CN112028649A - 一种节能环保的耐火砖及其制备方法 - Google Patents
一种节能环保的耐火砖及其制备方法 Download PDFInfo
- Publication number
- CN112028649A CN112028649A CN202010888671.1A CN202010888671A CN112028649A CN 112028649 A CN112028649 A CN 112028649A CN 202010888671 A CN202010888671 A CN 202010888671A CN 112028649 A CN112028649 A CN 112028649A
- Authority
- CN
- China
- Prior art keywords
- refractory brick
- base material
- energy
- saving
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种节能环保的耐火砖及其制备方法,涉及耐火砖技术领域,其配料中含有粘土基料、金属基料、保温基料、粘合剂和辅料,其中,按含量比计,粘土基料:金属基料:保温基料:结合剂:辅料=10:1:1.5:7:1。该节能环保的耐火砖及其制备方法,在耐火砖原料中加入有保温基料,硅藻泥具备保温隔热功效,属于保温隔热材料,聚氨酯作为建筑中外墙保温新材料,在运用于耐火砖中,不失为一种创新,硅藻泥和聚氨酯的加入,极大地提高了耐火砖的保温隔热性能,使得耐火砖更具节能环保意义,离心玻璃棉作为一种纤维多孔吸声材料,具有良好的隔音效果,进而可进一步提高耐火砖的环保性能。
Description
技术领域
本发明涉及耐火砖技术领域,具体为一种节能环保的耐火砖及其制备方法。
背景技术
节能材料广义上是指应用于节能环保产业的相关材料,节能环保产业指为节约能源资源、发展循环经济、保护环境提供技术基础和装备保障的产业,主要包括节能产业、资源循环利用产业和环保装备产业,涉及节能环保技术与装备、节能产品和服务等。
耐火砖是用耐火黏土或其他耐火原料烧制成的耐火材料,在建筑窑炉和各种热工设备中应用广泛。
现有的耐火砖取材多追求能提升耐火砖品质和性能的材料,比如碳化硅、酚醛树脂等,虽然耐火砖原料经过改进后,具有了更加优异的性能,但是耐火砖的节能环保性能较弱,很多耐火砖碎料除回收重新制砖以外,便不能用作他用。
发明内容
针对现有技术的不足,本发明提供了一种节能环保的耐火砖及其制备方法,解决了上述背景技术中提出的问题。
为实现以上目的,本发明通过以下技术方案予以实现:一种节能环保的耐火砖,其配料中含有粘土基料、金属基料、保温基料、粘合剂和辅料,其中,按含量比计,粘土基料:金属基料:保温基料:结合剂:辅料=10:1:1.5:7:1。
可选的,所述粘土基料由莫来石、玻璃相、方石英和钛白粉组成,其中莫来石占比30%,玻璃相占比35%,方石英占比20%,钛白粉占比15%。
可选的,所述金属基料由铁和铜铝合金组成,且铁的含量与铜铝合金的含量相等。
可选的,所述铁选用直径为1mm的粒状固体,所述铜铝合金选可过100目筛的粉状固体。
可选的,所述保温基料具体由硅藻泥、聚氨酯和离心玻璃棉组成,其中,按含量比计,硅藻泥:聚氨酯:离心玻璃棉=1:1:1。
可选的,所述粘合剂由水玻璃、水泥、黄糊精、石英砂和胶粉组成,其中,按含量比计,水玻璃:水泥:黄糊精:石英砂:胶粉=2:4:1:1:1。
可选的,所述辅料具体由十水硫酸钠和岩棉组成,其中十水硫酸钠和岩棉之间占比为1:1。
基于上述原料,本发明还公开了一种节能环保耐火砖的制备方法。
可选的,该制备方法具体步骤如下:
①将莫来石、玻璃相和方石英依次加入到粘合剂中,搅拌混合1h;
②加入钛白粉,搅拌1h;
③加入保温基料,搅拌1h;
④加入辅料,搅拌1h;
⑤加入铜铝合金,搅拌均匀;
⑥加入铁颗粒,搅拌均匀;
⑦上模,入炉前持续搅拌,入炉后,高温烧结。
本发明提供了一种节能环保的耐火砖及其制备方法,具备以下有益效果:该节能环保的耐火砖及其制备方法,在耐火砖原料中加入有保温基料,硅藻泥具备保温隔热功效,属于保温隔热材料,聚氨酯作为建筑中外墙保温新材料,在运用于耐火砖中,不失为一种创新,硅藻泥和聚氨酯的加入,极大地提高了耐火砖的保温隔热性能,使得耐火砖更具节能环保意义,离心玻璃棉作为一种纤维多孔吸声材料,具有良好的隔音效果,进而可进一步提高耐火砖的环保性能。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。
实施例1
