CN104212385A - 混凝土表面渗透型防水胶及其制备方法 - Google Patents
混凝土表面渗透型防水胶及其制备方法 Download PDFInfo
- Publication number
- CN104212385A CN104212385A CN201410428464.2A CN201410428464A CN104212385A CN 104212385 A CN104212385 A CN 104212385A CN 201410428464 A CN201410428464 A CN 201410428464A CN 104212385 A CN104212385 A CN 104212385A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- parts
- concrete surface
- waterproof glue
- type waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
混凝土表面渗透型防水胶，各组分的重量比为：蒸馏水：400-600；聚磷酸钠：0.5-5；十二水硫酸铝钾：2-10；乙二胺四乙酸：5-40；聚氧乙烯醚：0.5-3；过氧化氢：0.5-4；硅酸钠：2-10；苯丙乳液：200-400；硅烷氧烷乳液：50-300。按上述组分重量比称量各组分，先将苯丙乳乳液和硅烷氧烷乳液与蒸馏水混合均匀形成新乳液。将聚磷酸钠、十二水硫酸铝钾、乙二胺乙二酸、硅酸钠按量加入蒸馏水搅拌均匀后加入新乳液中。最后将过氧化氢和聚氧乙烯醚加入新乳液中搅拌均匀至没有气泡，最终形成产品。本发明具有渗透作用，耐腐蚀性能好，憎水抗渗性能优越，而且无毒无害，成本更低。
Description
技术领域：本发明涉及一种防水剂及其制备方法，尤其是一种混凝土表面渗透型防水胶及其制备方法。
背景技术：当前，尽管防水材料的更新换代层出不穷，施工方法也多种多样，但受到设计、材料、施工、环境及管理等多方面的影响下，建筑结构的渗漏水现象依然十分严重，有调查结果显示，在房屋渗漏水原因中，材料因素占20％，设计因素占26％，施工因素占48％，管理及客观维护因素占6％。因此，开发一种易于施工、适用性好、性能优良、经济实惠的防水剂是我们当前急需解决的问题。
此外，混凝土表面的渗透性与耐久性息息相关。混凝土的渗透性越好，越容易受到外界环境(如水冻。盐冻、碳化等)的影响，其耐久性越差。不少防水材料作用于混凝土基面，均起到隔离水的作用，并没有真正的与结构混凝土层成为整体，一旦搭接不良，易于窜水渗漏，后期防水堵漏处理困难。尤其对于渗漏的卫生间一般都需要剔凿掉瓷砖层后再进行防水处理，这就造成了不必要的浪费。虽然也有水泥基渗透结晶型防水材料、沥青基自粘卷材以及非固化沥青复合自黏卷材等新型防水材料的问世，但对其性能机理解释不清，而且材料价格相对较高。
因此，无论从建筑防水材料的更新换代的角度还是从某些防水材料存在的客观问题来分析，开发混凝土表面渗透型防水胶具有现实意义。
发明内容：针对上述现有技术的缺点，本发明提供了一种表面渗透、防潮憎水、施工简便、成本更低的混凝土表面渗透型防水胶及其制备方法。
