CN110744945A - 一种写真kt板及其制备方法和应用 - Google Patents

一种写真kt板及其制备方法和应用 Download PDF

Info

Publication number
CN110744945A
CN110744945A CN201911027627.5A CN201911027627A CN110744945A CN 110744945 A CN110744945 A CN 110744945A CN 201911027627 A CN201911027627 A CN 201911027627A CN 110744945 A CN110744945 A CN 110744945A
Authority
CN
China
Prior art keywords
layer
board
parts
white film
material layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911027627.5A
Other languages
English (en)
Inventor
高江华
宋连卿
赵红英
刘鹏飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henan Century Huitong Digital Technology Co Ltd
Original Assignee
Henan Century Huitong Digital Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henan Century Huitong Digital Technology Co Ltd filed Critical Henan Century Huitong Digital Technology Co Ltd
Priority to CN201911027627.5A priority Critical patent/CN110744945A/zh
Publication of CN110744945A publication Critical patent/CN110744945A/zh
Pending legal-status Critical Current

Abstract

本发明属于KT板技术领域，具体公开一种写真KT板，包括板芯层、第一材料层与第二材料层，第一材料层与第二材料层分别压合在板芯层的上、下表面；板芯层由丙烯腈‑丁二烯‑苯乙烯共聚物挤出发泡制得；第一材料层由第一白膜层及第一龙卡纸层组成，第一白膜层压合在第一龙卡纸层的上表面；第一白膜层由以下原料制成：乙烯法PVC树脂粉、轻质纳米钙、增塑剂、金红石型钛白粉、助剂、稳定剂；第二材料层包括第二龙卡纸层。本发明还提供一种KT写真板的制备方法和应用。本发明提供的写真KT板，具有能吸墨、不起包、挺度好、平整度好等优点。

Description

一种写真KT板及其制备方法和应用
技术领域
本发明属于KT板技术领域，具体公开一种写真KT板及其制备方法和应用。
背景技术
KT板是一种由聚苯乙烯颗粒经过发泡生成板芯，经过表面覆膜压合而成的一种新型材料，板体轻盈、不易变质、易于加工，并可直接在板上丝网印刷、油漆、裱覆背胶画面及喷绘，广泛用于广告展示促销、飞机航模、建筑装饰、文化艺术及包装等方面。在广告方面的用途一是用于产品宣传信息发布的展览、展示及通告用装裱衬板，另外就是被大量应用于丝网一次印刷，特别适合用于大范围统一宣传活动使用。
但现有的普通KT板挺度差，不能在写真机、喷绘机、UV打印机上使用，且容易起包。现有技术中为了在KT板上边呈现画面，只能先用写真机、喷绘机、UV打印机将画面喷印在车贴、PP背胶等不干胶材质上边，然后通过覆膜机转帖到KT板上边，这种工艺首先是不干胶材质的离型纸需要丢弃，造成环境污染，其次多了转帖工序影响成品率和效率，不干胶里边残存的小分子成分和溶剂还会腐蚀KT板表面造成起包，且普通KT板较软容易变形。
