SK280485B6 - Zmes na sklené vlákna - Google Patents
Zmes na sklené vlákna Download PDFInfo
- Publication number
- SK280485B6 SK280485B6 SK120-96A SK12096A SK280485B6 SK 280485 B6 SK280485 B6 SK 280485B6 SK 12096 A SK12096 A SK 12096A SK 280485 B6 SK280485 B6 SK 280485B6
- Authority
- SK
- Slovakia
- Prior art keywords
- weight
- glass
- oxide
- glass fiber
- fiber composition
- Prior art date
Description
Oblasť techniky
Vynález sa týka zloženia skleného vlákna, ktoré je biologicky odbúrateľné.
Doterajší stav techniky
Doteraz sú opísané zloženia niektorých sklených vlákien, o ktorých sa tvrdí, že sú biologicky odbúrateľné.
Biologická odbúrateľnosť zmesí na sklené vlákna má veľký význam, nakoľko rôzne výskumy uvádzajú, že niektoré sklené vlákna s veľmi malými priemermi v rozsahu menej ako 3 mikrometre môžu byť karcinogénne, zatiaľ čo biologicky odbúrateľné minerálne vlákna rovnakých rozmerov nemajú žiadnu karcinogenitu.
Ale zásadný význam má nielen biologická odbúrateľnosť, ale dôležité sú aj mechanické a tepelné vlastnosti sklených vlákien alebo výrobkov z nich, odolnosť sklených vlákien a spracovateľnosť zmesi na sklené vlákna. Napríklad sa sklené vlákna vo veľkom rozsahu používajú na izolačné účely. Pri tomto využití je nevyhnutná dostatočná stálosť proti vlhkosti.
Zloženie skleného vlákna musi tiež umožňovať výrobu vlákien s malými priemermi známymi spôsobmi, napríklad centrifugačnou technikou, zvlášť vnútornou centrifugačnou technikou (táto technika je opísaná napríklad v US-PS 4 203 745).
V EP spise č.0588 251 Al sa opisujú sklené vlákna, ktoré pozostávajú z anorganických vlákien obsahujúcich oxid kremičitý, oxid vápenatý a alkalický oxid s voľnou hydratačnou energiou viac ako - 5.00kcal/mol a cntalpiou tvarovania menej ako -210.0 kcal/mol., rýchlosť rozpúšťania v umelej extra bunkovej kvapaline je väčšia ako 750 ( počítané ako nanogramy vlákna/ na cm2 povrchu vlákna/za hodinu ), pričom stredný priemer vlákna nie je väčší ako 4,5 mikrometrov. Taktiež sa opisuje spôsob prípravy vlákien.
Podstata vynálezu
Vynález sa týka problému nového zloženia skleného vlákna, ktoré je charakterizované biologickou odbúrateľnosťou, má dobrú stabilitu alebo odolnosť proti vlhkosti a je ľahko vyrobiteľné.
Vynález je založený na zistení, že uvedený problém je riešiteľný zložením skleného vlákna, ktoré zahrnuje značné množstvá alkalických oxidov a oxidu boritého a obsahuje oxid titaničitý, oxid zirkoničitý, oxid zinočnatý, oxid manganatý, oxid bárnatý alebo zmesi dvoch alebo viacerých z týchto oxidov.
Ukázalo sa, že uvedené zloženie skleného vlákna spĺňa požiadavku na kombináciu nevyhnutných vlastností, najmä biologickej odbúrateľnosti, odolnosti proti vlhkosti a dobrej spracovateľnosti.
Predmetom tohto vynálezu je zloženie skleného vlákna, ktoré je biologicky odbúrateľné, a je charakterizované nasledujúcimi zložkami v hmotnostných percentách:
SiO2 | 50 až 60, |
A12O3 | menej ako 2, |
CaO + MgO | 10 až 16, |
Na2O + K2O | 14 až 19, |
B2O3 | 7 až 16, |
TiO2 | až do 4, |
ZrO, | až do 5, |
ZnO aždo 5,
MnO aždo 4,
BaO aždo 5
TiO2, ZrO2, ZnO, MnO, BaO 1 až 6,
Fe2O3, SrO aždo 2,
F. Li2O aždo 2,
PC3 aždo 4.
Zmesi na sklené vlákna podľa tohto vynálezu sú spracovateľné centrifugačnou technikou. Získané vlákna majú dobrú odolnosť proti vlhkosti. Zmesi na sklené vlákna dosť prekvapivo majú biologickú odbúrateľnosť. Stredný priemer vlákien je výhodne 10 mikrometrov alebo menej, výhodne medzi 2,5 až 5 mikrometrami.
