CN110479361A - 一种降油浆和多产低碳烯烃的助剂及其制备方法与应用 - Google Patents
一种降油浆和多产低碳烯烃的助剂及其制备方法与应用 Download PDFInfo
- Publication number
- CN110479361A CN110479361A CN201910828114.8A CN201910828114A CN110479361A CN 110479361 A CN110479361 A CN 110479361A CN 201910828114 A CN201910828114 A CN 201910828114A CN 110479361 A CN110479361 A CN 110479361A
- Authority
- CN
- China
- Prior art keywords
- molecular sieve
- auxiliary agent
- low
- slurry oil
- carbon olefines
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种降油浆和多产低碳烯烃的助剂，所述原料的干基相对含量为：40～55wt％含磷MFI分子筛、0～10wt％大孔分子筛、3～20wt％无机粘结剂、8～22wt％无机基质和15～40wt％粘土。该助剂用于催化裂化过程中，能够提高裂化液化气产率，提高液化气中丙烯浓度，提高催化裂化汽油的辛烷值，降低裂化产物中油浆的收率。本发明还公开了上述助剂的制备方法和应用。
Description
技术领域
本发明涉及石油炼制领域，尤其是一种降油浆和多产低碳烯烃的助剂及其制备方法与应用。
背景技术
催化裂化是石油炼制的重要过程，它是炼厂提高其经济效益的重要手段。催化裂化过程是重质油在催化剂的作用下，将转化成汽油、柴油、乙烯、丙烯、丁烯、油浆、干气、焦炭等产品。其中汽油、柴油、乙烯、丙烯、丁烯等产品的经济价值较高，而干气、油浆和焦炭的经济价值较低。
随着原油的重质化，催化裂化过程中的油浆收率逐渐增加。对为了弥补传统催化裂化催化剂的不足，向催化剂中添加油浆助剂，是降低油浆，增产汽油、柴油、液化气的重要途径。WO97/12011公开了一种油浆助剂，该助剂主要由氧化铝、无定形硅铝和分子筛组成，该助剂可以明显提高油浆的裂化能力。CN107376986A公开了一种油浆催化裂化助剂，该助剂由分子筛、基质、活性金属物质、非活性金属物质以及活性助剂组成，该助剂通过活性金属物质和非活性金属物质的协同效益，优化了酸中心数量和酸强度，促进了油浆的裂化能力，并具有优异的抗杂质污染和水热稳定性。CN101745373B公开了一种催化裂化助剂，该助剂含有阶梯孔氧化铝，用于催化裂化过程中，可以提高重油的裂化能力和轻质油的收率，焦炭选择性好。CN102974331B公开了一种催化裂化助剂，该助剂通过加入介孔硅铝材料，用于提高重油的裂化能力和轻质油的产率。CN104588051B公开了一种催化裂化助剂，该助剂以活性中孔材料、磷铝助剂等为原料，所得助剂具有较强的重油裂化能力，更高的轻质油产率及更好的焦炭选择性。US 7101473B2公开了一种高活性催化剂，该催化剂通过原位晶化得到，分子筛含量高，可以有效的降低油浆收率。上述的油浆助剂主要是通过增加助剂中介孔和大孔含量，提高基质的酸性，或提高助剂中的分子筛含量，从而提高助剂的裂化活性，降低油浆收率。
低碳烯烃主要包含乙烯、丙烯和丁烯，它们作为有机化工原料，全世界对低碳烯烃的需求逐年增加。流化催化裂化过程作为低碳烯烃的重要来源，通过向裂化装置中添加低碳烯烃助剂，是增产低碳烯烃的重要途径。CN101450321公开了一种增产丙烯的催化裂化助剂，该助剂加入抗凝结阻聚剂，以及分两步引入硅粘结剂。从而使该助剂具有增产丙烯和耐磨性能好，堆密度小的特点。CN103007988A公开了一种提高低碳烯烃浓度的裂化助剂，该助剂选用磷铝粘结剂，择型分子筛中额外含有磷，以及选自一种或几种过度金属。该助剂可以提高液化气中的丙烯浓度，降低焦炭和干气浓度。CN103785457A公开了一种提高低碳烯烃浓度的裂化助剂，该助剂选用含磷和过渡金属的β分子筛，该助剂可以提高液化气中的丙烯和异丁烯浓度，并提高裂化产物干气中的乙烯浓度。CN102851058A公开了一种提高裂化汽油辛烷值助剂，该助剂选用硅铝比30～150的ZSM-5分子筛，并用金属元素对分子筛进行改性。CN107971000A公开了一种含磷Beta分子筛的催化裂化助剂，该助剂选用含磷Beta分子筛为原料，分子筛的Al分布参数0.4～0.8，微孔比表面积420～520m2/g，介孔体积占总体积30～70wt％。当前市场上的低碳烯烃助剂主要是通过择型分子筛将较长链的烃类转化成丙烯等低碳烯烃。但这类低碳烯烃助剂的裂化活性通常降低，当它加入到催化裂化体系中时，它会稀释催化剂的活性组分，从而导致总体催化剂的裂化活性降低，油浆收率下降。
当前的降油浆助剂和多产低碳烯烃助剂分别具有降低油浆收率和多产低碳烯烃收率的功效，但降油浆助剂没有多产低碳烯烃的功效，多产低碳烯烃助剂也没有降低油浆收率的功效。对于同时具有多产低碳烯烃和少产油浆的催化裂化助剂还很少见诸报道。为了同时达到多产低碳烯烃和降油浆的效果，可以尝试同时添加多产低碳烯烃助剂和降低油浆助剂，但当前多产低碳烯烃助剂主要由磷铝粘结剂组成，助剂中的磷元素在反应过程中会扩散到催化剂和其它助剂中，造成催化剂的活性下降。笔者发现，当多产低碳烯烃助剂和降低油浆助剂组合使用时，产品中的油浆收率没有降低，反而提高了。与此同时，多产烯烃助剂的比表面积通常小于180m2/g，而油浆助剂的比表面积至少大于190m2/g，本发明的多产烯烃助剂和裂化油浆助剂孔道开放，比表面积大于190m2/g，具有很好的多产烯烃和和降油浆性能。
