CN111875917A - 一种夜间发光的感温变色tpe材料 - Google Patents
一种夜间发光的感温变色tpe材料 Download PDFInfo
- Publication number
- CN111875917A CN111875917A CN202010765492.9A CN202010765492A CN111875917A CN 111875917 A CN111875917 A CN 111875917A CN 202010765492 A CN202010765492 A CN 202010765492A CN 111875917 A CN111875917 A CN 111875917A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature
- color
- tpe material
- tpe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可用于线材中塑胶包覆层的夜间发光的感温变色TPE材料。该TPE材料的原料组分包括：苯乙烯‑丁二烯嵌段共聚物10‑50份；白矿油5‑20份；聚丙烯5‑30份；碳酸钙5‑30份；聚烯烃树脂5‑30份；荧光粉1‑20份；感温变色粉0.5‑5份；其中感温变色粉的原料组分为：三聚氰胺甲醛树脂10‑30份，苯乙烯‑马来酸酐共聚物3‑15份，硬脂酸甲酯30‑50份，硬脂酸乙酯5‑20份，黄色素‑37 1‑8份。本发明通过荧光粉在白天光线照射下吸收光线，待晚上发出荧光，同时TPE中添加的感温变色粉会随着温度变化改变颜色，这样当晚上室外温度下降后，感温色粉改变颜色，从而令荧光的颜色也会发生对应的变化，从而提醒使用者温度变化。
Description
技术领域：
本发明涉及线材材料技术领域，特指一种可用于线材中塑胶包覆层的夜间发光的感温变色TPE材料。
背景技术：
线材(例如导线、电线、电缆等)应用范围十分广泛，其最常规的线材为芯线(导线)外包覆一层塑胶保护层。目前的耳机线等数字产品中所述使用的线材一般采用TPE材料，其相对于传统的橡胶材料具有更好的弹性和耐老化特定，并且加工方便，并且便于挤出成型，利于线材的生产，所以在线材中广泛使用。
一般的TPE线材主要采用苯乙烯类材料制作，例如苯乙烯-丁二烯嵌段共聚物，其性能接近SBR橡胶。是制作电子线材的塑胶层的常规材料。但是，目前的此类产品仅仅从线材本身的耐老化、弹性等特性考虑，缺少其他方面的研究。例如，目前的TPE线材无法实现夜间发光的同时感测温度等特性，本发明人正式基于此提出以下技术方案。
发明内容：
本发明所要解决的技术问题就在于克服现有技术的不足，提供一种可用于线材中塑胶包覆层的夜间发光的感温变色TPE材料。
为了解决上述技术问题，本发明采用了下述技术方案：一种夜间发光的感温变色TPE材料，该TPE材料的原料组分包括：苯乙烯-丁二烯嵌段共聚物10-50份；白矿油5-20份；聚丙烯5-30份；碳酸钙5-30份；聚烯烃树脂5-30份；荧光粉1-20份；感温变色粉0.5-5份；其中感温变色粉的原料组分为：三聚氰胺甲醛树脂10-30份，苯乙烯-马来酸酐共聚物3-15份，硬脂酸甲酯30-50份，硬脂酸乙酯5-20份，黄色素-37 1-8份。
进一步而言，上述技术方案中，所述的荧光粉采用铝酸锶荧光粉。
进一步而言，上述技术方案中，所述的TPE材料的原料还包括抗氧剂，其对应组分为：1-10份。
进一步而言，上述技术方案中，所述的TPE材料用于制作线材芯线的塑胶包覆层。
