CN110773156A - 一种过渡金属单原子催化剂、其制备方法及应用 - Google Patents
一种过渡金属单原子催化剂、其制备方法及应用 Download PDFInfo
- Publication number
- CN110773156A CN110773156A CN201911141682.7A CN201911141682A CN110773156A CN 110773156 A CN110773156 A CN 110773156A CN 201911141682 A CN201911141682 A CN 201911141682A CN 110773156 A CN110773156 A CN 110773156A
- Authority
- CN
- China
- Prior art keywords
- transition metal
- peg
- preparation
- micromolecules
- boron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明实施例涉及一种过渡金属单原子催化剂、其制备方法及应用。该制备发方法包括下述步骤：将含氮小分子、含硼小分子、含氧分子和可溶性过渡金属盐溶于水中形成溶液；将溶液冷却、干燥、分散均匀后得到固体粉末；在保护性气体中碳化。本发明提供的制备方法中，通过选择特定的含氮小分子、含硼小分子、含氧分子，使得得到的过渡金属单原子催化剂的形貌是二维纳米片状结构和管状结构，与嵌在MOF微孔中的少量单原子位点相比，单原子位点在片状结构和管状结构上更加暴露，有利于催化活性的进一步提高；另外相对于MOF的原料而言，本发明制备方法中选择的特定原料廉价易得。
Description
技术领域
本发明涉及功能材料制备技术领域，具体涉及一种过渡金属单原子催化剂、其制备方法及应用。
背景技术
过渡金属单原子催化剂是指过渡金属以单原子形式均匀分散在载体上形成的具有优异催化性能的催化剂，近些年来受到了科学界和工业界的广泛关注。
现有技术在制备过渡金属单原子催化剂时，由于金属有机骨架(MOF)中的过渡金属节点是原子分散的，同时具备明确的配位环境，这使得其成为制备过渡金属单原子催化剂的理想模板，因此在制备过渡金属单原子催化剂时先液相制备MOF，然后将其碳化获得过渡金属单原子催化剂。然而，液相制备得到的MOF模板通常是三维的体相结构，最终碳化后得到的碳基单原子催化剂中大量的单原子位点是被包埋在体相结构内部的，仅有少量单原子位点暴露在碳载体表面，这实际上降低了金属组分的利用率，不利于催化活性的进一步提高；并且MOF中选取的特定配体通常价格高昂。研究人员一直在试图改进、替代上述方法。但总体上看，研究过渡金属单原子催化剂主要集中在如何精确地控制金属位点的局域配位环境、如何提高金属原子的负载量等方面，而很少考虑通过调节载体的结构和性质来实现过渡金属单原子位点的调控。
公开于该背景技术部分的信息仅仅旨在增加对本发明的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。
发明内容
发明目的
本发明的目的在于提供一种过渡金属单原子催化剂、其制备方法及应用。本发明提供的制备方法中，通过选择特定的含氮小分子、含硼小分子、含氧分子，使得得到的过渡金属单原子催化剂的形貌是二维纳米片状结构和管状结构，与嵌在MOF微孔中的少量单原子位点相比，单原子位点在片状结构和管状结构上更加暴露，有利于催化活性的进一步提高；另外相对于MOF的原料而言，本发明制备方法中选择的特定原料廉价易得。
解决方案
为实现本发明目的，本发明实施例提供了一种过渡金属单原子催化剂的制备方法，所述制备方法包括下述步骤：
将含氮小分子、含硼小分子、含氧分子和可溶性过渡金属盐溶于水中形成溶液；将溶液冷却、干燥、分散均匀后得到固体粉末；在保护性气体中碳化；其中：
