CN112387248A - 一种天然可释放负氧离子的萜烯类纳米复合材料及制备方法 - Google Patents
一种天然可释放负氧离子的萜烯类纳米复合材料及制备方法 Download PDFInfo
- Publication number
- CN112387248A CN112387248A CN202011120491.5A CN202011120491A CN112387248A CN 112387248 A CN112387248 A CN 112387248A CN 202011120491 A CN202011120491 A CN 202011120491A CN 112387248 A CN112387248 A CN 112387248A
- Authority
- CN
- China
- Prior art keywords
- parts
- terpene
- negative oxygen
- diatomite
- oxygen ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及萜烯类纳米复合材料技术领域，公开了一种天然可释放负氧离子的萜烯类纳米复合材料，彩叶草30‑60份、吊竹梅20‑40份、吊兰35‑70份、泡叶冷水花20‑50份、燕子掌10‑40份、芦荟15‑30份、负氧离子原液10‑20份和硅藻土100‑200份，本发明通过采用彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌和芦荟，利用释放负氧离子浓度较高的彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌和芦荟制成萜烯类纳米复合材料，比起传统制备材料，能够释放出大量负氧离子，效果更为优秀，本发明通过采用硅藻土，可以利用硅藻土作为萜烯类纳米复合材料的基质，由于硅藻土本身存在很多孔洞，所以无需采用造孔剂。
Description
技术领域
本发明涉及萜烯类纳米复合材料技术领域，具体为天然可释放负氧离子的萜烯类纳米复合材料及制备方法。
背景技术
随着国内外对室内空气质量标准的提高以及人们环保意识的增强，生态环保的多功能材料受到越来越多的关注。现有室内用人造装饰物会释放甲醛、氨、甲苯等可挥发有害物质，导致室内空气质量下降，不利于人们起居生活健康，而且，恶劣的室内环境为有害粉尘及细菌病毒提供了滋生环境，大大影响了人体健康。
专利号CN201610512774.1，公开了一种天然可释放负氧离子的萜烯类纳米复合材料及制备方法。该天然可释放负氧离子的萜烯类纳米复合材料包括：香樟1-40份、松花粉1-90份、蜂蜡1-60份、钩藤1-70份、荷叶1-30份、松针1-70份、艾草1-40份、基质1-200份，其制备方法：(1)称取上述香樟、松花粉、蜂蜡、钩藤、荷叶、松针和艾草，混合研磨，加去离子水，经蒸馏提取、分离得萜烯类物质；(2)称取上述基质，研磨活化；(3)将步骤(1)萜烯类物质加入到步骤(2)活化基质中，混合研磨后即得。该天然可释放负氧离子的萜烯类纳米复合材料组方科学、天然健康、能充分释放负氧离子、促进人体新陈代谢、提高免疫力并具抑菌、除菌、除臭功能。
但是，现有的天然可释放负氧离子的萜烯类纳米复合材料，在制备的过程中，采用香樟、松花粉、蜂蜡、钩藤、荷叶、松针和艾草混合研磨，但是这些材料都无法释放出大量的负氧离子，导致负氧离子的释放量不是很高，而且采用凹凸棒土作为基质，还需要利用额外的造孔剂，使凹凸棒土内部形成孔洞，不仅如此，凹凸棒土本身也不具备净化的功能。
发明内容
本发明的目的在于提供天然可释放负氧离子的萜烯类纳米复合材料及制备方法及方法，解决了背景技术中所提出的问题。
为实现上述目的，本发明提供如下技术方案：一种天然可释放负氧离子的萜烯类纳米复合材料，彩叶草30-60份、吊竹梅20-40份、吊兰35-70份、泡叶冷水花20-50份、燕子掌10-40份、芦荟15-30份、负氧离子原液10-20份和硅藻土100-200份。
作为本发明的一种优选实施方式，彩叶草30份、吊竹梅20份、吊兰35份、泡叶冷水花20份、燕子掌10份、芦荟15份、负氧离子原液10份和硅藻土100份。
