CN112851317A - 一种辊棒保护材料及其制备方法 - Google Patents
一种辊棒保护材料及其制备方法 Download PDFInfo
- Publication number
- CN112851317A CN112851317A CN202110088228.0A CN202110088228A CN112851317A CN 112851317 A CN112851317 A CN 112851317A CN 202110088228 A CN202110088228 A CN 202110088228A CN 112851317 A CN112851317 A CN 112851317A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide
- protection material
- roller
- alumina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种优化陶瓷岩板的辊棒保护材料及其制备方法，该辊棒保护材料由以下重量份数的原料制成：α‑氧化铝67‑77份、改性二氧化硅15‑20份、二氧化钙1‑7份、氧化镁0.3‑0.7份、氧化钠0.3‑0.7份、氧化钾0.3‑0.7份、胶辊印油83.9‑106.1份，本发明制得的辊棒保护材料可适应高温快烧，高温化学反应形成莫来石质耐火材料，排斥陶瓷砖坯高温熔融时的玻化液相，同时覆盖遮住了陶瓷坯体底部的玻化液相，有效保护岩板坯底，拓宽烧成范围，让陶瓷砖坯在辊棒上运行更加良好，保护辊棒免于结壳和棒钉，在烧制过程引起岩板平整度相关的问题，该保护层可显著降低辊棒得到维护的更换成本。
Description
技术领域
本发明涉及一种辊棒保护材料，特别是一种辊棒保护材料及其制备方法。
背景技术
辊道窑陶瓷砖的烧制成型过程中，要经历1000-1280℃的高温，陶瓷砖在高温区会软化，较易产生粘辊棒等问题，直接影响辊棒的使用寿命，所以在陶瓷砖坯底部布上辊棒保护材料，可以很好的将辊棒与陶瓷砖隔开，减少粘棒的产生，现有技术中大多采用单一的氧化物作为底浆，如氧化镁或氧化铝，使用铝矾土作砖底浆的企业较少，因为当高铝矾土粉体较细时，其耐火度偏低，影响辊棒的使用寿命；当高铝矾土颗粒较粗时，上浆性能差，不能起到隔离砖坯与辊棒的作用。
发明内容
为了克服现有技术的不足，本发明提供一种辊棒保护材料及其制备方法。
本发明解决其技术问题所采用的技术方案是：
一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝67-77份、改性二氧化硅15-20份、二氧化钙1-7份、氧化镁0.3-0.7份、氧化钠0.3-0.7份、氧化钾0.3-0.7份、胶辊印油83.9-106.1份。
优选地，所述α-氧化铝67份、改性二氧化硅15份、二氧化钙1份、氧化镁0.3份、氧化钠0.3份、氧化钾0.3份、胶辊印油83.9份。
优选地，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝77份、改性二氧化硅20份、二氧化钙7份、氧化镁0.7份、氧化钠0.7份、氧化钾0.7份、胶辊印油106.1份。
优选地，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝72份、改性二氧化硅17份、二氧化钙4份、氧化镁0.5份、氧化钠0.5份、氧化钾0.5份、胶辊印油94.5份。
优选地，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝75份、改性二氧化硅18份、二氧化钙6份、氧化镁0.6份、氧化钠0.4份、氧化钾0.5份、胶辊印油100.5份。
优选地，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝77份、改性二氧化硅20份、二氧化钙6份、氧化镁0.3份、氧化钠0.3份、氧化钾0.4份、胶辊印油104份。
优选地，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝68份、改性二氧化硅16份、二氧化钙7份、氧化镁0.7份、氧化钠0.3份、氧化钾0.5份、胶辊印油92.5份。
一种制备如上述辊棒保护材料的方法，其步骤如下：
