CN111825388A - 一种改性环氧沥青混凝土及其加工工艺 - Google Patents
一种改性环氧沥青混凝土及其加工工艺 Download PDFInfo
- Publication number
- CN111825388A CN111825388A CN202010569980.2A CN202010569980A CN111825388A CN 111825388 A CN111825388 A CN 111825388A CN 202010569980 A CN202010569980 A CN 202010569980A CN 111825388 A CN111825388 A CN 111825388A
- Authority
- CN
- China
- Prior art keywords
- asphalt
- modified epoxy
- parts
- epoxy asphalt
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种改性环氧沥青混凝土及其加工工艺,所述改性环氧沥青混凝土包括改性环氧沥青、砂、水泥、石、水、木质素、减水剂;其中改性环氧沥青由改性沥青、双酚A环氧树脂、固化剂、聚氨酯预聚体、增容剂反应制成。本发明,在环氧树脂分子链段上引入聚氨酯中柔性的C‑C链和C‑O‑C链,与环氧树脂可形成互穿网格结构,可提高材料的柔韧性。同时采用凹凸棒土对沥青改性,经凹凸棒土改性后的沥青,与矿料的粘附力增强,材料韧性增强;同时凹凸棒土可以吸附沥青散发出的酚、苯、蒽等有毒气体,减轻对人体的危害和环境的污染。本发明配比设计合理,具有较高实用性。
Description
技术领域
本发明涉及道路沥青技术领域,具体为一种改性环氧沥青混凝土及其加工工艺。
背景技术
近年来,环氧沥青材料作为一种新型的热固性高性能材料,在我国桥梁、道路铺装修补中的应用日益广泛。环氧沥青是将环氧树脂加入沥青中,经过与固化剂发生的固化反应后,沥青分子分散于环氧树脂形成的网状结构中,形成不可逆的固化物。与普通沥青或其它热塑性沥青相比环氧沥青具有无可比拟的优越的力学性能;主要是刚强度与高刚度、优良的疲劳性能良好的粘结性能和耐久性。而且环氧树脂可以提高沥青的耐酸、耐碱及有机溶剂对沥青的腐蚀,而在混合料中可以改善混合料的抗水损坏性能并提高沥青对石料的粘附性能。用环氧沥青拌制的沥青混合料,其路用性能普通沥青混合料优异得多。但环氧沥青材料韧性较差,固化后质脆、耐冲击性能差,且容易开裂。因此,提高和改善环氧沥青柔性、韧性,改善道路、桥梁铺装沥青混凝土的耐久性,如疲劳开裂、温缩开裂,已成为目前环氧沥青混凝土领域需要解决的问题。
发明内容
本发明的目的在于提供一种改性环氧沥青混凝土及其加工工艺,以解决现有技术中的问题。
为实现上述目的,本发明提供如下技术方案:一种改性环氧沥青混凝土,其特征在于:改性沥青混凝土包含如下组分,按重量份数计,改性环氧沥青12-27份、砂20-35、水泥15-25份、石20-35份、水7-13份、木质素7-13份、减水剂5-9份。
所述改性环氧沥青由改性沥青40-60份、双酚A环氧树脂35-55份、聚氨酯预聚体15-25份、增容剂5-9份、固化剂8-17份反应制得;其中改性沥青由石油沥青、凹凸棒土、丙基三甲基硅烷、乙二胺反应制得;固化剂由羟基苯环酸钠与酸酐类固化剂(酸酐类固化剂为聚二十碳烷二酸酸酐、聚壬二酸酐、聚癸二酸酐、及十二烯基丁二酸酐的一种或多种)1:1混合制得;增容剂为环氧型增容剂POE-g-GMA(甲基丙烯酸缩水甘油酯接枝乙烯-辛烯共聚物)。