发明内容
本发明提供一种写真KT板，具有能吸墨性能好、不起包、挺度好等优点。
本发明提供一种写真KT板，能够用于单面打印，其包括板芯层、第一材料层与第二材料层，所述第一材料层与所述第二材料层分别通过粘合剂压合在所述板芯层的上、下表面；
所述板芯层由丙烯腈-丁二烯-苯乙烯共聚物挤出发泡制得；
所述第一材料层由第一白膜层及第一龙卡纸层组成，所述第一白膜层通过粘合剂压合在所述第一龙卡纸层的上表面，且所述第一龙卡纸层靠近所述板芯层设置；
所述第一白膜层按重量份数计由以下原料制成：乙烯法PVC树脂粉45-65份、轻质纳米钙4-8份、增塑剂11-14份、金红石型钛白粉6-8份、助剂1-2份、稳定剂2-3份；
所述第二材料层包括第二龙卡纸层。
本发明还提供一种写真KT板，其所述第二材料层包括第二白膜层及所述第二龙卡纸层，所述第二白膜层通过粘合剂压合在所述第二龙卡纸层的上表面，所述第二龙卡纸层靠近所述板芯层设置，且所述第二白膜层的制成原料与所述第一白膜层的制成原料相同；该写真KT板能够用于双面打印。
优选地，所述第一龙卡纸层与所述第二龙卡纸层均为厚度为200-230um的龙卡纸。
优选地，所述第一白膜层与所述第二白膜层按重量份数计由以下原料制成：乙烯法PVC树脂粉60份、轻质纳米钙8份、增塑剂13.5份、金红石型钛白粉6份、助剂1.5份、稳定剂2.7份。
优选地，所述增塑剂为邻苯二甲酸二丁酯、邻苯二甲酸二辛酯、邻苯二甲酸二异壬酯、环氧大豆油、磷酸三甲苯酯、磷酸三苯酯、癸二酸二辛酯、氯化石蜡中的一种；所述稳定剂为液体钡锌稳定剂，所述助剂为甲基丙烯酸甲酯。
优选地，所述板芯层的制备方法如下：将丙烯腈-丁二烯-苯乙烯共聚物颗粒熔融，再向该物料里注入丁烷或者二氧化碳；将注入有丁烷或者二氧化碳的物料挤出发泡，发泡后的物料冷却、收卷、裁切，即得所述板芯层。
其中，用于单面打印的写真KT板的制备方法具体包括以下几个步骤：
S1：按重量份数称取乙烯法PVC树脂粉45-65份、轻质纳米钙4-8份、增塑剂11-14份、金红石型钛白粉6-8份、助剂1-2份、稳定剂2-3份，备用；
S2：在300-400r/min的搅拌速度下，将步骤S1中称取的乙烯法PVC树脂粉、轻质纳米钙、增塑剂、稳定剂、金红石型钛白粉、助剂分别依次加入搅拌机中，所有原料添加完毕后调整搅拌速度为900-1000r/min继续搅拌170s，得到中间产物，再将所述中间产物在170℃下熔融后，进一步在180℃条件下混合均匀，将得到的混合物料过滤，过滤得到的混合物料再在165℃下压延成薄膜，薄膜冷却定型后收卷打包，即得所述第一白膜层，备用；
S3：将步骤S2中得到的所述第一白膜层通过粘合剂加热压合在所述第一龙卡纸层上表面，即得到所述第一材料层；
S4：将所述板芯层、所述第一材料层与所述第二材料层分别加热至120℃，再将所述第一材料层、所述第二材料层分别通过粘合剂滚压贴合在所述板芯层的上、下表面，冷却定型，裁剪包装，即得所述KT写真板。
用于双面打印的写真KT板的制备方法与用于单面打印的写真KT板的制备方法相比，还包括如下步骤：
使用与所述第一白膜层的制备方法相同的方法制备所述第二白膜层，将所述第二白膜层通过粘合剂加热压合在所述第二龙卡纸层上表面，即得到所述第二材料层，且所述第二白膜层的制备方法与所述第一白膜层的制备方法相同。
优选地，所述粘合剂为乙烯-乙酸乙烯酯共聚物。
本发明还提供一种KT写真板的应用，用于单面打印或双面打印的所述写真KT板能够用作户外广告牌或展览展示道具或展会搭建材料。
相较于现有技术，本发明的有益效果为：
1、本发明提供的写真KT板，在专用KT板表面贴合一层高显色PVC面层，使KT板能直接在写真机、喷绘机、UV打印机上使用；
