CN102249595A - 外保温墙专用柔性质感涂料及其制备方法 - Google Patents
外保温墙专用柔性质感涂料及其制备方法 Download PDFInfo
- Publication number
- CN102249595A CN102249595A CN 201110109150 CN201110109150A CN102249595A CN 102249595 A CN102249595 A CN 102249595A CN 201110109150 CN201110109150 CN 201110109150 CN 201110109150 A CN201110109150 A CN 201110109150A CN 102249595 A CN102249595 A CN 102249595A
- Authority
- CN
- China
- Prior art keywords
- texture coating
- flexible texture
- special
- coating
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种外保温墙专用柔性质感涂料,先将水、防霉剂、防腐剂、分散剂、润湿剂、消泡剂、钛白粉和重钙按质量百分比混合在一起并进行高速分散备用;然后将乳液、石英砂和消泡剂,按质量百分比混合在一起,并加入到上述制备好的混合液中,进行中速搅拌;再将纤维素和水按质量百分比混合,并搅拌制成纤维素混合料备用;然后将上述经中速搅拌制得得混合物加入纤维素混合料进行搅拌,使纤维素混合料均匀地起到增稠效果;最后对上述成品进行调色处理。本发明不易开裂、粘结强度高,能有效防止涂料变质,而且具有良好的防水性和杰出的抗渗透性,具有优异的柔韧性,能弥补细微裂缝,延长了外保温墙的使用寿命,有效保护了建筑物。
Description
技术领域
本发明涉及建筑涂料技术领域,尤其涉及一种外保温墙专用柔性质感涂料及其制备方法。
背景技术
STUCCO(灰泥)源于欧美,开始是以水泥为粘结剂,为了避免开裂,改用乳液,做到了艺术装饰性与保护作用的统一,应用于内外墙保护。九十年代后,在欧美普及。最近开始在国内流行,主要是几家国外跨国公司的品牌。
中国专利CN101633812A《一种弹性质感涂料及其制备方法》主要用于公共建筑和住宅建筑的外墙装饰工程,采用的弹性乳液是硅丙或纯丙复配方法,同时采用了不同规格的重钙来制备,由于重钙的强度不如石英砂,同时该涂料的弹性太好,在应用于具有外保温墙体时与外保温苯板温差不同引起的延伸率不一致,这样会使该涂料开裂,不仅影响美观,而且容易渗水,影响外保温墙的使用寿命。而中国专利CN1364838A和CN101851450A均采用氟碳乳液和氟碳与有机硅乳液,这些乳液本身没有任何弹性,很容易造成装饰涂料的开裂,不仅影响外观,更重要的是表面水的侵入,使得外保温粘结胶浆和抹面胶浆吸水率大大提高。
其中,吸水率高的负作用是:
1、可引起混凝土结构性能破坏,如砂浆的碳化,钢筋锈蚀;
2、冻融破坏,使体积膨胀内应力太大,使抹面和粘结砂浆开裂;
3、苯板吸水后,导热系数升高,严重影响保温性能。
发明内容
本发明针对现有技术存在的问题提供一种外保温墙专用柔性质感涂料,在具有表面质感和花纹的同时不仅具有抗拉耐折、不易开裂、粘结强度高,能有效防止涂料变质,而且具有良好的防水性和杰出的抗渗透性,并具有优异的柔韧性,能弥补细微裂缝,从而有效保护建筑物,延长了外保温墙的使用寿命。
本发明针对现有技术存在的问题提供一种外保温墙专用柔性质感涂料的制备方法。
为实现上述目的,本发明的技术方案是:外保温墙专用柔性质感涂料,它由以下重量配比的原料组成:
其中各原料的重量配比为:
