CN1119176C - X光医用跟踪线 - Google Patents
X光医用跟踪线 Download PDFInfo
- Publication number
- CN1119176C CN1119176C CN 99116463 CN99116463A CN1119176C CN 1119176 C CN1119176 C CN 1119176C CN 99116463 CN99116463 CN 99116463 CN 99116463 A CN99116463 A CN 99116463A CN 1119176 C CN1119176 C CN 1119176C
- Authority
- CN
- China
- Prior art keywords
- ray
- polrvinyl chloride
- medical
- agent
- polymer support
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种X光医用跟踪线及其生产方法,具体地是以聚氯乙烯等无毒热稳定性塑料为载体,以硫酸钡为显影剂,加入其它无毒助剂,经共混、共聚、交联改性,然后喷丝、拉伸、牵引、定型等工序加工制成能被X光识别的细线状产品。本发明新产品能承受在强碱条件下的高温高压,耐酸、耐拉伸、不断裂、变型;在X光下显影清晰,无毒性反应,也无溶血反应。将该产品织入医用纱布中,使普通医用纱布具有在X光下显影成像的功能,而且每块纱布仅仅增加2厘钱左右的成本。
Description
本发明涉及一种外科用品中敷料用材料及其生产方法,具体地是一种织入或热压入普通医用纱布中使其具有被X光识别功能的X光医用跟踪线及其生产方法。
脱脂纱布是天然植物纤维,对X光射线具有吸附功能,在医用X光探查下不会显影成像。如果在医用纱布中增加显影功能,一旦因手术中的失误使纱布遗留在病人体内,则只须通过X光的检测就能发现,从而有利于医生正常准确地诊断,避免因病情诊断的复杂化及因此而带来不良后果。
给普通医用纱布中增加显影功能通常有二种方式:一是在纱布的表面上喷上可被X射线识别的标记。如:“新型医用显影纱布及其制做方法“(申请号:91110467、4;申请日:19930519),是将含有乙醇溶液、聚乙烯醇缩丁醛、邻苯二甲基二丁酯和碘番酸的浆液散点在脱脂纱布上,干燥、压实、成为附着牢固的标记符号,即保持了脱脂棉纱布的吸水性能,又能在X线下显示出标记符号,对人体组织无损害。但其标记不明显,在手术中不显眼,只有产生事故后才能通过X光检发现。且工艺复杂,成本高。
二是在医用纱布中加入用不透X射线的原料(通常是硫酸钡)和无毒载体制成的丝或带,将这些丝或带或是织入纱布中,或是将其附着于纱布表面,或是缝在纱布上。缝制方法显然不适合大工业化生产,附着于纱布表面则牢度不能保证。现在国外通常采用的方法是将上述具显影功能的丝或带(一般称为“钡线”、“安全阻力线”等)织入纱布中,使其具有显影功能。目前这类的“钡线”(或称“安全阻力线”等)以聚异丁烯、聚氯乙烯等聚合物为载体,加入40-42%的硫酸钡,以喷丝工艺制成,将其织入普通医用纱布中,其纱布不仅具有在X光下被识别的功能,而且因这类“钡线”为蓝色、绿色或其它有与血液跳色的颜色,在手术中易被与血肉区别,减少纱布残余事故。该产品无毒,且强度高,不会脱落。但这种“钡线”的含钡量低,显影不清晰。而且价格昂贵,不符合我国国情,不利于推广应用。
本发明的目的在于提供一种钡含量高,显影清晰,且生产工艺简单、价格低廉的用于纱入普通医用纱布中使其具有能被X光识别功能的X光医用跟踪线及其生产方法。
本发明的目的是以下述方式实现的:一种X光医用跟踪线,包括聚合物载体和硫酸钡显影剂,所述的跟踪线由聚合物载体、医用硫酸钡显影剂和助剂组成,聚合物载体为聚氯乙烯,助剂为熬合剂、热稳定剂、增塑剂和润滑剂,其重量百分比为:
聚合物载体 10-30
医用硫酸钡(98%) 60-68
熬合剂 0.01-1
热稳定剂 0.08-2
增塑剂 9.9-18
润滑剂 0.01-1
其生产方法是:第一步先将粉状聚合物载体混合均匀,再加入液体助剂混合均匀共聚,最后加入硫酸钡显影剂搅拌均匀;第二步是将第一步混合好的混合物加温至80-250℃后,喷丝、拉伸、牵引,冷却定型后得所需产品。
