CN111423635A - 一种防静电胶乳手套 - Google Patents
一种防静电胶乳手套 Download PDFInfo
- Publication number
- CN111423635A CN111423635A CN201911290553.4A CN201911290553A CN111423635A CN 111423635 A CN111423635 A CN 111423635A CN 201911290553 A CN201911290553 A CN 201911290553A CN 111423635 A CN111423635 A CN 111423635A
- Authority
- CN
- China
- Prior art keywords
- solution
- mold
- minutes
- drying
- gloves
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种防静电胶乳手套及制作方法，该手套由天然胶乳、聚氨酯乳液、硫化机、防老剂、防静电剂、促进剂、稳定剂等原材料制作而成。手套具有极好的弹性、防静电性能、无卤素、防滑、防油、无尘、PU部分无味，避免人体产生的静电对产品造成破坏，同时手套不含卤素，防止氯元素对电子产品的氧化破坏其精密程度，故该手套适合在电子行业、半导体、无尘车间及日常生活中广泛使用。
Description
技术领域
本发明涉及一种防静电胶乳手套，属于乳胶制品生产制备领域。
背景技术
随着科技的发展，在工业生产对环境的要求越来越高，在许多生产工序中都要求避免静电的产生。尤其是电子行业，因为静电会损伤电子元件，影响产品质量，传统的手套不具备防静电功能，无法消除工作环境和操作人员身上的静电。
中国专利CN105462006A、CN103932432A、CN104621800A、CN107936318A均公开了防静电胶乳手套，这些方案在一定程度上可以解决防静电性能问题，但这几种防静电手套在洁净清洗过程中均采用了氯洗的工序，这就有可能在手套表面存在氯元素的残留，氯元素具有强氧化性，会对精密的电子元件造成损伤，因此需要开发一种抗静电效果好且不含有氯元素的乳胶手套，起到保护产品、人体手部和洁净室环境的目的。
发明内容
本发明的目的是针对现有技术存在的不足，提供一种防静电胶乳手套及制作方法，此方法制备的胶乳手套不仅抗静电而且不含氯元素，它适合在电子行业、半导体、无尘车间及日常生活中广泛使用。
本发明采用的技术方案：
防静电胶乳手套的原料重量组成如下：
所述的抗静电剂为铵盐、二烷基磷酸盐或烷基二甲基胺乙内盐；
所述的硫化剂为硫磺、二硫化四甲基秋兰姆、二硫化吗啡啉中的一种以上；
所述的促进剂为乙基-苯基-二硫代氨基甲酸锌、二乙基二硫代氨基甲酸锌中的一种以上；
所述的防老剂为2，6-二叔丁基-4-甲基苯酚、甲叉-4426-S、4，4’-双(二甲基苄基)二苯胺中的一种以上；
所述的稳定剂为酪素、氨水、氢氧化钾中的一种以上。
2.根据权利要求1所述的一种防静电胶乳手套，其特征在于，防静电胶乳手套制作方法步骤如下：
(1)材料配制：配制凝固剂为质量分数为5％～15％硝酸钙溶液、5％～15％氯化钙溶液和 0.5％～5％玉米淀粉的混合溶液、0.5％～2％抗静电剂溶液、总固体含量20％～40％天然胶乳、总固体含量3％～10％聚氨酯乳液；
(2)清洗手套模具：将手模先在酸性洗模液中清洗，再在碱性洗模液中清洗，然后用清水漂洗干净，在60～80℃烘箱中烘10～20分钟；酸性洗模液为质量分数在0.5％～5％的盐酸溶液、硫酸溶液、硝酸溶液中的一种以上；碱性洗模液为质量分数在0.5％～5％的氢氧化钠溶液、氢氧化钾溶液中的一种以上；
