CN1128982A - 玻璃纤维组合物 - Google Patents
玻璃纤维组合物 Download PDFInfo
- Publication number
- CN1128982A CN1128982A CN95190487A CN95190487A CN1128982A CN 1128982 A CN1128982 A CN 1128982A CN 95190487 A CN95190487 A CN 95190487A CN 95190487 A CN95190487 A CN 95190487A CN 1128982 A CN1128982 A CN 1128982A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- weight
- oxide
- fiber compound
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一能生物降解的矿物纤维组合物以下列成分(按重量百分数计)为特征:SiO2:50到60;Al2O3:小于2;CaO+MgO:10到16;Na2O+K2O:14到19;B2O3:7到16;TiO2:0到4;ZrO2:0到5;ZnO:0到5;MnO:0到4;BaO:0到5;TiO2、ZrO2、ZnO、MnO、BaO:1到6;Fe2O3、SrO:0到2;F、Li2O:0到2;P2O3:0到4。
Description
本发明涉及一种能生物降解的玻璃纤维组合物。
现有技术描述了一些据说能生物降解的玻璃纤维组合物。
玻璃纤维组合物的生物降解性是十分重要的,因为许多研究指出:一些直径很小的、小于3微米的玻璃纤维可能是致癌的,而这样大小的能生物降解的玻璃纤维不显示致癌性。
但是,不只是生物降解性极端重要,玻璃纤维或由它制得的产品的机械性能、热性能,玻璃纤维的电阻以及玻璃纤维组合物的加工性能也都非常重要。例如,玻璃纤维大量用作绝缘材料,为此,玻璃纤维必须具有足够的耐湿性。
玻璃纤维组合物也必须能用已知的生产小直径玻璃纤维的方法,例如,离心技术,特别是内离心技术(此技术在美国专利US-PS 4 203 745中叙述),加工成型。
本发明主要是提供一种新型的玻璃纤维组合物,其特征是能生物降解、稳定性好,耐湿,而且容易加工。
本发明发现,通过提供一种玻璃纤维组合物,这种组合物中含有相当量的碱性氧化物和氧化硼,含有氧化钛、氧化锆、氧化锌、氧化锰、氧化钡或这些氧化物的二种或多种混合物,有上述特征的新型玻璃纤维就可得到。
已经证明,这样的玻璃纤维组合物满足上述必需的性质,即生物降解性、耐湿性和良好的加工成型性。
本发明目的是一种能生物降解的玻璃纤维组合物,其特征是以下列成分(按重量百分数)构成:
SiO2 50 ~ 60
Al2O3 < 2
CaO+MgO 10 ~ 16
Na2O+K2O 14 ~ 19
B2O3 7 ~ 16
TiO2 0 ~ 4
ZrO2 0 ~ 5
ZnO 0 ~ 5
MnO 0 ~ 4
BaO 0 ~ 5
TiO2,ZrO2,ZnO,MnO,BaO 1 ~ 6
Fe2O3,SrO 0 ~ 2
F,Li2O 0 ~ 2P2O3 0 ~ 4。
本发明的玻璃纤维组合物可用离心技术加工。所得的纤维耐湿性好。十分意外的是这种玻璃纤维组合物显示出生物降解性。纤维的平均直径最好是≤10微米,直径在2.5~5微米间更好。
根据一优选实施例,本发明的玻璃纤维组合物含1~4%(重量)的二氧化钛。
根据另一优选实施例,组合物含1~4%(重量)氧化锰。
根据另一优选实施例,组合物含1~4%(重量)氧化锌。
根据另一优选实施例,组合物含0.5~5%(重量),特别是0.5~3%(重量)的氧化锆。
根据另一优选实施例,组合物含有0.5~4%(重量)氧化钡。
最好使用氧化锆、氧化锌、氧化钛、氧化钡和氧化锰的混合物,尤其是两三种氧化物的混合物。
优选实施例是1~4%(重量)氧化钡与氧化钛或氧化锌的混合物。
其它优选实施例中氧化锌是和氧化钛混合,另外还可任选加入氧化锆,每种成分的量为1~3%(重量)。
其它的优选实施例中是氧化锆和氧化锌、氧化钛、氧化钡或氧化锰的混合物,这些成分的量为0.5~4%(重量),尤其是为0.5~1.5%(重量)更好。
含有氧化锆和/或氧化钡的那些组合物,若还含有0.5~2%(重量)氟和/或氧化锂更为有利。
氧化铝的量至少为0.1%(重量),尤其是至少为0.5%(重量)。
五氧化二磷增加可生物降解性。组合物最好含有0.1~2%(重量)的P2O5。
根据另一优选实施例,组合物含有小于2%(重量)的氧化镁。
本发明的玻璃纤维组合物耐湿性是由称作DGG法的标准方法测定的。在DGG法中,10克粒径在约360和400微米之间的细粒玻璃放在100毫升水中,在沸点维持5小时。在材料迅速冷却后过滤溶液,蒸发滤液至干。称量所得干材料的重量可计算出溶在水中的玻璃量。其量表示成每克测试玻璃的毫克数。