2、本发明提供的写真KT板，省去现有技术中转帖不干胶工序，减少离型材料丢弃；杜绝了不干胶里边残存的小分子成分和溶剂腐蚀PS表面造成起包的现象；同时200-230微米的龙卡纸也给KT板提供足够的支撑力和平整度，更方便用户使用和安装。
3、本发明提供的写真KT板，能够降低平面广告商生产成本，提升KT板材画面呈现效果，提高KT板材写真画面生产效率，拓展KT广告板应用领域，杜绝KT板画面起包，提高KT板挺度平整度。
附图说明
图1是实施例1-3提供的写真KT板的结构示意图；
图2是实施例4提供的写真KT板的结构示意图；
附图标记说明：1、板芯层；2、第一材料层；20、第二材料层；21、第一白膜层；22、第一龙卡纸层；23、第二龙卡纸层；24、第二白膜层。
具体实施方式
为了使本领域技术人员更好地理解本发明的技术方案能予以实施，下面结合具体实施例对本发明作进一步说明，但所举实施例不作为对本发明的限定。
实施例1
一种写真KT板，包括板芯层1、第一材料层2及第二材料层20，如图1所示，第一材料层2、第二材料层20分别通过乙烯-乙酸乙烯酯共聚物加热压合在板芯层1的上、下表面；
其中，使用的乙烯-乙酸乙酯共聚物为粘合剂，该物质为环保热熔胶，能够有效杜绝残存小分子成分和溶剂腐蚀表层，导致板层起包的现象出现；
第一材料层2包括第一白膜层21及第一龙卡纸层22，第一白膜层21通过乙烯-乙酸乙烯酯共聚物加热压合在第一龙卡纸层22上表面，且第一龙卡纸层22靠近板芯层1设置；
第二材料层20包括第二龙卡纸层23；
其中，第一龙卡纸层22与第二龙卡纸层23为厚度为200um的龙卡纸；
第一白膜层21由以下原料制成：乙烯法PVC树脂粉(台塑，S-65S)45g、轻质纳米钙(广硕化工，GS-6)4g、癸二酸二辛酯(美国埃克森)11g、金红石型钛白粉(安徽安纳达，ATP-312)6g、甲基丙烯酸甲酯(日本三菱，P-551A)1g、液体钡锌稳定剂(宝泰实业股份有限公司，BZ-695)2g。
该写真KT板的具体制备方法包括以下几个步骤：
S1：称取乙烯法PVC树脂粉45g、轻质纳米钙4g、癸二酸二辛酯11g、金红石型钛白粉6g、甲基丙烯酸甲酯1g、液体钡锌稳定剂2g，备用；
S2：将步骤S1中称取的乙烯法PVC树脂粉、轻质纳米钙、癸二酸二辛酯、液体钡锌稳定剂、金红石型钛白粉、甲基丙烯酸甲酯分别依次加入搅拌机中以300r/min的转速进行搅拌，所有原料添加完毕后换900r/min的转速继续搅拌170s，再将物料在170℃下熔融，然后在180℃条件下进一步使物料混合均匀，将得到的混合物料过滤后，在165℃下压延成薄膜，薄膜冷却定型后收卷打包，即得第一白膜层21，备用；
S3：将步骤S2中得到的第一白膜层21通过乙烯-乙酸乙烯酯共聚物加热压合在第一龙卡纸层22的上表面，得到第一材料层2；
S4：将丙烯腈-丁二烯-苯乙烯共聚物(PS)颗粒通过螺杆作用装入135℃挤出机，在螺杆挤出机后端向已经熔融的PS料中注入丁烷或者二氧化碳；紧接着将熔融的PS料通过模头挤出，PS熔融料出模头后由于丁烷或者二氧化碳挥发使PS料均匀发泡；发泡后的PS呈圆筒状，再先后经过水冷和风冷两道冷却后，将圆筒抛开、收卷、裁切，即得板芯层1；
S5：将板芯层1、第一材料层2及第二材料层20分别加热至120℃，在板芯层1的上、下表面涂抹乙烯-乙酸乙烯酯共聚物，再将第一材料层2及第二材料层20分别滚压贴合在板芯层1的上、下表面，冷却定型，裁剪包装，即得能够用于单面打印的KT写真板；
该KT写真板可用作户外广告牌或展览展示道具或展会搭建材料。
实施例2
一种写真KT板，包括板芯层1、第一材料层2及第二材料层20，如图1所示，第一材料层2及第二材料层20分别通过乙烯-乙酸乙烯酯共聚物压合在板芯层1的上、下表面；
其中，使用的乙烯-乙酸乙酯共聚物为粘合剂，该物质为环保热熔胶，能够有效杜绝残存小分子成分和溶剂腐蚀表层，导致板层起包的现象出现；
第一材料层2包括第一白膜层21及第一龙卡纸层22，第一白膜层21通过乙烯-乙酸乙烯酯共聚物压合在第一龙卡纸层22上表面，且第一龙卡纸层22靠近板芯层1设置；
