CN111884062A - 一种耐腐蚀开关柜 - Google Patents

一种耐腐蚀开关柜 Download PDF

Info

Publication number
CN111884062A
CN111884062A CN201911351926.4A CN201911351926A CN111884062A CN 111884062 A CN111884062 A CN 111884062A CN 201911351926 A CN201911351926 A CN 201911351926A CN 111884062 A CN111884062 A CN 111884062A
Authority
CN
China
Prior art keywords
layer
parts
corrosion
coating
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911351926.4A
Other languages
English (en)
Inventor
戴月平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HAIWANG ELECTRIC CO Ltd
Original Assignee
NANTONG HAIWANG ELECTRIC CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HAIWANG ELECTRIC CO Ltd filed Critical NANTONG HAIWANG ELECTRIC CO Ltd
Priority to CN201911351926.4A priority Critical patent/CN111884062A/zh
Publication of CN111884062A publication Critical patent/CN111884062A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种耐腐蚀开关柜，包括柜体，和设置在其内的开关柜隔板、各开关柜主体，所述柜体和开关柜隔板均由金属板材制作而成，依次设有耐腐蚀的涂料层、防腐层和面漆层，所述涂料层包括磷酸涂层和镁基复合涂层，所述磷酸涂层包括3‑9份湿法磷酸、5‑10份磷酸二氢钾、1‑5份碱金属氧化物、5‑20份硅酸盐，所述镁基复合涂层由基层、耐热层、面层组成，所述基层含有20‑23％的氧化镁；所述耐热层由甲基三甲氧基硅烷、钛酸烷基酯、硅烷偶联剂、PE酯、硼酸锌、硬脂酸、粉煤灰组成，所述面层含有原料重量占比为12‑18％的氧化镁。本申请在金属板材的基础上涂覆耐腐蚀的涂料层、防腐层和颜料层，三层保护层，提高了开关柜的耐腐蚀能力。

