CN110551996A - 一种适用于铝合金压铸后的钝化液 - Google Patents
一种适用于铝合金压铸后的钝化液 Download PDFInfo
- Publication number
- CN110551996A CN110551996A CN201911014505.2A CN201911014505A CN110551996A CN 110551996 A CN110551996 A CN 110551996A CN 201911014505 A CN201911014505 A CN 201911014505A CN 110551996 A CN110551996 A CN 110551996A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- passivation solution
- solution suitable
- percentage
- catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种适用于铝合金压铸后的钝化液，包含添加剂和载体，配方中的原料按重量百分比组成分别是：0.5～6%黄铜粉，10～35%硅油，1～10%钼酸铵，0～3%咪唑啉缓蚀剂，0～2.5%聚乙二醇，5～20%磷酸三钠，10～20%氧化銤，30～60%催化剂，通过本方法制备的产品，在压铸成型后，在铝合金外露的表面自动形成一厚度均匀且连续分布的稳定的氧化层。
Description
技术领域
本发明公开了一种适用于铝合金压铸后的钝化液。
背景技术
铝是一种银白色轻金属，有延展性，潮湿空气中能形成一层防止金属腐蚀的氧化膜，铝广泛的应用在各个领域内，铝较为容易在空气中氧化，受到腐蚀，现有的技术中，铝合金型材表面氧化技术却无法顺利应用于铝合金压铸技术中， 很难形成氧化层，即使能形成氧化层的，氧化层与铝合金铸件之间没有形成分子链层，容易分层，在外力作用氧化层即与铝合金分层并脱落。
发明内容
针对上述现有技术存在的问题，本发明提供一种适用于铝合金压铸后的钝化液，在压铸成型后，在铝合金外露的表面自动形成一厚度均匀且连续分布的稳定的氧化层。
为了实现上述目的，本发明通过以下技术方案实现：一种适用于铝合金压铸后的钝化液，配方中的原料按重量百分比组成分别是：0.5～6%黄铜粉，10～35%硅油，1～10%钼酸铵， 0～3%咪唑啉缓蚀剂，0～2.5%聚乙二醇，5～20%磷酸三钠，10～20%氧化銤，30～60%催化剂。
有益效果：通过本方法制备的产品，在压铸成型后，在铝合金外露的表面自动形成一厚度均匀且连续分布的稳定的氧化层。
具体实施方式
实施例1
一种适用于铝合金压铸后的钝化液，配方中的原料按重量百分比组成分别是：0.5%黄铜粉，10%硅油，1%钼酸铵，1%咪唑啉缓蚀剂，1%聚乙二醇，5%磷酸三钠，10%氧化銤，30%催化剂，此时氧化层分布不够均匀，不能很好的保护铝合金不受腐蚀。
实施例2
一种适用于铝合金压铸后的钝化液，配方中的原料按重量百分比组成分别是：6%黄铜粉，35%硅油，10%钼酸铵，3%咪唑啉缓蚀剂，2.5%聚乙二醇，20%磷酸三钠，20%氧化銤，60%催化剂，此时生产成本较高，性价比不高。
实施例3
一种适用于铝合金压铸后的钝化液，配方中的原料按重量百分比组成分别是：4%黄铜粉，23%硅油，5%钼酸铵， 1.5%咪唑啉缓蚀剂，1.25%聚乙二醇，13%磷酸三钠，15%氧化銤，45%催化剂，此时在压铸成型后，在铝合金外露的表面自动形成一厚度均匀且连续分布的稳定的氧化层。
Claims (4)
1.一种适用于铝合金压铸后的钝化液，包含添加剂和载体，其特征在于，配方中的原料按重量百分比组成分别是：0.5～6%黄铜粉，10～35%硅油，1～10%钼酸铵，0～3%咪唑啉缓蚀剂，0～2.5%聚乙二醇，5～20%磷酸三钠，10～20%氧化銤，30～60%催化剂。
2.根据权利要求1所述的适用于铝合金压铸后的钝化液，其特征在于，配方中的原料按重量百分比组成分别是：0.5%黄铜粉，10%硅油，1%钼酸铵，1%咪唑啉缓蚀剂，1%聚乙二醇，5%磷酸三钠，10%氧化銤，30%催化剂。
3.根据权利要求1所述的适用于铝合金压铸后的钝化液，其特征在于，配方中的原料按重量百分比组成分别是：6%黄铜粉，35%硅油，10%钼酸铵，3%咪唑啉缓蚀剂，2.5%聚乙二醇，20%磷酸三钠，20%氧化銤，60%催化剂。
4.根据权利要求1所述的适用于铝合金压铸后的钝化液，其特征在于，配方中的原料按重量百分比组成分别是：4%黄铜粉，23%硅油，5%钼酸铵，1.5%咪唑啉缓蚀剂，1.25%聚乙二醇，13%磷酸三钠，15%氧化銤，45%催化剂。