一种节能环保的耐火砖,其配料中含有粘土基料、金属基料、保温基料、粘合剂和辅料,其中,按含量比计,粘土基料:金属基料:保温基料:结合剂:辅料=10:1:1.5:7:1;
粘土基料由莫来石、玻璃相、方石英和钛白粉组成,其中莫来石占比30%,玻璃相占比35%,方石英占比20%,钛白粉占比15%;
钛白粉粘附力强,不易起化学变化,化学性能稳定,熔点很高,具有良好的耐火性能,在粘土基料中加入少量的钛白粉,使得整个粘土基料更加稳定,不易氧化,同时也使得粘土基料附上白色,烧结成耐火砖后更加美观,同时钛白粉也能够相应提高耐火砖的耐高温性能;
金属基料由铁和铜铝合金组成,且铁的含量与铜铝合金的含量相等;
进一步地,铁选用直径为1mm的粒状固体,铜铝合金选可过100目筛的粉状固体;
铁用于保证耐火砖的强度和硬度,铜铝合金用于保证耐火砖具有良好的吸热能力,从而能够快速撤温;
保温基料具体由硅藻泥、聚氨酯和离心玻璃棉组成,其中,按含量比计,硅藻泥:聚氨酯:离心玻璃棉=1:1:1;
硅藻泥具备保温隔热功效,属于保温隔热材料,聚氨酯作为建筑中外墙保温新材料,在运用于耐火砖中,不失为一种创新,硅藻泥和聚氨酯的加入,极大地提高了耐火砖的保温隔热性能,使得耐火砖更具节能环保意义,离心玻璃棉作为一种纤维多孔吸声材料,具有良好的隔音效果,进而可进一步提高耐火砖的环保性能;
粘合剂由水玻璃、水泥、黄糊精、石英砂和胶粉组成,其中,按含量比计,水玻璃:水泥:黄糊精:石英砂:胶粉=2:4:1:1:1;
粘合剂中,水泥占据主要部分,其次是水玻璃,水玻璃与水泥基本可以满足耐火砖的烧制需求,黄糊精的加入,则有效增大了粘合剂的粘度,石英砂和胶粉的加入,进一步提高了粘合剂的粘度,使得粘合剂具有强粘性,而石英砂的加入,间或可生成少许瓷砖,可以更进一步地提高耐火砖的耐火性能;
辅料具体由十水硫酸钠和岩棉组成,其中十水硫酸钠和岩棉之间占比为1:1;
十水硫酸钠能够较好地吸收热量,岩棉可以吸声,该两种物料的加入,进一步提高了耐火砖的性能。
实施例2
一种节能环保耐火砖的制备方法,该制备方法具体步骤如下:
①将莫来石、玻璃相和方石英依次加入到粘合剂中,搅拌混合1h;
②加入钛白粉,搅拌1h;
③加入保温基料,搅拌1h;
④加入辅料,搅拌1h;
⑤加入铜铝合金,搅拌均匀;
⑥加入铁颗粒,搅拌均匀;
⑦上模,入炉前持续搅拌,入炉后,高温烧结。
综上,该节能环保的耐火砖及其制备方法,在耐火砖原料中加入有保温基料,硅藻泥具备保温隔热功效,属于保温隔热材料,聚氨酯作为建筑中外墙保温新材料,在运用于耐火砖中,不失为一种创新,硅藻泥和聚氨酯的加入,极大地提高了耐火砖的保温隔热性能,使得耐火砖更具节能环保意义,离心玻璃棉作为一种纤维多孔吸声材料,具有良好的隔音效果,进而可进一步提高耐火砖的环保性能。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种节能环保的耐火砖,其特征在于:该耐火砖的配料中含有粘土基料、金属基料、保温基料、粘合剂和辅料,其中,按含量比计,粘土基料:金属基料:保温基料:结合剂:辅料=10:1:1.5:7:1。
2.根据权利要求1所述的一种节能环保的耐火砖,其特征在于:所述粘土基料由莫来石、玻璃相、方石英和钛白粉组成,其中莫来石占比30%,玻璃相占比35%,方石英占比20%,钛白粉占比15%。
3.根据权利要求1所述的一种节能环保的耐火砖,其特征在于:所述金属基料由铁和铜铝合金组成,且铁的含量与铜铝合金的含量相等。
4.根据权利要求3所述的一种节能环保的耐火砖,其特征在于:所述铁选用直径为1mm的粒状固体,所述铜铝合金选可过100目筛的粉状固体。
5.根据权利要求1所述的一种节能环保的耐火砖,其特征在于:所述保温基料具体由硅藻泥、聚氨酯和离心玻璃棉组成,其中,按含量比计,硅藻泥:聚氨酯:离心玻璃棉=1:1:1。
6.根据权利要求1所述的一种节能环保的耐火砖,其特征在于:所述粘合剂由水玻璃、水泥、黄糊精、石英砂和胶粉组成,其中,按含量比计,水玻璃:水泥:黄糊精:石英砂:胶粉=2:4:1:1:1。
7.根据权利要求1所述的一种节能环保的耐火砖,其特征在于:所述辅料具体由十水硫酸钠和岩棉组成,其中十水硫酸钠和岩棉之间占比为1:1。
8.一种节能环保耐火砖的制备方法,其特征在于:该制备方法包含权利要求1-7所述的任意一项节能环保的耐火砖,该制备方法具体步骤如下:
①将莫来石、玻璃相和方石英依次加入到粘合剂中,搅拌混合1h;
②加入钛白粉,搅拌1h;
③加入保温基料,搅拌1h;
④加入辅料,搅拌1h;
⑤加入铜铝合金,搅拌均匀;
⑥加入铁颗粒,搅拌均匀;
⑦上模,入炉前持续搅拌,入炉后,高温烧结。