CN111925180B - 一种粘结石膏 - Google Patents

一种粘结石膏 Download PDF

Info

Publication number
CN111925180B
CN111925180B CN202010715352.0A CN202010715352A CN111925180B CN 111925180 B CN111925180 B CN 111925180B CN 202010715352 A CN202010715352 A CN 202010715352A CN 111925180 B CN111925180 B CN 111925180B
Authority
CN
China
Prior art keywords
gypsum
tea
powder
bonding
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202010715352.0A
Other languages
English (en)
Other versions
CN111925180A (zh
Inventor
刘文君
陈红霞
葛俊巧
张晓菲
冉秀云
杨正波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China National Building Materials Innovation and Technology Research Institute Co Ltd
Original Assignee
China National Building Materials Innovation and Technology Research Institute Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China National Building Materials Innovation and Technology Research Institute Co Ltd filed Critical China National Building Materials Innovation and Technology Research Institute Co Ltd
Priority to CN202010715352.0A priority Critical patent/CN111925180B/zh
Publication of CN111925180A publication Critical patent/CN111925180A/zh
Application granted granted Critical
Publication of CN111925180B publication Critical patent/CN111925180B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种粘结石膏，所述粘结石膏包括：石膏粉、胶粘剂、茶粉、减水剂、纤维素醚和可再分散性乳胶粉。优选地，粘结石膏按重量份计包括：100份石膏粉、0.2‑1.2份胶粘剂、0.1‑0.6份茶粉、0.5‑1份减水剂、0.3‑1.5份纤维素醚和0.5‑3份可再分散性乳胶粉。本发明提供的粘结石膏凝结时间在50min左右，可有效满足施工要求。同时本发明的粘结石膏强度高，韧性好，安全环保，适用范围广。

