CN112156025B - Silver ion induction biological micro-current membrane cloth and preparation method thereof - Google Patents
Silver ion induction biological micro-current membrane cloth and preparation method thereof Download PDFInfo
- Publication number
- CN112156025B CN112156025B CN202011060115.1A CN202011060115A CN112156025B CN 112156025 B CN112156025 B CN 112156025B CN 202011060115 A CN202011060115 A CN 202011060115A CN 112156025 B CN112156025 B CN 112156025B
- Authority
- CN
- China
- Prior art keywords
- silver ion
- skin
- magnetic
- biological micro
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses silver ion induction biological micro-current membrane cloth and a preparation method thereof, wherein the silver ion induction biological micro-current membrane cloth comprises a base cloth layer, wherein a plurality of linear magnetic strips made of silver ion magnetic slurry are arranged on the base cloth layer; the silver ion magnetic slurry comprises the following components in percentage by mass: 1% -20% of magnetic powder; ag 2+ 1% -10% of the solution; 10% -30% of germanite powder; 40% -65% of an adhesive; 2% -25% of a solubilizer; the balance of water. The silver ion induction biological micro-current membrane cloth can continuously generate micro-current to act on skin, so that the skin is compact and elastic, the formation of melanin in the skin is effectively reduced, and the silver ion induction biological micro-current membrane cloth has good whitening and freckle removing effects without damaging the natural physiological state of cells; simultaneously, the oxygen content of the skin is improved, and the health state of the skin is maintained.
Description
Technical Field
The invention belongs to the field of cosmetic base materials, and particularly relates to silver ion induction biological micro-current membrane cloth and a preparation method thereof.
Background
White, ruddy and beautiful skin has been advocated by most oriental women all the time, the demand of skin care products for whitening, removing freckles, tightening and removing wrinkles occupies a large proportion in the cosmetic market, and people hope to obtain white, smooth, tight and elastic skin by using the skin care products.
Human skin is rich in various collagen fibers, and with the increase of age, the regeneration of the collagen fibers is weaker than aging metabolism, the skin elasticity is reduced, and the phenomena of relaxation and wrinkles occur. The skin care product has two main ways of resisting wrinkles: (1) Wrinkles are smoothed by stretching under physical action, such as heat energy ultrasonic waves, film forming agents and the like, although the effect is quick, the wrinkles are not durable; (2) biochemical action: the skin is smooth and plump by the fact that active ingredients of small molecules directly penetrate through the stratum corneum to reach the inside of the dermis, synthesis of collagen and collagen fibers is improved or promoted, and broken collagen fibers are repaired.
The color of the skin is affected by many factors, and the concentration of melanin in the skin is the most important factor in determining the color of the skin. Melanin production by the skin is a self-protective mechanism for protecting the skin from further UV damage. The formation of melanin is that tyrosine in melanocyte tissue is gradually converted into melanin through intermediates such as dopa, dopaquinone, dopachrome and dihydroxyindole under the action of enzymes such as tyrosinase and the like; melanin moves layer by layer through cell metabolism to reach the skin epidermis layer, deepens the skin color and shows that the skin turns black; the pigment is unevenly distributed on the surface of the skin, and color spots, such as freckles, sunburn, black spots and the like, can be formed. The whitening action mechanism of the whitening and freckle removing product is mainly as follows: (1) inhibition of melanin production: such as the use of a tyrosinase competitive inhibitor to inhibit tyrosinase activity, thereby reducing or preventing melanin production; or using strong reducing agent to convert melanin to colorless precursor substance, and reducing melanin deposition. (2) promoting melanin metabolism: melanin is metabolized along with the renewal of keratinocytes, and aging and shedding of keratinocytes are accelerated by using salicylic acid, tartaric acid, mandelic acid, and the like, thereby accelerating the metabolism of melanin and achieving the whitening effect.