所述的防霉剂是异噻唑啉酮类,防腐剂是异噻唑啉酮类,分散剂是聚羧酸铵盐,润湿剂是非离子型,消泡剂是矿物油。
所述的乳液是核壳纯丙乳液。
所述的纤维素是羟丙基纤维素或羟乙基纤维素,增稠剂包括聚氨酯类、水性膨润土类和丙烯酸酯类。
所述的柔性质感涂料中还包含有适量的色浆。
制备上述涂料的方法是:步骤一,将水、防霉剂、防腐剂、分散剂、润湿剂、消泡剂、钛白粉和重钙,按上述质量百分比混合在一起并进行高速分散,备用;
步骤二,将乳液、石英砂和消泡剂,按上述质量百分比混合在一起,并加入到上述步骤一制备好的混合液中,进行中速搅拌;
步骤三,将纤维素和水按上述质量百分比混合,并搅拌制成纤维素混合料,备用;
步骤四,再将上述步骤二经中速搅拌制得得混合物加入步骤三制成的纤维素混合料进行搅拌,使纤维素混合料均匀地起到增稠效果;
步骤五,对上述成品进行调色处理,加入适量的色浆,以实现调色、对色处理。
所述步骤三将纤维素和水搅拌的时间为10-20分钟。
所述步骤四的搅拌时间是10-20分钟。
本发明的有益效果是:采用柔性乳液使该涂料与外保温的配套性能更优,增加了抗开裂剂,使涂料不易开裂;添加了防冻剂,解决了冬季储存和运输涂料变质问题;采用了石英砂使该涂料的粘结强度更高,同时还能弥补细微裂缝,增添了立体艺术感染性。通过色浆可以根据需要直接进行色彩调配;本发明不仅具有装饰和保护墙面的功能,它还富有抗拉耐折、不易开裂、充分体现无机材料的外观装饰性、耐候性、保色性、耐火性、耐磨性、耐玷污性、高度的防水性和杰出的抗渗透性,其优异的附着力和完美的遮盖率使涂层不易脱落、粉化、起壳等,并抗菌防霉,而且具有较强的防潮、保温、隔音等功能;且无毒,环保,其优异的柔韧性,能弥补裂痕,令建筑物外观不受破坏,最大限度地保护建筑物,使保温性能常年保持良好。另外,本发明与外保温苯板温差引起的延伸率一致,防止该涂料开裂,不易渗水,延长了外保温墙的使用寿命。
具体实施方式
实施例一:
外保温墙专用柔性质感涂料,它由以下重量配比的原料组成:
制备上述涂料的方法是:步骤一,将水、防霉剂、防腐剂、分散剂、润湿剂、消泡剂、钛白粉和重钙,按上述质量百分比混合在一起并进行高速分散,备用;
步骤二,将乳液、石英砂和消泡剂,按上述质量百分比混合在一起,并加入到上述步骤一制备好的混合液中,进行中速搅拌;
步骤三,将纤维素和水按上述质量百分比混合,搅拌10-20分钟,并搅拌制成纤维素混合料,备用;
步骤四,再将上述步骤二经中速搅拌制得得混合物加入步骤三制成的纤维素混合料进行搅拌,使纤维素混合料均匀地起到增稠效果,搅拌10-20分钟制成成品;
步骤五,对步骤四的成品进行调色处理,加入适量的色浆,以实现调色、对色处理。
其中,所述的防霉剂是异噻唑啉酮类,防腐剂是异噻唑啉酮类,这样能广谱杀菌,既防霉又抗藻,户外耐候效果佳。
分散剂是聚羧酸铵盐,能帮助润湿分散填充料及有机颜料,可以使基料中的矿物粒子形成高流态浆料,显著改善涂膜的耐水性及调色性。
润湿剂是非离子型,通过这种润湿剂具有良好的表面活性剂、突出的润湿性能,能显著降低水的表面张力,尤其在低浓度下特别有效。
消泡剂是矿物油,亮泽、鲜艳、能与人类自然亲近无伤害性。
所述的乳液是核壳纯丙乳液,通过这种乳液使本发明具有粒径小、高光泽、耐候性极佳、耐水、耐污染性强等特点。
所述的纤维素是羟丙基纤维素或羟乙基纤维素,通过羟丙基纤维素具有优良的成膜性,所成膜非常坚韧,光泽性良好,弹性充分。而通过羟乙基纤维素具有增稠、悬浮、粘合、浮化、成膜、分散、保水及提供保护胶体。
增稠剂包括聚氨酯类、水性膨润土类和丙烯酸酯类等。
其中,聚氨酯类增稠剂能通过改变原料种类及组成,大幅度地改变产品形态及其性能,得到从柔软到坚硬的最终产品。