所述含氮小分子选自三聚氰胺、双氰胺、尿素中的任意一种或多种；
所述含硼小分子选自硼酸、氧化硼中的任意一种或多种；
所述含氧分子选自聚乙二醇、聚乙烯醇中的一种或多种。
上述制备方法在一种可能的实现方式中，所述含氮小分子为尿素，所述含硼小分子为硼酸，所述含氧分子为聚乙二醇。
上述制备方法在一种可能的实现方式中，所述的聚乙二醇(PEG)包括：PEG-400、PEG-600、PEG-800、PEG-1000、PEG-2000、PEG-4000、PEG-6000、PEG-8000、PEG-10000中的一种或多种；可选地，所述聚乙二醇为PEG-2000或PEG-8000。
上述制备方法在一种可能的实现方式中，所述冷却为急速冷却；可选地，所述急速冷却的方式为置于液氮中。
上述制备方法在一种可能的实现方式中，所述的可溶性金属盐包括钒、铬、锰、铁、钴、镍、铜、钼、钌、铑、钯的硝酸盐、氯化物、醋酸盐、硫酸盐中的一种或多种；可选地包括RuCl3、FeCl3、Ni(NO3)2、Ag(NO3)2中的一种或多种；进一步可选地为RuCl3·H2O、FeCl3·6H2O、Ni(NO3)2·6H2O、Ag(NO3)2。
上述制备方法在一种可能的实现方式中，尿素、硼酸、聚乙二醇和过渡金属盐的用量比为(1-10g)：(0.05-0.5g)：(0.1-2g)：(0.005-0.5mmol)；可选地为(5-6g)：(0.15-0.2g)：(0.5-0.6g)：(0.01-0.015mmol)。
上述制备方法在一种可能的实现方式中，碳化的温度为600-1000℃，碳化的时间为4-8小时；可选地碳化的温度为800-900℃，碳化的时间为6小时。
上述制备方法在一种可能的实现方式中，所述的保护性气体为氮气(N2)、氩气(Ar)、氢氩混合气(H2/Ar)等的一种或多种。
上述制备方法在一种可能的实现方式中，干燥的的方式为冷冻干燥。
上述制备方法在一种可能的实现方式中，所述制备方法包括以下步骤：常温下将5-6g尿素、0.15-0.2g硼酸、0.5-0.6g聚乙二醇和0.01-0.015mmol过渡金属盐溶于水得到澄清均一的混合溶液，随后将该混合溶液置于液氮中冷却形成低温块体，并冷冻干燥除去水，然后通过研磨或球磨处理得到均匀的固体粉末；接着将所述固体粉末在惰性气体气氛中碳化。
本发明实施例还提供了上述制备方法制得的过渡金属单原子催化剂。
本发明实施例还提供了上述制备方法制得的过渡金属单原子催化剂在电催化析氢反应中的应用。
上述应用在一种可能的实现方式中，所述过渡金属单原子催化剂为管状结构。
有益效果
1)本发明提供的制备方法中，通过选择特定的含氮小分子、含硼小分子、含氧分子，使得得到的过渡金属单原子催化剂的形貌是二维纳米片状结构和管状结构，与嵌在MOF微孔中的少量单原子位点相比，单原子位点在片状结构和管状结构上更加暴露，有利于催化活性的进一步提高。
2)本发明提供的制备方法中，所选择的特定原料相对于MOF的原料而言廉价易得；并且反应工艺简单、流程短，适合高通量制备过渡金属单原子催化剂。
3)本发明提供的制备方法中，得到的过渡金属单原子催化剂与MOF碳化后得到的过渡金属单原子催化剂不同。其中：后者是一个刚性结构，在特定应用中如果一种过渡金属单原子催化剂效果不佳，整个体系都需要更换；而本发明得到的过渡金属单原子催化剂不能形成具有特定晶型的、类似MOF的结构，但可以通过调节所加入聚乙二醇的平均分子量，实现碳基载体的曲率、形貌和表面积的调控，从而实现在特定应用的调节。
4)本发明提供的制备方法中，急速冷却的目的是为了让四种原料同时“结冰”，形成一体，防止组成不均一的做法。
5)本发明提供的制备方法适用于多种可溶性过渡金属盐，适用范围广。
6)本发明提供的制备方法制备的过渡金属单原子催化剂在电催化析氢反应中进行应用时，管状结构的效果更佳。