本发明中选用酸酐类固化剂,既可以将环氧树脂与沥青固化,又可以起到增韧剂的作用。POE-g-GMA为环氧型树脂专用增容剂,具有优越的加工流动性和增韧性;与酸酐类固化剂协同作用,可增强改性环氧沥青的韧性,在道路、桥梁铺装时表现出良好的抗裂效果。
改性环氧沥青混凝土的加工工艺,包括以下步骤:
(1)制备聚氨酯预聚体;取4,4′-二苯基甲烷二异氰酸酯(MDI)搅拌,向MDI中滴入乙二胺聚醚,升温并控制速度为2℃/min;温度为78-80℃时停止升温,保温老化2h,制得聚氨酯预聚体;
乙二胺聚醚为乙二胺起始的纯环氧丙烷聚醚,其分子表面含具有催化作用的胺基,分子活性较高;可快速与异氰酸酯反应,制得的预聚体活性较高。
(2)制备改性沥青:取凹凸棒土矿料和去离子水混合,搅拌40-50min,静置2-3h,取上层凹凸棒土悬浊液,将悬浊液离心分离得到的凹凸棒土,烘干;将烘干后的凹凸棒土分散于10%浓度的硫酸溶液中,温度为58-60℃条件下,搅拌0.5-1h;冷却过滤,去离子水冲洗,烘干,得到酸活化的凹凸棒土;
丙基三甲基硅烷和乙二胺以1:1质量比加入乙醇溶液中,温度为88-92℃条件下,反应12-14h后过滤,去离子水冲洗,得到溶液Ⅰ;取酸活化的凹凸棒土分散于甲苯溶剂,升高温度,开启搅拌,向其中滴加溶液Ⅰ;当温度为115-125℃时停止加热,氮气保压,充分反应20-24h;乙醇溶液抽提洗涤,烘干研磨,得到物质A;取石油沥青加热至125-160℃,边搅拌边加入物质A,搅拌25-40min后,制得改性沥青。
凹凸棒土是一种具有链层状结构的黏土矿物,具有多种优异的物理化学性能,如吸附性、增强性、耐候性等;由于凹凸棒土比表面积大易团聚,且表面含有极性羟基,与高聚物的亲和性很差,在传统混凝土领域只能作为填料使用;为了发挥其优异性能,本发明中对凹凸棒土先进行酸活化处理,再在丙基三甲基硅烷作用下,与乙二胺发生接枝反应;制得带有胺基基团的凹凸棒土,胺基凹凸棒土对石油沥青改性后,沥青被附于凹凸棒土的优异特性能;拥有较强的耐酸碱性、耐腐蚀性和抗老化性;同时在生产沥青混料时,能够吸附沥青中释放出的酚、萘、蒽、苯有毒气体,减少对人体危害和环境污染;粘附能力强,改性沥青与矿料的粘附性增强,沥青混料的韧性增大。
(3)制备改性环氧沥青;取双酚A环氧树脂,加入溶剂丙二醇甲醚、丙酮溶液、催化剂二丁基二月桂酸锡,其质量比为2:1:0.1;制得双酚A环氧树脂反应液;升温至46-50℃,向其中加入改性沥青和聚氨酯预聚体,搅拌均匀;升温至88-90℃,充分反应15-20min;每隔20min测定其-NCO含量,当-NCO含量为0时,反应结束;依次加入固化剂羟基苯环酸钠与酸酐类固化剂1:1混合物、增容剂POE-g-GMA,混合搅拌,制得改性环氧沥青。
改性环氧沥青制备过程中,当温度达到88-90℃,双酚A环氧树脂反应液会和聚氨酯预聚体发生化学反应、在其分子链段上接入预聚体中柔性的C-C链和C-O-C链,又有活性的酰胺基团,与环氧树脂可形成互穿的立体网络结构,使其具有较高强度和韧性。当改性环氧树脂和沥青经固化剂固化凝结后,互穿的立体网络结构得到固定,两个聚合物网络相互结合,强度增大,可抵抗更大的外力作用;故聚氨酯改性的环氧树脂,与改性沥青固化粘结后,制得的改性环氧沥青的强度和韧性提高。
(4)制备改性环氧沥青混凝土,步骤如下;温度为120-140℃条件下,加入改性环氧沥青、水、木质素,充分搅拌2-3min;再加入水泥、砂、石、减水剂搅拌2-3min,制得改性环氧沥青混凝土。