本发明的玻璃纤维组合物的生物降解性是把1克如DGG法描述的玻璃粉放人pH值为7.4的生理溶液中来测试。生理溶液成分如下:
NaCl 6.78
NH4Cl 0.535
NaHCO3 2.268
NaH2PO4H2O 0.166
(柠檬酸钠)2H2O 0.059
甘氨酸 0.450
H2SO4 0.049
CaCl2 0.022
动力学试验条件选择为如Scholze和Conradt中描述的那样。流速为300毫升/天。试验的持续时间是14天。结果表示成14天后在溶液中SiO2量的百分数×100。
本发明在下列参考实例中有更详细的描述。
实例
组成如表I和II中的玻璃被熔化。
所有玻璃组合物可很好地用离心技术加工。
倒数第二行是DGG法测得的数值。最后一行是按上述测定方法得到的生物降解性值。
表 I
实例 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15SiO2 54 53 53.5 54 53 54 53 53.5 53.5 53.5 55.5 52 53 52.5 54.7Al2O3 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 1.9 1 0.5 0.5CaO 8.5 8.5 8.5 8.5 8.5 8.5 8.5 8.5 8.5 8.5 8.5 8.0 8.5 8.5 8.5MgO 3.5 3.5 3.5 3.5 3.5 3.5 3.5 3.5 3.5 3.5 3.5 3.6 3.5 3.5 3.5Na2O 17 17 17 17 17 17 17 17 17 17 15.8 14.5 17 17 14.0K2O 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.2 0.5 0.5 0.5 1.0B2O3 13 13 13 13 13 13 13 12 12 12 12 14.5 13 12 12TiO2 2 2 2 2 1.0 2 2 1.0MnO 2 2 2ZnO 2 2 1 1.5ZrO2 2 2 2 2BaO 2 3.5 4.0P2O5 1.0 1 1 1Fe2O3 0.3SrO2 0.3F 0.6 0.7Li2O 0.4 0.3DGG 45 45 40 40 40 35 35 30 30 30 30 25 50 35 20生物降解性 500 550 500 550 600 550 600 450 450 500 550 500 550 450 450
表 II
实例 16 17 18 19SiO2 54 53.9 52.7 55.0Al2O3 0.5 0.4 0.5 0.5CaO 8.5 8.5 8.0 8.0MgO 1.8 1.5 1.8 1.5Na2O 18.0 18.0 17.3 16.0K2O 0.7 0.7 0.7 0.5B2O3 13.5 13.0 14.0 12.5TiO2 2.0 2.0MnOZnO 3.0ZrO2 2.0 2.0BaO 3.0P2O5Fe2O3SrO2FLi2O 0.4 0.4杂质 1.0 1.0 0.6 0.6
Claims (10)
1.一种可生物降解的玻璃纤维组合物,以下列成分(按重量百分数计)为特征:
SiO 50 ~ 60
Al2O3 < 2
CaO+MgO 10 ~ 16
Na2O+K2O 14 ~ 19
B2O3 7 ~ 16
TiO2 0 ~ 4
ZrO 0 ~ 5
ZnO 0 ~ 5
MnO 0 ~ 4
BaO 0 ~ 5
TiO,ZrO,ZnO,MnO,BaO 1 ~ 6
Fe2O3,SrO 0 ~ 2
F,Li2O 0 ~ 2
P2O3 0 ~ 4。
2.权利要求1的玻璃纤维组合物,其特征在于二氧化钛含量为1~4%(重量)。
3.权利要求1的玻璃纤维组合物,其特征在于氧化锰的含量为1~4%(重量)。
4.权利要求1的玻璃纤维组合物,其特征在于氧化锌的含量为1~4%(重量)。
5.权利要求1的玻璃纤维组合物,其特征在于氧化锆的含量为0.5~3%(重量)。
6.权利要求1的玻璃纤维组合物,其特征在于氧化钡的含量为0.5~4%(重量)。
7.权利要求1的玻璃纤维组合物,其特征在于假如组合物含有氧化锆和/或氧化钡,它也含有0.5~2%(重量)的氟和/或氧化锂。
8.权利要求1的玻璃纤维组合物,其特征在于组合物含有与氧化锆、氧化锌、氧化钛和/或氧化锰混合的氧化钡。
9.权利要求1的玻璃纤维组合物,其特征在于组合物含有与氧化锌、氧化钛、氧化钡和/或氧化锰混合的氧化锆。
10.权利要求1的玻璃纤维组合物,其特征在于组合物含有<2%(重量)的氧化镁。