At present, a plurality of beauty and skin care facial masks with whitening, wrinkle-removing and other effects mainly achieve the required effects by soaking nutrient essence liquid by using common mask cloth, but the effects generated by using the facial masks are very little, and the skin health can be influenced by some irritant components added into the essence liquid.
The invention researches a piece of membrane cloth with combined functions and effects, can improve and repair skin by matching with the energy of the skin, recovers the health state of the skin, has a whitening effect, and can better meet the market demand.
Disclosure of Invention
The invention aims to provide a silver ion induction biological micro-current membrane cloth which can continuously generate micro-current to act on skin, so that the skin is compact and elastic, the formation of melanin in the skin is effectively reduced, the skin whitening and freckle removing effects are good, the oxygen content of the skin can be improved, and the skin whitening and healthy state can be maintained.
The invention also aims to provide a preparation method of the silver ion induction biological micro-current membrane cloth.
The invention is realized by the following technical scheme:
a silver ion induction biological micro-current membrane cloth comprises a base cloth layer, wherein a plurality of linear magnetic strips made of silver ion magnetic slurry are arranged on the base cloth layer; the silver ion magnetic slurry comprises the following components in percentage by mass:
1% -20% of magnetic powder;
Ag 2+ 1% -10% of the solution;
10% -30% of germanite powder;
40% -65% of an adhesive;
2% -25% of a solubilizer;
the balance of water.
The linear shape is a curved shape or a linear shape. According to the product requirements, various linear magnetic stripe patterns can be manufactured; the pattern can be plants, animal insects, grid lines or the like; the plant may be a flower; the animal insect may be a butterfly.
Preferably, the Ag is calculated by mass percentage 2+ The solution is 2% -5%; the germanite powder accounts for 15% -20%. Wherein, the Ag is 2+ Ag in solution 2+ The mass concentration of the active carbon is 4000ppm to 6000ppm. The Ag is 2+ The solution can be prepared by high-temperature extraction by electrolysis, is colorless, odorless, and free of impurities, and can be directly contacted with human skin.
32 electrons are arranged around the germanium atomic nucleus, and 4 electrons on the outermost orbit do irregular motion; once the temperature rises (above 32 ℃), an electron on the outermost orbital will leave the orbital by absorbing energy. According to the invention, germanite powder is added into the membrane cloth, and under the action of human body temperature, electrons and germanium ions can be emitted. The germanite powder is 1200 to 2000 meshes.
The magnetic powder is selected from any one of metal magnetic powder, metal oxide magnetic powder or magnetic graphene powder; specifically, the metal magnetic powder can be neodymium iron boron magnetic powder; the metal oxide magnetic powder can be ferroferric oxide magnetic powder.
The adhesive is selected from any one or more of acrylic polymer, silica gel, polyvinyl chloride or polyurethane.
The solubilizer is polyalcohol; the polyalcohol is any one or more of glycerol, propylene glycol, dipropylene glycol or ethylene butanediol.
According to the invention, a soft base fabric layer which is attached to the skin can be selected according to the product requirements, and specifically, the base fabric layer can be any one of non-woven fabric, knitted fabric or woven fabric.
The invention also provides a preparation method of the silver ion induction biological micro-current membrane cloth, which comprises the following steps:
(1) Putting germanite powder into solubilizer to be soaked for 1~3 days;
(2) Mixing with other components and stirring for 30 to 40 minutes; stirring at a rotation speed of 900 to 1200 rpm; obtaining silver ion magnetic slurry;
(3) Extruding the silver ion magnetic slurry on the base cloth layer by adopting a point plastic process to form a linear magnetic strip, and drying at the temperature of 90-110 ℃ for 1~2 minutes to obtain the silver ion induction biological micro-current membrane cloth.
The silver ion induction biological micro-current membrane cloth can be particularly applied to facial masks, eye masks or body pastes.