附图说明
一个或多个实施例通过与之对应的附图中的图片进行示例性说明，这些示例性说明并不构成对实施例的限定。在这里专用的词“示例性”意为“用作例子、实施例或说明性”。这里作为“示例性”所说明的任何实施例不必解释为优于或好于其它实施例。
图1a、图1b分别为本发明实施例1得到的过渡金属单原子催化剂的场发射扫描电镜照片和扫描透射电镜照片。
图2a、图2b分别为本发明实施例2得到的过渡金属单原子催化剂的场发射扫描电镜照片和扫描透射电镜照片。
图3为将实施例1和2中的管状和片状催化剂进行电化学析氢反应性能比较的结果图。
图4a、图4b分别为本发明实施例3得到的过渡金属单原子催化剂的场发射扫描电镜照片和扫描透射电镜照片。
图5a、图5b分别为本发明实施例4得到的过渡金属单原子催化剂的场发射扫描电镜照片和扫描透射电镜照片。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。另外，为了更好的说明本发明，在下文的具体实施方式中给出了众多的具体细节。本领域技术人员应当理解，没有某些具体细节，本发明同样可以实施。在一些实施例中，对于本领域技术人员熟知的原料、元件、方法、手段等未作详细描述，以便于凸显本发明的主旨。
除非另有其它明确表示，否则在整个说明书和权利要求书中，术语“包括”或其变换如“包含”或“包括有”等等将被理解为包括所陈述的元件或组成部分，而并未排除其它元件或其它组成部分。
以下实施例中所使用的各型号PEG均是本领域的常规型号，可从商购渠道获得。
实施例1
常温下将5g尿素、0.15g硼酸、0.5g PEG-2000和0.01mmol RuCl3·H2O溶于超纯水中得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为900摄氏度，自然冷却后得到负载有金属钌单原子位点的纳米管状催化剂。产物的场发射扫描电镜照片如图1a所示，球差校正的高角环形暗场扫描透射电镜照片如图1b所示，从图1b中可以看出管状结构表面有金属单原子。
实施例2
常温下将5g尿素、0.15g硼酸、0.5g PEG-8000和0.01mmol RuCl3·H2O溶于超纯水中得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为900摄氏度，自然冷却后得到负载有金属钌单原子位点的纳米片状催化剂。产物的场发射扫描电镜照片如图2a所示，球差校正的高角环形暗场扫描透射电镜照片如图2b所示，从图2b中可以看出管状结构表面有金属单原子。
将实施例1和2中的管状和片状催化剂的电化学析氢反应性能比较，分别将实施例1中的管状结构和实施例2中的片状结构配成2mg/mL浓度的溶液，滴涂到玻碳电极上，在三电极体系下测试其HER性能，如图3所示，管状的过电位明显比片状的要小40mV，这归因于管状材料的表面更大的曲率导致其负电荷分布更加集中在单原子位点附近，因而有利于氢的析出。
实施例3
常温下将5g尿素、0.15g硼酸、0.5g PEG-2000和0.01mmol FeCl3·6H2O溶于超纯水中得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为900摄氏度，自然冷却后得到负载有金属铁单原子位点的纳米管状催化剂。产物的场发射扫描电镜照片如图4a所示，球差校正的高角环形暗场扫描透射电镜照片如图4b所示，从图4b中可以看出管状结构表面有金属单原子。
实施例4
常温下将5g尿素、0.15g硼酸、0.5g PEG-2000和0.01mmol Ni(NO3)2·6H2O溶于超纯水中得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为900摄氏度，自然冷却后得到负载有金属铁单原子位点的纳米管状催化剂。产物的场发射扫描电镜照片如图5a所示，球差校正的高角环形暗场扫描透射电镜照片如图5b所示，从图5b中可以看出管状结构表面有金属单原子。