(3)浸渍：将清洗干净的手模浸渍在凝固剂溶液中20～60秒，放入60～100℃的烘箱中烘15～25分钟；将带有凝固剂的手模浸渍在总固体含量为20％～40％的天然胶乳中10～25秒，放入80～120℃的烘箱中烘15～30分钟；凝固剂质量分数为5％～15％硝酸钙溶液、5％～15％氯化钙溶液和0.5％～5％玉米淀粉的混合溶液；
(4)卷边；
(5)将卷边后的带有手套的手模浸渍在总固体含量为3％～10％聚氨酯乳液中10～30秒，放入80～120℃的烘箱中烘15～30分钟；
(6)沥滤：产品在卷边后在80～95℃水中进行沥滤，沥滤时间30～60秒；
(7)烘干温度80℃～120℃，烘干时间10分钟～20分钟，脱模；
(8)步骤(7)脱模后的手套在抗静电剂溶液中进行泡洗20～60分钟，再用干衣机在70～100℃条件下烘20～40分钟，得到防静电胶乳手套。
本发明的有益效果：无氯元素大幅减少手套对精密电子产品的氧化，胶乳手套防静电性能增强了20％～50％，采用PU对手套表面进行处理，方便穿戴，低粉量降低到2毫克以下，起到保护产品、人体手部和洁净室环境的目的。
具体实施方式
下面结合实施例对本发明做进一步阐述。
目前市场上出售的手套在高端电子产品领域防静电性能差，含有卤素，在使用过程中易伤害皮肤和氧化电子元器件。因此需要一种去强的防静电又不含卤素的防静电手套，保护皮肤和电子元器件。
实施例1
防静电胶乳手套的原料重量组成如下：
所述的抗静电剂为铵盐。
所述的硫化剂为硫磺；
所述的促进剂为乙基-苯基-二硫代氨基甲酸锌；
所述的防老剂为2，6-二叔丁基-4-甲基苯酚；
所述的稳定剂为酪素、氨水。
防静电胶乳手套制作方法步骤如下：
(1)材料配制：配制凝固剂、抗静电剂溶液、天然胶乳和聚氨酯乳液；
(2)清洗手套模具：将手模先在酸性洗模液中清洗，再在碱性洗模液中清洗，然后用清水漂洗干净，在60℃烘箱中烘10分钟；酸性洗模液为质量分数在0.5％％的盐酸溶液；碱性洗模液为质量分数在0.5％的氢氧化钠溶液；
(3)浸渍：将清洗干净的手模浸渍在凝固剂溶液中20秒，放入60℃的烘箱中烘15分钟；将带有凝固剂的手模浸渍在总固体含量在20％的天然胶乳中10秒，放入80℃的烘箱中烘15分钟；凝固剂为质量分数为5％硝酸钙溶液、5％氯化钙溶液和0.5％玉米淀粉的混合溶液；
(4)卷边。
(5)将卷边后的带有手套的手模浸渍在总固体含量3％聚氨酯乳液中10秒，放入80℃的烘箱中烘15分钟；
(6)沥滤：产品在卷边后在80℃水中进行沥滤，沥滤时间30秒；
(7)烘干温度80℃，烘干时间10分钟，脱模；
(8)步骤(7)脱模后的手套在抗静电剂溶液中进行泡洗20分钟，再用干衣机在70℃条件下烘20分钟，得到防静电胶乳手套。
实施例2
防静电胶乳手套的原料重量组成如下：
所述的防静电剂为离子型抗静电剂中的二烷基磷酸盐。
所述的硫化剂为硫磺、二硫化四甲基秋兰姆；
所述的促进剂为二乙基二硫代氨基甲酸锌；
所述的防老剂为甲叉-4426-S、4，4’-双(二甲基苄基)二苯胺；
所述的稳定剂为酪素。
防静电胶乳手套制作方法步骤如下：
(1)材料配制：配制凝固剂、抗静电剂溶液、天然胶乳和聚氨酯乳液；
(2)清洗手套模具：将手模先在酸性洗模液中清洗，再在碱性洗模液中清洗，然后用清水漂洗干净，在70℃烘箱中烘15分钟；酸性洗模液为质量分数在1％的盐酸溶液；碱性洗模液为质量分数在1％的氢氧化钠溶液；
(3)浸渍：将清洗干净的手模浸渍在凝固剂溶液中40秒，放入80℃的烘箱中烘20分钟；将带有凝固剂的手模浸渍在总固体含量在30％的天然胶乳中15秒，放入100℃的烘箱中烘20分钟；凝固剂为质量分数为10％硝酸钙溶液、10％氯化钙溶液和3％玉米淀粉的混合溶液；
(4)卷边。
(5)将卷边后的带有手套的手模浸渍在总固体含量5％聚氨酯乳液中20秒，放入100℃的烘箱中烘20分钟；
(6)沥滤：产品在卷边后在85℃水中进行沥滤，沥滤时间45秒；
(7)烘干温度100℃，烘干时间15分钟，脱模；