木质素是具有优良柔韧性的三维网状结构生物高分子,可与改性沥青系统中的凹凸棒土层状结构贯穿,形成紧密的立体网络结构;使改性沥青系统具有更大的支撑力和耐久力,提高系统的稳定性、强度、密实度和均匀度,使改性环氧沥青混凝土铺装时,表现出良好的抗开裂作用。
与现有技术相比,本发明的有益效果是:
本发明,在双酚A环氧树脂分子链段上引入柔性的C-C链和C-O-C链,使得改性环氧沥青的柔性和韧性提高。处理后的凹凸棒土对沥青改性,与沥青相容性更高,使沥青表现出较强的耐酸碱性、耐腐蚀性和抗老化性;凹凸棒土粘附能力强,经凹凸棒土改性后的沥青,与矿料的粘附性增强,沥青混料的韧性增大。木质素的三维结构与改性沥青中的层状结构结合,形成紧密的空间网络结构;进一步增强改性环氧沥青混凝土系统的支撑力和耐久力,使改性环氧沥青混凝土在铺装桥梁、道路时,表现出良好的韧性,抗开裂性。
具体实施方式:
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
一种改性环氧沥青混凝土,包含如下重量份数的组分;改性环氧沥青12份、砂20份、水泥15份、石20份、水7份、木质素7份、减水剂5份。
改性环氧沥青包括改性沥青40份、双酚A环氧树脂35份、聚氨酯预聚体15份、增容剂5份、固化剂8份。
改性沥青包括石油沥青、凹凸棒土、丙基三甲基硅烷、乙二胺;所述固化剂由羟基苯环酸钠与聚二十碳烷二酸酸1:1混合制得;所述增容剂为POE-g-GMA。
改性环氧沥青混凝土的加工工艺,包括以下步骤:
(1)制备聚氨酯预聚体;取4,4′-二苯基甲烷二异氰酸酯(MDI)搅拌,向MDI中滴入乙二胺聚醚,升温并控制速度为2℃/min;温度为78℃时停止升温,保温老化2h,制得聚氨酯预聚体。
(2)制备改性沥青:取凹凸棒土矿料和去离子水混合,搅拌40min,静置2h,取上层凹凸棒土悬浊液,将悬浊液离心分离得到的凹凸棒土,烘干;将烘干后的凹凸棒土分散于10%浓度的硫酸溶液中,温度为58℃条件下,搅拌0.5h;冷却过滤,去离子水冲洗,烘干,得到酸活化的凹凸棒土;
丙基三甲基硅烷和乙二胺以1:1质量比加入乙醇溶液中,温度为88℃条件下,反应12h后过滤,去离子水冲洗,得到溶液Ⅰ;
取酸活化的凹凸棒土分散于甲苯溶剂,升高温度,开启搅拌,向其中滴加溶液Ⅰ;当温度为115℃时停止加热,氮气保压,充分反应20h;乙醇溶液抽提洗涤,烘干研磨,得到物质A;
取石油沥青加热至125℃,边搅拌边加入物质A,搅拌25min后,制得改性沥青。
(3)制备改性环氧沥青;取双酚A环氧树脂,加入溶剂丙二醇甲醚、丙酮溶液、催化剂二丁基二月桂酸锡,其质量比为2:1:0.1;制得双酚A环氧树脂反应液;升温至46℃,向其中加入改性沥青和聚氨酯预聚体,搅拌均匀;升温至88℃,充分反应15min;每隔20min测定其-NCO含量,当-NCO含量为0时,反应结束;依次加入固化剂羟基苯环酸钠与聚二十碳烷二酸酸1:1混合物、增容剂POE-g-GMA,混合搅拌,制得改性环氧沥青。
(4)制备改性环氧沥青混凝土;温度为120℃条件下,加入改性环氧沥青、水、木质素,充分搅拌2min;再加入水泥、砂、石、减水剂搅拌2min,制得改性环氧沥青混凝土。
实施例2
一种改性环氧沥青混凝土,包含如下重量份数的组分;改性环氧沥青19份、砂31份、水泥23份、石21份、水9份、木质素12份、减水剂6份。
改性环氧沥青包括改性沥青45份、双酚A环氧树脂47份、聚氨酯预聚体19份、增容剂6份、固化剂13份。