实施例5
常温下将4g双氰胺、0.15g硼酸、0.5g PEG-8000和0.01mmol Ni(NO3)2·6H2O溶于超纯水得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为900摄氏度，自然冷却后得到负载有金属镍单原子位点的纳米片状催化剂。
实施例6
常温下将6g尿素、0.2g硼酸、0.6g PEG-2000和0.015mmol Ag(NO3)2溶于超纯水得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为800摄氏度，自然冷却后得到负载有金属银单原子位点的纳米管状催化剂。
实施例7
常温下将6g尿素、0.2g硼酸、0.6g PEG-8000和0.015mmol Ag(NO3)2溶于超纯水得到澄清均一的混合溶液，对水中的各物质浓度不做限定，随后将该混合溶液置于液氮中急速冷却形成低温块体，冷冻干燥以彻底除去水，然后通过研磨或球磨处理得到均匀的固体粉末以使之后的碳化均匀。接着将上述固体粉末在氩气中碳化6小时，碳化温度为900摄氏度，自然冷却后得到负载有金属银单原子位点的纳米片状催化剂。
最后应说明的是：以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。
Claims (10)
1.一种过渡金属单原子催化剂的制备方法，其特征在于：包括下述步骤：
将含氮小分子、含硼小分子、含氧分子和可溶性过渡金属盐溶于水中形成溶液；将溶液冷却、干燥、分散均匀后得到固体粉末；在保护性气体中碳化；其中：
所述含氮小分子选自三聚氰胺、双氰胺、尿素中的任意一种或多种；
所述含硼小分子选自硼酸、氧化硼中的任意一种或多种；
所述含氧分子选自聚乙二醇、聚乙烯醇中的一种或多种。
2.根据权利要求1所述的制备方法，其特征在于：所述含氮小分子为尿素，所述含硼小分子为硼酸，所述含氧分子为聚乙二醇。
3.根据权利要求2所述的制备方法，其特征在于：所述的聚乙二醇包括：PEG-400、PEG-600、PEG-800、PEG-1000、PEG-2000、PEG-4000、PEG-6000、PEG-8000、PEG-10000中的一种或多种；可选地，所述聚乙二醇为PEG-2000或PEG-8000。
4.根据权利要求1所述的制备方法，其特征在于：所述冷却为急速冷却；可选地，所述急速冷却的方式为置于液氮中。
5.根据权利要求1所述的制备方法，其特征在于：所述的可溶性过渡金属盐包括钒、铬、锰、铁、钴、镍、铜、钼、钌、铑、钯的硝酸盐、氯化物、醋酸盐、硫酸盐中的一种或多种；可选地包括RuCl3、FeCl3、Ni(NO3)2、Ag(NO3)2中的一种或多种；进一步可选地为RuCl3·H2O、FeCl3·6H2O、Ni(NO3)2·6H2O、Ag(NO3)2。
6.根据权利要求2所述的制备方法，其特征在于：尿素、硼酸、聚乙二醇和过渡金属盐的用量比为(1-10g)：(0.05-0.5g)：(0.1-2g)：(0.005-0.5mmol)；可选地为(5-6g)：(0.15-0.2g)：(0.5-0.6g)：(0.01-0.015mmol)。
7.根据权利要求1所述的制备方法，其特征在于：碳化的温度为600-1000℃，碳化的时间为4-8小时；可选地碳化的温度为800-900℃，碳化的时间为6小时。
8.一种根据权利要求1-7之一所述的制备方法制得的过渡金属单原子催化剂。
9.一种根据权利要求1-7之一所述的制备方法制得的过渡金属单原子催化剂在电催化析氢反应中的应用。
10.根据权利要求9所述的应用，所述过渡金属单原子催化剂为管状结构。