作为本发明的一种优选实施方式，彩叶草45份、吊竹梅30份、吊兰50份、泡叶冷水花35份、燕子掌25份、芦荟20份、负氧离子原液15份和硅藻土160份。
作为本发明的一种优选实施方式，彩叶草60份、吊竹梅40份、吊兰70份、泡叶冷水花50份、燕子掌40份、芦荟30份、负氧离子原液20份和硅藻土200份。
一种天然可释放负氧离子的萜烯类纳米复合材料，利用一种天然可释放负氧离子的萜烯类纳米复合材料制备方法，所述一种天然可释放负氧离子的萜烯类纳米复合材料制备方法的步骤如下：
步骤一：将彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌、芦荟和负氧离子原液利用混合设备进行混合，接着利用研磨设备研磨成纳米形态，经水蒸气蒸馏提取，冷却后经油水分离得萜烯类物质混合溶液，将所得萜烯类物质混合溶液在120°条件下真空烘干2h，得萜烯类物质；
步骤二：接着将硅藻土放入到研磨设备中，研磨50-60h进行活化处理；
步骤三：将步骤一烘干的萜烯类物质加入到步骤二活化的硅藻土中，加入氧化锆球，混合研磨96-100h，经筛分去除氧化锆球，即得天然可释放负氧离子的萜烯类纳米复合材料。
作为本发明的一种优选实施方式，所述步骤一中的混合设备，可为螺旋混合机、双螺旋混合机和锥形混合机当中的一种或几种。
作为本发明的一种优选实施方式，所述步骤一和步骤二中的研磨设备，为纳米级研磨机。
与现有技术相比，本发明的有益效果如下：
1.本发明通过采用彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌和芦荟，利用释放负氧离子浓度较高的彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌和芦荟制成萜烯类纳米复合材料，比起传统制备材料，能够释放出大量负氧离子，效果更为优秀，本发明通过采用硅藻土，可以利用硅藻土作为萜烯类纳米复合材料的基质，由于硅藻土本身存在很多孔洞，所以无需采用造孔剂，而且硅藻泥具备独特的分子筛结构，具有极强的物理吸附性和离子交换功能，可以有效去除空气中的游离甲醛、苯、氨等有害物质及因宠物、吸烟、垃圾所产生的气味，净化室内空气，本发明通过采用负氧离子原液，在制备的过程中，直接添加大量负氧离子原液，使萜烯类纳米复合材料内部存在大量负氧离子，进一步增加了萜烯类纳米复合材料的负氧离子释放量。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述，本发明的其它特征、目的和优点将会变得更明显：
图1为本发明天然可释放负氧离子的萜烯类纳米复合材料及制备方法的流程图。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
在本发明的描述中，需要理解的是，术语“上”、“下”、“前”、“后”、“左”、“右”、“顶”、“底”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制；在本发明的描述中，需要说明的是，除非另有明确的规定和限定，术语“安装”、“相连”、“设置”应做广义理解，例如，可以是固定相连、设置，也可以是可拆卸连接、设置，或一体地连接、设置。对于本领域的普通技术人员而言，可以具体情况理解上述术语在本发明中的具体含义。
请参阅图1，本发明提供一种技术方案：一种天然可释放负氧离子的萜烯类纳米复合材料，彩叶草30-60份、吊竹梅20-40份、吊兰35-70份、泡叶冷水花20-50份、燕子掌10-40份、芦荟15-30份、负氧离子原液10-20份和硅藻土100-200份。
进一步的，彩叶草30份、吊竹梅20份、吊兰35份、泡叶冷水花20份、燕子掌10份、芦荟15份、负氧离子原液10份和硅藻土100份。
进一步的，彩叶草45份、吊竹梅30份、吊兰50份、泡叶冷水花35份、燕子掌25份、芦荟20份、负氧离子原液15份和硅藻土160份。
进一步的，彩叶草60份、吊竹梅40份、吊兰70份、泡叶冷水花50份、燕子掌40份、芦荟30份、负氧离子原液20份和硅藻土200份。
