CN110475006A - 柔性保护盖板及显示装置 - Google Patents

柔性保护盖板及显示装置 Download PDF

Info

Publication number
CN110475006A
CN110475006A CN201910699335.XA CN201910699335A CN110475006A CN 110475006 A CN110475006 A CN 110475006A CN 201910699335 A CN201910699335 A CN 201910699335A CN 110475006 A CN110475006 A CN 110475006A
Authority
CN
China
Prior art keywords
cover board
protective cover
flexible protective
hardening coat
layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910699335.XA
Other languages
English (en)
Inventor
何春梅
陈宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan China Star Optoelectronics Semiconductor Display Technology Co Ltd
Original Assignee
Wuhan China Star Optoelectronics Semiconductor Display Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan China Star Optoelectronics Semiconductor Display Technology Co Ltd filed Critical Wuhan China Star Optoelectronics Semiconductor Display Technology Co Ltd
Priority to CN201910699335.XA priority Critical patent/CN110475006A/zh
Priority to US16/957,755 priority patent/US20210116968A1/en
Priority to PCT/CN2019/107024 priority patent/WO2021017121A1/zh
Publication of CN110475006A publication Critical patent/CN110475006A/zh
Pending legal-status Critical Current

Abstract

一种柔性保护盖板，用于贴附于一显示面板上，所述柔性保护盖板包括至少两层硬化涂层和设置于相邻两层硬化涂层之间的透明层，使得所述硬化涂层与所述透明层交替设置。在本发明中，由于所述硬化涂层的模量比所述透明层的模量大，可以明显增加所述柔性保护盖板的硬度。经仿真计算验证，与传统的柔性盖板相比，本发明所述的柔性保护盖板在保持相同柔性及耐弯折性的同时，硬度提升了8％。