水性膨润土类增稠剂膨润土具有很强的吸湿性,能吸附相当于自身体积8-20倍的水而膨胀至30倍;在水介质中能分散呈胶体悬浮液,并具有一定的粘滞性、触变性和润滑性,它和泥沙等的掺和物具有可塑性和粘结性,有较强的阳离子交换能力和吸附能力。
丙烯酸酯类增稠剂具有优良的抗臭氧性、气密性、耐屈挠和耐裂口增长性,以及抗紫外线变色性等。
所述的柔性质感涂料中还包含有适量的色浆。
本发明采用柔性乳液使该涂料与外保温的配套性能更优,增加了抗开裂剂,使其不易开裂,添加了防冻剂,解决了冬季储存和运输涂料变质问题,采用了石英砂使该涂料的粘结强度更高,能弥补细微裂缝、增添了立体艺术感染性,而且防止渗水,提高了外保温苯板的保温性能,延长了它的使用寿命。
本发明完全不加溶剂,属于纯粹的、无毒的环境友好型产品。最关键的是大大降低了吸水率,使建筑物寿命延长,保温性能常年保持良好。
实施例二:
其中各原料的重量配比为:
其它与实施例一基本相同,在此不再赘述。
实施例三:
其它与实施例一基本相同,在此不再赘述。
本发明是为建筑物提供完善的外保温与艺术涂料的有机结合的整体。使用时先在外保温体系上加阳离子封闭底漆,外墙同色底漆,二道柔性质感涂料,最后水性氟碳罩面墙漆。由于一般外保温抹面砂浆在北方地区PH为12,阳离子封闭底漆可保证优异的抗水、抗碱、抗盐折性能,避免涂料的发花泛碱。水性氟碳罩面墙漆可大大提高涂料的耐污性,使几年后建筑物仍然焕然一新,外墙同色底漆的作用是为了提高遮盖力。
本发明能提供客户所需要的表面质感和花纹,色彩丰富,采用滚筒创造雅致多变的拉毛效果,还可用喷枪薄喷、批刀薄批、搓、滚、压或沫涂等多种施工方法,产生强烈洞石效果和刮砂效果。而且本发明不仅具有装饰和保护墙面的功能,它还具有抗拉耐折、不易开裂、充分体现无机材料的外观装饰性、耐候性、保色性、耐火性、耐磨性、耐玷污性、无毒、无味、粘接力强、高度的防水性和杰出的抗渗透性。其优异的附着力和完美的遮盖率使涂层不易脱落、粉化、起壳等,并抗菌防霉,涂层厚度通常在1-3MM,是乳胶漆的100倍。因此,具有较强的防潮、保温、隔音等功能,其优异的柔韧性能弥补达2MM的裂痕,令建筑物外观不受破坏,是起各种保护作用的涂层,能有效地阻止外界恶劣环境对建筑物侵蚀,延长建筑物外保温墙体的寿命。
Claims (9)
3.根据权利要求1所述的外保温墙专用柔性质感涂料,其特征在于:所述的防霉剂是异噻唑啉酮类,防腐剂是异噻唑啉酮类,分散剂是聚羧酸铵盐,润湿剂是非离子型,消泡剂是矿物油。
4.根据权利要求1所述的外保温墙专用柔性质感涂料,其特征在于:所述的乳液是核壳纯丙乳液。
5.根据权利要求4所述的外保温墙专用柔性质感涂料,其特征在于:所述的纤维素是羟丙基纤维素或羟乙基纤维素,增稠剂包括聚氨酯类、水性膨润土类和丙烯酸酯类。
6.根据权利要求1所述的外保温墙专用柔性质感涂料,其特征在于:所述的柔性质感涂料中还包含有适量的色浆。
7.根据权利要求1所述的外保温墙专用柔性质感涂料的制备方法,其特征在于:
步骤一,将水、防霉剂、防腐剂、分散剂、润湿剂、消泡剂、钛白粉和重钙,按上述质量百分比混合在一起并进行高速分散,备用;
步骤二,将乳液、石英砂和消泡剂,按上述质量百分比混合在一起,并加入到上述步骤一制备好的混合液中,进行中速搅拌;
步骤三,将纤维素和水按上述质量百分比混合,并搅拌制成纤维素混合料,备用;
步骤四,再将上述步骤二经中速搅拌制得得混合物加入步骤三制成的纤维素混合料进行搅拌,使纤维素混合料均匀地起到增稠效果;
步骤五,对上述成品进行调色处理,加入适量的色浆,以实现调色、对色处理。
8.根据权利要求7所述的外保温墙专用柔性质感涂料的制备方法,其特征在于:所述步骤三将纤维素和水搅拌的时间为10-20分钟。
9.根据权利要求7所述的外保温墙专用柔性质感涂料的制备方法,其特征在于:所述步骤四的搅拌时间是10-20分钟。