改性沥青包括石油沥青、凹凸棒土、丙基三甲基硅烷、乙二胺;所述固化剂由羟基苯环酸钠与聚壬二酸酐1:1混合制得;所述增容剂为POE-g-GMA。
改性环氧沥青混凝土的加工工艺,包括以下步骤:
(1)制备聚氨酯预聚体;取4,4′-二苯基甲烷二异氰酸酯(MDI)搅拌,向MDI中滴入乙二胺聚醚,升温并控制速度为2℃/min;温度为79℃时停止升温,保温老化2h,制得聚氨酯预聚体。
(2)制备改性沥青:取凹凸棒土矿料和去离子水混合,搅拌43min,静置2.5h,取上层凹凸棒土悬浊液,将悬浊液离心分离得到的凹凸棒土,烘干;将烘干后的凹凸棒土分散于10%浓度的硫酸溶液中,温度为59℃条件下,搅拌0.75h;冷却过滤,去离子水冲洗,烘干,得到酸活化的凹凸棒土;
丙基三甲基硅烷和乙二胺以1:1质量比加入乙醇溶液中,温度为90℃条件下,反应13h后过滤,去离子水冲洗,得到溶液Ⅰ;
取酸活化的凹凸棒土分散于甲苯溶剂,升高温度,开启搅拌,向其中滴加溶液Ⅰ;当温度为117℃时停止加热,氮气保压,充分反应23h;乙醇溶液抽提洗涤,烘干研磨,得到物质A;
取石油沥青加热至139℃,边搅拌边加入物质A,搅拌25-40min后,制得改性沥青。
(3)制备改性环氧沥青;取双酚A环氧树脂,加入溶剂丙二醇甲醚、丙酮溶液、催化剂二丁基二月桂酸锡,其质量比为2:1:0.1;制得双酚A环氧树脂反应液;升温至49℃,向其中加入改性沥青和聚氨酯预聚体,搅拌均匀;升温至89℃,充分反应17min;每隔20min测定其-NCO含量,当-NCO含量为0时,反应结束;依次加入固化剂羟基苯环酸钠与聚壬二酸酐1:1混合物、增容剂POE-g-GMA,混合搅拌,制得改性环氧沥青。
(4)制备改性环氧沥青混凝土;温度为135℃条件下,加入改性环氧沥青、水、木质素,充分搅拌2.5min;再加入水泥、砂、石、减水剂搅拌2.5min,制得改性环氧沥青混凝土。
实施例3
一种改性环氧沥青混凝土,包含如下重量份数的组分;改性环氧沥青27份、砂35份、水泥25份、石35份、水13份、木质素13份、减水剂9份。
改性环氧沥青包括改性沥青60份、双酚A环氧树脂55份、聚氨酯预聚体25份、增容剂9份、固化剂17份。
改性沥青包括石油沥青、凹凸棒土、丙基三甲基硅烷、乙二胺;所述固化剂由羟基苯环酸钠与聚癸二酸酐1:1混合制得;所述增容剂为POE-g-GMA。
改性环氧沥青混凝土的加工工艺,包括以下步骤:
(1)制备聚氨酯预聚体;取4,4′-二苯基甲烷二异氰酸酯(MDI)搅拌,向MDI中滴入乙二胺聚醚,升温并控制速度为2℃/min;温度为80℃时停止升温,保温老化2h,制得聚氨酯预聚体。
(2)制备改性沥青:取凹凸棒土矿料和去离子水混合,搅拌50min,静置3h,取上层凹凸棒土悬浊液,将悬浊液离心分离得到的凹凸棒土,烘干;将烘干后的凹凸棒土分散于10%浓度的硫酸溶液中,温度为60℃条件下,搅拌1h;冷却过滤,去离子水冲洗,烘干,得到酸活化的凹凸棒土;
丙基三甲基硅烷和乙二胺以1:1质量比加入乙醇溶液中,温度为92℃条件下,反应14h后过滤,去离子水冲洗,得到溶液Ⅰ;
取酸活化的凹凸棒土分散于甲苯溶剂,升高温度,开启搅拌,向其中滴加溶液Ⅰ;当温度为125℃时停止加热,氮气保压,充分反应24h;乙醇溶液抽提洗涤,烘干研磨,得到物质A;
取石油沥青加热至160℃,边搅拌边加入物质A,搅拌40min后,制得改性沥青。
