CN111673239A - Copper/steel composite material connecting method for preset joint - Google Patents

Copper/steel composite material connecting method for preset joint Download PDF

Info

Publication number
CN111673239A
CN111673239A CN202010430764.XA CN202010430764A CN111673239A CN 111673239 A CN111673239 A CN 111673239A CN 202010430764 A CN202010430764 A CN 202010430764A CN 111673239 A CN111673239 A CN 111673239A
Authority
CN
China
Prior art keywords
welding
copper
steel
preset joint
joint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202010430764.XA
Other languages
Chinese (zh)
Other versions
CN111673239B (en
Inventor
张敏
杜明科
张云龙
李静
董玉凡
苟川东
王博玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xian University of Technology
Original Assignee
Xian University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xian University of Technology filed Critical Xian University of Technology
Priority to CN202010430764.XA priority Critical patent/CN111673239B/en
Publication of CN111673239A publication Critical patent/CN111673239A/en
Application granted granted Critical
Publication of CN111673239B publication Critical patent/CN111673239B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a copper/steel composite material connecting method of a preset joint, which comprises the following specific operation steps: step 1: preparing a copper steel preset joint: preparing a copper-steel composite welding seam with a reasonable specification by using an electric arc additive technology to serve as a preset joint; step 2: and selecting solid welding wires with the same components according to the components of the base metal, and completing the welding of the copper test plate, the steel test plate and the copper steel preset joint by adopting gas metal arc welding. The method can improve the welding quality and the comprehensive mechanical property of the copper-steel dissimilar metal welding joint, and provides a brand new thought for the connection of copper/steel dissimilar metals.

Description

Copper/steel composite material connecting method for preset joint
Technical Field
The invention belongs to the technical field of dissimilar metal welding, and particularly relates to a method for connecting a copper/steel composite material of a preset joint.
Background
In the field of industrial manufacturing, a welding structure made of a single metal cannot meet the use requirements, and therefore, in order to ensure the use performance of the welding structure, a composite material is used to replace the single material in most cases, so that the requirements of both economic benefit and structural strength are met. In the field of manufacturing large transformer oil tanks, copper-steel dissimilar metals are almost all used for welding, and the structure has the advantages of shielding an external magnetic field, increasing the heat dissipation speed, ensuring the strength of a tank body and the like.
However, the welding difficulty of copper-steel dissimilar metals is large. This is because the two metals have large differences in their physicochemical properties, and thus, many welding defects such as unfused, blowholes, and permeation cracks are generated during welding. In which the penetration cracks formed on the steel side reduce the strength of the joint and over time the cracks may propagate and extend throughout the welded joint, causing the welded structure to fail. Therefore, a reasonable joint transition form must be designed, and a reasonable welding process is selected to prevent various welding defects generated in the copper-steel welding process as much as possible, so that the comprehensive mechanical property of the structural member is improved.
Disclosure of Invention
The invention aims to provide a copper/steel composite material connecting method for a preset joint, which can improve the welding quality and the comprehensive mechanical property of a copper-steel dissimilar metal welding joint.
The invention adopts the technical scheme that a copper/steel composite material connecting method of a preset joint comprises the following specific operation steps:
step 1: preparing a copper steel preset joint: preparing a copper-steel composite welding seam with a reasonable specification by using an electric arc additive technology to serve as a preset joint;
step 2: and selecting solid welding wires with the same components according to the components of the base metal, and completing the welding of the copper test plate, the steel test plate and the copper steel preset joint by adopting gas metal arc welding.
The present invention is also characterized in that,
in the step 1, the preparation materials of the copper-steel preset joint are a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, the specific preparation parameters of the copper-steel preset joint are that the welding current is 190-210A on the steel side of ①, the welding voltage is 21-24V, the welding speed is 5-8 mm/S, and the volume fraction of protective gas is 90% Ar + the volume fraction of protective gas is 10% CO2The volume percentage sum of the components is 100%, the gas flow is 15-18L/min, the welding current on the copper side of ② is 210-240A, the welding voltage is 22-26V, the welding speed is 4-6 mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 15-18L/min.
In the step 1, the specification of the copper steel preset joint prepared by the electric arc additive technology is as follows: the length is 100mm × 5-8 mm × 5 mm.
In the step 2, the copper test plate is a T2-Y red copper plate, and the steel test plate is a Q345B plate; the specifications of the copper test plate and the steel test plate are as follows: length × width × height is 100mm × 50mm × 5 mm.