一种天然可释放负氧离子的萜烯类纳米复合材料，利用一种天然可释放负氧离子的萜烯类纳米复合材料制备方法，所述一种天然可释放负氧离子的萜烯类纳米复合材料制备方法的步骤如下：
步骤一：将彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌、芦荟和负氧离子原液利用混合设备进行混合，接着利用研磨设备研磨成纳米形态，经水蒸气蒸馏提取，冷却后经油水分离得萜烯类物质混合溶液，将所得萜烯类物质混合溶液在120°条件下真空烘干2h，得萜烯类物质；
步骤二：接着将硅藻土放入到研磨设备中，研磨50-60h进行活化处理；
步骤三：将步骤一烘干的萜烯类物质加入到步骤二活化的硅藻土中，加入氧化锆球，混合研磨96-100h，经筛分去除氧化锆球，即得天然可释放负氧离子的萜烯类纳米复合材料。
进一步的，所述步骤一中的混合设备，可为螺旋混合机、双螺旋混合机和锥形混合机当中的一种或几种。
进一步的，所述步骤一和步骤二中的研磨设备，为纳米级研磨机。
实施例一
所述的萜烯类纳米复合材料，包括以下原料及其重量分数：彩叶草30份、吊竹梅20份、吊兰35份、泡叶冷水花20份、燕子掌10份、芦荟15份、负氧离子原液10份和硅藻土100份。
制备步骤如下：
a.将上述原料按照重量份数称取；
步骤一：将彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌、芦荟和负氧离子原液利用混合设备进行混合，接着利用研磨设备研磨成纳米形态，经水蒸气蒸馏提取，冷却后经油水分离得萜烯类物质混合溶液，将所得萜烯类物质混合溶液在120°条件下真空烘干2h，得萜烯类物质；
步骤二：接着将硅藻土放入到研磨设备中，研磨50-60h进行活化处理；
步骤三：将步骤一烘干的萜烯类物质加入到步骤二活化的硅藻土中，加入氧化锆球，混合研磨96-100h，经筛分去除氧化锆球，即得天然可释放负氧离子的萜烯类纳米复合材料。
实施例二
所述的萜烯类纳米复合材料，包括以下原料及其重量分数：彩叶草45份、吊竹梅30份、吊兰50份、泡叶冷水花35份、燕子掌25份、芦荟20份、负氧离子原液15份和硅藻土160份。
制备步骤如下：
a.将上述原料按照重量份数称取；
步骤一：将彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌、芦荟和负氧离子原液利用混合设备进行混合，接着利用研磨设备研磨成纳米形态，经水蒸气蒸馏提取，冷却后经油水分离得萜烯类物质混合溶液，将所得萜烯类物质混合溶液在120°条件下真空烘干2h，得萜烯类物质；
步骤二：接着将硅藻土放入到研磨设备中，研磨50-60h进行活化处理；
步骤三：将步骤一烘干的萜烯类物质加入到步骤二活化的硅藻土中，加入氧化锆球，混合研磨96-100h，经筛分去除氧化锆球，即得天然可释放负氧离子的萜烯类纳米复合材料。
实施例三
所述的萜烯类纳米复合材料，包括以下原料及其重量分数：彩叶草60份、吊竹梅40份、吊兰70份、泡叶冷水花50份、燕子掌40份、芦荟30份、负氧离子原液20份和硅藻土200份。
制备步骤如下：
a.将上述原料按照重量份数称取；
步骤一：将彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌、芦荟和负氧离子原液利用混合设备进行混合，接着利用研磨设备研磨成纳米形态，经水蒸气蒸馏提取，冷却后经油水分离得萜烯类物质混合溶液，将所得萜烯类物质混合溶液在120°条件下真空烘干2h，得萜烯类物质；
步骤二：接着将硅藻土放入到研磨设备中，研磨50-60h进行活化处理；
步骤三：将步骤一烘干的萜烯类物质加入到步骤二活化的硅藻土中，加入氧化锆球，混合研磨96-100h，经筛分去除氧化锆球，即得天然可释放负氧离子的萜烯类纳米复合材料。
传统萜烯类纳米复合材料数据参数表1如下：
| 测试项目 | 负氧离子释放量 | 空气过滤效果 |
| 参数指标 | 一般 | 差 |
实施例一萜烯类纳米复合材料数据参数表2如下：
| 测试项目 | 负氧离子释放量 | 空气过滤效果 |
| 参数指标 | 良好 | 一般 |
实施例二萜烯类纳米复合材料数据参数表3如下：
| 测试项目 | 负氧离子释放量 | 空气过滤效果 |
| 参数指标 | 优 | 良好 |
