。
作为本实施例的优选实施方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的三种。
作为本实施例的优选实施方案，所述的树脂为聚烯烃树脂。
作为本实施例的优选实施方案，所述的加工助剂为聚乙烯蜡。
作为本实施例的优选实施方案，所述的生物剂包括生物培养基和生物降解剂。
作为本实施例的优选实施方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中的三种。
作为本实施例的优选实施方案，所述的生物降解剂包括生物酶和生物菌。
实施例4
一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为本实施例的优选实施方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉的混合物。
作为本实施例的优选实施方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中的四种。
作为本实施例的优选实施方案，所述的热敏剂为硬脂酸锰。
作为本实施例的优选实施方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物的混合物。
作为本实施例的优选实施方案，所述的树脂为聚烯烃树脂。
作为本实施例的优选实施方案，所述的加工助剂为石蜡。
作为本实施例的优选实施方案，所述的生物剂包括生物培养基和生物降解剂。
作为本实施例的优选实施方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中四种。
作为本实施例的优选实施方案，所述的生物降解剂包括生物酶和生物菌。
实施例5
一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为本实施例的优选实施方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中的至少一种。
作为本实施例的优选实施方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中的五种。
作为本实施例的优选实施方案，所述的热敏剂为硬脂酸锰。
作为本实施例的优选实施方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的至少一种。
作为本实施例的优选实施方案，所述的树脂为聚烯烃树脂。
作为本实施例的优选实施方案，所述的加工助剂为石蜡。
作为本实施例的优选实施方案，所述的生物剂包括生物培养基和生物降解剂。
作为本实施例的优选实施方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖的混合物。
作为本实施例的优选实施方案，所述的生物降解剂包括生物酶和生物菌。
实施例6
一种聚烯烃全降解母料的制作方法，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
作为本实施例的优选实施方案，所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中的至少一种。
作为本实施例的优选实施方案，所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁的混合物。
作为本实施例的优选实施方案，所述的热敏剂为硬脂酸锰。
作为本实施例的优选实施方案，所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的至少一种。
作为本实施例的优选实施方案，所述的树脂为聚烯烃树脂。
作为本实施例的优选实施方案，所述的加工助剂为聚乙烯蜡、石蜡中的一种。
作为本实施例的优选实施方案，所述的生物剂包括生物培养基和生物降解剂。
作为本实施例的优选实施方案，所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中的至少一种。
作为本实施例的优选实施方案，所述的生物降解剂包括生物酶和生物菌。
本发明的原理：在光或热(工业堆肥条件下)的作用下，将聚合物降解至数均分子量28000以下(实测不超过15000)，同时，聚合物表面由憎水性转变为亲水性，在加入的生物菌、生物酶及环境中存在的真菌和细菌等的共同作用下将聚合物彻底降解为二氧化碳、水和所含元素的盐类。其中，所含的钙及其他微量金属元素能成为植物生长的肥料或所需的微量元素，有望彻底解决白色污染的问题。本发明中使用的热敏剂、光敏剂还作为填充材料的表面活化处理剂。光敏剂、热敏剂和生物降解材料均匀附着在填充材料表面，有利于其在聚合物中的均匀分散。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种聚烯烃全降解母料的制作方法，其特征在于，具体包括以下步骤：
1)准备原料：填充材料、光敏剂、热敏剂、助氧化剂、生物剂、树脂、加工助剂；
2)将填充材料、生物剂加入高速混合机中，加热至100℃以上后向高速混合机中加入光敏剂、热敏剂，混匀，加入树脂及加工助剂混匀，经双螺杆挤出机挤出造粒。
2.根据权利要求1所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的填充材料为方解石粉、轻质碳酸钙、高岭土、滑石粉中的至少一种。
3.根据权利要求1所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的光敏剂为过渡金属的硬脂酸盐、过渡金属的羧酸盐、二苯甲酮、二苯甲酮衍生物、铁盐类化合物、二茂铁中的至少一种。
4.根据权利要求1所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的热敏剂为硬脂酸锰。
5.根据权利要求1所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的助氧化剂为脂肪酸、油酸、脂肪酸化合物、油酸化合物中的至少一种。
6.根据权利要求1所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的树脂为聚烯烃树脂。
7.根据权利要求1所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的加工助剂为聚乙烯蜡、石蜡中的一种。
8.根据权利要求1-7任一项所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的生物剂包括生物培养基和生物降解剂。
9.根据权利要求8所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的生物培养基为蛋白质、氨基酸、多糖、寡糖、单糖中的至少一种。
10.根据权利要求8所述的一种聚烯烃全降解母料的制作方法，其特征在于：所述的生物降解剂包括生物酶和生物菌。