CN110527335A - 太阳能光伏支架用高防尘防水涂层 - Google Patents
太阳能光伏支架用高防尘防水涂层 Download PDFInfo
- Publication number
- CN110527335A CN110527335A CN201910869151.3A CN201910869151A CN110527335A CN 110527335 A CN110527335 A CN 110527335A CN 201910869151 A CN201910869151 A CN 201910869151A CN 110527335 A CN110527335 A CN 110527335A
- Authority
- CN
- China
- Prior art keywords
- parts
- photovoltaic bracket
- waterproof coating
- solar photovoltaic
- high dustproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及光伏技术领域，尤其是一种太阳能光伏支架用高防尘防水涂层；其质量份组成如下：羟基丙烯酸树脂20‑30份、疏水性石蜡8‑12份、疏水剂15‑20份、消泡剂1.2‑2.5份、分散剂1.2‑2.4份、邻羟基苯甲酸苯乙酯2.5‑6份、对甲基苯甲酸间苯二酚酯0.8‑3.2份、纳米银粒子0.6‑3.6份、甲酸香茅酯2‑5份、丙烯酸‑β‑羟乙酯1.8‑4.8份；本发明中的太阳能光伏支架用高防尘防水涂层，添加了疏水性石蜡、疏水剂、邻羟基苯甲酸苯乙酯、对甲基苯甲酸间苯二酚酯、纳米银粒子、甲酸香茅酯和丙烯酸‑β‑羟乙酯，不仅增强了涂层的防水防尘性能，而且可以增加膜层的强度，提高膜层在光伏支架表面的附着力，延长膜层对光伏支架的保护寿命，延长光伏支架的使用寿命。
Description
技术领域
本发明涉及光伏技术领域，尤其是一种太阳能光伏支架用高防尘防水涂层。
背景技术
太阳能光伏支架，是太阳能光伏发电系统中为了摆放、安装、固定太阳能面板设计的特殊的支架。一般材质有铝合金、碳钢及不锈钢。固定安装方式直接将太阳能光伏组件朝向低纬度地区放置(与地面成一定的角度)，以串并联的方式组成太阳能光伏阵列，从而达到太阳能光伏发电的目的。其固定方式有多种，如地面固定方式就有桩基法(直接埋入法)、混凝土块配重法、预埋法、地锚法等，屋面固定方式随屋面材料不同而有不同的方案。
光伏支架在使用时，一般是暴露在空气中的，长时间使用后，容易在光伏支架的表面积累灰尘，而且长时间使用后，雨水的侵蚀容易使得光伏支架的表面锈蚀，从而影响光伏支架的使用寿命和使用安全性。
发明内容
针对现有技术存在的上述问题，本发明提供一种能有效保护光伏支架的防尘防水性能的太阳能光伏支架用高防尘防水涂层。
为解决上述技术问题，本发明采用的技术方案如下：
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂20-30份、疏水性石蜡8-12份、疏水剂15-20份、消泡剂1.2-2.5份、分散剂1.2-2.4份、邻羟基苯甲酸苯乙酯2.5-6份、对甲基苯甲酸间苯二酚酯0.8-3.2份、纳米银粒子0.6-3.6份、甲酸香茅酯2-5份、丙烯酸-β-羟乙酯1.8-4.8份。
进一步的，所述疏水剂为聚硅烷的水性阳离子溶液。
进一步的，所述消泡剂选用乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或几种。
进一步的，所述消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
进一步的，所述分散剂选用水玻璃、三聚磷酸钠、六偏磷酸钠、三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶和脂肪酸聚乙二醇酯中的一种或几种。
进一步的，所述分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
进一步的，还包括水性树脂分散体2-6份。
采用本发明的技术方案的有益效果是：
本发明中的太阳能光伏支架用高防尘防水涂层，添加了疏水性石蜡、疏水剂、邻羟基苯甲酸苯乙酯、对甲基苯甲酸间苯二酚酯、纳米银粒子、甲酸香茅酯和丙烯酸-β-羟乙酯，不仅增强了涂层的防水防尘性能，而且可以增加膜层的强度，提高膜层在光伏支架表面的附着力，延长膜层对光伏支架的保护寿命，延长光伏支架的使用寿命。
具体实施方式
下面通过具体实施方式对本发明作进一步详细说明。除非特别说明，下面实施方式中所使用的技术均为本领域内的技术人员已知的常规技术；所使用的仪器设备和试剂等，均为本领域内的技术人员可以通过公共途径如商购等获得的。
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂20-30份、疏水性石蜡8-12份、疏水剂15-20份、消泡剂1.2-2.5份、分散剂1.2-2.4份、邻羟基苯甲酸苯乙酯2.5-6份、对甲基苯甲酸间苯二酚酯0.8-3.2份、纳米银粒子0.6-3.6份、甲酸香茅酯2-5份、丙烯酸-β-羟乙酯1.8-4.8份。
其中，疏水剂为聚硅烷的水性阳离子溶液。
其中，消泡剂选用乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或几种。
其中，消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