Description

一种粘结石膏
技术领域
本发明涉及建筑材料技术领域，具体涉及一种高强粘结石膏。
背景技术
石膏作为一种新型的建筑材料，具有优良的防火、调节空气湿度、绿色安全环保等技术特征，在建筑领域得到了广泛的应用。粘结石膏是以半水石膏为主要成分的粘结材料，主要用于粘结纸面石膏板、石膏空心砌块及各种石膏构件。但目前市场上的粘结石膏粘结强度不高，柔韧性较差，脆性较大，并且粘结石膏品种较为单一，不能满足多元化的市场需求。
中国是世界上最大的产茶国之一，由于生产和销售环节的问题，许多低档茶滞销，大部分只能作为废物倾倒，这是资源的浪费。
发明内容
本发明提供了一种粘结石膏，具体提出了一种废茶作为缓凝剂的高强粘结石膏配方，该粘结石膏具备适宜的凝结时间，并具有茶香气味，对废茶进行了回收利用，经济环保，并且该粘结石膏强度高，韧性好。
本发明提供了一种粘结石膏，所述粘结石膏包括：石膏粉、胶粘剂、废茶粉、减水剂、纤维素醚和可再分散性乳胶粉；
优选地，所述粘结石膏由上述组分组成。
在本发明提供的粘结石膏中，所述粘结石膏按重量份计包括：100份石膏粉、0.2-1.2份胶粘剂、0.1-0.6份茶粉、0.5-1份减水剂、0.3-1.5份纤维素醚和0.5-3份可再分散性乳胶粉。
在本发明提供的粘结石膏中，所述胶粘剂为动物胶或植物胶。
在本发明提供的粘结石膏中，优选地，所述动物胶为骨胶或皮胶中的一种或多种；
在本发明提供的粘结石膏中，优选地，所述植物胶为预糊化淀粉、糊精、松香、阿拉伯树胶和天然橡胶中的一种或多种。
在本发明提供的粘结石膏中，所述茶的粒径为30-100μm；
在本发明提供的粘结石膏中，所述茶粉原料可以选用市场上无法销售的茶叶。
在本发明提供的粘结石膏中，所述茶粉为发酵型废茶；
在本发明提供的粘结石膏中，所述发酵型废茶选自铁观音茶、乌龙茶、红茶和黑茶中的一种或多种。
在本发明提供的粘结石膏中，茶叶在发酵过程中产生了一些碳水化合物，碳水化合物存在一定量的羟基，这些亲水性基团(羟基)与水作用后形成一层稳定的水膜，抑制半水石膏的水化，因此茶叶粉除具有茶香气味同时对石膏具有缓凝作用。
在本发明提供的粘结石膏中，所述石膏为脱硫石膏熟料、天然石膏熟料、钛石膏和磷石膏熟料中的一种或多种。可实现脱硫石膏、钛石膏和磷石膏固体废弃物的循环利用。
在本发明提供的粘结石膏中，可选地，所述石膏熟料粒径为20-150μm。
在本发明提供的粘结石膏中，所述减水剂选自聚羧酸系减水剂或萘系减水剂中的一种或多种。
在本发明提供的粘结石膏中，所述纤维素醚选自羟丙基甲基纤维素(HPMC)或羟乙基甲基纤维素(HEMC)中的一种或两种；
可选地，所述纤维素醚的粘度为1500-4000mPa·s。
在本发明提供的粘结石膏中，所述的可再分散性乳胶粉为醋酸乙烯－乙烯共聚物或醋酸乙烯酯均聚物中的一种或两种。
本发明中石膏及天然有机胶粘剂，提高了粘结石膏的粘结强度，同时对于固体废弃物脱硫石膏、钛石膏、磷石膏的循环利用起到了良好的促进作用；熟石膏作为胶凝材料时，其水化凝结速度很快，初终凝时间一般为6-30min，可用于操作的时间往往只有5-10min，不能满足石膏基材料施工要求，故需要加入缓凝剂，本发明中茶粉具有缓凝作用，可延长粘结石膏凝结时间，同时粘结石膏具有了茶香气味。同时实现了废茶的回收利用，具有很好的经济效益和社会效益。
本发明中的纤维素醚及可再分散性乳胶粉的加入，增加了粘结石膏的保水性能，改善施工性能，提高了粘结石膏的强度。
本发明的其它特征和优点将在随后的说明书中阐述，并且，部分地从说明书中变得显而易见，或者通过实施本发明而了解。本发明的其他优点可通过在说明书中所描述的方案来发明实现和获得。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明白，下文对本发明的实施例进行详细说明。需要说明的是，在不冲突的情况下，本发明中的实施例及实施例中的特征可以相互任意组合。
本发明实施例中提供了一种粘结石膏，所述粘结石膏包括：石膏粉、胶粘剂、废茶粉、减水剂、纤维素醚和可再分散性乳胶粉；
优选地，所述粘结石膏由上述组分组成。
在本发明实施例中，所述粘结石膏按重量份计包括：100份石膏粉、0.2-1.2份胶粘剂、0.1-0.6份茶粉、0.5-1份减水剂、0.3-1.5份纤维素醚和0.5-3份可再分散性乳胶粉。
本发明实施例中，所述胶粘剂为动物胶或植物胶。
本发明实施例中，优选地，所述动物胶为骨胶或皮胶中的一种或多种；
本发明实施例中，优选地，所述植物胶为预糊化淀粉、糊精、松香、阿拉伯树胶和天然橡胶中的一种或多种。
本发明实施例中，所述茶的粒径为30-100μm；
本发明实施例中，所述茶粉原料可以选用市场上无法销售的茶叶。
本发明实施例中，所述茶粉为发酵型废茶；
本发明实施例中，所述发酵型废茶选自铁观音茶、乌龙茶、红茶和黑茶中的一种或多种。
本发明实施例中，茶叶在发酵过程中产生了一些碳水化合物，碳水化合物存在一定量的羟基，这些亲水性基团(羟基)与水作用后形成一层稳定的水膜，抑制半水石膏的水化，因此茶叶粉除具有茶香气味同时对石膏具有缓凝作用。
本发明实施例中，所述石膏为脱硫石膏熟料、天然石膏熟料、钛石膏和磷石膏熟料中的一种或多种。可实现脱硫石膏、钛石膏和磷石膏固体废弃物的循环利用。
本发明实施例中，可选地，所述石膏熟料粒径为20-150μm。
本发明实施例中，所述减水剂选自聚羧酸系减水剂或萘系减水剂中的一种或多种。
本发明实施例中，所述纤维素醚选自羟丙基甲基纤维素(HPMC)或羟乙基甲基纤维素(HEMC)中的一种或两种；
可选地，所述纤维素醚的粘度为1500-4000mPa·s。
本发明实施例中，所述的可再分散性乳胶粉为醋酸乙烯－乙烯共聚物或醋酸乙烯酯均聚物中的一种或两种。
实施例1
本实施例中，所述石膏粉为粒径在100μm的脱硫石膏熟料；
所述胶黏剂为骨胶胶黏剂，购自阜城县云海粘合剂贸易有限公司，AA-C牌号；
所述茶粉为粒径为50μm的铁观音废茶茶粉；
所述减水剂为聚羧酸减水剂，购自湖北山树风建材科技有限公司，SSF-4000牌号；
所述纤维素醚为羟丙基甲基纤维素，粘度为3450mPa·s，购自山东欧度纤维素有限公司，100000S牌号；
所述可再分散性乳胶粉为醋酸乙烯-乙烯共聚物，购自德国瓦克公司，5010N牌号。
粘结石膏按重量份计包括：100重量份石膏粉、0.5重量份胶粘剂、0.1重量份废茶粉、0.7重量份减水剂、0.6重量份纤维素醚、1重量份可再分散性乳胶粉。
将上述组分混合搅拌均匀，即得粘结石膏。
实施例2
在本实施例中，所述石膏粉为粒径在130μm的天然石膏熟料；
所述胶黏剂为预糊化淀粉胶黏剂，购自宁津嘉和节能材料有限公司；
所述茶粉为粒径为70μm的乌龙茶废茶；
所述减水剂为聚羧酸减水剂，购自湖北山树风建材科技有限公司，SSF-4000牌号；
所述纤维素醚为羟乙基甲基纤维素纤维素，粘度为3700mPa·s，购自陶氏化学有限公司，Xtra 40-50牌号；
所述可再分散性乳胶粉为醋酸乙烯酯均聚物，购自广州原野实业有限公司公司，DY5010牌号。
粘结石膏按重量份计包括：100重量份石膏粉、0.7重量份胶粘剂、0.4重量份废茶粉、0.8重量份减水剂、1重量份纤维素醚、1.5重量份可再分散性乳胶粉。
将上述组分混合搅拌均匀，即得粘结石膏。
实施例3
在本实施例中，所述石膏粉为粒径在80μm的钛石膏熟料；
所述胶黏剂为阿拉伯树胶胶黏剂，购自河北徐氏蜂蜡有限公司，kibble牌号；
所述废茶粉为粒径为90μm的红茶废茶；
所述减水剂为萘系减水剂，购自沈阳兴正和化工有限公司，SNF-C牌号；
所述纤维素醚为羟丙基甲基纤维素，粘度为2650mPa·s，购自山东欧度纤维素有限公司，75000S牌号；
所述可再分散性乳胶粉为醋酸乙烯-乙烯共聚物，购自德国瓦克公司，5010N牌号。
粘结石膏按重量份计包括：100重量份石膏粉、1.2重量份胶粘剂、0.6重量份废茶粉、0.8重量份减水剂、1.2重量份纤维素醚、2重量份可再分散性乳胶粉。
将上述组分混合搅拌均匀，即得粘结石膏。
对比例1
本对比例与实施例1的不同之处仅在于：粘结石膏中不添加发酵废茶。其余各原料、原料用量和制备过程均与实施例1相同。
将上述组分混合搅拌均匀，即得粘结石膏。
对比例2
本对比例与实施例1的不同之处仅在于：各组分用量不同，各组分用量如下：100重量份石膏粉、0.1重量份胶粘剂、0.05重量份茶粉、0.5重量份减水剂、0.2重量份纤维素醚、0.4重量份可再分散性乳胶粉。
将上述组分混合搅拌均匀，即得粘结石膏。
对比例3
本对比例与实施例1的区别仅在于，使用苹果酸缓凝剂(购自郑州市金水区丰茂化工产品商行，牌号123)替换实施例1中的茶粉。其余各原料、原料用量和制备过程均与实施例1相同。
性能测试
根据建材行业标准JC/T 1025-2007规定的方法测试上述实施例1-3和对比例1-2中的粘结石膏的性能。测试结果如下表1所示。
表1实施效果
Figure BDA0002597960630000071
测试结果表明，本发明提供的粘结石膏凝结时间在50min左右，可有效满足施工要求。同时本发明的粘结石膏强度高，韧性好，安全环保，适用范围广。
虽然本发明所揭露的实施方式如上，但所述的内容仅为便于理解本发明而采用的实施方式，并非用以限定本发明。任何本发明所属领域内的技术人员，在不脱离本发明所揭露的精神和范围的前提下，可以在实施的形式及细节上进行任何的修改与变化，但本发明的专利保护范围，仍须以所附的权利要求书所界定的范围为准。