According to the silver ion induction biological micro-current membrane cloth, the surface of the membrane cloth is provided with the plurality of linear magnetic strips, so that a magnetic field can be generated on the surface of the membrane cloth. Ag in the magnetic strip when used after soaking in water 2+ Can be rapidly dissolved in water to make the medium between the membrane cloth and the skin contain Ag 2+ The electrolyte solution of (4); when the temperature of the membrane cloth reaches 32 ℃ through skin heat conduction of germanite powder in the magnetic strip, electrons on the outermost side rail of the germanium are separated from the rail, and electrons and germanium ions are continuously generated. The silver ionThe electron-inductive biological micro-current membrane cloth can generate micro-current in the using process, acts on the skin through a medium, stimulates 'Maisina antennal corpuscle' in the skin to cause the biological effect of cell self-tightening, thereby playing the effects of tightening the skin and reducing wrinkles, and enabling the skin to be tight and elastic; in addition, it promotes Ag 2+ Can better penetrate into deep layer of skin due to Ag 2+ The skin whitening cream has a high oxidation-reduction potential (1.987V), can oxidize melanin and dopaquinone in skin cells, can prevent tyrosine from forming dopaquinone under the action of tyrosinase, and effectively reduces the formation of melanin, so that the skin whitening cream has the effects of whitening and removing freckles; in addition, after germanium ions enter the skin, the oxygen content of the skin can be improved, the skin whitening effect can be maintained, and the skin health can be recovered due to the fact that germanium has the function of dehydrogenation and oxygen enrichment.
Under the action of human body temperature, the germanium stone powder on the membrane cloth can continuously emit germanium ions and electrons, so that the membrane cloth continuously generates micro-current, and a continuous effect can be achieved on the action of the skin.
Compared with the prior art, the invention has the following beneficial effects:
(1) According to the silver ion induction biological micro-current membrane cloth, the silver ion induction biological micro-current membrane cloth with combined functions and effects is prepared by matching the magnetic powder, the silver ions and the germanite powder, and in the using process, micro-current can be continuously generated to act on the skin, so that the skin is compact and elastic, the effects of whitening and removing freckles are good, meanwhile, the oxygen content of the skin can be improved, the skin whitening effect is maintained, and the skin health is recovered.
(2) The silver ion induction biological micro-current membrane cloth disclosed by the invention can effectively compact and whiten the skin, does not destroy the natural physiological state of cells, recovers the healthy state of the skin and is high in safety.
(3) The silver ion induction biological micro-current membrane cloth can be used after being directly soaked and wetted in water, and is simple and convenient.
Detailed Description
The present invention will be described in detail with reference to specific examples. The following examples will assist those skilled in the art in further understanding the invention, but are not intended to limit the invention in any way. It should be noted that variations and modifications can be made by persons skilled in the art without departing from the concept of the invention. All falling within the scope of the present invention.
The starting materials used in the examples and comparative examples are now described below, but are not limited to these materials, and are commercially available:
magnetic powder: neodymium iron boron magnetic powder;
Ag 2+ solution: 4000ppm;
germanium stone powder: 1250 mesh;
adhesive: an acrylic polymer;
solubilizer: dipropylene glycol;
preparation of examples and comparative examples:
(1) Weighing the components according to the proportion in the table 1, and soaking germanite powder in a solubilizer for 2 days;
(2) Mixing and stirring the germanite powder and the solubilizer soaked in the step (1) with other components for 30 minutes; the stirring speed is 900 revolutions per minute; obtaining silver ion magnetic slurry;
(3) And extruding the silver ion magnetic slurry on the base cloth layer by adopting a point plastic process to form a linear magnetic strip, and drying at the temperature of 100 ℃ for 1 minute to obtain the silver ion induction biological micro-current membrane cloth.
Table 1: the dosage ratio of each component of example 1~3 and comparative example 1~2
The prepared silver ion induction micro-current membrane cloth is prepared into a mask cloth product for efficacy test, and common blank non-woven fabrics are used as a comparison group, and the specific test mode is as follows:
1. test site: beauty salon, shogao shozu, guangzhou (more than 400 active customers);
2. the test population: volunteers of middle and high-grade brand cosmetic populations such as the Jiaolan, the Yashilan indigo, the lancome, the Dior, the senshengtang and the like are used for years; volunteers were randomly drawn from the beauty parlor clients to form 7 test groups of people, which were: example 1 mask cloth group, example 2 mask cloth group, example 3 mask cloth group, comparative example 1 mask cloth group, comparative example 2 mask cloth group, comparative example 3 mask cloth group, blank film cloth group, each group 20 persons.
