CN104193257A - 一种应用于外墙瓷砖粘结用的干料 - Google Patents

一种应用于外墙瓷砖粘结用的干料 Download PDF

Info

Publication number
CN104193257A
CN104193257A CN201410385163.6A CN201410385163A CN104193257A CN 104193257 A CN104193257 A CN 104193257A CN 201410385163 A CN201410385163 A CN 201410385163A CN 104193257 A CN104193257 A CN 104193257A
Authority
CN
China
Prior art keywords
parts
tiles
tile
glue
siccative
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410385163.6A
Other languages
English (en)
Inventor
孙卉
王秀凤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANJING SUBAO ENERGY-SAVING TECHNOLOGY Co Ltd
Original Assignee
NANJING SUBAO ENERGY-SAVING TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANJING SUBAO ENERGY-SAVING TECHNOLOGY Co Ltd filed Critical NANJING SUBAO ENERGY-SAVING TECHNOLOGY Co Ltd
Priority to CN201410385163.6A priority Critical patent/CN104193257A/zh
Publication of CN104193257A publication Critical patent/CN104193257A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种应用于外墙瓷砖粘结用的干料，它包括以下各组分：硅酸盐水泥为400~500重量份，石英砂为500~600重量份，粘度为8万~12万的羟丙基甲基纤维素为2~3重量份，可再分散性乳胶粉为10~20重量份，有机硅憎水剂为0.3~0.5重量份，淀粉醚为0.5~1.0重量份，甲酸钙为0.5~1.0重量份，聚羧酸减水剂为1~2重量份，聚乙烯醇2488为2~4重量份。使用的本发明粘贴瓷砖，瓷砖与基层墙体粘结牢固，防水性能好，抗返碱性能优；而在施工时，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可，本发明的瓷砖胶抗流挂性能好，粘结力强，瓷砖找平速度快，降低了施工难度。