Vo výhodnom uskutočnení vynálezu zmes na sklené vlákna obsahuje 1 až 4 % hmotnostné oxidu titaničitého.
V ďalšom výhodnom uskutočnení vynálezu zmes na sklené vlákna obsahuje 1 až 4 % hmotnostné oxidu manganatého.
V ďalšom výhodnom uskutočnení vynálezu zmes na sklené vlákna obsahuje 1 až 4 % hmotnostné oxidu zinočnatého.
V ďalšom výhodnom uskutočnení vynálezu zmes na sklené vlákna obsahuje 0,5 až 5 % hmotnostných, výhodne 0,5 až 3 % hmotnostné, oxidu zirkoničitého.
V ďalšom výhodnom uskutočnení vynálezu zmes na sklené vlákna obsahuje 0,5 až 4 % hmotnostné oxidu bárnatého.
Zvlášť je výhodné použitie zmesí oxidov oxidu zirkoniéitého, oxidu zinočnatého, oxidu titaničitého, oxidu bárnatého a oxidu manganatého, zvlášť zmesí dvoch alebo troch z týchto oxidov.
Výhodné uskutočnenia sú oxid bárnatý v množstve 1 až 4 % hmotnostné zmiešané s oxidom titaničitým alebo oxidom zinočnatým.
V ďalších výhodných uskutočneniach je oxid zinočnatý zmiešaný s oxidom titaničitým a voliteľne dodatočne s oxidom zirkoničitým, kde každá zložka môže byť prítomná v množstvách od 1 do 3 % hmotnostných.
Ďalšie výhodné uskutočnenia vynálezu sú zmesi oxidu zirkoničitého s oxidom zinočnatým, oxidom titaničitým, oxidom bámatým alebo oxidom manganatým, zložky sú prítomné v množstvách 0,5 až 4 % hmotnostné, zvlášť 0,5 až 1,5 % hmotnostného.
Pri zmesiach obsahujúcich oxid zirkoničitý a/alebo oxid bárnatý je výhodné, ak zmes tiež obsahuje 0,5 až 2 % hmotnostné fluóru a/alebo oxidu lítneho.
Oxid hlinitý môže byť prítomný v množstve najmenej 0,1 % hmotnostného a zvlášť najmenej 0,5 % hmotnostného.
Oxid fosforečný zvyšuje biologickú odbúrateľnosť. Zmesi výhodne obsahujú 0,1 až 2 % hmotnostné P2O3.
Podľa ďalšieho výhodného uskutočnenia zmes obsahuje menej ako 2 % hmotnostné oxidu horečnatého.
Odolnosť proti vlhkosti sklených vlákien podľa tohto vynálezu sa určovala známymi štandardnými metódami, ako je napríklad DGG metóda. V DGG metóde sa 10 g jemne rozomletého skla s veľkosťou zŕn medzi asi 360 a 400 mikrometrov udržuje pri teplote varu počas piatich hodín v 100 ml vody. Po rýchlom ochladení materiálu sa roztok prefiltruje a určitý objem filtrátu sa odparí dosucha. Hmotnosť takto získaného suchého materiálu dovoľuje vypočítať množstvo rozpusteného skleného materiálu vo vode. Množstvo sa uvádza v miligramoch na gram testovaného skla.
Biologická odbúrateľnosť sklených zmesí podľa tohto vynálezu sa testovala zavedením 1 g skleného prášku, ako je písaný pre DGG metódu, do fyziologického roztoku s uvedeným zložením a pH hodnotou 7,4:
Claims (1)
- PATENTOVÉ NÁROKYNaCl 6,78,NH4C1 0,535,NaHCOj 2,268,NaH2PO4.H2O 0,166, (Na3citran).2H2O 0,059,Glycin 0,450,H2SO4 0,049,CaCl2 0,022.1. Zmes na sklené vlákna, ktoré sú biologicky odbúrateľné, vyznačujúca sa tým, že má nasledujúce zložky v hmotnostných percentách:Dynamické podmienky testu sa vyberali tak, ako je opísané v Scholze a Conradt. Rýchlosť toku bola 300 ml/deň. Test trval 14 dní. Výsledky sú uvedené ako percento SiO2 v roztoku x 100 po 14 dňoch.Vynález bude ilustrovaný podrobnejšie na nasledujúcich príkladoch.