CN104559373A - 一种外墙防水涂料及其制备方法 - Google Patents

一种外墙防水涂料及其制备方法 Download PDF

Info

Publication number
CN104559373A
CN104559373A CN201410841780.2A CN201410841780A CN104559373A CN 104559373 A CN104559373 A CN 104559373A CN 201410841780 A CN201410841780 A CN 201410841780A CN 104559373 A CN104559373 A CN 104559373A
Authority
CN
China
Prior art keywords
parts
powder
agent
white
waterproof paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410841780.2A
Other languages
English (en)
Inventor
张同波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingjian Group Co Ltd
Original Assignee
Qingjian Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingjian Group Co Ltd filed Critical Qingjian Group Co Ltd
Priority to CN201410841780.2A priority Critical patent/CN104559373A/zh
Publication of CN104559373A publication Critical patent/CN104559373A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种外墙防水涂料，包括下列质量份数的组分，甲基丙烯酸酯10-12份，硅丙乳液20-40份，白石粉20-30份，白硅酸盐熟料10-15份，珍珠岩粉4-6份，脱硫粉8-10份，丙烯酸15-30份，超细二氧化硅粉3-8份，分散剂1-2份，流平剂0.3-1.0份，增稠剂2-3份，防腐剂0.5-1.5份，消泡剂0.3-0.5份，抗裂剂0.6-0.9份，水20-30份，纤维素醚0.05-0.1份，十二烷基苯磺酸钠0.1-0.2份。本发明的耐候性防水外墙涂料，具有极佳的高耐候性、防水性、耐化学腐蚀性、耐水性、耐擦洗性和耐人工老化等优点。

Description

一种外墙防水涂料及其制备方法
技术领域
本发明涉及一种建筑材料，尤其是一种外墙防水涂料及其制备方法。
背景技术
涂料的应用较为广泛，在建筑物的外墙、地面等地方都有用到。建筑防水涂料是在常温下呈无固定形状的粘稠状液态高分子合成材料，经涂布后，通过溶剂的挥发或水分的蒸发或反应固化后在基层表面可形成坚韧的防水涂膜的材料。目前建筑外墙涂料种类有苯丙涂料、纯丙涂料、丙烯酸涂料、环氧涂料、氟碳涂料等。建筑外墙防水涂料由于是在室外使用，常年累月的接受风吹日晒，因此与室内防水涂料相比，需要更强的防水抗渗能力，保色性能好，能够抵抗紫外线的照射。在夏季温度过高时，经过长时间的暴晒后，涂料也会有开裂的情况产生。大多数建筑物墙体以水泥砂浆抹面为基层，当受到温度变化、冻融循环等因素影响时，墙体通常会产生裂缝，随着基层的裂纹产生和扩展导致涂层也产生开裂；随着时间延长及上述破坏因素的积聚，裂缝会进一步加大、加深，不仅影响美观，更重要的是对建筑物产生不利影响甚至危害。
发明内容
本发明要解决的是提供一种价格低廉又环保的外墙防水涂料及其制备方法。
为解决上述技术问题，本发明的外墙防水涂料，包括下列质量份数的组分，甲基丙烯酸酯10-12份，硅丙乳液20-40份，白石粉20-30份，白硅酸盐熟料10-15份，珍珠岩粉4-6份，脱硫粉8-10份，丙烯酸15-30份，超细二氧化硅粉3-8份，分散剂1-2份，流平剂0.3-1.0份，增稠剂2-3份，防腐剂0.5-1.5份，消泡剂0.3-0.5份，抗裂剂0.6-0.9份，水20-30份，纤维素醚0.05-0.1份，十二烷基苯磺酸钠0.1-0.2份。
所述抗裂剂包括，丙烯酸乳液0.2份，乙二醇0.1份，甲基纤维素0.05份，玻璃纤维0.05份，聚丙烯酰胺0.5份。
优选的，所述组分的质量份数为甲基丙烯酸酯10份，硅丙乳液25份，白石粉25份，白硅酸盐熟料12份，珍珠岩粉5份，脱硫粉8份，丙烯酸15份，超细二氧化硅粉5份，分散剂1份，流平剂0.4份，增稠剂2份，防腐剂0.5份，消泡剂0.5份，抗裂剂0.8份，水20份，纤维素醚0.1份，十二烷基苯磺酸钠0. 2份。
本发明还涉及一种制造如权利要求1所述的外墙防水涂的方法，包括下列步骤，将20-30份水、10-12份甲基丙烯酸酯、20-40份硅丙乳液、 15-30份丙烯酸混合，盐酸调节pH至3，升温至50℃，搅拌30分钟；在上述混合物中加入20-30份白石粉、10-15份白硅酸盐熟料、4-6份珍珠岩粉、8-10份脱硫粉、1-2份分散剂，升温至80℃～90℃后研磨3小时，研磨转速为至少500转每分钟；后冷却至40-50℃，将混合物PH调节至7.5-8.5，加入流平剂0.3-1.0份，增稠剂2-3份，防腐剂0.5-1.5份，消泡剂0.3-0.5份，抗裂剂0.6-0.9份，纤维素醚0.05-0.1份，十二烷基苯磺酸钠0.1-0.2份，搅拌30分钟。
本发明的耐候性防水外墙涂料，具有极佳的高耐候性、防水性、耐化学腐蚀性、耐水性、耐擦洗性和耐人工老化等优点。本发明的外墙涂料绿色环保，不存在有机溶剂的污染，对人体没有伤害，保温涂料附着力强，可与基体牢固结合，不会产生起皮、脱落现象。
具体实施方式
实施例1
本发明的外墙防水涂料，包括下列质量份数的组分，甲基丙烯酸酯10份，硅丙乳液25份，白石粉22份，白硅酸盐熟料12份，珍珠岩粉4份，脱硫粉10份，丙烯酸20份，超细二氧化硅粉4份，分散剂1份，流平剂0.5份，增稠剂2份，防腐剂0.8份，消泡剂0.4份，抗裂剂0.8份，水25份，纤维素醚0.07份，十二烷基苯磺酸钠0.15份，抗裂剂包括，丙烯酸乳液0.2份，乙二醇0.1份，甲基纤维素0.05份，玻璃纤维0.05份，聚丙烯酰胺0.5份。
实施例2
本发明的外墙防水涂料，包括下列质量份数的组分，甲基丙烯酸酯10份，硅丙乳液25份，白石粉25份，白硅酸盐熟料12份，珍珠岩粉5份，脱硫粉8份，丙烯酸15份，超细二氧化硅粉5份，分散剂1份，流平剂0.4份，增稠剂2份，防腐剂0.5份，消泡剂0.5份，抗裂剂0.8份，水20份，纤维素醚0.1份，十二烷基苯磺酸钠0. 2份。抗裂剂包括，丙烯酸乳液0.2份，乙二醇0.1份，甲基纤维素0.05份，玻璃纤维0.05份，聚丙烯酰胺0.5份。
本发明的制造外墙防水涂的方法，包括下列步骤，将20-30份水、10-12份甲基丙烯酸酯、20-40份硅丙乳液、 15-30份丙烯酸混合，盐酸调节pH至3，升温至50℃，搅拌30分钟；在上述混合物中加入20-30份白石粉、10-15份白硅酸盐熟料、4-6份珍珠岩粉、8-10份脱硫粉、1-2份分散剂，升温至80℃～90℃后研磨3小时，研磨转速为至少500转每分钟；后冷却至40-50℃，将混合物PH调节至7.5-8.5，加入流平剂0.3-1.0份，增稠剂2-3份，防腐剂0.5-1.5份，消泡剂0.3-0.5份，抗裂剂0.6-0.9份，纤维素醚0.05-0.1份，十二烷基苯磺酸钠0.1-0.2份，搅拌30分钟。

