CN103030346A - 外墙装饰砂浆 - Google Patents
外墙装饰砂浆 Download PDFInfo
- Publication number
- CN103030346A CN103030346A CN201210471387XA CN201210471387A CN103030346A CN 103030346 A CN103030346 A CN 103030346A CN 201210471387X A CN201210471387X A CN 201210471387XA CN 201210471387 A CN201210471387 A CN 201210471387A CN 103030346 A CN103030346 A CN 103030346A
- Authority
- CN
- China
- Prior art keywords
- parts
- decorative mortar
- cement
- mortar
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及建筑材料领域,具体涉及一种高性能的外墙装饰砂浆;包括如下质量份的组分,水泥100份、石英砂200份、水29份、减水剂1~2份、乳胶粉2~3.5份、锂蒙脱石1~2份、纤维素醚0.02~0.15份和消泡剂0.35~0.5份;经测试表明本发明的外墙装饰砂浆,构成简单、成本低、物理力学性能好、不易损坏、使用寿命长。
Description
技术领域
本发明涉及建筑材料领域,具体涉及一种高性能的外墙装饰砂浆。
背景技术
随着我国国力的增强,城市化进程加快,房地产和建筑行业在近些年就有了飞速的发展,人们对建筑物外墙装饰的需求也越来越高。
外墙装饰基本上以三大类材料为主,一是陶瓷质贴面墙砖,二是外墙涂料,三是外墙装饰砂浆,前两类材料存在成本高、耐受性差、易脱落、变色、质感不强等缺点,有逐步被外墙装饰砂浆替代的趋势,外墙装饰砂浆是一种具有装饰效果的墙面抹灰材料的总称。主要是由水泥、砂、石灰、石膏、钙粉、黏土等无机天然材料构成,添加一定量的矿物颜料。施工工艺可采用喷、涂、抹等方法,展现出丰富多彩的饰面效果,真正实现现代技术与理想艺术的完美融合,提升建筑的品位和价值。
如中国授权专利ZL200810004309.2公开了一种外墙装饰砂浆,采用粉煤灰、白水泥、水渣、熟石灰、甲基纤维素、碳酸钙、乳胶粉、钛白粉、消泡剂按照一定的比例混合制得。其虽然在一定程度上满足了人们对与外墙装饰的需求,但是其仍在存着着如下的一些不足:组分和配比的选定存在较大的复杂性,部分组分对其他行业具有较大依赖性,且外墙装饰砂浆成型后的物理力学性能不佳,特别是抗压、抗折强度和拉伸粘结强度不高,易由于外力的作用损坏,使用寿命不长。
发明内容
本发明要解决的技术问题是提供一种构成简单、成本低、物理力学性能好、不易损坏、使用寿命长的外墙装饰砂浆。
为了实现上述目的,本发明提供一种外墙装饰砂浆,包括如下质量份的组分,水泥100份、石英砂200份、水29份、减水剂1~2份、乳胶粉2~3.5份、锂蒙脱石1~2份、纤维素醚0.02~0.15份和消泡剂0.35~0.5份。
作为优选方案,根据实验效果,选择限定所述各组分的质量份如下:水泥100份、石英砂200份、水29份、减水剂1~1.5份、乳胶粉2.3~3.1份、锂蒙脱石1~1.5份、纤维素醚0.04~0.1份和消泡剂0.4~0.5份。
作为优选方案,根据实验的最佳效果,限定所述各组分的质量份如下:水泥100份、石英砂200份、水29份、减水剂1.2份、乳胶粉2.5份、锂蒙脱石1.2份、纤维素醚0.05份和消泡剂0.5份。