(3)制备改性环氧沥青;取双酚A环氧树脂,加入溶剂丙二醇甲醚、丙酮溶液、催化剂二丁基二月桂酸锡,其质量比为2:1:0.1;制得双酚A环氧树脂反应液;升温至50℃,向其中加入改性沥青和聚氨酯预聚体,搅拌均匀;升温至90℃,充分反应20min;每隔20min测定其-NCO含量,当-NCO含量为0时,反应结束;依次加入固化剂羟基苯环酸钠与聚癸二酸酐1:1混合物、增容剂POE-g-GMA,混合搅拌,制得改性环氧沥青。
(4)制备改性环氧沥青混凝土;温度为140℃条件下,加入改性环氧沥青、水、木质素,充分搅拌3min;再加入水泥、砂、石、减水剂搅拌3min,制得改性环氧沥青混凝土。
对比例1
一种改性环氧沥青混凝土,包含如下重量份数的组分;石油沥青27份、砂35份,水泥25份,石35份,水13份、减水剂9份。
固化剂由羟基苯环酸钠与聚癸二酸酐1:1混合制得;增容剂为POE-g-GMA。
环氧沥青混凝土的加工工艺,包括以下步骤;
(1)制备环氧沥青;取石油沥青,升温至160℃;依次加入固化剂羟基苯环酸钠与聚癸二酸酐1:1混合物、增容剂POE-g-GMA,混合搅拌,制得环氧沥青。
(4)制备环氧沥青混凝土,步骤如下;温度为140℃条件下,加入环氧沥青、水泥、水、凹凸棒土、木质素,充分搅拌3min;再加入砂、石、减水剂搅拌3min,制得环氧沥青混凝土。
对比例2
一种改性环氧沥青混凝土,包含如下重量份数的组分;石油沥青27份、砂35份,水泥25份,石35份,水13份、减水剂9份。
固化剂由羟基苯环酸钠与聚癸二酸酐1:1混合制得;增容剂为POE-g-GMA。
环氧沥青混凝土的加工工艺,包括以下步骤;
(1)制备环氧沥青;取石油沥青,升温至160℃;依次加入固化剂羟基苯环酸钠与聚癸二酸酐1:1混合物、增容剂POE-g-GMA,混合搅拌,制得环氧沥青。
(4)制备环氧沥青混凝土,步骤如下;温度为140℃条件下,加入环氧沥青、水泥、水,充分搅拌3min;再加入砂、石、减水剂搅拌3min,制得环氧沥青混凝土。
检测数据对比分析
实施例1-3为本发明技术方案;对比例1与实施例的区别,是对比例1使用普通环氧沥青、且凹凸棒土作为矿料直接加入混凝土中;对比例2与实施例的区别,是对比例2使用普通环氧沥青,混凝土中不添加凹凸棒土和木质素。
1)柔性分析
取实施例1-3制得的改性环氧沥青混凝土、对比例1-2制得的环氧沥青混凝土,同步制成尺寸150mm*150mm*150mm的标准小梁试件。在温度为-9~-10℃,加载速率为55mm/min条件,进行弯曲试验;加载直至小梁试件破坏,即为试验终点。检测数据见表1
项目 | 破坏应变,με | 弯拉强度,Mpa |
实施例1 | 3499 | 27.9 |
实施例2 | 3739 | 28.7 |
实施例3 | 3832 | 29.8 |
对比例1 | 2957 | 27.4 |
对比例1 | 2839 | 27.0 |
表1
由表1数据可知,小梁试件的破坏应力实施例1-3>对比例1>对比例2>对比例1;所以本发明制备的改性环氧沥青抵抗破坏应变能力最强;小梁试件的弯拉强度实施例1-3>对比例1>对比例2,所以本发明制备的改性环氧沥青混凝土在发生较大变性时,强度依然较大,抗裂性强。
2)韧性分析
取实施例1-3制得的改性环氧沥青混凝土、对比例1-2制得的环氧沥青混凝土,同步制成尺寸150mm*150mm*150mm的标准小梁试件。取标准小梁试件,进行疲劳试验;应力控制,荷载为最大破坏力的0.2、0.3、0.5倍。结果见表2
由表2数据可知,在同一应力水平下,实施例1-3中疲劳次数<对比例1<对比例2;说明本发明制备的改性环氧沥青混凝土,其抗疲劳能力强,韧性表现优良。