发明内容
本发明的目的之一在于提供一种降油浆和多产低碳烯烃的助剂，该助剂用于催化裂化过程中，能够提高裂化液化气产率，提高液化气中丙烯浓度，提高催化裂化汽油的辛烷值，降低裂化产物中油浆的收率。
为实现上述目的，本发明提供的技术方案是：一种降油浆和多产低碳烯烃的助剂，所述原料的干基相对含量为：40～55wt％含磷MFI分子筛、0～10wt％大孔分子筛、3～20wt％无机粘结剂、8～22wt％无机基质和15～40wt％粘土；优选地，所述原料的干基相对含量为：45～50wt％含磷MFI分子筛，0～5wt％大孔分子筛，10～15wt％无机粘结剂：8～12wt％无机基质，20～30wt％粘土。
所述助剂的比表面积大于190m2/g，所述助剂中P2O5含量小于2wt％。
所述含磷MFI分子筛的SiO2/Al2O3摩尔比为10～50，分子筛中P2O5的含量为1～5wt％；优选地，含磷MFI分子筛的SiO2/Al2O3摩尔比为20～40，分子筛中P2O5的含量为2～4wt％。
所述的含磷MFI分子筛中的磷元素可以是在MFI合成过程中将P引入分子筛中，也可以是通过磷酸或磷酸盐后浸渍在MFI分子筛上。
所述大孔分子筛为Y型分子筛和/或Beta型分子筛。
所述Y型分子筛为稀土改性的Y型分子筛、磷改性的Y型分子筛、稀土和磷改性的Y型分子筛、超稳Y分子筛和/或稀土改性的超稳Y分子筛。
所述无机粘结剂为氧化铝粘结剂、氧化硅粘结剂和/或硅铝粘结剂。
所述无机基质为经过焙烧后的氧化铝和/或无定形硅铝，无机基质的总比表面积>200m2/g。
所述粘土为高岭土、蒙拓土、凹凸棒石、硅藻土和/或海泡石。
本发明的目的之二在于提供上述降油浆和多产低碳烯烃的助剂的制备方法，包括以下步骤：以含磷MFI分子筛、大孔分子筛、无机粘结剂、无机基质、粘土为原料喷雾成型，在450℃～750℃下焙烧固化0.1～10h，即得。
需要说明的是，本发明的助剂可采用通用方法制备得到，并不特别限定该助剂的制备方法。可以采用通用的助剂的制备方法如：将作为主要成分的分子筛、基质、粘结剂、粘土等物质加入去离子水中，打浆形成固含量为20～50wt％的浆液，喷雾成型。
所述焙烧固化温度优选为500～600℃，焙烧时间为1～3h。
所述喷雾成型步骤包括：将含磷MFI分子筛、大孔分子筛、无机粘结剂、无机基质、粘土、水一步或分步混合和打浆处理得到浆液，然后再进行喷雾成型。
本发明的目的之三在于提供上述降油浆和多产低碳烯烃的助剂用于常压渣油、减压渣油、常压蜡油、减压蜡油、直馏蜡油和/或焦化蜡油的催化裂化。
本发明中催化裂化助剂的使用条件为常规的催化裂化反应条件，一般来说，所述的催化裂化反应温度450～650℃，剂油比为4～15；优选的，反应温度490～600℃，剂油比为4～15。
所述助剂占催化裂化体系总催化剂质量的1～30wt％，优选地为5～15wt％。
具体实施方式
下面通过具体实施方式对本发明的权利要求做进一步的详细说明，但不构成任何限定。
在以下实施例和对比例中，样品的比表面积采用BET低温氮吸附法测定，样品的元素组成采用X射线荧光光谱仪测得，样品的磨损指数采用磨损指数分析仪测得。
对比例1：
在搅拌条件下，将3.6kg(干基)高岭土和1.4kg(干基)铝溶胶加入5kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石(比表面积240m2/g，下同)，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入4kg(干基)H-ZSM-5分子筛(SiO2/Al2O3摩尔比为27)和4.5kg去离子水的浆液。继续打浆30min，所得浆液的固含量为40wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到对比助剂C-1。
对比助剂C-1的磨损指数为1.2wt％/h，比表面积为178m2/g，P2O5含量为0wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
对比例2：
在搅拌条件下，将0.75kg(干基)拟薄水铝石分散到1.2kg去离子水中，再缓慢加入4kg浓磷酸(含85wt％H3PO4)，在60℃下搅拌至液体透明，制备得到磷铝粘结剂。将5.5kg(干基)高岭土加入到20kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入0.75kg(干基)铝溶胶粘结剂，再加入上述磷铝粘结剂。搅拌30min后，再加入5kg(干基)H-ZSM-5分子筛(SiO2/Al2O3摩尔比为27)和6kg去离子水的浆液。继续打浆30min，浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到对比助剂C-2。
对比助剂C-2的磨损指数为6.2wt％/h，比表面积为81m2/g，P2O5含量为17.11wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
