CN102206072A - 一种新型高炉矿渣基保温干粉的配方设计 - Google Patents

一种新型高炉矿渣基保温干粉的配方设计 Download PDF

Info

Publication number
CN102206072A
CN102206072A CN2011100686629A CN201110068662A CN102206072A CN 102206072 A CN102206072 A CN 102206072A CN 2011100686629 A CN2011100686629 A CN 2011100686629A CN 201110068662 A CN201110068662 A CN 201110068662A CN 102206072 A CN102206072 A CN 102206072A
Authority
CN
China
Prior art keywords
furnace slag
thermal
formula
blast
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011100686629A
Other languages
English (en)
Inventor
李政平
仪旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANG HAI QIPA ENVIRONMENTAL TECH CO LTD
Original Assignee
SHANG HAI QIPA ENVIRONMENTAL TECH CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANG HAI QIPA ENVIRONMENTAL TECH CO LTD filed Critical SHANG HAI QIPA ENVIRONMENTAL TECH CO LTD
Priority to CN2011100686629A priority Critical patent/CN102206072A/zh
Publication of CN102206072A publication Critical patent/CN102206072A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型高炉矿渣基保温干粉的配方设计,属于建筑节能保温材料技术领域。配方设计包括以下组成部分:(1)高炉矿渣;(2)增强料;(3)钙化剂;(4)保温填充料;(5)稠化剂。本发明采用特殊的配方设计,设计成分简单,生产过程简易,使用成本低廉的高炉矿渣为基料,减少废弃排放,变废为宝,实现环境友好型可循环工业,在配方中添加无机保温填充料,绿色环保,高效节能,配方产品与水混合后可成为优质保温砂浆。干粉密度为1.7-1.8g/cm3,凝固后抗压强度达到10MPa,平均导热系数为0.045w/(m.k)。

Description

一种新型高炉矿渣基保温干粉的配方设计
技术领域
[0001] 本发明涉及一种新型高炉矿渣基保温干粉的配方设计,属于建筑节能保温材料技术领域。
背景技术
[0002] 干粉砂浆是指经干燥筛分处理的骨料(如石英砂)、无机胶凝材料(如水泥)和添加剂(如聚合物)等按一定比例进行物理混合而成的一种颗粒状或粉状,以袋装或散装的形式运至工地,加水拌和后即可直接使用的物料。又称作砂浆干粉料、干混料、干拌粉,有些建筑黏合剂也属于此类。干粉砂浆在建筑业中以薄层发挥粘结、衬垫、防护和装饰作用,建筑和装修工程应用极为广泛。
[0003] 传统的干粉一般都是用作粘结和装饰,功能较为单一。砂浆品种不丰富。国外已经开发了逾千种的干粉砂浆品种,而我国则还不到百种,因此在使用中出现砂浆不配套、不满足功能的现象,给砂浆的推广使用带来极为不利的影响。
[0004] 本发明采用特殊的配方设计,设计成分简单,生产过程简易,使用成本低廉的高炉矿渣为基料,减少废弃排放,变废为宝,实现环境友好型可循环工业,在配方中添加无机保温填充料,绿色环保,高效节能,配方产品与水混合后可成为优质保温砂浆。干粉密度为 1. 7-1. 8g/cm3,凝固后抗压强度达到lOMPa,平均导热系数为0. 045w/(m. k)。
发明内容
[0005] 本发明的目的在于提供一种新型高炉矿渣基保温干粉的配方。
[0006] 1. 一种新型高炉矿渣基保温干粉的配方,包括如下组成部分:
[0007] (1)高炉矿渣;
[0008] (2)增强料;
[0009] (3)钙化剂;
[0010] (4)保温填充料;
[0011] ⑶稠化剂。
[0012] 2.高炉矿渣为酸性矿渣,规格如下:
[0013] Al2O3 含量彡 30%,CaO 含量彡 20% ;
[0014] 粉碎后细度(0. 08mm方孔筛筛余)3-30% ;
[0015] 3.增强料为水泥,其规格为52. 5级普通硅酸盐水泥。
[0016] 4.钙化剂为石灰,有效氧化钙含量在65%-80%之间。
[0017] 5.保温填充料包括珍珠岩,海泡石,蛭石,玻璃微珠等,填充料粉末直径在 50-70um。
[0018] 6.稠化剂包括天然石膏,氟石膏,钛白石膏,磷石膏等。
[0019] 7.各组分质量百分比如下:
[0020]高炉矿渣,40-50% ;[0021]增强料,20-¾%;
[0022]钙化剂,10-15%;
[0023] 保温填充料,8-10%;
[0024]稠化剂,3_5%。
具体实施方式
[0025] 通过以下的实施例将进一步理解本发明,但不能限定本发明的内容。
[0026] 实施例1
[0027] 一种新型高炉矿渣基保温干粉的配方:
[0028] 高炉矿渣,50%;
[0029] 52.5级普通硅酸盐水泥,20 % ;
[0030]石灰,15%;
[0031]海泡石,10%;
[0032]磷石膏,5%。
[0033] 实施例2
[0034] 一种新型高炉矿渣基保温干粉的配方:
[0035] 高炉矿渣,40%;
[0036] 52.5级普通硅酸盐水泥,20 % ;
[0037]石灰,10%;
[0038] 中空玻璃微珠,25%;
[0039] 钛白石膏,5%。

Claims (8)

1. 一种新型高炉矿渣基保温干粉的配方设计,其特征在于,包括如下组成部分:(1)高炉矿渣;(2)增强料;(3)钙化剂;(4)保温填充料;(5)稠化剂。
2.根据权利要求1所述的设计,其特征在于,在(1)中所述高炉矿渣为酸性矿渣,规格如下:Al2O3含量彡30%, CaO含量彡20% ; 粉碎后细度(0. 08mm方孔筛筛余)3-30% ;
3.根据权利要求1所述的设计,其特征在于,在O)中,所述增强料为水泥,其规格为 52. 5级普通硅酸盐水泥。
4.根据权利要求1所述的设计,其特征在于,在C3)中,所述钙化剂为石灰,有效氧化钙含量在65% -80%之间。
5.根据权利要求1所述的设计,其特征在于,在(4)中,保温填充料包括珍珠岩,海泡石,蛭石,玻璃微珠等,填充料粉末直径在50-70um。
6.根据权利要求1所述的设计,其特征在于,在(¾中,所用稠化剂包括天然石膏,氟石膏,钛白石膏,磷石膏等。
7.根据权利要求1所述的设计,各组分质量百分比如下: 高炉矿渣,40-50% ;增强料,20-25% ; 钙化剂,10-15% ; 保温填充料,8-10% ; 稠化剂,3-5%。
8.根据权利要求1〜7任一项所述对一种新型高炉矿渣基保温干粉的配方设计。
CN2011100686629A 2011-03-22 2011-03-22 一种新型高炉矿渣基保温干粉的配方设计 Pending CN102206072A (zh)