综上所述,本发明制备的改性环氧沥青混凝土和用凹凸棒土作为矿料的环氧沥青混凝土相比,柔性和韧性更强;本发明对凹凸棒土处理,使其对高聚物相容性更好;再用其改性沥青,充分发挥了凹凸棒土的耐候性、增韧性、吸附性等优异性能。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (9)
1.一种改性环氧沥青混凝土,其特征在于:所述改性环氧沥青混凝土包含如下组分;按重量份数计,改性环氧沥青12-27份、砂20-35份、水泥15-25份、石20-35份、水7-13份、木质素7-13份、减水剂5-9份。
2.根据权利要求1所述的一种改性环氧沥青混凝土,其特征在于;所述改性环氧沥青包含如下组分;改性沥青40-60份、双酚A环氧树脂35-55份、聚氨酯预聚体15-25份、增容剂5-9份、固化剂8-17份。
3.根据权利要求2所述的一种改性环氧沥青混凝土,其特征在于;所述改性沥青包括石油沥青、凹凸棒土、丙基三甲基硅烷、乙二胺;所述固化剂由羟基苯环酸钠与酸酐类固化剂1:1混合制得;所述增容剂为POE-g-GMA。
4.根据权利要求3所述的一种改性环氧沥青混凝土,其特征在于;所述酸酐类固化剂为聚二十碳烷二酸酸酐、聚壬二酸酐、聚癸二酸酐、十二烯基丁二酸酐的一种或多种。
5.一种改性环氧沥青混凝土的加工工艺,其特征在于,包括以下步骤:
(1)制备聚氨酯预聚体;
(2)制备改性沥青;
(3)制备改性环氧沥青;
(4)制备改性环氧沥青混凝土。
6.根据权利要求5所述的改性环氧沥青混凝土的加工工艺,其特征在于,所述(1)制备聚氨酯预聚体,步骤如下;取4,4′-二苯基甲烷二异氰酸酯(MDI)搅拌,向MDI中滴加乙二胺聚醚,升温并控制速度为2℃/min;温度为78-80℃时停止升温,保温老化2h,制得聚氨酯预聚体。
7.根据权利要求5所述的改性环氧沥青混凝土的加工工艺,其特征在于所述(2)制备改性沥青,步骤如下:
取凹凸棒土矿料和去离子水混合,搅拌40-50min,静置2-3h,取上层凹凸棒土悬浊液,将悬浊液离心分离得到的凹凸棒土,烘干;将烘干后的凹凸棒土分散于10%浓度的硫酸溶液中,温度为58-60℃条件下,搅拌0.5-1h;冷却过滤,去离子水冲洗,烘干,得到酸活化的凹凸棒土;
丙基三甲基硅烷和乙二胺以1:1质量比加入乙醇溶液中,温度为88-92℃条件下,反应12-14h后过滤,去离子水冲洗,得到溶液Ⅰ;
取酸活化的凹凸棒土分散于甲苯溶剂,升高温度,开启搅拌,向其中滴加溶液Ⅰ;当温度为115-125℃时停止加热,氮气保压,充分反应20-24h;乙醇溶液抽提洗涤,烘干研磨,得到物质A;
取石油沥青加热至125-160℃,边搅拌边加入物质A,搅拌25-40min后,制得改性沥青。
8.根据权利要求5所述的改性环氧沥青混凝土的加工工艺,其特征在于,所述(3)制备改性环氧沥青,步骤如下;
取双酚A环氧树脂,加入溶剂丙二醇甲醚、丙酮溶液、催化剂二丁基二月桂酸锡,其质量比为2:1:0.1;制得双酚A环氧树脂反应液,升温至46-50℃时,向其中加入改性沥青和聚氨酯预聚体,搅拌均匀;升温至88-90℃,充分反应15-20min;每隔20min测定其-NCO含量,当-NCO含量为0时,反应结束;依次加入固化剂羟基苯环酸钠与酸酐类固化剂1:1混合物、增容剂POE-g-GMA,混合搅拌,制得改性环氧沥青。
9.根据权利要求5所述的改性环氧沥青混凝土的加工工艺,其特征在于,所述(4)制备改性环氧沥青混凝土,步骤如下;温度为120-140℃条件下,加入改性环氧沥青、水、木质素,充分搅拌2-3min;再加入水泥、砂、石、减水剂搅拌2-3min,制得改性环氧沥青混凝土。