对比例3：
在搅拌条件下，将2.5kg(干基)拟薄水铝石和1kg(干基)REY分子筛(SiO2/Al2O3摩尔比为5，RE2O3含量为8wt％)加入到10kg去离子水中，搅拌30min，得到分子筛和拟薄水铝石的混合浆液。
在搅拌条件下，将3.7kg(干基)高岭土加入14kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入2kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入2kg酸性硅溶胶溶液(含40wt％SiO2)。搅拌20min后，再加入上述分子筛和拟薄水铝石的混合浆液。继续打浆30min，所得浆液的固含量为25wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到对比助剂C-3。
对比助剂C-3的磨损指数为1.1wt％/h，比表面积为284m2/g，P2O5含量为0wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例1：
利用磷酸二氢氨对H-ZSM-5分子筛(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过550℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为3.2wt％。
将5kg(干基)含磷ZSM-5分子筛加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)高岭土和1.4kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-1。
助剂LOBC-1的磨损指数为1.2wt％/h，比表面积为196m2/g，P2O5含量为1.47wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例2：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为2.8wt％。
将5.5kg(干基)含磷ZSM-5分子筛加入到6kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.4kg(干基)高岭土和1.3kg(干基)铝溶胶加入3.5kg去离子水中，高速搅拌1h，待高岭土完全分散在浆液中后，再加入0.8kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过500℃焙烧3h，得到多产低碳烯烃和降油浆双功能助剂LOBC-2。
助剂LOBC-2的磨损指数为0.5wt％/h，比表面积为205m2/g，P2O5含量为1.54wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例3：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为29)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为2wt％。
将4kg(干基)含磷ZSM-5分子筛和0.9kg(干基)稀土和磷改性的Y型分子筛(骨架SiO2/Al2O3摩尔比为5，RE2O3为4wt％，P2O5为1wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)蒙拓土和0.3kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入2.2kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再0.3kg(干基)加入酸性硅溶胶(含40wt％SiO2)。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为40wt％；浆液经过均质和磨细处理后，喷雾成型，再经过500℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-3。
助剂LOBC-3的磨损指数为2.1wt％/h，比表面积为226m2/g，P2O5含量为0.89wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例4：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为10)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为5wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)超稳Y型分子筛(骨架SiO2/Al2O3摩尔比为9)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)凹凸棒石加入6kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，加入1.4kg(干基)酸性硅溶胶(SiO2含量为40wt％)。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-4。