其中，分散剂选用水玻璃、三聚磷酸钠、六偏磷酸钠、三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶和脂肪酸聚乙二醇酯中的一种或几种。
其中，分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
其中，还包括水性树脂分散体2-6份。
实施例1
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂20份、疏水性石蜡8份、疏水剂15份、消泡剂1.2份、分散剂1.2份、邻羟基苯甲酸苯乙酯2.5份、对甲基苯甲酸间苯二酚酯0.8份、纳米银粒子0.6份、甲酸香茅酯2份、丙烯酸-β-羟乙酯1.8份。
其中，疏水剂为聚硅烷的水性阳离子溶液。
其中，消泡剂选用乳化硅油。
其中，分散剂选用水玻璃。
实施例2
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂21份、疏水性石蜡9份、疏水剂16份、消泡剂1.5份、分散剂1.5份、邻羟基苯甲酸苯乙酯3份、对甲基苯甲酸间苯二酚酯1份、纳米银粒子0.9份、甲酸香茅酯2.5份、丙烯酸-β-羟乙酯2.1份。
其中，疏水剂为聚硅烷的水性阳离子溶液。
其中，消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
其中，分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
其中，还包括水性树脂分散体2份。
实施例3
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂25份、疏水性石蜡10份、疏水剂18份、消泡剂1.8份、分散剂1.8份、邻羟基苯甲酸苯乙酯4份、对甲基苯甲酸间苯二酚酯2份、纳米银粒子2.1份、甲酸香茅酯3.5份、丙烯酸-β-羟乙酯3。
其中，疏水剂为聚硅烷的水性阳离子溶液。
其中，消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
其中，分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
其中，还包括水性树脂分散体4份。
实施例4
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂26份、疏水性石蜡10份、疏水剂18份、消泡剂2.1份、分散剂2.2份、邻羟基苯甲酸苯乙酯5份、对甲基苯甲酸间苯二酚酯3份、纳米银粒子3.2份、甲酸香茅酯4.5份、丙烯酸-β-羟乙酯4份。
其中，疏水剂为聚硅烷的水性阳离子溶液。
其中，消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
其中，分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
其中，还包括水性树脂分散体5份。
实施例5
太阳能光伏支架用高防尘防水涂层，其质量份组成如下：羟基丙烯酸树脂30份、疏水性石蜡12份、疏水剂20份、消泡2.5份、分散剂2.4份、邻羟基苯甲酸苯乙酯6份、对甲基苯甲酸间苯二酚酯3.2份、纳米银粒子3.6份、甲酸香茅酯5份、丙烯酸-β-羟乙酯4.8份。
其中，疏水剂为聚硅烷的水性阳离子溶液。
其中，消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
其中，分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
其中，还包括水性树脂分散体6份。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。
Claims (7)
1.太阳能光伏支架用高防尘防水涂层，其特征在于：其质量份组成如下：羟基丙烯酸树脂20-30份、疏水性石蜡8-12份、疏水剂15-20份、消泡剂1.2-2.5份、分散剂1.2-2.4份、邻羟基苯甲酸苯乙酯2.5-6份、对甲基苯甲酸间苯二酚酯0.8-3.2份、纳米银粒子0.6-3.6份、甲酸香茅酯2-5份、丙烯酸-β-羟乙酯1.8-4.8份。
2.根据权利要求1所述的太阳能光伏支架用高防尘防水涂层，其特征在于：所述疏水剂为聚硅烷的水性阳离子溶液。
3.根据权利要求1所述的太阳能光伏支架用高防尘防水涂层，其特征在于：所述消泡剂选用乳化硅油、高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚和聚二甲基硅氧烷中的一种或几种。
4.根据权利要求3所述的太阳能光伏支架用高防尘防水涂层，其特征在于：所述消泡剂选用聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚和聚氧丙烯甘油醚的混合物，其质量比为1:1:2。
5.根据权利要求1所述的太阳能光伏支架用高防尘防水涂层，其特征在于：所述分散剂选用水玻璃、三聚磷酸钠、六偏磷酸钠、三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶和脂肪酸聚乙二醇酯中的一种或几种。
6.根据权利要求5所述的太阳能光伏支架用高防尘防水涂层，其特征在于：所述分散剂选用纤维素衍生物和古尔胶的混合物，其质量比为1:3。
7.根据权利要求1所述的太阳能光伏支架用高防尘防水涂层，其特征在于：还包括水性树脂分散体2-6份。