实施例三萜烯类纳米复合材料数据参数表4如下：
| 测试项目 | 负氧离子释放量 | 空气过滤效果 |
| 参数指标 | 极优 | 优 |
综上述，参照表1、表2、表3和表4的数据对比得到，本发明通过采用彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌和芦荟，利用释放负氧离子浓度较高的彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌和芦荟制成萜烯类纳米复合材料，比起传统制备材料，能够释放出大量负氧离子，效果更为优秀，本发明通过采用硅藻土，可以利用硅藻土作为萜烯类纳米复合材料的基质，由于硅藻土本身存在很多孔洞，所以无需采用造孔剂，而且硅藻泥具备独特的分子筛结构，具有极强的物理吸附性和离子交换功能，可以有效去除空气中的游离甲醛、苯、氨等有害物质及因宠物、吸烟、垃圾所产生的气味，净化室内空气，本发明通过采用负氧离子原液，在制备的过程中，直接添加大量负氧离子原液，使萜烯类纳米复合材料内部存在大量负氧离子，进一步增加了萜烯类纳米复合材料的负氧离子释放量。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点，对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
需注意的是本申请当中的制备方法在对比文件中已经公开，所以在本申请当中并没有详细的进行描述。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (7)
1.一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于：彩叶草30-60份、吊竹梅20-40份、吊兰35-70份、泡叶冷水花20-50份、燕子掌10-40份、芦荟15-30份、负氧离子原液10-20份和硅藻土100-200份。
2.根据权利要求1所述的一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于：彩叶草30份、吊竹梅20份、吊兰35份、泡叶冷水花20份、燕子掌10份、芦荟15份、负氧离子原液10份和硅藻土100份。
3.根据权利要求1所述的一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于：彩叶草45份、吊竹梅30份、吊兰50份、泡叶冷水花35份、燕子掌25份、芦荟20份、负氧离子原液15份和硅藻土160份。
4.根据权利要求1所述的一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于：彩叶草60份、吊竹梅40份、吊兰70份、泡叶冷水花50份、燕子掌40份、芦荟30份、负氧离子原液20份和硅藻土200份。
5.一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于，利用权利要求1～4中任一权利要求所述的一种天然可释放负氧离子的萜烯类纳米复合材料制备方法，所述一种天然可释放负氧离子的萜烯类纳米复合材料制备方法的步骤如下：
步骤一：将彩叶草、吊竹梅、吊兰、泡叶冷水花、燕子掌、芦荟和负氧离子原液利用混合设备进行混合，接着利用研磨设备研磨成纳米形态，经水蒸气蒸馏提取，冷却后经油水分离得萜烯类物质混合溶液，将所得萜烯类物质混合溶液在120°条件下真空烘干2h，得萜烯类物质；
步骤二：接着将硅藻土放入到研磨设备中，研磨50-60h进行活化处理；
步骤三：将步骤一烘干的萜烯类物质加入到步骤二活化的硅藻土中，加入氧化锆球，混合研磨96-100h，经筛分去除氧化锆球，即得天然可释放负氧离子的萜烯类纳米复合材料。
6.根据权利要求5所述的一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于：所述步骤一中的混合设备，可为螺旋混合机、双螺旋混合机和锥形混合机当中的一种或几种。
7.根据权利要求5所述的一种天然可释放负氧离子的萜烯类纳米复合材料，其特征在于：所述步骤一和步骤二中的研磨设备，为纳米级研磨机。。