Description

一种耐腐蚀开关柜
技术领域
本发明涉及开关柜技术领域，尤其涉及一种耐腐蚀开关柜。
背景技术
开关柜是输配电中必须的电气设备，为了保护开关柜的外壳，现有技术中一般会在开关柜的柜体表面喷涂料以形成涂料层进而起到防止开关柜的柜体表面的腐蚀，同时起到抗绝缘的作用。大部分的电气设备安装于室外，虽然涂料层中含有大量的有机物，然而在自然条件下涂料层会出现老化的情况，那么涂料层所要起到的作用便会直线下降，进而导致电气设备的外壳会出现腐蚀老化的情况，同时也使得电气设备的安全性难以得到保障。所以研究一种耐腐蚀性能的开关柜很有意义。
发明内容
为克服现有技术中存在的开关柜耐腐蚀性能不佳的问题，本发明提供了一种耐腐蚀开关柜。
一种耐腐蚀开关柜，包括柜体，和设置在其内的开关柜隔板、各开关柜主体，所述柜体和开关柜隔板均由金属板材制作而成，所述金属板材上从内向外依次设有耐腐蚀的涂料层、防腐层和面漆层，所述涂料层包括磷酸涂层和镁基复合涂层，所述磷酸涂层包括如下重量份的各组分：3-9份湿法磷酸、5-10份磷酸二氢钾、1-5份碱金属氧化物、5-20份硅酸盐，所述镁基复合涂层由基层、耐热层、面层组成，所述基层含有原料重量占比为20-23％的氧化镁；所述耐热层由甲基三甲氧基硅烷、钛酸烷基酯、硅烷偶联剂、PE酯、硼酸锌、硬脂酸、粉煤灰组成，所述面层含有原料重量占比为12-18％的氧化镁。
在本发明一优选实施例中，所述基层由以下组分按重量百分比组成：20-23％氧化镁、 3-4％氧化钡、11-13％氧化锌、15-16％铁氧化合物、氧化硼12-14％，余量为二氧化硅。
在本发明一优选实施例中，所述耐热层由以下组分按重量份配比组成：甲基三甲氧基硅烷3-9份、钛酸烷基酯1-5份、硅烷偶联剂25-28份，PE酯12-17份，硼酸锌1-5份、硬脂酸2-7份、粉煤灰10-25份。
在本发明一优选实施例中，所述面层由以下组分按重量百分比组成：12-18％氧化铝、 7-8％氧化镁、15-16％铁氧化合物、氧化硼12-14％，余量为二氧化硅。
在本发明一优选实施例中，所述涂料层的制备方法为，采用电弧喷涂法在柜体和隔板表面形成磷酸基涂层、镁基复合涂层。
在本发明一优选实施例中，所述电弧喷涂的电压为30-32V，电流100-110A，喷涂距离为150±5mm，雾化气体为氩气，所述雾化气体压力0.6-0.75MPa。
在本发明一优选实施例中，所述防腐层的厚度大于等于150μm。
在本发明一优选实施例中，所述防腐层是将柜体和隔板放入电解质溶液中，柜体和隔板作为阴极，在外接电流的作用下，使其表面形成一层镀层，电镀完成后在柜体和隔板表面涂覆一层防腐剂，并将其冷却凝固而成。
在本发明一优选实施例中，所述面漆层的厚度大于等于200微米。在本发明一优选实施例中，所述面漆层为聚四氟乙烯涂料，高温固化形成面漆层。
与现有技术相比，本发明的有益效果是：
(1)本申请在金属板材的基础上涂覆耐腐蚀的涂料层、防腐层和颜料层，三层保护层，提高了开关柜的耐腐蚀能力；
(2)涂料层采用电弧喷涂形成磷酸基涂层、镁基复合涂层，提高了开关柜的耐蚀性，电解质溶液为金属、合金、半导体微粒，电镀完成后镀层可根据不同的溶液微粒形成不同的镀层；
(3)本申请在面漆层中添加聚四氟乙烯，聚四氟乙烯具有良好的化学稳定性、耐腐蚀性、密封性、电绝缘性以及良好的抗老化性，能够有效降低开关柜表面在外界环境中遭到雨水浸泡时被腐蚀的几率，使得开关柜壳体表面的漆能够被使用更长的时间。
具体实施方式
以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅用以解释本发明，并不用于限定本发明。
一种耐腐蚀开关柜，包括柜体，和设置在其内的开关柜隔板、各开关柜主体，所述柜体和开关柜隔板均由金属板材制作而成，所述金属板材上从内向外依次设有耐腐蚀的涂料层、防腐层和面漆层，所述涂料层包括磷酸涂层和镁基复合涂层，所述磷酸涂层包括如下重量份的各组分：3-9份湿法磷酸、5-10份磷酸二氢钾、1-5份碱金属氧化物、5-20份硅酸盐，所述镁基复合涂层由基层、耐热层、面层组成，所述基层含有原料重量占比为20-23％的氧化镁；所述耐热层由甲基三甲氧基硅烷、钛酸烷基酯、硅烷偶联剂、PE酯、硼酸锌、硬脂酸、粉煤灰组成，所述面层含有原料重量占比为12-18％的氧化镁。
在本实施例中，所述基层由以下组分按重量百分比组成：20-23％氧化镁、3-4％氧化钡、11-13％氧化锌、15-16％铁氧化合物、氧化硼12-14％，余量为二氧化硅。
在本实施例中，所述耐热层由以下组分按重量份配比组成：甲基三甲氧基硅烷3-9份、钛酸烷基酯1-5份、硅烷偶联剂25-28份，PE酯12-17份，硼酸锌1-5份、硬脂酸2-7份、粉煤灰10-25份。
在本发明一优选实施例中，所述面层由以下组分按重量百分比组成：12-18％氧化铝、7-8％氧化镁、15-16％铁氧化合物、氧化硼12-14％，余量为二氧化硅。在本实施例中，所述涂料层的制备方法为，采用电弧喷涂法在柜体和隔板表面形成磷酸基涂层、镁基复合涂层。
在本实施例中，所述电弧喷涂的电压为30-32V，电流100-110A，喷涂距离为150±5mm，雾化气体为氩气，所述雾化气体压力0.6-0.75MPa。
在本实施例中，所述防腐层的厚度大于等于150μm。
在本实施例中，所述防腐层是将柜体和隔板放入电解质溶液中，柜体和隔板作为阴极，在外接电流的作用下，使其表面形成一层镀层，电镀完成后在柜体和隔板表面涂覆一层防腐剂，并将其冷却凝固而成。
进一步的，在本实施例中，电解质溶液为金属、合金、半导体微粒，电镀完成后镀层可根据不同的溶液微粒形成不同的镀层。
进一步的，在本实施例中，柜体和隔板需在电解质溶液中放置4-8h完成电镀工作。
在本实施例中，所述面漆层的厚度大于等于200微米。
在本实施例中，所述面漆层为聚四氟乙烯涂料，高温固化形成面漆层。
本申请在金属板材的基础上涂覆耐腐蚀的涂料层、防腐层和颜料层，三层保护层，提高了开关柜的耐腐蚀能力；涂料层采用电弧喷涂形成磷酸基涂层、镁基复合涂层，提高了开关柜的耐蚀性，电解质溶液为金属、合金、半导体微粒，电镀完成后镀层可根据不同的溶液微粒形成不同的镀层；本申请在面漆层中添加聚四氟乙烯，聚四氟乙烯具有良好的化学稳定性、耐腐蚀性、密封性、电绝缘性以及良好的抗老化性，能够有效降低开关柜表面在外界环境中遭到雨水浸泡时被腐蚀的几率，使得开关柜壳体表面的漆能够被使用更长的时间。
上述说明示出并描述了本发明的优选实施例，如前所述，应当理解本发明并非局限于本文所披露的形式，不应看作是对其他实施例的排除，而可用于各种其他组合、修改和环境，并能够在本文所述发明构想范围内，通过上述教导或相关领域的技术或知识进行改动。而本领域人员所进行的改动和变化不脱离本发明的精神和范围，则都应在本发明所附权利要求的保护范围内。