Description

一种应用于外墙瓷砖粘结用的干料
技术领域
本发明公开了一种建筑墙体粘贴瓷砖使用的瓷砖胶干料，本发明尤其是涉及一种应用于外墙瓷砖粘结用的干料。
背景技术
近年来，我国对于建筑的技术要求越来越高，对建筑材料的防水防火和外观要求也越来越高，而粘贴瓷砖是建筑节能材料的其中的一个重要组成，粘贴瓷砖不仅能够满足对建筑外观多样化的要求，而且具有良好的防水性能和防火性能，其主要组成材料为无机防火A级材料，所以防火性能优异，而且其材料粘结力强，强度高，耐候性能耗，抗返碱性能高，而传统的瓷砖胶材料在粘结力和耐候性、抗返碱性能方面不能够让人完全满意。
目前的建筑墙体粘贴瓷砖后，在经过长时间的受潮以及风吹雨淋日晒后，易出现返碱甚至脱落现象。
发明内容
本发明的目的是克服现有技术中存在的不足，提供一种粘结力强、强度高、耐候性好、抗返碱性能强、无毒无害无污染的环保节能的墙体瓷砖胶干料。
按照本发明提供的技术方案，所述一种粘贴瓷砖的瓷砖胶干料包括以下各组分：普通硅酸盐水泥为400～500重量份，石英砂为500～600重量份，粘度为8万～12万的羟丙基甲基纤维素为2～3重量份，可再分散性乳胶粉为10～20重量份，有机硅憎水剂为0.3～0.5重量份，淀粉醚为0.5～1.0重量份，甲酸钙为0.5～1.0重量份，聚羧酸减水剂为1～2重量份，聚乙烯醇2488为2～4重量份。
所述水泥为标号42.5#普通硅酸盐水泥或52.5#普通硅酸盐水泥。
所述石英砂为分级干燥砂，粒径为0.1～1.5mm。
所述聚羧酸减水剂为聚酯型结构的聚羧酸减水剂或者聚醚型结构的聚羧酸减水剂。
使用的本发明粘贴瓷砖，瓷砖与基层墙体粘结牢固，防水性能好，抗返碱性能优；而在施工时，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可，本发明的瓷砖胶抗流挂性能好，粘接力强，瓷砖找平速度快，这样就缩短了施工时间，降低了施工难度。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
以下实施例使用的羟丙基甲基纤维素醚由赫克力士天普化工有限公司提供，其型号为：M4025。
以下实施例使用的可再分散性乳胶粉为阿克苏诺贝尔(上海)有限公司提供，其型号为：60W。
以下实施例使用的淀粉醚为阿克苏诺贝尔(上海)有限公司所提供，其型号为：ET542。
以下实施例使用的有机硅憎水剂为阿克苏诺贝尔(上海)有限公司所提供，其型号为：SEAL80。
以下实施例使用的聚羧酸减水剂为瑞士SIKA公司所提供，其型号为：VIS3301。
以下实施例使用的聚乙烯醇2488为日本可乐丽公司所提供，其型号为：PVA224。
实施例1
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为400kg，粒径为0.1～1.5mm石英砂为600kg，粘度为8万～12万的羟丙基甲基纤维素为2kg，可再分散性乳胶粉为10kg，有机硅憎水剂为0.3kg，淀粉醚为0.5kg，甲酸钙为0.5kg，聚酯型结构的聚羧酸减水剂为1kg，聚乙烯醇2488为2kg。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表1。
表1
实施例2
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为500kg，粒径为0.1～1.5mm石英砂为500kg，粘度为8万～12万的羟丙基甲基纤维素为3kg，可再分散性乳胶粉为20kg，有机硅憎水剂为0.5kg，淀粉醚为1.0kg，甲酸钙为1.0kg，聚酯型结构的聚羧酸减水剂为2kg，聚乙烯醇2488为4kg。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表2。
表2
实施例3
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为450kg，粒径为0.1～1.5mm石英砂为550kg，粘度为8万～12万的羟丙基甲基纤维素为2.5kg，可再分散性乳胶粉为15kg，有机硅憎水剂为0.4kg，淀粉醚为0.7kg，甲酸钙为0.8kg，聚酯型结构的聚羧酸减水剂为1.5kg，聚乙烯醇2488为3kg。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表3。
表3
实施例4
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为425kg，粒径为0.1～1.5mm石英砂为575kg，粘度为8万～12万的羟丙基甲基纤维素为2.2kg，可再分散性乳胶粉为12kg，有机硅憎水剂为0.35kg，淀粉醚为0.8kg，甲酸钙为0.58kg，聚醚型结构的聚羧酸减水剂为1.2kg，聚乙烯醇2488为2.5kg。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表4。
表4
实施例5
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为475kg，粒径为0.1～1.5mm石英砂为525kg，粘度为8万～12万的羟丙基甲基纤维素为2.8kg，可再分散性乳胶粉为17kg，有机硅憎水剂为0.5kg，淀粉醚为0.8kg，甲酸钙为0.6kg，聚醚型结构的聚羧酸减水剂为1.8kg，聚乙烯醇2488为2.7kg。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表5。
表5
实施例6
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为460kg，粒径为0.1～1.5mm石英砂为540kg，粘度为8万～12万的羟丙基甲基纤维素为2.4kg，可再分散性乳胶粉为16kg，有机硅憎水剂为0.4kg，淀粉醚为0.6kg，甲酸钙为0.6kg，聚醚型结构的聚羧酸减水剂为1.3kg，聚乙烯醇2488为3.2重量份。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表6。
表6
实施例7
一种瓷砖胶干料包括以下各组分：
牌号为42.5#普通硅酸盐水泥为440kg，粒径为0.1～1.5mm石英砂为560kg，粘度为8万～12万的羟丙基甲基纤维素为2.6kg，可再分散性乳胶粉为14kg，有机硅憎水剂为0.4kg，淀粉醚为0.8kg，甲酸钙为0.6kg，聚醚型结构的聚羧酸减水剂为1.7kg，聚乙烯醇2488为2.8kg。该瓷砖胶干料加水210～230kg搅拌均匀即可得到瓷砖胶，只需将本发明加水制成的砂浆直接批刮在瓷砖上面，将瓷砖粘贴在墙体上压实找平即可。该配比制作的瓷砖胶的性能参数见表1。
表7
本发明中的羟丙基甲基纤维素具有保水增稠的作用；
可再分散性乳胶粉，增加砂浆内聚力，增加粘结力，耐水性等作用；
有机硅憎水剂，提高砂浆的防水性能；
淀粉醚，增加砂浆的抗流挂性，增稠；
甲酸钙，增加砂浆强度，改善防冻性；
聚羧酸减水剂，改善砂浆流动性，减少拌合水，增加砂浆强度；
聚乙烯醇，增加砂浆粘稠度，提高砂浆强度；上述多种材料组合起来，使各种材料的亲和性大大的增强，促进水泥水化，协助胶粉成膜，并使砂浆内部结构的密实度结构，并且该发明产品对于瓷砖粘贴的墙体要求低，不仅对于无机结构墙体如混凝土界面、砌砖界面有优良的粘贴性能，对于有机界面，如木板界面等也具有良好的粘结性能。

Claims (4)

1.一种应用于外墙瓷砖粘结用的干料，其特征是该瓷砖胶干料包括以下各组分：普通硅酸盐水泥为400~500重量份，石英砂为500~600重量份，粘度为8万~12万的羟丙基甲基纤维素为2~3重量份，可再分散性乳胶粉为10~20重量份，有机硅憎水剂为0.3~0.5重量份，淀粉醚为0.5~1.0重量份，甲酸钙为0.5~1.0重量份，聚羧酸减水剂为1~2重量份，聚乙烯醇2488为2~4重量份。
2.如权利要求1所述的应用于外墙瓷砖粘结用的干料，其特征是：普通硅酸盐水泥为42.5#或者52.5#水泥。
3.如权利要求1所述的应用于外墙瓷砖粘结用的干料，其特征是：所述石英砂为分级干燥砂，粒径0.1~1.5mm。
4.如权利要求1所述的应用于外墙瓷砖粘结用的干料，其特征是：所述聚羧酸减水剂为聚酯型结构的聚羧酸减水剂或者聚醚型结构的聚羧酸减水剂。
CN201410385163.6A 2014-08-06 2014-08-06 一种应用于外墙瓷砖粘结用的干料 Pending CN104193257A (zh)