采用上述技术方案后，本发明与现有技术相比较具有如下有益效果：本发明中在TPE材料中添加了荧光粉和感温变色粉，通过荧光粉在白天光线照射下吸收光线，待晚上发出荧光，实现夜间发光效果。同时，TPE中添加的感温变色粉会随着温度变化改变颜色，这样当晚上室外温度下降后，感温色粉改变颜色，从而令荧光的颜色也会发生对应的变化，从而提醒使用者温度变化。
具体实施方式：
下面结合具体实施例对本发明进一步说明。
本发明为一种夜间发光的感温变色TPE材料，该TPE材料的原料组分包括：
上述原料中，苯乙烯-丁二烯嵌段共聚物是制作苯乙烯类TPE的主要材料，其性能接近SBR橡胶，具有较好的弹性，并且而且透明性也非常好，适合本发明中光线的透射。
所述的聚丙烯材料也是一种热塑性优良的合成树脂，其为无色透明或半透明状，具有耐化学性、耐热性、电绝缘性、高强度机械性能和良好的高耐磨加工性能等。聚丙烯材料与上述的苯乙烯-丁二烯嵌段共聚物材料熔融共混可以形成一种网络相互交织的聚合物，从而进一步提升TPE材料的性能。例如在保持弹性系数不变情况下进一步提升材料的耐寒和耐热性能，适合制作线材。
所述的聚烯烃树脂，这里所述的聚烯烃树脂可以是上述的聚丙烯材料，也可以是聚乙烯等树脂，其作用于上述的聚丙烯材料相同。
所述的白矿油，即矿物油。
所述的碳酸钙作为材料中的填充材料，并且具有一定的阻燃效果。
所述的抗氧剂可采用丙酸正十八碳醇酯抗氧剂。
所述的荧光粉采用铝酸锶荧光粉。例如，可采用氮化物改性的铝酸锶荧光粉，这样可进一步提升荧光粉的余辉时间，令TPE材料在夜间使用时间更长。
所述的感温变色粉的原料组分为：
其起到感温变色的原料为：黄色素-37,其其化学式为：N，N-二甲基-4-[2-[2-(辛氧基)苯基]-6-苯基-4-吡啶基]-苯胺。其会随温度变化显色效果出现不同的变化。
所述的感温变色粉三聚氰胺甲醛树脂的稳定性非常好，其与苯乙烯-马来酸酐共聚物、硬脂酸甲酯、硬脂酸乙酯可以形成一种微胶囊，令感温变色原料稳定，在于TPE其他材料混合时保持稳定，从而实现更好的感温变色效果。
本发明所述的TPE材料用于制作线材芯线的塑胶包覆层。具体制作方法如下：按照以下组分准备原料，
其中，所述的感温变色粉的原料组分为：
制作时，首先制备感温变色粉。首先，将苯乙烯-马来酸酐共聚物中加入硬脂酸甲酯和硬脂酸乙酯，混合均匀。然后加入黄色素-37，在进行混合搅拌均匀。接着，在搅拌状态下逐渐加入三聚氰胺甲醛树脂，最后得到干燥后得到感温变色粉。
然后制作TPE材料，将苯乙烯-丁二烯嵌段共聚物、白矿油、聚丙烯、聚烯烃树脂混合，并搅拌均匀。
接着，向上述混合均匀的原料中加入碳酸钙、荧光粉、感温变色粉、抗氧剂，继续搅拌均匀。
最后，将上述的混合的材料进行造粒，得到本发明所述的一种夜间发光的感温变色TPE材料。将该材料用于线材的生产设备中，挤出成型，制作成各种不同类型的电子产品线材即可。
当然，以上所述仅为本发明的具体实施例而已，并非来限制本发明实施范围，凡依本发明申请专利范围所述构造、特征及原理所做的等效变化或修饰，均应包括于本发明申请专利范围内。
Claims (4)
1.一种夜间发光的感温变色TPE材料，其特征在于，该TPE材料的原料组分包括：
其中感温变色粉的原料组分为：三聚氰胺甲醛树脂10-30份，苯乙烯-马来酸酐共聚物3-15份，硬脂酸甲酯30-50份，硬脂酸乙酯5-20份，黄色素-371-8份。
2.根据权利要求1所述的一种夜间发光的感温变色TPE材料，其特征在于：所述的荧光粉采用铝酸锶荧光粉。
3.根据权利要求1所述的一种夜间发光的感温变色TPE材料，其特征在于：所述的TPE材料的原料还包括抗氧剂，其对应组分为：1-10份。
4.根据权利要求1所述的一种夜间发光的感温变色TPE材料，其特征在于：所述的TPE材料用于制作线材芯线的塑胶包覆层。