In the step 2, the adopted solid welding wires are S201 red copper welding wires and CHW50C6 carbon steel welding wires respectively, and the specifications of the welding wires are phi 1.2 mm.
In the step 2, welding technological parameters of the copper-steel preset joint and the test plate are ① Q345B welding of the test plate and the preset joint, wherein the welding current is 200-225A, the welding voltage is 22-25V, the welding speed is 5-8 mm/s, and the volume fraction of protective gas is 90% Ar + the volume fraction of protective gas is 10% CO2The volume percentage sum of the components is 100%, the gas flow is 15-18L/min, and the ② T2-Y red copper test plate and the copper steel preset joint are welded, wherein the welding current is 220-245A, the welding voltage is 23-27V, the welding speed is 4-6 mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 15-18L/min.
The invention has the beneficial effects that:
1. the method of the invention adopts the preset joint to replace the traditional welding line, realizes the conversion from heterogeneous welding to homogeneous welding and reduces the welding difficulty.
2. The method of the invention utilizes the electric arc material increase technology to prepare the preset joint, and the latter layer of welding bead is equivalent to the former layer of welding bead which is subjected to heat treatment, so that the comprehensive mechanical property of the whole welding joint is improved.
3. The method can reduce the probability of welding defects caused by the difference of the thermal physical properties of dissimilar materials.
4. The method does not need to preheat the T2-Y copper plate before welding, thereby improving the welding efficiency.
Drawings
FIG. 1 is a schematic view of the assembly and welding of a test plate and a preset joint.
FIG. 2 is a schematic view of a stretch break in example 3 of the present invention.
Detailed Description
The present invention will be described in detail below with reference to the accompanying drawings and specific embodiments.
The invention discloses a copper/steel composite material connecting method of a preset joint, which comprises the following specific operation steps as shown in figure 1:
step 1: preparing a copper steel preset joint: preparing a copper-steel composite welding seam with a reasonable specification by using an electric arc additive technology to serve as a preset joint;
in the step 1, the preparation materials of the copper-steel preset joint are a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, the specific preparation parameters of the copper-steel preset joint are that the welding current is 190-210A on the steel side of ①, the welding voltage is 21-24V, the welding speed is 5-8 mm/S, and the volume fraction of protective gas is 90% Ar + the volume fraction of protective gas is 10% CO2The total volume percentage of the components is 100%, the gas flow is 15-18L/min, the copper side of ② is welding current is 210-240A, welding voltage is 22-26V, welding speed is 4-6 mm/s, inert protective gas is pure argon with volume percentage of 99.99%, and the flow is 15-18L/min;
in the step 1, the specification of the copper steel preset joint prepared by the electric arc additive technology is as follows: the length is 100mm × 5-8 mm × 5 mm.
In the step 1, surfacing three layers of each material, and mechanically polishing and cleaning each layer of welding bead in the material increasing process to prevent impurities;
step 2: selecting solid welding wires with the same components according to the components of the base metal, and completing the welding of a copper test plate, a steel test plate and a copper steel preset joint by adopting gas metal arc welding;
in the step 2, the copper test plate is a T2-Y red copper plate, and the steel test plate is a Q345B plate; the specifications of the copper test plate and the steel test plate are as follows: length × width × height ═ 100mm × 50mm × 5 mm;
in step 2, the T2-Y red copper and Q345B test plates must be cleaned before welding.
In the step 2, the adopted solid welding wires are S201 red copper welding wires and CHW50C6 carbon steel welding wires respectively, and the specifications of the welding wires are phi 1.2 mm;
in the step 2, welding technological parameters of the copper-steel preset joint and the test plate are ① Q345B welding of the test plate and the preset joint, wherein the welding current is 200-225A, the welding voltage is 22-25V, the welding speed is 5-8 mm/s, and the volume fraction of protective gas is 90% Ar + the volume fraction of protective gas is 10% CO2The volume percentage sum of the components is 100%, the gas flow is 15-18L/min, and the ② T2-Y red copper test plate and the copper steel preset joint are welded, wherein the welding current is 220-245A, the welding voltage is 23-27V, the welding speed is 4-6 mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 15-18L/min.
In examples 1 to 5, the test pieces Q345B and T2-Y were each 100X 50X 5mm in size.