Claims (10)

1.一种耐腐蚀开关柜，其特征在于，包括柜体，和设置在其内的开关柜隔板、各开关柜主体，所述柜体和开关柜隔板均由金属板材制作而成，所述金属板材上从内向外依次设有耐腐蚀的涂料层、防腐层和面漆层，所述涂料层包括磷酸涂层和镁基复合涂层，所述磷酸涂层包括如下重量份的各组分：3-9份湿法磷酸、5-10份磷酸二氢钾、1-5份碱金属氧化物、5-20份硅酸盐，所述镁基复合涂层由基层、耐热层、面层组成，所述基层含有原料重量占比为20-23％的氧化镁；所述耐热层由甲基三甲氧基硅烷、钛酸烷基酯、硅烷偶联剂、PE酯、硼酸锌、硬脂酸、粉煤灰组成，所述面层含有原料重量占比为12-18％的氧化镁。
2.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述基层由以下组分按重量百分比组成：20-23％氧化镁、3-4％氧化钡、11-13％氧化锌、15-16％铁氧化合物、氧化硼12-14％，余量为二氧化硅。
3.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述耐热层由以下组分按重量份配比组成：甲基三甲氧基硅烷3-9份、钛酸烷基酯1-5份、硅烷偶联剂25-28份，PE酯12-17份，硼酸锌1-5份、硬脂酸2-7份、粉煤灰10-25份。
4.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述面层由以下组分按重量百分比组成：12-18％氧化铝、7-8％氧化镁、15-16％铁氧化合物、氧化硼12-14％，余量为二氧化硅。
5.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述涂料层的制备方法为，采用电弧喷涂法在柜体和隔板表面形成磷酸基涂层、镁基复合涂层。
6.根据权利要求5所述的一种耐腐蚀开关柜，其特征在于：所述电弧喷涂的电压为30-32V，电流100-110A，喷涂距离为150±5mm，雾化气体为氩气，所述雾化气体压力0.6-0.75MPa。
7.根据权利要求5所述的一种耐腐蚀开关柜，其特征在于：所述防腐层的厚度大于等于150μm。
8.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述防腐层是将柜体和隔板放入电解质溶液中，柜体和隔板作为阴极，在外接电流的作用下，使其表面形成一层镀层，电镀完成后在柜体和隔板表面涂覆一层防腐剂，并将其冷却凝固而成。
9.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述面漆层的厚度大于等于200微米。
10.根据权利要求1所述的一种耐腐蚀开关柜，其特征在于：所述面漆层为聚四氟乙烯涂料，高温固化形成面漆层。
CN201911351926.4A 2019-12-25 2019-12-25 一种耐腐蚀开关柜 Pending CN111884062A (zh)