3. The test method comprises the following steps: the skin change condition of the face is tested by using a microampere amperemeter and an Antera skin tester every 5 minutes when the mask cloth is used.
4. The test instrument and the test method comprise the following steps:
(1) Microampere ammeter: the microcurrent intensity was tested using a microampere ammeter while the mask was applied to the face. Fixing the positive pole of the microampere ammeter at the center of the chin, fixing the negative pole at the center of the forehead, and measuring first data; the second data was then obtained by fixing the positive electrode to the left cheek and the negative electrode to the right cheek. And finally, averaging the data obtained by the two measurements to obtain the micro-current intensity of the face when the mask is used. The stress reaction can be generated when healthy skin is subjected to micro-current of more than 20 muA.
(2) Antera skin tester: a hand-held skin tester Antera manufactured by ireland was used. The handheld probe of the tester is provided with different light wave emissions, and various wrinkles and pores can be better distinguished under white light; under UV light, deep pigmentation and the existence of various nutritional components such as collagen and elastin can be better seen; the blood vessel morphology was relatively visible under red light, and the blood oxygen content of the facial skin was measured using red light (660 nm) and near infrared light (940 nm). The detector can irradiate the skin through light sources with different wavelengths, then obtains various data of the skin through software data analysis, tests the skin at four points of the forehead, two cheeks and the chin of the face, and then obtains an average value by measuring the obtained data through the four points:
skin color: the color analyzer measures skin color using a L a B color space method.
The color range of L is white-black, including various impurity deposits and natural skin pigments; (the lower the distribution rate, the less melanin in the skin).
The color range of A is red-green, and the A is substances such as capillary vessels, proteins and the like in the skin; (capillary and protein cell distribution rate: 20% -33%).
B coverage spans from blue-yellow, deep skin lesions and shadows caused by allergies, such as: erythema, etc.; (distribution rate less than 5% is healthy skin).
Skin elasticity: skin rebound firmness was tested using a hand-held ant instrument to hold the probe at a weight pressure of 360 grams. Faster rebound times indicate better skin elasticity; the greater the recoil force the healthier the skin. Skin elasticity range of healthy skin is: 0.0005 to 0.002N/cm/sec.
Skin blood oxygen concentration: measuring the blood oxygen content of the skin by using red light (660 nm) and near infrared light (940 nm), wherein the normal coefficient is that the blood oxygen content reaches 94 percent, and the skin is healthier as the blood oxygen concentration is higher; the blood oxygen content in the skin can also be used to assess the fair level of the skin, the higher the oxygen content the lower the melanin level and vice versa the higher the melanin level.
5. And (3) analyzing test data: data for each test of each group was recorded and statistically analyzed.
The micro-current intensity: the counted range of the test data for each group of 20 persons;
skin color: the statistical range of the test data of each group of 20 persons;
skin elasticity: the counted range of the test data for each group of 20 persons;
skin blood oxygen concentration: the data were averaged for each group of 20 persons.
/>
/>
As can be seen from the comparison between 1~3 and the blank mask cloth group, the blank mask cloth group uses the common blank non-woven fabric for testing, and the skin color, skin elasticity and skin blood oxygen concentration are not changed obviously in the using process, and the effect of improving the skin is not obvious; the silver ion induction biological micro-current membrane cloth can continuously generate micro-current with effective intensity to act on the skin to restore the skin elasticity, the distribution rate of skin color L is obviously reduced, the skin color A and the skin color B are restored within the range of healthy skin, and the blood oxygen concentration of the skin is increased.