第二材料层20包括第二龙卡纸层23；
其中，第一龙卡纸层22与第二龙卡纸层23均为厚度为200um的龙卡纸；
第一白膜层21由以下原料制成：乙烯法PVC树脂粉(台塑，S-65S)65g、轻质纳米钙(广硕化工，GS-6)8g、氯化石蜡(美国埃克森)14g、金红石型钛白粉(安徽安纳达，ATP-312)8g、甲基丙烯酸甲酯(日本三菱，P-551A)2g、液体钡锌稳定剂(宝泰实业股份有限公司，BZ-695)3g。
具体制备方法包括以下几个步骤：
S1：称取乙烯法PVC树脂粉65g、轻质纳米钙8g、氯化石蜡14g、金红石型钛白粉8g、甲基丙烯酸甲酯2g、液体钡锌稳定剂3g，备用；
S2：将步骤S1中称取的乙烯法PVC树脂粉、轻质纳米钙、氯化石蜡、液体钡锌稳定剂、金红石型钛白粉、甲基丙烯酸甲酯分别依次加入搅拌机以转速300r/min进行搅拌，所有原料添加完毕后换转速为1000r/min继续搅拌170s，再将物料在170℃下熔融，然后在180℃条件下进一步使物料混合均匀，将得到的混合物料过滤后，在165℃下压延成薄膜，薄膜冷却定型后收卷打包，即得第一白膜层21，备用；
S3：将步骤S2中得到的第一白膜层21通过乙烯-乙酸乙烯酯共聚物压合在第一龙卡纸层22的上表面，得到第一材料层2；
S4：将丙烯腈-丁二烯-苯乙烯共聚物(PS)颗粒通过螺杆作用装入135℃挤出机，在螺杆挤出机后端向已经熔融的PS料中注入丁烷或者二氧化碳；紧接着将熔融的PS料通过模头挤出，PS熔融料出模头后由于丁烷或者二氧化碳挥发使PS料均匀发泡；发泡后的PS呈圆筒状，再先后经过水冷和风冷两道冷却后，将圆筒抛开、收卷、裁切，即得板芯层1；
S5：将板芯层1、第一材料层2及第二材料层20分别加热至120℃，在板芯层1的上、下表面涂抹乙烯-乙酸乙烯酯共聚物，再将第一材料层2及第二材料层20分别滚压贴合在板芯层1的上、下表面，冷却定型，裁剪包装，即得能够用于单面打印的KT写真板；
该KT写真板可用作户外广告牌或展览展示道具或展会搭建材料。
实施例3
一种写真KT板，包括板芯层1、第一材料层2及第二材料层20，如图1所示，第一材料层2及第二材料层20分别通过乙烯-乙酸乙烯酯共聚物压合在板芯层1的上、下表面；
其中，使用的乙烯-乙酸乙酯共聚物为粘合剂，该物质为环保热熔胶，能够有效杜绝残存小分子成分和溶剂腐蚀表层，导致板层起包的现象出现；
第一材料层2包括第一白膜层21及第一龙卡纸层22，第一白膜层21通过乙烯-乙酸乙烯酯共聚物压合在第一龙卡纸层22上表面，且第一龙卡纸层22靠近板芯层1设置；
第二材料层20包括第二龙卡纸层23；
其中，第一龙卡纸层22与第二龙卡纸层23均为厚度为200um的龙卡纸；
第一白膜层21由以下原料制成：乙烯法PVC树脂粉(台塑，S-65S)60g、轻质纳米钙(广硕化工，GS-6)8g、邻苯二甲酸二异壬酯(美国埃克森)13.5g、金红石型钛白粉(安徽安纳达，ATP-312)6g、甲基丙烯酸甲酯(日本三菱，P-551A)1.5g、液体钡锌稳定剂(宝泰实业股份有限公司，BZ-695)2.7g。
具体制备方法包括以下几个步骤：
S1：称取乙烯法PVC树脂粉60g、轻质纳米钙8g、邻苯二甲酸二异壬酯13.5g、金红石型钛白粉6g、甲基丙烯酸甲酯1.5g、液体钡锌稳定剂2.7g，备用；
S2：将步骤S1中称取的乙烯法PVC树脂粉、轻质纳米钙、邻苯二甲酸二异壬酯、液体钡锌稳定剂、金红石型钛白粉、甲基丙烯酸甲酯分别依次加入搅拌机中以转速为350r/min进行搅拌，所有原料添加完毕后换转速为950r/min继续搅拌170s，再将物料在170℃下熔融，然后在180℃条件下进一步使物料混合均匀，将得到的混合物料过滤后，在165℃下压延成薄膜，薄膜冷却定型后收卷打包，即得所述第一白膜层21，备用；
S3：将步骤S2中得到的第一白膜层21通过乙烯-乙酸乙烯酯共聚物压合在第一龙卡纸层22的上表面，得到第一材料层2；