Claims (9)

1.一种粘结石膏，所述粘结石膏按重量份计由以下组分组成：100份石膏粉、0.2-1.2份胶粘剂、0.1-0.6份茶粉、0.5-1份减水剂、0.3-1.5份纤维素醚和0.5-3份可再分散性乳胶粉；
所述胶粘剂为动物胶或植物胶；
所述动物胶为骨胶或皮胶中的一种或多种；
所述植物胶为预糊化淀粉、糊精、松香、阿拉伯树胶和天然橡胶中的一种或多种。
2.根据权利要求1所述的粘结石膏，其中，所述茶粉的粒径为30-100μm。
3.根据权利要求2所述的粘结石膏，其中，所述茶粉原料为发酵型茶；
所述发酵型茶选自铁观音茶、乌龙茶、红茶和黑茶中的一种或多种。
4.根据权利要求1所述的粘结石膏，其中，所述石膏为脱硫石膏熟料、天然石膏熟料、钛石膏和磷石膏熟料。
5. 根据权利要求4所述的粘结石膏，其中，所述石膏熟料粒径为20-150 μm。
6.根据权利要求1所述的粘结石膏，其中，所述减水剂选自聚羧酸系减水剂或萘系减水剂中的一种或多种。
7.根据权利要求1所述的粘结石膏，其中，所述纤维素醚选自羟丙基甲基纤维素或羟乙基甲基纤维素中的一种或两种。
8. 根据权利要求7所述的粘结石膏，其中，所述纤维素醚的粘度为1500-4000 mPa·s。
9.根据权利要求1所述的粘结石膏，其中，所述的可再分散性乳胶粉为醋酸乙烯－乙烯共聚物或醋酸乙烯酯均聚物中的一种或两种。
CN202010715352.0A 2020-07-23 2020-07-23 一种粘结石膏 Active CN111925180B (zh)