Description

柔性保护盖板及显示装置
技术领域
本发明涉及显示技术领域，特别涉及一种柔性保护盖板及应用该柔性保护盖板的显示装置。
背景技术
折叠手机是未来技术发展趋势。开发折叠手机较关键的部品材料为柔性盖板，即相当于保护屏幕的3D玻璃盖板。
目前，由于玻璃盖板的弯折技术尚不成熟，透明聚酰亚胺搭配硬化涂层材料是目前主流的开发方向。如图1所示的是目前常规的柔性盖板1。如图1所示，所述柔性盖板1包括一透明聚酰亚胺层2和一硬化涂层3。在图1所示的柔性盖板1中，所述硬化涂层3的厚度将直接影响所述柔性盖板1的硬度。所述硬化涂层3的厚度越厚，所述柔性盖板1的硬度越高，但在弯折时会产生断裂；而所述硬化涂层3的厚度降低则会使所述柔性盖板1的柔性增加，但存在硬度不足的问题。因此，如图1所示的常规柔性盖板1的硬度于柔性相互限制而无法达到完美平衡。
因此，有必要提供一种新的柔性盖板，以克服上述缺陷。
发明内容
本发明的目的在于提供一种柔性保护盖板，通过设置硬化涂层，可以明显增加所述柔性保护盖板的硬度。
为了达到上述目的，根据本发明的一方面，提供一种柔性保护盖板，用于贴附于一显示面板上；所述柔性保护盖板包括至少两层硬化涂层和设置于相邻两层硬化涂层之间的透明层。这样，在本发明所述柔性保护盖板中，所述硬化涂层与所述透明层呈现交替设置，并且，所述硬化涂层作为所述柔性保护盖板的表面。即，呈现多层结构的所述柔性保护盖板的顶层和底层均为硬化涂层。
在本发明一实施例中，所述柔性保护盖板包括依次设置的第一硬化涂层、第一透明层、第二硬化涂层。
在本发明一实施例中，至少一层硬化涂层的材料为氮化硅、氧化硅、氮化硅掺杂的有机材料、氧化硅掺杂的有机材料中的任一种。例如，所述第一硬化涂层和所述第二硬化涂层的至少一者的材料为氮化硅、氧化硅、氮化硅掺杂的有机材料、氧化硅掺杂的有机材料中的任一种。
在本发明一实施例中，所述柔性保护盖板还包括：设置在所述第二硬化涂层上的第二透明层、以及设置在所述第二透明层上的第三硬化涂层。
在本发明一实施例中，所有所述硬化涂层的厚度总和小于或等于20μm。
在本发明一实施例中，所有所述透明层的厚度总和小于或等于80μm。
在本发明一实施例中，所有所述硬化涂层的厚度总和可以是1～20μm范围中的任意一个数值。所有所述硬化涂层的厚度总和可以是例如但不限于：2μm，4μm，6μm，8μm，10μm，12μm，14μm，16μm，18μm，20μm。
在本发明一实施例中，所有所述透明层的厚度总和可以是1～80μm范围中的任意一个数值。所有所述硬化涂层的厚度总和可以是例如但不限于：5μm，10μm，15μm，20μm，25μm，30μm，35μm，40μm，45μm，50μm，55μm，60μm，65μm，70μm，75μm，80μm。
在本发明一实施例中，每一所述硬化涂层的厚度相同。
在本发明一实施例中，每一所述透明层的厚度相同。
在本发明一实施例中，所述柔性保护盖板包括至少一层第一硬化涂层和至少一层第二硬化涂层；其中，所述第二硬化涂层的材料为氮化硅、氧化硅、氮化硅掺杂的有机材料、或氧化硅掺杂的有机材料。
在本发明一实施例中，所述柔性保护盖板包括一第一硬化涂层，设置于所述第一硬化涂层上的第一层透明层，以及，设置于所述透明层上的一第二硬化涂层。优选地，所述柔性保护盖板还包括设置于所述第二硬化涂层上的第二层透明层，以及设置于所述透明层上的第二层所述第一硬化涂层。
在本发明一实施例中，所述透明层的材料为透明聚酰亚胺、聚对苯二甲酸乙二醇酯(PET)、聚萘二甲酸乙二醇酯(PEN)、聚甲基丙烯酸甲酯(PMMA)中的至少一种。
本领域技术人员可以理解的是，如无特殊说明，本发明所述硬化涂层中的至少一层或第一硬化涂层由本领域已知的材料制成。
根据本发明的另一方面，提供一种显示装置，包括一显示面板和上述任意所述的柔性保护盖板，其中，所述柔性保护盖板设置于所述显示面板的一侧面上。尤其是，所述柔性保护盖板设置于所述显示面板用于显示的一侧面上。
在本发明一实施例中，所述柔性保护盖板的所述硬化涂层覆盖并接触所述显示面板的所述侧面上。尤其是，所述柔性保护盖板的所述硬化涂层覆盖并接触所述显示面板的用于显示的侧面上。