Example 1
The method comprises the following steps of 1, preparing a preset joint by adopting a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, finishing additive preparation of the preset joint by utilizing a welding robot, wherein the specification of the joint is 100 × 5 × 5mm, three layers of materials are overlaid, each layer of welding bead is polished by a steel wire brush to prevent inclusion, and the specific additive preparation parameters are that the welding current of the preset joint at the steel side ① is 190A, the welding voltage is 21V, the welding speed is 5mm/S, the volume fraction is 90 percent Ar and the volume fraction is 10 percent CO2The volume percentage sum of the components is 100 percent, the gas flow is 15L/min, ② the preparation of the preset joint at the copper side comprises the welding current of 210A, the welding voltage of 22V, the welding speed of 4mm/s and the inert protective gas of 99.99 percent by volumeThe flow rate of pure argon gas is 15L/min.
And 2, cleaning the test plate before welding, including mechanical grinding, acetone or alcohol cleaning, selecting an S201 red copper welding wire with the diameter of 1.2mm and a CHW50C6 carbon steel welding wire as weld filler metals, and realizing the connection of a preset joint and Q345B and T2-Y red copper test plates by adopting gas metal arc welding, wherein the specifications of the two plates are both 100 × 50 × 5mm, and the specific parameters of the welding process are ① Q345B test plate and the preset joint, namely the welding current is 200A, the welding voltage is 22V, the welding speed is 5mm/S, the volume fraction is 90% Ar + the volume fraction is 10% CO2The total volume percentage of the components is 100%, the gas flow is 15L/min, ② T2-Y copper test plate is connected with a preset joint, the welding current is 220A, the welding voltage is 23V, the welding speed is 4mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 15L/min.
In the welded joint prepared by the method for connecting the copper/steel composite material of the preset joint in the embodiment 1, the tensile strength is 208Mpa through mechanical property detection, the welded joint is partially broken in a heat affected zone of a T2-Y copper test plate, and the elongation after breakage is 11.6%.
Example 2
The method comprises the following steps of 1, preparing a preset joint by adopting a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, finishing additive preparation of the preset joint by utilizing a welding robot, wherein the specification of the joint is 100 × 5.5.5 5.5 × 5mm, three layers of surfacing welding of each material are formed, each layer of welding bead is polished by a steel wire brush to prevent inclusion, and the specific additive preparation parameters comprise that the welding current of the preset joint at the steel side ① is 200A, the welding voltage is 22V, the welding speed is 5.5mm/S, the volume fraction is 90% Ar + the volume fraction is 10% CO2The total volume percentage of the components is 100 percent, the gas flow is 16L/min, and the ② copper side preset joint is prepared, wherein the welding current is 220A, the welding voltage is 23V, the welding speed is 4.5mm/s, the inert protective gas is pure argon with the volume percentage of 99.99 percent, and the flow is 16L/min.
And 2, cleaning the test plate before welding, including mechanical polishing and acetone or alcohol cleaning. Then selecting an S201 red copper welding wire with the diameter of 1.2mm, CHW50C6 carbon steel welding wire is used as welding seam filling metal, the preset joint is connected with Q345B and T2-Y red copper test plates by adopting gas metal arc welding, the specification of the two plates is 100 × 50 × 5mm, and the specific parameters of the welding process are ① Q345B test plate is connected with the preset joint, the welding current is 210A, the welding voltage is 22.5V, the welding speed is 5.5mm/s, the volume fraction is 90% Ar + the volume fraction is 10% CO2The total volume percentage of the components is 100%, the gas flow is 16L/min, ② T2-Y copper test plate is connected with a preset joint, the welding current is 230A, the welding voltage is 24.5V, the welding speed is 4.5mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 16L/min.
In the welding joint prepared by the method for connecting the copper/steel composite material of the preset joint in the embodiment 2, the tensile strength is 188Mpa through mechanical property detection, the joint strength is reduced due to inclusions in the preset joint, the copper side of the preset joint is broken in the stretching process, and the elongation after breakage is 9%.
Example 3
The method comprises the following steps of 1, preparing a preset joint by adopting a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, finishing additive preparation of the preset joint by utilizing a welding robot, wherein the specification of the joint is 100 × 6.5.5 6.5 × 5mm, three layers of surfacing welding of each material are formed, each layer of welding bead is polished by a steel wire brush to prevent inclusion, and the specific additive preparation parameters comprise that the welding current of the preset joint at the steel ① side is 205A, the welding voltage is 23.5V, the welding speed is 6.5mm/S, and the volume fraction of Ar & lt + & gt is 90% and the volume fraction of CO & lt + & gt is 10%2The total volume percentage of the components is 100%, the gas flow is 16L/min, ② the preparation of the copper side preset joint, the welding current is 235A, the welding voltage is 25V, the welding speed is 5mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 16L/min.