助剂LOBC-4的磨损指数为0.9wt％/h，比表面积为208m2/g，P2O5含量为2wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例5：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为2.7wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)稀土改性的超稳Y型分子筛(骨架SiO2/Al2O3摩尔比为9，RE2O3为8wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)硅藻土加入6kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，加入1.4kg(干基)硅铝粘结剂(SiO2含量为30wt％，Al2O3含量为3wt％)。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-5。
助剂LOBC-5的磨损指数为1.2wt％/h，比表面积为213m2/g，P2O5含量为1.08wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例6：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为50)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为1wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)P改性的Y型分子筛(骨架SiO2/Al2O3摩尔比为5，P2O5为1wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2kg(干基)海泡石和2kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)磨细无定形硅铝(比表面积289m2/g)。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过750℃焙烧0.1h，得到多产低碳烯烃和降油浆双功能助剂LOBC-6。
助剂LOBC-6的磨损指数为0.9wt％/h，比表面积为221m2/g，P2O5含量为0.5wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例7：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为3.2wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)稀土Y型分子筛(骨架SiO2/Al2O3摩尔比为5，RE2O3为4wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)高岭土和1.4kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-7。
助剂LOBC-7的磨损指数为0.8wt％/h，比表面积为217m2/g，P2O5含量为1.28wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例8：
利用磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为3.2wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)Beta型分子筛(SiO2/Al2O3摩尔比为20)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)高岭土和1.4kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-8。
助剂LOBC-8的磨损指数为1.3wt％/h，比表面积为204m2/g，P2O5含量为1.28wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例9：
利用磷酸对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为3.2wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)稀土超稳Y型分子筛(骨架SiO2/Al2O3摩尔比为9，RE2O3为4wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)高岭土和1.4kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-9。
助剂LOBC-9的磨损指数为0.7wt％/h，比表面积为218m2/g，P2O5含量为1.28wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例10：