为实现上述目的，本发明采用的技术方案是：混凝土表面渗透型防水胶，包括聚磷酸钠、十二水硫酸铝钾、乙二胺四乙酸、聚氧乙烯醚、过氧化氢、硅酸钠、苯丙乳液、硅烷氧烷乳液，各组分的重量比为：蒸馏水：400-600；聚磷酸钠：0.5-5；十二水硫酸铝钾：2-10；乙二胺四乙酸：5-40；聚氧乙烯醚：0.5-3；过氧化氢：0.5-4；硅酸钠：2-10；苯丙乳液：200-400；硅烷氧烷乳液：50-300。
优选的,苯丙乳液和硅烷氧烷乳液固含量50％左右。
混凝土表面渗透型防水胶的制备方法是：按上述组分重量比称量各组分，先将苯丙乳乳液和硅烷氧烷乳液与蒸馏水混合均匀形成新乳液。将聚磷酸钠、十二水硫酸铝钾、乙二胺乙二酸、硅酸钠按量加入蒸馏水搅拌均匀后加入新乳液中。最后将过氧化氢和聚氧乙烯醚加入新乳液中搅拌均匀至没有气泡，最终形成产品。
本发明中，固体组分的细度控制在150～200目左右，纯度95％以上。
本发明特点如下：
1、渗透作用，可渗透至混凝土内部；
2、耐腐蚀性能好，可安全应用于防腐工程；
3、憎水抗渗性能优越，与混凝土形成有机整体，阻断渗水通道；
4、无毒无害，可安全用于饮用水工程，耐久性好；
5、施工方便，既可以喷涂刷涂于混凝土表面，又可以掺合于混凝土。
具体实施方式：
混凝土表面渗透型防水胶，是由聚磷酸钠、十二水硫酸铝钾、乙二胺四乙酸、聚氧乙烯醚、过氧化氢、硅酸钠、苯丙乳液、硅烷氧烷乳液组成。各组分的重量比如下表所示：
按照上述比例和前面的制备方法，可以制备出施工方式不同，性能要求略有差异的混凝土表面渗透型防水胶。
防水胶按照前面所述的重量比称量好后，按规定放料顺序放料后搅拌均匀。刷涂或喷涂时，先将混凝土基面清理干净，喷刷涂要均匀，宜喷刷涂三遍，每遍间隔2小时左右，表面涂层厚度一般为0.8～1.5mm。对于掺合混凝土用量一般为胶凝材料用量的3～5％，具体水灰比还要根据具体实际情况施工前确定。该防水胶具有高渗透性，高触变性能，深入混凝土表面后形成的涂膜抗渗防潮憎水性能优越。尤其是掺入混凝土后，大大增加了混凝土的柔性和抗渗性，提高了混凝土的耐久性。
本发明是一种新型混凝土表面渗透型防水胶，其材料不但施工操作性高，而且适应设计要求和材料更新换代的发展，综合了渗透结晶型防水材料的渗透性和乳液类产品柔性好，粘结强度高等特点，可广泛应用于新建建筑和既有建筑混凝土结构地下室、内外墙、卫生间等抗渗混凝土、防水砂浆、防水涂料、防水漆中，起到防潮、抗渗。憎水等作用。
Claims (4)
1.混凝土表面渗透型防水胶，其特征在于：包括聚磷酸钠、十二水硫酸铝钾、乙二胺四乙酸、聚氧乙烯醚、过氧化氢、硅酸钠、苯丙乳液、硅烷氧烷乳液，各组分的重量比为：蒸馏水：400-600；聚磷酸钠：0.5-5；十二水硫酸铝钾：2-10；乙二胺四乙酸：5-40；聚氧乙烯醚：0.5-3；过氧化氢：0.5-4；硅酸钠：2-10；苯丙乳液：200-400；硅烷氧烷乳液：50-300。
2.如权利要求1所述的混凝土表面渗透型防水胶，其特征在于，苯丙乳液和硅烷氧烷乳液含固量为50％。
3.混凝土表面渗透型防水胶的制备方法，其特征在于：按权利要求1所述重量比称量各组分，先将苯丙乳乳液和硅烷氧烷乳液与蒸馏水混合均匀形成新乳液，将聚磷酸钠、十二水硫酸铝钾、乙二胺乙二酸、硅酸钠按量加入蒸馏水搅拌均匀后加入新乳液中，最后将过氧化氢和聚氧乙烯醚加入新乳液中搅拌均匀至没有气泡，最终形成产品。
4.如权利要求3所述的混凝土表面渗透型防水胶的制备方法，其特征在于：固体组分的细度控制在150～200目，纯度95％以上。