在本发明一实施例中，所述显示面板为一柔性显示面板。
在本发明一优选实施例中，提供一种显示装置，包括一显示面板和设置于所述显示面板用于显示的一侧面上的一柔性保护盖板；其中，所述柔性保护盖板包括至少两层硬化涂层和设置于相邻两层硬化涂层之间的透明层，使得所述硬化涂层与所述透明层交替设置，并且，所述硬化涂层覆盖并接触所述显示面板用于显示的侧面。
在本发明一优选实施例中，提供一种显示装置，包括一显示面板和设置于所述显示面板用于显示的一侧面上的一柔性保护盖板；其中，所述柔性保护盖板包括至少一层第一硬化涂层和至少一层第二硬化涂层，所述第二硬化涂层的材料为氮化硅或氧化硅，并且，所述第一硬化涂层覆盖并接触所述显示面板用于显示的所述侧面上。优选地，所述柔性保护盖板还包括设置于所述第二硬化涂层上的第二层透明层，以及设置于所述透明层上的第二层所述第一硬化涂层。
在上述实施例中，所述第一硬化涂层与所述第二硬化涂层的厚度总和小于20μm，所述透明层的厚度总和小于80μm。并且优选地，所述第一硬化涂层的厚度与所述第二硬化涂层的厚度相同，并且，每一所述透明层的厚度相同。
在上述实施例中，所述第一硬化涂层的材料本领域常规形成保护盖板的硬化涂层材料，例如但不限于：包含纳米无机颗粒(如SiO2)的涂层，二氧化硅有机-无机复合组合物等。
在上述实施例中，所述透明层的材料为透明聚酰亚胺、聚对苯二甲酸乙二醇酯(PET)、聚萘二甲酸乙二醇酯(PEN)、聚甲基丙烯酸甲酯(PMMA)中的至少一种。
在本发明的所述柔性保护盖板中，由于所述硬化涂层的模量比所述透明层的模量大，可以明显增加所述柔性保护盖板的硬度。经仿真计算验证，与传统的柔性盖板相比，本发明所述的柔性保护盖板在保持相同柔性及耐弯折性的同时，硬度提升了8％。
附图说明
图1是一常规柔性盖板的结构示意图；
图2是根据本发明一实施例的柔性保护盖板的结构示意图；
图3A为常规柔性盖板经纳米压痕仿真模拟分析获得的下沉量；图3B为图2所示柔性保护盖板经纳米压痕仿真模拟分析获得的下沉量；
图4是根据本发明另一实施例的柔性保护盖板的结构示意图；
图5是根据本发明一实施例的显示器件的结构示意图。
具体实施方式
以下，结合具体实施方式，对本发明的技术进行详细描述。应当知道的是，以下具体实施方式仅用于帮助本领域技术人员理解本发明，而非对本发明的限制。
实施例1.柔性保护盖板100
在本实施例中，提供一柔性保护盖板100。如图2所示，所述柔性保护盖板100包括三层硬化涂层101和两层透明层102，所述硬化涂层101与所述透明层102交替设置。即，在本实施例中，所述柔性保护盖板100的底层和顶层均为一层硬化涂层101，并且所述底层与所述顶层中间还夹设一层硬化涂层101，所述两层透明层102分别夹设于相邻两层所述硬化涂层101之间，如此形成如图2所示的所述硬化涂层101与所述透明层102交替设置的层叠结构。
在本实施例中，所述硬化涂层101的材料为本领域已知的硬化涂层(或硬化层)材料，例如但不限于：包含纳米无机颗粒(如SiO2)的涂层，二氧化硅有机-无机复合组合物等。所述透明层102的材料为透明聚酰亚胺。
并且，在本实施例中，所有所述硬化涂层101的厚度总和小于20μm，例如但不限于：2μm，4μm，6μm，8μm，10μm，12μm，14μm，16μm，18μm，20μm。在本实施例中，所有所述透明层102的厚度总和小于80μm，例如但不限于：5μm，10μm，15μm，20μm，25μm，30μm，35μm，40μm，45μm，50μm，55μm，60μm，65μm，70μm，75μm，80μm。优选地，每一所述硬化涂层101的厚度相同，并且每一所述透明层102的厚度相同。
为了验证本实施例的所述柔性保护盖板100的性能，在本实施例中，通过纳米压痕的仿真模拟，分别对本实施例所述的柔性保护盖板100与图1所示常规柔性盖板1计算下压深度，分别获得图3A所示的所述常规柔性盖板1的下沉量及图3B所示的所述柔性保护盖板100的下沉量。在本实施例中，以所述柔性保护盖板100(或所述柔性盖板1)的下沉量表征所述柔性保护盖板100(或所述柔性盖板1)的硬度。经计算，如图3A和图3B所示，本实施例所述的柔性保护盖板100的下沉量相较于图1所示的柔性盖板1的下沉量降低8％，说明本实施例所述的柔性保护盖板100具有更好的硬度。