And 2, cleaning the test plate before welding, including mechanical polishing and acetone or alcohol cleaning. Then selecting an S201 red copper welding wire with the diameter of 1.2mm and a CHW50C6 carbon steel welding wire as welding seam filler metals, and realizing the connection of the preset joint and Q345B and T2-Y red copper test plates by adopting gas metal arc weldingThe specification of the two plates is 100 × 50 × 5mm, and the specific parameters of the welding process are that ① Q345B test plate is connected with a preset joint, the welding current is 215A, the welding voltage is 23V, the welding speed is 6.5mm/s, the volume fraction is 90 percent Ar + the volume fraction is 10 percent CO2The total volume percentage of the components is 100%, the gas flow is 16L/min, ② T2-Y copper test plate is connected with a preset joint, the welding current is 235A, the welding voltage is 25V, the welding speed is 5mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 16L/min.
In combination with the microscopic diagram of the fracture shown in fig. 2, it can be seen that no welding defects such as pores and microcracks are found at the fracture, and a large number of shallow dimples exist, which belong to typical ductile fracture.
In example 3, the welded joint prepared by the method for connecting copper/steel composite materials with the preset joint has tensile strength of 239Mpa through mechanical property detection, is broken in a welding heat affected zone of a T2-Y red copper test plate, and has elongation percentage after breakage of 14.2%.
Example 4
The method comprises the following steps of 1, preparing a preset joint by adopting a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, finishing additive preparation of the preset joint by utilizing a welding robot, wherein the specification of the joint is 100 × 8 × 5mm, three layers of materials are overlaid, each layer of welding bead is polished by a steel wire brush to prevent inclusion, and the specific additive preparation parameters are that the welding current of the preset joint at the steel side ① is 210A, the welding voltage is 24V, the welding speed is 8mm/S, the volume fraction is 90 percent Ar, and the volume fraction is 10 percent CO2The total volume percentage of the components is 100 percent, the gas flow is 18L/min, ② the preparation of the copper side preset joint comprises the welding current is 240A, the welding voltage is 26V, the welding speed is 6mm/s, the inert protective gas is pure argon with the volume percentage of 99.99 percent, and the flow is 18L/min.
And 2, cleaning the test plate before welding, including mechanical polishing and acetone or alcohol cleaning. Then selecting an S201 red copper welding wire with the diameter of 1.2mm and a CHW50C6 carbon steel welding wire as welding seam filler metals, and realizing the preset joint and Q345B and T2-Y red copper test plates by adopting gas metal arc weldingThe specification of the two plates is 100 × 50 × 5mm, and the specific parameters of the welding process are that the ① Q345B test plate is connected with a preset joint, the welding current is 225A, the welding voltage is 25V, the welding speed is 8mm/s, the volume fraction is 90 percent Ar + the volume fraction is 10 percent CO2The total volume percentage of the components is 100%, the gas flow is 18L/min, ② T2-Y copper test plate is connected with a preset joint, the welding current is 245A, the welding voltage is 27V, the welding speed is 6mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 18L/min.
In example 4, the welded joint prepared by the method for connecting copper/steel composite materials with a preset joint has a tensile strength of 228Mpa, and is broken in a heat affected zone of a T2-Y red copper test plate, and the elongation after breakage is 12.1% by mechanical property detection.
Example 5
The method comprises the following steps of 1, preparing a preset joint by adopting a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, finishing additive preparation of the preset joint by utilizing a welding robot, wherein the specification of the joint is 100 × 7 × 5mm, three layers of materials are overlaid, each layer of welding bead is polished by a steel wire brush to prevent inclusion, and the specific additive preparation parameters are that the welding current of the preset joint at the steel side ① is 200A, the welding voltage is 24V, the welding speed is 8mm/S, the volume fraction is 90 percent Ar, and the volume fraction is 10 percent CO2The total volume percentage of the components is 100 percent, the gas flow is 18L/min, ② the preparation of the copper side preset joint comprises the welding current is 240A, the welding voltage is 26V, the welding speed is 6mm/s, the inert protective gas is pure argon with the volume percentage of 99.99 percent, and the flow is 18L/min.