(1)、制备粉料：将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾以转速25-35转/分搅拌25-35分钟，得到粉料；
(2)、制备辊棒保护材料：将步骤(1)制得的粉料与胶辊印油以1:1的比例研磨8-10小时，得到辊棒保护材料；
(3)、砖坯应用：将步骤(2)制得的辊棒保护材料用辊筒印刷底浆机应用在砖坯底部，令砖坯底部上浆均匀、饱满。
优选地，步骤(1)中制得的粉料颗粒度D97≤149μm。
优选地，步骤(2)中制得的辊棒保护材料颗粒度D99≤45μm，比重为1.25-1.45g/cm3。
本发明的有益效果是：本发明制得的辊棒保护材料可适应高温快烧，高温化学反应形成莫来石质耐火材料，排斥陶瓷砖坯高温熔融时的玻化液相，同时覆盖遮住了陶瓷坯体底部的玻化液相，有效保护岩板坯底，拓宽烧成范围，让陶瓷砖坯在辊棒上运行更加良好，保护辊棒免于结壳和棒钉，在烧制过程引起岩板平整度相关的问题，该保护层可显著降低辊棒得到维护的更换成本。
具体实施方式
以下通过具体实施例进一步介绍本发明的实施及所具有的有益效果，不能构成对本发明实施范围的限定。
一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：α-氧化铝67-77份、改性二氧化硅15-20份、二氧化钙1-7份、氧化镁0.3-0.7份、氧化钠0.3-0.7份、氧化钾0.3-0.7份、胶辊印油83.9-106.1份。
所述α-氧化铝、改性二氧化硅和过氧化钙在窑炉1200℃煅烧时，辊棒表面高温化学反应形成莫来石质耐火材料，排斥陶瓷砖坯高温熔融时的玻化液相，同时覆盖遮住了陶瓷坯体底部的玻化液相，尤其瓷砖在窑炉高温煅烧时，让陶瓷砖坯在辊棒上运行更加良好，保护辊棒免于结壳和棒钉，在烧制过程引起岩板平整度相关的问题，该保护层可显著降低辊棒得到维护的更换成本，同时与岩板坯体的无机材料高温化学反应，相对提高岩板内质的韧性。
一种制备如上述辊棒保护材料的方法，其步骤如下：
(1)、制备粉料：将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾以转速25-35转/分搅拌25-35分钟，得到粉料，优选地，该搅拌步骤使用卧式搅拌机进行搅拌；
(2)、制备辊棒保护材料：将步骤(1)制得的粉料与胶辊印油以1:1的比例研磨8-10小时，得到辊棒保护材料，优选地，该研磨步骤使用球磨机进行研磨；
(3)、砖坯应用：将步骤(2)制得的辊棒保护材料用辊筒印刷底浆机应用在砖坯底部，令砖坯底部上浆均匀、饱满。
优选地，步骤(1)中制得的粉料颗粒度D97≤149μm。
优选地，步骤(2)中制得的辊棒保护材料颗粒度D99≤45μm，比重为1.25-1.45g/cm3。
本发明中，关于温度和压力没有特别强调的部分，均为常温常压。
对于上述配方的一种辊棒保护材料，发明人设计试验了多个实施例并按照上述方法制作：
实施例1：一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：所述α-氧化铝67份、改性二氧化硅15份、二氧化钙1份、氧化镁0.3份、氧化钠0.3份、氧化钾0.3份、胶辊印油83.9份。
所述步骤(1)中将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾加入卧式搅拌机，以转速30转/分搅拌30分钟。
实施例2：一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：该辊棒保护新型材料由以下重量份数的原料制成：α-氧化铝77份、改性二氧化硅20份、二氧化钙7份、氧化镁0.7份、氧化钠0.7份、氧化钾0.7份、胶辊印油106.1份。
所述步骤(1)中将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾加入卧式搅拌机，以转速25转/分搅拌25分钟。
实施例3：一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：该辊棒保护新型材料由以下重量份数的原料制成：α-氧化铝72份、改性二氧化硅17份、二氧化钙4份、氧化镁0.5份、氧化钠0.5份、氧化钾0.5份、胶辊印油94.5份。
所述步骤(1)中将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾加入卧式搅拌机，以转速35转/分搅拌35分钟。