S4：将丙烯腈-丁二烯-苯乙烯共聚物(PS)颗粒通过螺杆作用装入135℃挤出机，在螺杆挤出机后端向已经熔融的PS料中注入丁烷或者二氧化碳；紧接着将熔融的PS料通过模头挤出，PS熔融料出模头后由于丁烷或者二氧化碳挥发使PS料均匀发泡；发泡后的PS呈圆筒状，再先后经过水冷和风冷两道冷却后，将圆筒抛开、收卷、裁切，即得板芯层1；
S5：将板芯层1、第一材料层2及第二材料层20分别加热至120℃，在板芯层1的上、下表面涂抹乙烯-乙酸乙烯酯共聚物，再将第一材料层2及第二材料层20分别滚压贴合在板芯层1的上、下表面，冷却定型，裁剪包装，即得能够用于单面打印的KT写真板；
该KT写真板可用作户外广告牌或展览展示道具或展会搭建材料。
实施例4
与上述实施例的不同仅在于：
第二材料层20包括第二白膜层24及第二龙卡纸层23，且第二白膜层24通过乙烯-乙酸乙烯酯共聚物压合在第二龙卡纸层223的上表面，且第二龙卡纸层23靠近板芯层1设置，该写真KT板能够用于双面打印，具体如图2所示。
该写真KT板的制备方法与实施例1～3提供的写真KT板的制备方法相比，还包括如下步骤：
将第二白膜层24通过乙烯-乙酸乙烯酯共聚物压合在第二龙卡纸层23的上表面，即得到第二材料层20。
需要说明的是，第二白膜层24的制备方法与第一白膜层21的制备方法相同。
由于本发明各实施例提供的写真kt板的性能基本相同，故以下仅采用实施例1得到写真KT板进行性能测试。
1、挺度测试
将普通KT板(合肥猎户广告有限公司生产，货号L-KT001)和写真KT板裁成2.5厘米宽10厘米长，各取五块；然后支承在6厘米宽腾空的支架上边；取1公斤重的标准砝码悬挂在悬空KT板正中间，对比两种KT板变形情况，结果见表1。
表1普通KT板和写真KT板的挺度测试结果
Figure BDA0002249137860000101
由表1可知，本发明提供的写真KT板在砝码防止10分钟内均无变形，在放置30时出现稍微下弯的情况，去掉砝码后又能恢复，相较于普通KT板具有较佳的挺度。
2、平整度测试
将1.2米*2.4米普通KT板和写真KT板各取20张正品，分别平放在平整玻璃测试台上边观察72小时，对比与玻璃测试板贴合程度，结果见表2。
表2普通KT板和写真KT板的平整度测试结果
Figure BDA0002249137860000111
由表2可知，本发明提供的写真KT板平整度和平整度保持效果明显比普通KT板要好。
3、打印测试
将普通KT板和写真KT板分别在户外写真机、喷绘机、UV写真机上面打图测试，对比打印效果，结果见表3。
表3打印测试结果
样品 户外写真机测试 喷绘机测试 UV写真机测试
普通KT板 流墨、画面一片模糊 流墨、画面一片模糊 画面清晰，画面颜色脱落
写真KT板 画面清晰，画面不脱落 画面清晰，画面不脱落 画面清晰，画面颜色不脱落
由表3可知，本发明提供的写真KT板在户外写真机、喷绘机、UV写真机上打印的画面清晰，且颜色均不脱落，相较于普通KT板具有更好的打印效果。
需要说明的是，本发明权利要求书中涉及数值范围时，应理解为每个数值范围的两个端点以及两个端点之间任何一个数值均可选用，由于采用的步骤方法与实施例1～4相同，为了防止赘述，本发明描述了优选的实施例，但本领域内的技术人员一旦得知了基本创造性概念，则可对这些实施例作出另外的变更和修改。所以，所附权利要求意欲解释为包括优选实施例以及落入本发明范围的所有变更和修改。
显然，本领域的技术人员可以对本发明进行各种改动和变型而不脱离本发明的精神和范围。这样，倘若本发明的这些修改和变型属于本发明权利要求及其等同技术的范围之内，则本发明也意图包含这些改动和变型在内。

Claims (10)

1.一种写真KT板，其特征在于，包括板芯层(1)、第一材料层(2)与第二材料层(20)，所述第一材料层(2)与所述第二材料层(20)分别通过粘合剂压合在所述板芯层(1)的上、下表面；
