JP4072971B1 - 溶融亜鉛めっきの表面処理方法 - Google Patents
溶融亜鉛めっきの表面処理方法 Download PDFInfo
- Publication number
- JP4072971B1 JP4072971B1 JP2006275876A JP2006275876A JP4072971B1 JP 4072971 B1 JP4072971 B1 JP 4072971B1 JP 2006275876 A JP2006275876 A JP 2006275876A JP 2006275876 A JP2006275876 A JP 2006275876A JP 4072971 B1 JP4072971 B1 JP 4072971B1
- Authority
- JP
- Japan
- Prior art keywords
- hot dip
- dip galvanizing
- surface treatment
- treatment method
- cooling water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
【解決手段】被処理品を溶融亜鉛めっき浴に浸漬及び上昇後の冷却工程において、冷却水は、亜鉛表面に亜鉛との難水溶性の塩を形成する、有機酸又はアミン類が含まれていることを特徴とする。
【選択図】 図1
Description
溶融亜鉛めっきは金属光沢が高いものの、白錆が発生しやすく、例えば特開2002−356786号に示すようにクロメート処理を施す場合が多い。
しかし、クロメート処理液には6価クロムが含まれているので環境負荷低減の観点からクロメート処理に代替できる表面処理が必要であった。
また、溶融亜鉛めっき製品に塗装処理する場合にあっては、塗装の密着性を確保すべく、リン酸塩処理等の化成皮膜処理や、表面研削を施しているのが現状であり、生産性向上の観点から塗装前処理の省力化が要求されていた。
即ち、被処理品を溶融亜鉛めっき浴から上昇し引き上げた直後のめっき表面は活性であり、このエネルギーを利用すれば冷却水に有機酸やアミン類を添加するだけで化成皮膜が形成され、且つ既設の生産設備に大きな改造が不要であることが明らかになった。
亜鉛めっきの表面に発生する白錆は水酸化亜鉛であることから本発明において冷却水に添加する有機酸又はアミン類は亜鉛の表面に水に難溶性の塩を形成するものであればよいがタンニン酸を用いるのが好ましい。
タンニン酸は接着剤効果も有しているからである。
特に鉛(Pb)の替わりにビスマス(Bi)等を添加した環境対応亜鉛めっきにおいてはBiが表面に濃縮されやすく、白錆が発生しやすいがこの種の鉛レス亜鉛めっき鋼板等においても防錆効果が高い。
(サンプルの作製)
冷却水にタンニン酸を質量比率で1%、5%溶解させた溶液を作製し、被処理品をめっき浴に浸漬後この溶液でサンプルを冷却した。
比較サンプルとして、クロメート処理有り、無しのものを作製した。
サンプル品仕様を図1にまとめて示す。
溶融亜鉛メッキ浴の条件は、440〜550℃の範囲がよく本サンプルの場合450℃に設定した。
また、浴組成も溶融亜鉛めっきに供されている各種浴成が適用できる。
本サンプルはPbレスCdレスの環境対応めっき浴を用い、質量%でZn:97.5%以上、Al:0.005%、Bi:0.3%及びPb:50ppm以下、Cd:10ppm以下のものを用いた。
(試験方法)
(1)亜鉛めっき後の一次防錆試験
各サンプルに対して、4日間の散水暴露試験を実施した。
散水には雨水を使用した。
(2)亜鉛めっき上の塗装性試験
各サンプルに対して、エポキシ粉体焼付け塗装(焼付け温度:250℃、塗膜厚さ:約80μm)を行い、碁盤目試験により塗装密着性を評価した。
(試験結果)
(1)亜鉛めっき後の一次防錆性
4日間の散水暴露試験後の各サンプルの表面状態を図2に示す。
クロメート処理無しサンプル3においては、表面全面に白錆が発生していたが、タンニン溶液サンプル1、2においては、一般の水冷サンプル3より防錆性能は向上していた。
タンニン酸の濃度を5%にしたサンプル1は、表面にタンニンのお茶色が部分的に濃く現れているものの白錆の発生はサンプル2より少ない。
タンニン酸を冷却水に添加すると白錆の発生を抑える効果があるが5%を超えるとタンニンの色が表面に出現することから5%以下がよい。
好ましくは0.5〜3.0%の範囲である。
本発明においてはめっき浴から引き上げためっき表面は高温になっていて、活性が高いので薄い濃度であっても充分に難溶性の皮膜が形成される。
また、浸漬時間も10秒以上確保できれば充分である。
一般的な生産ラインでは10〜30秒の範囲がよい。
また、冷却水は放流方式でも循環方式でもよいが放流水に所定の割合でタンニン酸を添加する方法の方が冷却水の品質を維持しやすい。
(2)亜鉛めっき上の塗装性
碁盤目試験の結果を図3に示す。
サンプル3、4は、塗装がほとんど密着しておらず、タンニン酸が入った冷却水に通したサンプル1、2は、サンプル3、4に比べ格段に塗装密着性が向上しているのが明らかになった。
タンニン酸は渋柿の渋み成分として存在しているものであり人体及び環境にも優しいので環境負荷を低減した溶融亜鉛めっき処理品が得られる。
Claims (2)
- 被処理品を溶融亜鉛めっき浴に浸漬し、次に上昇直後の表面活性な状態から、水にタンニン酸を0.5〜5.0質量%溶解した冷却水に浸漬して冷却することを特徴とする溶融亜鉛めっきの表面処理方法。
- 被処理品を溶融亜鉛めっき浴に浸漬し、次に上昇直後の表面活性な状態から、水にタンニン酸を0.5〜5.0質量%溶解した冷却水に浸漬することにより冷却して得られることを特徴とする溶融亜鉛めっき処理品の生産方法。