其中,1,水泥作为胶凝材料,通常可采用普通硅酸盐水泥、铝酸盐水泥、硫铝酸盐水泥等或普硅酸盐水泥掺加少量的铝酸盐水泥,硫铝酸盐水泥等,处于装饰效果的需要最好选择白水泥;2,石英砂作为装饰性集料,根据需求也可以将碎石、彩釉砂等装饰性集料,石英砂粒度的选择优选遵循以下条件,10~20目的占所选石英砂质量的10%,20~40目的占30%,40~80目的占50%,80~120目的占10%;3,减水剂选择聚羧酸减水剂,其与不同种类的水泥均具有较好的相容性,即使在低掺量时,也能使混凝土具有高流动性,并且在低水灰比时具有低粘度和良好的保坍性能,是配制装饰砂浆较好选择;4,乳胶粉作为聚合物外加剂,均匀掺入乳胶粉以后,砂浆的抗拉强度、弹性、柔性和封闭性均有提高;5,锂蒙脱石的加入可以提高砂浆的润滑性,很好的延长可操作时间,便于砂浆的涂抹;6,纤维素醚对砂浆具有良好的保水和增稠效果,保水作用使砂浆在使用过程中不会因为缺水而导致水泥水化不完全而使表面起粉,增稠作用则能是砂浆的结构强度大大增强,明显改善砂浆的黏性,但是过量的话会影响浆体孔结构,使硬化水泥浆体内部疏松多孔而导致强度降低;7,消泡剂:消泡剂的作用是进行消泡,消除高分子材料引人或拌合时搅拌造成的气泡,消泡剂消除砂浆内部封闭的气泡,从而改善了砂浆孔隙结构,降低了砂浆的空隙率,消泡剂还可以有效地控制砂浆的含气量,而砂浆内部有合适的含气量不仅可以提高砂浆的工作性,还可以改善其抗渗、抗冻和耐久性能等性能。
此外根据装饰的需要还可以在外墙装饰砂浆中加入适量的着色剂,制作五颜六色、绚丽多彩的外墙装饰,由于氧化铁颜料具有优良的着色和应用性能,价格便宜,又具有吸收紫外线而保护应用体系中的基料不发生降解的优点,本发明采用氧化铁颜料为着色剂。由于采用了适当比例范围的乳胶粉、纤维素醚和消泡剂,本发明的外墙装饰砂浆,构成简单、成本低、物理力学性能好、不易损坏、使用寿命长。
具体实施方式
本发明实施例外墙装饰砂浆,包括如下质量份的组分:
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 | |
水泥 | 100 | 100 | 100 | 100 | 100 | 100 |
石英砂 | 200 | 200 | 200 | 200 | 200 | 200 |
水 | 29 | 29 | 29 | 29 | 29 | 29 |
减水剂 | 1 | 2 | 1.5 | 1.7 | 2.4 | 1.2 |
乳胶粉 | 3.5 | 2 | 3 | 2.3 | 3.1 | 2.5 |
锂蒙脱石 | 1.3 | 1 | 1.8 | 1.5 | 2 | 1.2 |
纤维素醚 | 0.02 | 0.04 | 0.1 | 0.04 | 0.15 | 0.05 |
消泡剂 | 0.4 | 0.35 | 0.5 | 0.45 | 0.48 | 0.5 |
根据外墙的颜色的深浅需求,可以适当添加着色剂,本实验的各实施例中水泥选用上海爱嘉装饰生成的Q/YLB1-2008白水泥,强度为32.5、细度≥120目;石英砂粒度的选择遵循以下条件,10~20目的占所选石英砂质量的10%,20~40目的占30%,40~80目的占50%,80~120目的占10%;减水剂选择重庆科之杰新材料公司生产的聚羧酸高效减水剂,其固含量在23%左右;纤维素醚为重庆科之杰新材料公司生产;消泡剂采用P818有机硅类消泡剂;乳胶粉为行业常用的普通乳胶粉。
以实施例6的组分及配方为例,将其混合并搅拌均匀,按照JC/T 1024-2007标准实验测试得出本发明外墙装饰砂浆的物理力学性能如下表:
由上表的数据分析可见采用本发明组分和配比的外墙装饰砂浆制作的外墙完全满足JC/T 1024-2007标准的要求,而且其构成简单、成本低、物理力学性能好、不易损坏、使用寿命长。
以上所述的仅是本发明的部分优选实施方式,应当指出,对于本领域的技术人员来说,在不脱离本发明组分及配比的前提下,还可以作出若干改进,这些也应该视为本发明的保护范围。
Claims (3)
1.一种外墙装饰砂浆,其特征在于:包括如下质量份的组分,水泥100份、石英砂200份、水29份、减水剂1~2份、乳胶粉2~3.5份、锂蒙脱石1~2份、纤维素醚0.02~0.15份和消泡剂0.35~0.5份。
2.根据权利要求1所述的外墙装饰砂浆,其特征在于: 所述各组分的质量份如下:水泥100份、石英砂200份、水29份、减水剂1~1.5份、乳胶粉2.3~3.1份、锂蒙脱石1~1.5份、纤维素醚0.04~0.1份和消泡剂0.4~0.5份。
3.根据权利要求1所述的外墙装饰砂浆,其特征在于: 所述各组分的质量份如下:水泥100份、石英砂200份、水29份、减水剂1.2份、乳胶粉2.5份、锂蒙脱石1.2份、纤维素醚0.05份和消泡剂0.5份。