利用磷酸对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，再经过500℃焙烧2h，得到含磷ZSM-5分子筛，所得分子筛中P2O5的含量为5wt％。
将4kg(干基)含磷ZSM-5分子筛和1kg(干基)稀土超稳Y型分子筛(骨架SiO2/Al2O3摩尔比为9，RE2O3为4wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.6kg(干基)高岭土和1.4kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-10。
助剂LOBC-10的磨损指数为0.6wt％/h，比表面积为217m2/g，P2O5含量为2wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
实施例11：
依次利用稀土盐和磷酸二氢氨对H-ZSM-5(SiO2/Al2O3摩尔比为27)进行浸渍和闪蒸干燥，经过500℃焙烧2h，得到含磷和含稀土ZSM-5分子筛，所得分子筛中P2O5的含量为3.2wt％，RE2O3的含量为1.8wt％。
将4kg(干基)含磷和含稀土ZSM-5分子筛和1kg(干基)稀土超稳Y型分子筛(骨架SiO2/Al2O3摩尔比为9，RE2O3为4wt％)加入到5.5kg去离子水中，高速搅拌30min，得到含磷MFI分子筛浆液。
在搅拌条件下，将2.5kg(干基)高岭土和1.5kg(干基)铝溶胶加入4kg去离子水中，高速搅拌2h，待高岭土完全分散在浆液中后，再加入1kg(干基)拟薄水铝石，在通过HCl调节浆液的pH至2.5～3.5，使拟薄水铝石发生成胶反应。搅拌30min后，再加入上述分子筛浆液。继续打浆30min，所得浆液的固含量为41wt％；浆液经过均质后，喷雾成型，再经过550℃焙烧2h，得到多产低碳烯烃和降油浆双功能助剂LOBC-11。
助剂LOBC-11的磨损指数为0.6wt％/h，比表面积为212m2/g，P2O5含量为1.28wt％。经过金属和水蒸气钝化处理后，添加15wt％该助剂，用于催化裂化过程中的裂化性能如表3。
在上述实施例和对比例中的催化裂化反应在微型流化床反应器(ACE)和配套气相色谱上评价，研究法辛烷值(RON)采用Agilent公司的气相色谱仪7980A分析。主催化剂工业RFCC平衡剂，对比例和实施例中的助剂分别浸渍4000ppm V和2000ppm Ni之后，再经810℃、100wt％水蒸气老化10h后，用15wt％助剂+85wt％RFCC平衡剂进行催化裂化性能评价。其它检测参见(《石油和石油产品试验方法国家标准》中国标准出版社出版1989年)。
RFCC平衡剂的主要性质如表1，测试原料油的性质如表2。85wt％RFCC平衡剂+15wt％实施例和对比例助剂的催化裂化性能如表3。
表1 RFCC平衡剂的主要性质
表2原料油性质
表3为实施例和对比例样品的催化裂化性能
表3中对比例和实施例中的助剂分别浸渍4000ppm V和2000ppm Ni之后，再经810℃、100wt％水蒸气老化10h后，用15wt％助剂+85wt％RFCC平衡剂进行催化裂化性能评价。催化裂化反应温度为540℃，进油速度为1.2g/min，进油时间为1.5min，剂油比为5。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，在本发明的精神和原则内可以有各种更改和变化，这些等同的变型或替换等，均包含在本发明的保护范围之内。
Claims (10)
1.一种降油浆和多产低碳烯烃的助剂，其特征在于，所述原料的干基相对含量为：40～55wt％含磷MFI分子筛、0～10wt％大孔分子筛、3～20wt％无机粘结剂、8～22wt％无机基质和15～40wt％粘土。
2.根据权利要求1所述降油浆和多产低碳烯烃的助剂，其特征在于，所述含磷MFI分子筛的SiO2/Al2O3摩尔比为10～50，分子筛中P2O5的含量为1～5wt％。
3.根据权利要求1所述降油浆和多产低碳烯烃的助剂，其特征在于，所述大孔分子筛为Y型分子筛和/或Beta型分子筛。
4.根据权利要求3所述降油浆和多产低碳烯烃的助剂，其特征在于，所述Y型分子筛为稀土改性的Y型分子筛、磷改性的Y型分子筛、稀土和磷改性的Y型分子筛、超稳Y分子筛和/或稀土改性的超稳Y分子筛。
5.根据权利要求1所述降油浆和多产低碳烯烃的助剂，其特征在于，所述无机粘结剂为氧化铝粘结剂、氧化硅粘结剂和/或硅铝粘结剂。
6.根据权利要求1所述降油浆和多产低碳烯烃的助剂，其特征在于，所述无机基质为经过焙烧后的氧化铝和/或无定形硅铝，无机基质的总比表面积>200m2/g。
7.根据权利要求1所述降油浆和多产低碳烯烃的助剂，其特征在于，所述粘土为高岭土、蒙拓土、凹凸棒石、硅藻土和/或海泡石。
8.一种如权利要求1所述降油浆和多产低碳烯烃的助剂的制备方法，其特征在于，包括以下步骤：以含磷MFI分子筛、大孔分子筛、无机粘结剂、无机基质、粘土为原料喷雾成型，在450℃～750℃下焙烧固化0.1～10h，即得。
9.一种如权利要求1所述降油浆和多产低碳烯烃的助剂用于常压渣油、减压渣油、常压蜡油、减压蜡油、直馏蜡油和/或焦化蜡油的催化裂化。
10.根据权利要求9所述降油浆和多产低碳烯烃的助剂的应用，其特征在于，所述助剂占催化裂化体系总催化剂质量的1～30wt％。