所述板芯层(1)由丙烯腈-丁二烯-苯乙烯共聚物挤出发泡制得；
所述第一材料层(2)由第一白膜层(21)及第一龙卡纸层(22)组成，所述第一白膜层(21)通过粘合剂压合在所述第一龙卡纸层(22)的上表面，且所述第一龙卡纸层(22)靠近所述板芯层(1)设置；
所述第一白膜层(21)按重量份数计由以下原料制成：乙烯法PVC树脂粉45-65份、轻质纳米钙4-8份、增塑剂11-14份、金红石型钛白粉6-8份、助剂1-2份、稳定剂2-3份；
所述第二材料层(20)包括第二龙卡纸层(23)。
2.根据权利要求1所述的写真KT板，其特征在于，所述第二材料层(20)还包括第二白膜层(24)，所述第二白膜层(24)通过粘合剂压合在所述第二龙卡纸层(23)的上表面，所述第二龙卡纸层(23)靠近所述板芯层(1)设置；且所述第二白膜层(24)的制成原料与所述第一白膜层(21)的制成原料相同。
3.根据权利要求1或2所述的写真KT板，其特征在于，所述第一龙卡纸层(22)及所述第二龙卡纸层(23)均为厚度200-230um的龙卡纸。
4.根据权利要求1或2所述的写真KT板，其特征在于，所述第一白膜层(21)与所述第二白膜层(24)按重量份数计由以下原料制成：乙烯法PVC树脂粉60份、轻质纳米钙8份、增塑剂13.5份、金红石型钛白粉6份、助剂1.5份、稳定剂2.7份。
5.根据权利要求4所述的写真KT板，其特征在于，所述增塑剂为邻苯二甲酸二丁酯、邻苯二甲酸二辛酯、邻苯二甲酸二异壬酯、环氧大豆油、磷酸三甲苯酯、磷酸三苯酯、癸二酸二辛酯、氯化石蜡中的一种；所述稳定剂为液体钡锌稳定剂，所述助剂为甲基丙烯酸甲酯。
6.根据权利要求1所述的写真KT板，其特征在于，所述板芯层(1)的制备方法如下：将丙烯腈-丁二烯-苯乙烯共聚物颗粒熔融，再向该物料里注入丁烷或者二氧化碳；将注入有丁烷或者二氧化碳的物料挤出发泡，发泡后的物料冷却、收卷、裁切，即得所述板芯层(1)。
7.根据权利要求1所述的写真KT板的制备方法，其特征在于，具体包括以下几个步骤：
S1：按重量份数称取乙烯法PVC树脂粉45-65份、轻质纳米钙4-8份、增塑剂11-14份、金红石型钛白粉6-8份、助剂1-2份、稳定剂2-3份，备用；
S2：在300-400r/min的搅拌速度下，将步骤S1中称取的乙烯法PVC树脂粉、轻质纳米钙、增塑剂、稳定剂、金红石型钛白粉、助剂分别依次加入搅拌机中，所有原料添加完毕后调整搅拌速度为900-1000r/min继续搅拌170s，得到中间产物，再将所述中间产物在170℃下熔融后，进一步在180℃条件下混合均匀，将得到的混合物料过滤，过滤得到的混合物料再在165℃下压延成薄膜，薄膜冷却定型后收卷打包，即得所述第一白膜层(21)，备用；
S3：将步骤S2中得到的所述第一白膜层(21)通过粘合剂加热压合在所述第一龙卡纸层(22)上表面，即得到所述第一材料层(2)；
S4：将所述板芯层(1)、所述第一材料层(2)与所述第二材料层(20)分别加热至120℃，再将所述第一材料层(2)、所述第二材料层(20)分别通过粘合剂滚压贴合在所述板芯层(1)的上、下表面，冷却定型，裁剪包装，即得所述KT写真板。
8.根据权利要求7所述的写真KT板的制备方法，其特征在于，还包括以下步骤：使用与所述第一白膜层(21)的制备方法相同的方法制备所述第二白膜层(24)，再将所述第二白膜层(24)通过粘合剂加热压合在所述第二龙卡纸层(23)上表面，即得到所述第二材料层(20)，且所述第二白膜层(24)的制备方法与所述第一白膜层(21)的制备方法相同。
9.根据权利要求7或8所述的写真KT板的制备方法，其特征在于，所述粘合剂为乙烯-乙酸乙烯酯共聚物。
10.一种权利要求1所述的写真KT板在户外广告牌、展览展示道具或展会搭建材料中的应用。
CN201911027627.5A 2019-10-28 2019-10-28 一种写真kt板及其制备方法和应用 Pending CN110744945A (zh)