实施例4：一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：该辊棒保护新型材料由以下重量份数的原料制成：α-氧化铝75份、改性二氧化硅18份、二氧化钙6份、氧化镁0.6份、氧化钠0.4份、氧化钾0.5份、胶辊印油100.5份。
所述步骤(1)中将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾加入卧式搅拌机，以转速26转/分搅拌33分钟。
实施例5：一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：该辊棒保护材料由以下重量份数的原料制成：α-氧化铝77份、改性二氧化硅20份、二氧化钙6份、氧化镁0.3份、氧化钠0.3份、氧化钾0.4份、胶辊印油104份。
所述步骤(1)中将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾加入卧式搅拌机，以转速35转/分搅拌25分钟。
实施例6：一种辊棒保护材料，该辊棒保护材料由以下重量份数的原料制成：该辊棒保护材料由以下重量份数的原料制成：α-氧化铝68份、改性二氧化硅16份、二氧化钙7份、氧化镁0.7份、氧化钠0.3份、氧化钾0.5份、胶辊印油92.5份。
所述步骤(1)中将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾加入卧式搅拌机，以转速25转/分搅拌35分钟。
本申请中的所有范围，包括原料的重量份数范围及生产参数范围等，均包含两个终值。
以上的实施方式不能限定本发明创造的保护范围，专业技术领域的人员在不脱离本发明创造整体构思的情况下，所做的均等修饰与变化，均仍属于本发明创造涵盖的范围之内。
Claims (10)
1.一种辊棒保护材料，其特征在于该辊棒保护材料由以下重量份数的原料制成：α-氧化铝67-77份、改性二氧化硅15-20份、二氧化钙1-7份、氧化镁0.3-0.7份、氧化钠0.3-0.7份、氧化钾0.3-0.7份、胶辊印油83.9-106.1份。
2.根据权利要求1所述的辊棒保护材料，其特征在于所述α-氧化铝67份、改性二氧化硅15份、二氧化钙1份、氧化镁0.3份、氧化钠0.3份、氧化钾0.3份、胶辊印油83.9份。
3.根据权利要求1所述的辊棒保护材料，其特征在于该辊棒保护新型材料由以下重量份数的原料制成：α-氧化铝77份、改性二氧化硅20份、二氧化钙7份、氧化镁0.7份、氧化钠0.7份、氧化钾0.7份、胶辊印油106.1份。
4.根据权利要求1所述的辊棒保护材料，其特征在于该辊棒保护新型材料由以下重量份数的原料制成：α-氧化铝72份、改性二氧化硅17份、二氧化钙4份、氧化镁0.5份、氧化钠0.5份、氧化钾0.5份、胶辊印油94.5份。
5.根据权利要求1所述的辊棒保护材料，其特征在于该辊棒保护新型材料由以下重量份数的原料制成：α-氧化铝75份、改性二氧化硅18份、二氧化钙6份、氧化镁0.6份、氧化钠0.4份、氧化钾0.5份、胶辊印油100.5份。
6.根据权利要求1所述的辊棒保护材料，其特征在于该辊棒保护材料由以下重量份数的原料制成：α-氧化铝77份、改性二氧化硅20份、二氧化钙6份、氧化镁0.3份、氧化钠0.3份、氧化钾0.4份、胶辊印油104份。
7.根据权利要求1所述的辊棒保护材料，其特征在于该辊棒保护材料由以下重量份数的原料制成：α-氧化铝68份、改性二氧化硅16份、二氧化钙7份、氧化镁0.7份、氧化钠0.3份、氧化钾0.5份、胶辊印油92.5份。
8.一种制备如权利要求1至7任一权利要求所述辊棒保护材料的方法，其特征在于其步骤如下：
(1)、制备粉料：将上述重量份数的α氧化铝、改性二氧化硅、二氧化钙、氧化镁、氧化钠、氧化钾以转速25-35转/分搅拌25-30分钟，得到粉料；
(2)、制备辊棒保护材料：将步骤(1)制得的粉料与胶辊印油以1:1的比例研磨8-10小时，得到辊棒保护材料；
(3)、砖坯应用：将步骤(2)制得的辊棒保护材料用辊筒印刷底浆机应用在砖坯底部，令砖坯底部上浆均匀、饱满。
9.根据权利要求8所述的辊棒保护材料的制备方法，其特征在于步骤(1)中制得的粉料颗粒度D97≤149μm。
10.根据权利要求8所述的辊棒保护材料的制备方法，其特征在于步骤(2)中制得的辊棒保护材料颗粒度D99≤45μm，比重为1.25-1.45g/cm3。