Comparative example 1 to example 1, example 1 compares the magnetic powder, ag 2+ When the facial mask is used with the germanite powder, microcurrent with effective strength can be generated to act on skin after 10min of use, the skin color, the skin elasticity and the skin blood oxygen concentration are obviously improved, and the facial mask cloth of the comparative example 1 does not contain Ag 2+ The micro-current intensity generated after 20min of use is enough to cause the stress response of the skin, the skin color L is not obviously improved, and the whitening effect is poor.
Comparative example 2 comparing with example 1, example 1 has magnetic powder, ag 2+ The germanium ion can be matched with the germanium ion, so that microcurrent with effective intensity can be continuously generated in the using process, and the skin color, the skin elasticity and the skin blood oxygen concentration can be well improved; the mask cloth of comparative example 2 does not contain germanite powder, the intensity of micro-current generated is not enough to cause the skin to generate effective stress reaction, the blood oxygen concentration of the skin cannot be improved, and Ag 2+ The improvement effect on skin color L is poor, and the whitening effect is poor.
Comparative example 3 and example 1, the mask cloth of example 1 contains magnetic powder and Ag 2+ And germanium ions, which can generate micro-current and promote Ag 2+ And the effect of germanium ions on skin, and obviously reducing skinThe rate of distribution of color L, with an increase in skin blood oxygen concentration; comparative example 3 the mask cloth was not added with magnetic powder, and the micro-current generated during the use was weak in strength and Ag 2+ The function of the germanium stone powder cannot be effectively exerted, and the effects of improving skin color L and skin blood oxygen concentration are not obvious.
Claims (7)
1. The silver ion induction biological micro-current membrane cloth is characterized by comprising a base cloth layer, wherein a plurality of linear magnetic strips made of silver ion magnetic slurry are arranged on the base cloth layer;
the silver ion magnetic slurry comprises the following components in percentage by mass:
1% -20% of magnetic powder;
Ag 2+ 1% -10% of the solution;
10% -30% of germanite powder;
40% -65% of an adhesive;
2% -25% of a solubilizer;
the balance of water;
the Ag is 2+ Ag in solution 2+ The mass concentration of the active carbon is 4000ppm to 6000ppm;
the germanite powder is 1200 to 2000 meshes.
2. The silver ion-sensitive biofluidic membrane cloth of claim 1, wherein the Ag is present in a mass percentage 2+ The solution is 2% -5%; the germanite powder accounts for 15% -20%.
3. The silver ion-sensitive biological micro-current membrane cloth according to claim 1, wherein the magnetic powder is selected from any one of metal magnetic powder, metal oxide magnetic powder or magnetic graphene powder; the metal magnetic powder is neodymium iron boron magnetic powder; the metal oxide magnetic powder is ferroferric oxide magnetic powder.
4. The silver ion-sensitive biological micro-current membrane cloth of claim 1, wherein the adhesive is selected from any one or more of acrylic acid polymer, silica gel, polyvinyl chloride or polyurethane.
5. The silver ion-sensitive biological micro-current membrane cloth according to claim 1, wherein the solubilizer is a polyhydric alcohol; the polyalcohol is any one or more of glycerol, propylene glycol, dipropylene glycol or ethylene butanediol.
6. The silver ion induction biological micro-current membrane cloth of claim 1, wherein the base cloth layer is any one of non-woven fabric, knitted fabric or woven fabric.
7. The method for preparing silver ion-induced biological micro-current membrane cloth according to any one of claims 1~6, comprising the steps of:
(1) Putting germanite powder into solubilizer to be soaked for 1~3 days;
(2) Mixing with other components and stirring for 30 to 40 minutes; stirring at a rotation speed of 900 to 1200 rpm; obtaining silver ion magnetic slurry;
(3) Extruding the silver ion magnetic slurry on the base cloth layer by adopting a point plastic process to form a linear magnetic strip, and drying at the temperature of 90-110 ℃ for 1~2 minutes to obtain the silver ion induction biological micro-current membrane cloth.