And 2, cleaning the test plate before welding, including mechanical polishing, acetone or alcohol cleaning, selecting an S201 red copper welding wire with the diameter of 1.2mm and a CHW50C6 carbon steel welding wire as weld filler metals, and realizing the connection of a preset joint and Q345B and T2-Y red copper test plates by adopting gas metal arc welding, wherein the specifications of the two plates are both 100 × 50 × 5mm, and the specific parameters of the welding process are ① Q345B test plate and the preset joint, namely the welding current is 220A, the welding voltage is 25V, the welding speed is 8mm/S, and the volume fraction is 90% Ar+ volume fraction of 10% CO2The total volume percentage of the components is 100%, the gas flow is 18L/min, ② T2-Y copper test plate is connected with a preset joint, the welding current is 245A, the welding voltage is 27V, the welding speed is 6mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 18L/min.
In example 5, the welded joint prepared by the method for connecting copper/steel composite materials with the preset joint has a tensile strength of 220Mpa, and is broken in a heat affected zone of a T2-Y red copper test plate, and the elongation after breakage is 11.8% through mechanical property detection.
The comparison of five groups of tests shows that the welded joint prepared by the method for connecting the copper/steel composite material of the preset joint has good weld surface forming and no obvious cracks and inclusions. Due to the fact that conversion from heterogeneous material connection to homogeneous material connection is achieved, welding defects such as permeation cracks, air holes and incomplete fusion are avoided, and mechanical properties of all aspects of a welding joint are greatly improved compared with direct welding of a copper steel test plate.
The mechanical properties of the weld joints prepared in the five examples are shown in table 1.
Table 1 examples 1-5 weld joint mechanical properties
Numbering Tensile strength/Mpa Elongation after rupture/%)
Example 1 208 11.6
Example 2 188 9
Example 3 239 14.2
Example 4 228 12.1
Example 5 220 11.8

Claims (6)

1. A copper/steel composite material connecting method of a preset joint is characterized by comprising the following specific operation steps:
step 1: preparing a copper steel preset joint: preparing a copper-steel composite welding seam with a reasonable specification by using an electric arc additive technology to serve as a preset joint;
step 2: and selecting solid welding wires with the same components according to the components of the base metal, and completing the welding of the copper test plate, the steel test plate and the copper steel preset joint by adopting gas metal arc welding.
2. The method for connecting the copper/steel composite material of the preset joint as claimed in claim 1, wherein in the step 1, the preparation materials of the copper-steel preset joint are a CHW50C6 carbon steel welding wire with the diameter of 1.2mm and an S211 silicon bronze welding wire, the specific preparation parameters of the copper-steel preset joint are ① steel side, welding current is 190-210A, welding voltage is 21-24V, welding speed is 5-8 mm/S, and protective gas is 90% Ar + 10% CO by volume fraction2The volume percentage sum of the components is 100%, the gas flow is 15-18L/min, the welding current is 210-240A, the welding voltage is 22-26V, and the welding speed is 4-6 mm/s on the copper side of ②The inert protective gas is pure argon with the volume percentage of 99.99%, and the flow rate is 15-18L/min.
3. The method for connecting the copper/steel composite materials of the preset joints according to claim 1, wherein in the step 1, the specifications of the copper-steel preset joint prepared by using the arc additive technology are as follows: the length is 100mm × 5-8 mm × 5 mm.
4. The method for connecting copper/steel composite materials of preset joints according to claim 1, wherein in the step 2, the copper test plate is a T2-Y red copper plate, and the steel test plate is a Q345B plate; the specifications of the copper test plate and the steel test plate are as follows: length × width × height is 100mm × 50mm × 5 mm.
5. The method for connecting the copper/steel composite materials of the preset joint as claimed in claim 4, wherein the solid welding wires adopted in the step 2 are S201 red copper welding wires and CHW50C6 carbon steel welding wires, and the specifications of the welding wires are all phi 1.2 mm.
6. The method for connecting the copper/steel composite material of the preset joint as claimed in claim 5, wherein in the step 2, the welding process parameters of the copper-steel preset joint and the test plate are ① Q345B, the welding current is 200-225A, the welding voltage is 22-25V, the welding speed is 5-8 mm/s, and the protective gas is 90% by volume Ar + 10% by volume CO2The volume percentage sum of the components is 100%, the gas flow is 15-18L/min, and the ② T2-Y red copper test plate and the copper steel preset joint are welded, wherein the welding current is 220-245A, the welding voltage is 23-27V, the welding speed is 4-6 mm/s, the inert protective gas is pure argon with the volume percentage of 99.99%, and the flow is 15-18L/min.
CN202010430764.XA 2020-05-20 2020-05-20 Copper/steel composite material connecting method for preset joint Active CN111673239B (en)