CN111139067A - 宽频梯度的led荧光粉的制备 - Google Patents
宽频梯度的led荧光粉的制备 Download PDFInfo
- Publication number
- CN111139067A CN111139067A CN202010002231.1A CN202010002231A CN111139067A CN 111139067 A CN111139067 A CN 111139067A CN 202010002231 A CN202010002231 A CN 202010002231A CN 111139067 A CN111139067 A CN 111139067A
- Authority
- CN
- China
- Prior art keywords
- preparation
- fluorescent powder
- led fluorescent
- broadband gradient
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
宽频梯度的LED荧光粉的制备及应用，它涉及LED荧光粉领域。它的制备方法包括十个步骤。采用上述技术方案后，本发明的有益效果为：制备得到的宽频梯度LED荧光粉更细腻，分散性好，堆积密度好，散射强度大，发光效率高，被激发后发出的光近似自然白光，发光均匀，并且生产成本低。
Description
技术领域
本发明涉及LED荧光粉领域，具体涉及宽频梯度的LED荧光粉的制备。
背景技术
LED照明（半导体照明）被认为是人类的照明革命，其发光原理与白炽灯和节能灯有着本质的差别，其技术缓解涵盖：1、LED外延片技术；2、LED芯片技术；3、LED荧光粉及封装技术；4、LED分选技术；5、半导体照明灯具及光学系统技术；6、半导体照明电源及控制技术。其中，外延片、芯片技术及荧光粉技术系LED的关键技术所在，决定着LED照明产品的质量、性价比和应用。
近些年来，随着白光照明显色性要求的不断提高，液晶显示器及要求高显色性的照明 领域特别是液晶LED电视的迅速发展，要求LED发光具有高色彩表现性，用紫外或深紫外LED激发三种或多种荧光粉的混合物、由红绿蓝三色LED芯片组装形成白光照明光源 等方法成为研究人员努力的方向。然而，基于红绿蓝三色LED芯片混合产生白光的途径 存在白光颜色随温度和时间的变化而退化或不稳定、混合过程复杂、黄-绿颜色之间有间 隙等缺点，使其发展受到一定的限制。
目前市面上现有的宽频梯度的LED荧光粉制备技术不够完善，得到的LED荧光粉不够细腻，导致运用时发光不够均匀，且成本较高，因此需要新的宽频梯度的LED荧光粉的制备技术。
发明内容
本发明的目的在于针对现有技术的缺陷和不足，提供宽频梯度的LED荧光粉的制备及应用，制备得到的宽频梯度LED荧光粉更细腻，分散性好，堆积密度好，散射强度大，发光效率高，被激发后发出的光近似自然白光，发光均匀，并且生产成本低。
为实现上述目的，本发明采用以下技术方案是：它的制备方法包括以下步骤：步骤一，按照所需制备的荧光粉各组分的摩尔比，分别称取相应原材料，制成原料母液；步骤二，将和分别溶于浓盐酸配制成0.1mol/L的和溶液；步骤三，按化学计量式比量取、、和溶液充分混合，搅拌30-60min，得到混合物A；步骤四，将原料母液加入过量的混合物A中，使其充分反应，得到反应溶液；步骤五，控制反应溶液的温度在25-85℃之间，陈化12-24h；步骤六，在陈化后的反应溶液中加入分散剂，并通过改变的掺杂量调节荧光粉的发光效率，经离心、过滤、洗涤、干燥得到组分均一的前驱沉淀物；步骤七，将步骤六中得到的干燥前驱沉淀物放入箱式高温烧结炉并通入还原性气体，在800-1000℃环境下煅烧1.5-3h，保温3-6h，结束后在还原性气体氛围下冷却至室温；步骤八，取出煅烧物，将其粉碎、过筛去除大颗粒，得到白色粉末；步骤九，白色粉末与纯净水或有机溶剂混合得到浆料，接着经过洗涤、过滤得到膏状荧光体；步骤十，膏状荧光体经过干燥、冷却后研磨并过筛得到所需目数的LED荧光粉。
宽频梯度的LED荧光粉可应用于节能、经济环保型照明灯、大屏幕显示、手机及数码小计、军用等领域。
所述步骤三中搅拌速度为400-800rpm。
所述的步骤五中反应溶液的PH值控制在8-10之间。
所述的步骤六中离心速度为4500-7000rpm。
所述的步骤七中还原性气体为惰性气体或氢气与惰性气体的混合物。