(8)步骤(7)脱模后的手套在抗静电剂溶液中进行泡洗30分钟，再用干衣机在85℃条件下烘30分钟，得到防静电胶乳手套。
实施例3
防静电胶乳手套的原料重量组成如下：
所述的防静电剂为烷基二甲基胺乙内盐；
所述的硫化剂为硫磺、二硫化吗啡啉；
所述的促进剂为乙基-苯基-二硫代氨基甲酸锌；
所述的防老剂为甲叉-4426-S、4，4’-双(二甲基苄基)二苯胺；
所述的稳定剂为酪素、氨水。
具体制备该手套的步骤如下：
(1)材料配制：配制凝固剂、抗静电剂溶液、天然胶乳和聚氨酯乳液；
(2)清洗手套模具：将手模先在酸性洗模液中清洗，再在碱性洗模液中清洗，然后用清水漂洗干净，在80℃烘箱中烘20分钟；酸性洗模液为质量分数在5％的盐酸溶液；碱性洗模液为质量分数在5％的氢氧化钠溶液；
(3)浸渍：将清洗干净的手模浸渍在凝固剂溶液中60秒，放入100℃的烘箱中烘25分钟；将带有凝固剂的手模浸渍在总固体含量在40％的天然胶乳中25秒，放入120℃的烘箱中烘30分钟；凝固剂为质量分数为15％硝酸钙溶液、15％氯化钙溶液和5％玉米淀粉的混合溶液；
(4)卷边；
(5)将卷边后的带有手套的手模浸渍在总固体含量10％聚氨酯乳液中30秒，放入120℃的烘箱中烘30分钟；
(6)沥滤：产品在卷边后在95℃水中进行沥滤，沥滤时间60秒；
(7)烘干温度120℃，烘干时间20分钟，脱模；
(8)步骤(7)脱模后的手套在抗静电剂溶液中进行泡洗60分钟，再用干衣机在100℃条件下烘40分钟，得到防静电胶乳手套。
该防静电胶乳手套无氯元素大幅减少手套对精密电子产品的氧化，胶乳手套防静电性能增强了20％～50％，采用PU对手套表面进行处理，方便穿戴，低粉量降低到2毫克以下，起到保护产品、人体手部和洁净室环境的目的。
Claims (2)
1.一种防静电胶乳手套，其特征在于防静电胶乳手套的原料重量组成如下：
所述的抗静电剂为铵盐、二烷基磷酸盐或烷基二甲基胺乙内盐；
所述的硫化剂为硫磺、二硫化四甲基秋兰姆、二硫化吗啡啉中的一种以上；
所述的促进剂为乙基-苯基-二硫代氨基甲酸锌、二乙基二硫代氨基甲酸锌中的一种以上；
所述的防老剂为2，6-二叔丁基-4-甲基苯酚、甲叉-4426-S、4，4’-双(二甲基苄基)二苯胺中的一种以上；
所述的稳定剂为酪素、氨水、氢氧化钾中的一种以上。
2.根据权利要求1所述的一种防静电胶乳手套，其特征在于，防静电胶乳手套制作方法步骤如下：
(1)材料配制：配制凝固剂为质量分数为5％～15％硝酸钙溶液、5％～15％氯化钙溶液和0.5％～5％玉米淀粉的混合溶液、0.5％～2％抗静电剂溶液、总固体含量20％～40％天然胶乳、总固体含量3％～10％聚氨酯乳液；
(2)清洗手套模具：将手模先在酸性洗模液中清洗，再在碱性洗模液中清洗，然后用清水漂洗干净，在60～80℃烘箱中烘10～20分钟；酸性洗模液为质量分数在0.5％～5％的盐酸溶液、硫酸溶液、硝酸溶液中的一种以上；碱性洗模液为质量分数在0.5％～5％的氢氧化钠溶液、氢氧化钾溶液中的一种以上；
(3)浸渍：将清洗干净的手模浸渍在凝固剂溶液中20～60秒，放入60～100℃的烘箱中烘15～25分钟；将带有凝固剂的手模浸渍在总固体含量为20％～40％的天然胶乳中10～25秒，放入80～120℃的烘箱中烘15～30分钟；凝固剂质量分数为5％～15％硝酸钙溶液、5％～15％氯化钙溶液和0.5％～5％玉米淀粉的混合溶液；
(4)卷边；
(5)将卷边后的带有手套的手模浸渍在总固体含量为3％～10％聚氨酯乳液中10～30秒，放入80～120℃的烘箱中烘15～30分钟；
(6)沥滤：产品在卷边后在80～95℃水中进行沥滤，沥滤时间30～60秒；
(7)烘干温度80℃～120℃，烘干时间10分钟～20分钟，脱模；
(8)步骤(7)脱模后的手套在抗静电剂溶液中进行泡洗20～60分钟，再用干衣机在70～100℃条件下烘20～40分钟，得到防静电胶乳手套。