Claims (4)

1.一种外墙防水涂料，其特征在于：包括下列质量份数的组分，甲基丙烯酸酯10-12份，硅丙乳液20-40份，白石粉20-30份，白硅酸盐熟料10-15份，珍珠岩粉4-6份，脱硫粉8-10份，丙烯酸15-30份，超细二氧化硅粉3-8份，分散剂1-2份，流平剂0.3-1.0份，增稠剂2-3份，防腐剂0.5-1.5份，消泡剂0.3-0.5份，抗裂剂0.6-0.9份，水20-30份，纤维素醚0.05-0.1份，十二烷基苯磺酸钠0.1-0.2份。
2.按照权利要求1所述的外墙防水涂料，其特征在于：所述抗裂剂包括，丙烯酸乳液0.2份，乙二醇0.1份，甲基纤维素0.05份，玻璃纤维0.05份，聚丙烯酰胺0.5份。
3.按照权利要求2所述的外墙防水涂料，其特征在于：所述组分的质量份数为甲基丙烯酸酯10份，硅丙乳液25份，白石粉25份，白硅酸盐熟料12份，珍珠岩粉5份，脱硫粉8份，丙烯酸15份，超细二氧化硅粉5份，分散剂1份，流平剂0.4份，增稠剂2份，防腐剂0.5份，消泡剂0.5份，抗裂剂0.8份，水20份，纤维素醚0.1份，十二烷基苯磺酸钠0. 2份。
4.一种制造如权利要求1所述的外墙防水涂的方法，其特征在于：包括下列步骤，
将20-30份水、10-12份甲基丙烯酸酯、20-40份硅丙乳液、 15-30份丙烯酸混合，盐酸调节pH至3，升温至50℃，搅拌30分钟；
在上述混合物中加入20-30份白石粉、10-15份白硅酸盐熟料、4-6份珍珠岩粉、8-10份脱硫粉、1-2份分散剂，升温至80℃～90℃后研磨3小时，研磨转速为至少500转每分钟；
后冷却至40-50℃，将混合物PH调节至7.5-8.5，加入流平剂0.3-1.0份，增稠剂2-3份，防腐剂0.5-1.5份，消泡剂0.3-0.5份，抗裂剂0.6-0.9份，纤维素醚0.05-0.1份，十二烷基苯磺酸钠0.1-0.2份，搅拌30分钟。
CN201410841780.2A 2014-12-30 2014-12-30 一种外墙防水涂料及其制备方法 Pending CN104559373A (zh)