所述的步骤八中分散剂由聚乙烯酸、乙醇、聚乙二醇400、聚乙二醇600中的一种或多种组成。
采用上述技术方案后，本发明有益效果为：制备得到的宽频梯度LED荧光粉更细腻，分散性好，堆积密度好，散射强度大，发光效率高，被激发后发出的光近似自然白光，发光均匀，并且生产成本低。
具体实施方式
本具体实施方式采用的技术方案是：它的制备方法包括以下步骤：步骤一，按照所需制备的荧光粉各组分的摩尔比，分别称取相应原材料，制成原料母液；步骤二，将和分别溶于浓盐酸配制成0.1mol/L的和溶液；步骤三，按化学计量式比量取、、和溶液充分混合，搅拌30-60min，得到混合物A；步骤四，将原料母液加入过量的混合物A中，使其充分反应，得到反应溶液；步骤五，控制反应溶液的温度在25-85℃之间，陈化12-24h；步骤六，在陈化后的反应溶液中加入分散剂，并通过改变的掺杂量调节荧光粉的发光效率，经离心、过滤、洗涤、干燥得到组分均一的前驱沉淀物；步骤七，将步骤六中得到的干燥前驱沉淀物放入箱式高温烧结炉并通入还原性气体，在800-1000℃环境下煅烧1.5-3h，保温3-6h，结束后在还原性气体氛围下冷却至室温；步骤八，取出煅烧物，将其粉碎、过筛去除大颗粒，得到白色粉末；步骤九，白色粉末与纯净水或有机溶剂混合得到浆料，接着经过洗涤、过滤得到膏状荧光体；步骤十，膏状荧光体经过干燥、冷却后研磨并过筛得到所需目数的LED荧光粉。
宽频梯度的LED荧光粉可应用于节能、经济环保型照明灯、大屏幕显示、手机及数码小计、军用等领域。
所述步骤三中搅拌速度为400-800rpm。
所述的步骤五中反应溶液的PH值控制在8-10之间。
所述的步骤六中离心速度为4500-7000rpm。
所述的步骤七中还原性气体为惰性气体或氢气与惰性气体的混合物。
所述的步骤八中分散剂由聚乙烯酸、乙醇、聚乙二醇400、聚乙二醇600中的一种或多种组成。醇类是一种良好的分散剂，可以使各种不同组分混合物均匀，使用成本不高。
采用上述技术方案后，本发明有益效果为：制备得到的宽频梯度LED荧光粉更细腻，分散性好，堆积密度好，散射强度大，发光效率高，被激发后发出的光近似自然白光，发光均匀，并且生产成本低。
以上所述，仅用以说明本发明的技术方案而非限制，本领域普通技术人员对本发明的技术方案所做的其它修改或者等同替换，只要不脱离本发明技术方案的精神和范围，均应涵盖在本发明的权利要求范围当中。
Claims (7)
1.宽频梯度的LED荧光粉的制备，其特征在于它包括以下步骤：步骤一，按照所需制备的荧光粉各组分的摩尔比，分别称取相应原材料，制成原料母液；步骤二，将和分别溶于浓盐酸配制成0.1mol/L的和溶液；步骤三，按化学计量式比量取、、和溶液充分混合，搅拌30-60min，得到混合物A；步骤四，将原料母液加入过量的混合物A中，使其充分反应，得到反应溶液；步骤五，控制反应溶液的温度在25-85℃之间，陈化12-24h；步骤六，在陈化后的反应溶液中加入分散剂，并通过改变的掺杂量调节荧光粉的发光效率，经离心、过滤、洗涤、干燥得到组分均一的前驱沉淀物；步骤七，将步骤六中得到的干燥前驱沉淀物放入箱式高温烧结炉并通入还原性气体，在800-1000℃环境下煅烧1.5-3h，保温3-6h，结束后在还原性气体氛围下冷却至室温；步骤八，取出煅烧物，将其粉碎、过筛去除大颗粒，得到白色粉末；步骤九，白色粉末与纯净水或有机溶剂混合得到浆料，接着经过洗涤、过滤得到膏状荧光体；步骤十，膏状荧光体经过干燥、冷却后研磨并过筛得到所需目数的LED荧光粉。
2.宽频梯度的LED荧光粉的应用，其特征在于它可应用于以下领域：节能、经济环保型照明灯、大屏幕显示、手机及数码小计、军用等领域。
3.根据权利要求1所述的宽频梯度的LED荧光粉的制备，其特征在于：所述步骤三中搅拌速度为400-800rpm。
4.根据权利要求1所述的宽频梯度的LED荧光粉的制备，其特征在于：所述的步骤五中反应溶液的PH值控制在8-10之间。
5.根据权利要求1所述的宽频梯度的LED荧光粉的制备，其特征在于：所述的步骤六中离心速度为4500-7000rpm。
6.根据权利要求1所述的宽频梯度的LED荧光粉的制备，其特征在于：所述的步骤七中还原性气体为惰性气体或氢气与惰性气体的混合物。
7.根据权利要求1所述的宽频梯度的LED荧光粉的制备，其特征在于：所述的步骤八中分散剂由聚乙烯酸、乙醇、聚乙二醇400、聚乙二醇600中的一种或多种组成。