CN111303682A - 金属氟碳漆专用柔性腻子粉 - Google Patents
金属氟碳漆专用柔性腻子粉 Download PDFInfo
- Publication number
- CN111303682A CN111303682A CN202010311491.7A CN202010311491A CN111303682A CN 111303682 A CN111303682 A CN 111303682A CN 202010311491 A CN202010311491 A CN 202010311491A CN 111303682 A CN111303682 A CN 111303682A
- Authority
- CN
- China
- Prior art keywords
- powder
- fluorocarbon paint
- special
- metal fluorocarbon
- flexible putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于建筑材料技术领域,具体涉及一种金属氟碳漆专用柔性腻子粉。本发明金属氟碳漆专用柔性腻子粉,由以下重量百分比的组分组成:白水泥17.5~20%,提钛尾渣7.5~10%,灰钙粉12~15%,石英粉30~34%,重钙粉18~20%,滑石粉5~6%,羟丙基甲基纤维素0.56~0.8%,柔性乳胶粉0.56~0.8%,木质纤维0.5~0.6%,淀粉醚0.05~0.1%,丙二醇0.8~1%。本发明腻子粉用于金属氟碳漆,解决了墙面开裂、脱落等问题。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种金属氟碳漆专用柔性腻子粉。
背景技术
随着建筑业的逐年发展,外墙涂料的使用量越来越大。其中,金属氟碳漆以优异的金属装饰性、防水性、耐久性、清洁性和高的性价比,从众多外墙涂料中脱颖而出,受到了各界用户的青睐。金属氟碳漆的应用,可有效地解决旧建筑外墙装饰功能性和持久性不强的问题。市面现有普通外墙柔性腻子的主要成分为:水泥25~30%,灰钙粉5~8%,石英砂40~45%,重钙粉20~25%,羟丙基甲基纤维素4.5~5.5‰,柔性乳胶粉4.5~5.5‰,木质纤维6~8‰,淀粉醚0.3~0.8‰,但是腻子的粘接强度不足,随着时间的推移,会造成金属氟碳漆外墙面开裂、脱落等现象的发生。
发明内容
本发明所要解决的技术问题是提供一种金属氟碳漆专用柔性腻子粉,由以下重量百分比的组分组成:白水泥17.5~20%,提钛尾渣7.5~10%,灰钙粉12~15%,石英粉30~34%,重钙粉18~20%,滑石粉5~6%,羟丙基甲基纤维素0.56~0.8%,柔性乳胶粉0.56~0.8%,木质纤维0.5~0.6%,淀粉醚0.05~0.1%,丙二醇0.8~1%。
具体的,上述金属氟碳漆专用柔性腻子粉中,所述提钛尾渣为高温碳化-低温氯化工艺产生的高钛型高炉渣经提钛后所产生的尾渣。主要成分为Al2O3 51~53%,CaO 21~23%。
优选的,上述金属氟碳漆专用柔性腻子粉中,所述白水泥为42.5R白水泥。
优选的,上述金属氟碳漆专用柔性腻子粉中,所述提钛尾渣的粒度为325~400目。更优选350目。
优选的,上述金属氟碳漆专用柔性腻子粉中,所述灰钙粉的粒度为170~230目。更优选200目。
优选的,上述金属氟碳漆专用柔性腻子粉中,所述石英粉的粒度为80~120目。更优选120目。
优选的,上述金属氟碳漆专用柔性腻子粉中,所述重钙粉的粒度为170~230目。更优选200目。
本发明金属氟碳漆专用柔性腻子粉,在外墙柔性腻子的基础上进行了改进,加入了提钛尾渣。加入提钛尾渣的腻子干燥后强度有了大幅度提升,也可有效提高漆膜对腻子层的吸附能力,解决了墙面开裂、脱落的问题,施工性能更好。
具体实施方式
本发明金属氟碳漆专用柔性腻子粉,由以下重量百分比的组分组成:白水泥17.5~20%,提钛尾渣7.5~10%,灰钙粉12~15%,石英粉30~34%,重钙粉18~20%,滑石粉5~6%,羟丙基甲基纤维素0.56~0.8%,柔性乳胶粉0.56~0.8%,木质纤维0.5~0.6%,淀粉醚0.05~0.1%,丙二醇0.8~1%。
本发明提钛尾渣是利用攀钢开发的“高温碳化-低温选择性氯化”工艺,从现行工艺条件下产生特有的高钛型高炉渣经1600~1800℃高温提取钛,经研磨后形成的产物。主要成分为Al2O3含量51~53%,CaO含量21~23%,其物相主要为铝酸钙、尖晶石,是一种潜在的含铝资源。其主要成分详见表1:
表1攀钢提钛尾渣化学成分%
成分 | SiO<sub>2</sub> | Al<sub>2</sub>O<sub>3</sub> | CaO | MgO | Fe | TiO<sub>2</sub> | S |
含量 | 3.4~3.5 | 51~53 | 21~23 | 1~1.4 | 0.4~0.5 | 1~1.2 | 0.25~0.35 |
本发明金属氟碳漆专用柔性腻子粉配方中添加提钛尾渣,提钛尾渣中含有二氧化硅、三氧化二铝、氧化钙、氧化镁、二氧化钛等成分。二氧化硅为酸性氧化物,呈白色粉末,其分子状态呈三维链状结构,相互聚集的氢键之间可在外部剪切力消除后迅速复原,有较高的强度和延伸率,可有效防止腻子层开裂、脱落。三氧化二铝为两性氧化物,强度很高,可提高腻子强度。氧化钙是一种无机化合物,呈白色粉末,遇水后生成氢氧化钙,是很好的胶凝材料,在建筑行业中应用广泛。氧化镁是一种离子化合物,具有碱性氧化物的通性,属于胶凝材料,可与氧化钙结合,提高腻子的粘接强度。二氧化钛为白色粉末的两性氧化物,有很好的紫外线掩蔽作用。TiO2中Ti-O键的极性较大,表面吸附的水因极化发生解离,容易形成羟基,这种表面羟基可提高TiO2作为吸附剂及各种单体的性能,为表面改性提供方便。本发明通过对各组分含量进行调整和优化,使金属氟碳漆专用腻子具有良好的粘接强度、硬度以及优异的施工性能。
本发明金属氟碳漆专用柔性腻子粉在使用时,将除提钛尾渣之外的所有成分混合,加入适量水混合混匀,静置后再加入提钛尾渣,再充分混合即可。
进一步的,在使用时,将除提钛尾渣之外的所有成分混合后按照2.5~2.8﹕1的质量比加入水(即2.5~2.8kg除提钛尾渣之外的原料加入1kg水),搅拌至充分均匀,静置5~10分钟后再加入提钛尾渣,充分搅拌至充分均匀,以充分发挥提钛尾渣的使用性能。
实施例
表2
对本发明实施例和对比例的性能进行测试,测试方法为《外墙柔性腻子》GB/T23455-2009,结果见下表3。
表3
同时,本发明与对比例起皮、褶皱、开裂、脱落情况见下表4:
表4
序号 | 缺陷名称 | 普通外墙柔性腻子 | 本发明金属氟碳漆专用柔性腻子 | 备注 |
1 | 起皮 | 8处 | 2处 | 每1000㎡ |
2 | 褶皱 | 10处 | 1处 | 每1000㎡ |
3 | 开裂 | 12处 | 2处 | 每1000㎡ |
4 | 脱落 | 10处 | 1处 | 每1000㎡ |
可见,本发明金属氟碳漆专用腻子粉具有良好的效果。
Claims (8)
1.金属氟碳漆专用柔性腻子粉,其特征在于:由以下重量百分比的组分组成:白水泥17.5~20%,提钛尾渣7.5~10%,灰钙粉12~15%,石英粉30~34%,重钙粉18~20%,滑石粉5~6%,羟丙基甲基纤维素0.56~0.8%,柔性乳胶粉0.56~0.8%,木质纤维0.5~0.6%,淀粉醚0.05~0.1%,丙二醇0.8~1%。
2.根据权利要求1所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述提钛尾渣为高温碳化-低温氯化工艺产生的高钛型高炉渣经提钛后所产生的尾渣。
3.根据权利要求1或2所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述提钛尾渣主要成分为Al2O3 51~53%,CaO 21~23%。
4.根据权利要求1~3任一项所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述白水泥为42.5R白水泥。
5.根据权利要求1~4任一项所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述提钛尾渣的粒度为325~400目;优选350目。
6.根据权利要求1~5任一项所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述灰钙粉的粒度为170~230目;优选200目。
7.根据权利要求1~6任一项所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述石英粉的粒度为80~120目;优选120目。
8.根据权利要求1~7任一项所述的金属氟碳漆专用柔性腻子粉,其特征在于:所述重钙粉的粒度为170~230目;优选200目。