本发明所用的聚氯乙烯载体还可以为聚氯乙烯和聚丙烯混合物;或聚氯乙烯和聚乙烯混合物;或聚氯乙烯、聚丙烯和聚乙烯混合物,混合物重量百分比分别为:聚氯乙烯∶聚丙烯 55-99∶1-45
聚氯乙烯∶聚乙烯 30-99∶1-70
聚氯乙烯∶聚丙烯∶聚乙烯 60-80∶10-30∶5-15
本发明中所用的助剂中的的熬合剂为亚磷酸酯;热稳定剂为环氧大豆油、硬脂酸钙和硬脂酸锌;增塑剂为磷苯二甲酸二辛脂;或810;或偏苯三酸三辛脂;或对本二甲酸二辛脂;润滑剂为硬脂酸。
热稳定剂所用的环氧大豆油,硬脂酸钙和硬脂酸锌的重量百分比为55-75∶10-25∶10-20。
本发明钡含量高,显影性清晰,无任何毒性反应和溶血性反应,且强度高。其断裂负荷>2.5N;断裂伸长系>250%;拉伸强度>4Mpa;耐热性>120℃。而且生产工艺简单,将其织入或热压入现有的普通医用纱布,每块纱布仅仅只增加2厘左右的成本。
实施例1:将聚氯乙烯10Kg、亚磷酸酯0.1Kg、环氧大豆油0.55Kg、硬脂酸钙0.20Kg、硬脂酸锌0.18Kg、邻苯二甲酸二辛脂8.8Kg、硬脂酸0.1Kg混合搅拌均匀,再加入医用硫酸钡35Kg混合搅拌均匀,加热至120度左右,喷丝、拉伸、牵引、冷却到室温定型,制成直径为0.65-0.70mm的成品。
实施例2:将聚氯乙烯5.5Kg、聚丙烯4.5Kg混合均匀,再加亚磷酸酯0.08Kg、环氧大豆油0.58Kg、硬脂酸钙0.2Kg、硬脂酸锌0.17Kg、810酯10kg、硬脂酸0.1kg混合搅拌均匀,再加入医用硫酸钡34.5kg混合搅拌均匀,加热至150度左右,喷丝、拉伸、牵引,冷却到室温定型,制成直径为0.65-0.70mm的成品。
实施例3:将聚氯乙烯8kg、聚乙烯4kg混合均匀后,加入亚磷酸酯0.09kg、环氧大豆油0.6kg、硬脂酸钙0.2kg、硬脂酸锌0.16kg、偏苯三酸三辛脂9kg、硬脂酸0.14kg混合搅拌均匀,再加入医用硫酸钡33.5kg混合搅拌均匀,加热至200度,喷丝、拉伸、牵引,冷却到室温定型,制成直径为0.65-0.70mm的成品。
实施例4:将聚氯乙烯5kg、聚乙烯1kg、聚丙烯1kg混合均匀后,加入亚磷酸酯0.05kg、环氧大豆油0.65kg、硬脂酸钙0.10kg、硬脂酸锌0.23kg、对苯二甲酸二辛脂9.8kg、硬脂酸0.1kg混合搅拌均匀,再加入医用硫酸钡38kg混合搅拌均匀,加热至200度左右,喷丝、拉伸、牵引,冷却到室温定型,制成直径为0.65-0.70mm的成品。
Claims (7)
1、一种X光医用跟踪线,包括聚合物载体和硫酸钡显影剂,其特征在于它还包括助剂,助剂为熬合剂、热稳定剂、增塑剂和润滑剂,其重量百分比为:
聚合物载体 10-30
医用硫酸钡(98%) 60-68
熬合剂 0.01-1
热稳定剂 0.08-2
增塑剂 9.9-18
润滑剂 0.01-1
其中,聚合物载体含有聚氯乙烯;熬合剂为亚磷酸酯;热稳定剂为环氧大豆油、硬脂酸钙和硬脂酸锌的混合物;润滑剂为硬脂酸。
2、生产如权利要求1所述的X光医用跟踪线的方法,其特征在于第一步先将粉状聚合物载体混合均匀,再加入助剂混合均匀共聚,最后加入硫酸钡显影剂搅拌均匀;第二步是将第一步混合好的混合物加温至80-250℃后,喷丝、拉伸、牵引,冷却定型后得所需产品。
3、如权利要求1所述的X光医用跟踪线,其特征在于所述的聚合物载体也可为聚氯乙烯和聚丙烯混合物,其重量百分比为:
聚氯乙烯 55-99
聚丙烯 1-45
4、如权利要求1所述的X光医用跟踪线,其特征在于所述的聚合物载体也可为聚氯乙烯和聚乙烯的混合物,其重量百分比:
聚氯乙烯 30-99
聚乙烯 1-70
5、如权利要求1所述的X光医用跟踪线,其特征在于所述的聚合物载体也可为聚氯乙烯、聚丙烯和聚乙烯的混合物,其重量百分比为:
聚氯乙烯 60-80
聚丙烯 10-30
聚乙烯 5-15
6、如权利要求1所述的X光医用跟踪线,其特征在于所述的助剂中的增塑剂为邻苯二甲酸二锌脂,或810酯,或偏苯三酸三辛脂,或对苯二甲酸二辛脂。
7、如权利要求1所述的X光医用跟踪线,其特征在于所述的热稳定剂环氧大豆油、硬脂酸钙和硬脂酸锌的重量百分比为:
环氧大豆油 55-75
硬脂酸钙 10-25
硬脂酸锌 10-20