实施例2.柔性保护盖板200
在本实施例中，提供一柔性保护盖板200。如图4所示，所述柔性保护盖板200包括：一第一硬化涂层201，设置于所述第一硬化涂层201上的第一层透明层202，设置于所述透明层202上的一第二硬化涂层203，设置于所述第二硬化涂层203上的第二层透明层202，以及设置于所述透明层202上的第二层所述第一硬化涂层201。
在本实施例中，所述第一硬化涂层201的材料为本领域已知的硬化涂层(或硬化层)材料，例如但不限于：包含纳米无机颗粒(如SiO2)的涂层，二氧化硅有机-无机复合组合物等。所述透明层102的材料为透明聚酰亚胺。所述第二硬化涂层201的材料为氮化硅，氧化硅，或氧化硅掺杂有机材料。
显然，在本实施例中，所述柔性保护盖板200与实施例1的所述柔性保护盖板100的主要区别在于中间一层硬化涂层(即，第二硬化涂层201)由氮化硅，氧化硅，或氧化硅掺杂有机材料制成。
在本实施例中，所有所述第一硬化涂层201与所述第二硬化涂层202的厚度总和小于20μm，例如但不限于：2μm，4μm，6μm，8μm，10μm，12μm，14μm，16μm，18μm，20μm。在本实施例中，所有所述透明层202的厚度总和小于80μm。优选地，每一所述第一硬化涂层201的厚度相同，例如但不限于：5μm，10μm，15μm，20μm，25μm，30μm，35μm，40μm，45μm，50μm，55μm，60μm，65μm，70μm，75μm，80μm。同时，所述第二硬化涂层202的厚度与所述第一硬化涂层201的厚度相同；并且，每一所述透明层202的厚度相同。
与实施例1相似的，为了验证本实施例的所述柔性保护盖板200的性能，通过纳米压痕的仿真模拟计算本实施例所述的柔性保护盖板200的下压深度，以所述柔性保护盖板200的下沉量表征所述柔性保护盖板200的硬度。经计算，相较于实施例1所述的柔性保护盖板100，本实施例所述的柔性保护盖板200的下压量降低8％；并且，相较于图1所示的常规柔性盖板1，本实施例所述的柔性保护盖板200的下压量降低16％。可见，本实施例所述的柔性保护盖板200具有更好的硬度。
实施例3.显示装置
在本实施例中，提供一种显示装置300。如图5所示，所述显示装置300包括一显示面板310和一柔性保护盖板320。所述显示面板310为一柔性显示面板，可以是一柔性OLED显示面板，或者是一柔性液晶显示面板。本领域技术人员可以理解的是，所述显示面板310具有本领域已知的结构，并还可以在一侧面311上具有一触控层(未图示)，以形成一触控显示面板。所述柔性保护盖板320设置于所述显示面板310的所述侧面311上。本领域技术人员可以理解的是，所述侧面311具体为所述显示面板310用于显示的侧面。此外，本领域技术人员可以理解的是，当所述侧面311上还具有一触控层而形成一触控显示面板时，所述柔性保护盖板320设置于触控层上，以起到保护的作用。
所述柔性保护盖板320可以具有与实施例1所述的柔性保护盖板100相同的结构，也可以具有与实施例2所述的柔性保护盖板200相同的结构，此处不再赘述。
本发明已由上述相关实施例加以描述，然而上述实施例仅为实施本发明的范例。必需指出的是，已公开的实施例并未限制本发明的范围。相反地，包含于权利要求书的精神及范围的修改及均等设置均包括于本发明的范围内。

Claims (10)

1.一种柔性保护盖板，用于贴附于显示面板上，其特征在于，所述柔性保护盖板包括至少两层硬化涂层和设置于相邻两层硬化涂层之间的透明层，使得所述硬化涂层与所述透明层交替设置。
2.如权利要求1所述的柔性保护盖板，其特征在于，所述柔性保护盖板包括依次设置的第一硬化涂层、第一透明层、第二硬化涂层。
3.如权利要求2所述的柔性保护盖板，其特征在于，所述柔性保护盖板还包括：设置在所述第二硬化涂层上的第二透明层、以及设置在所述第二透明层上的第三硬化涂层。
4.如权利要求1所述的柔性保护盖板，其特征在于，所有所述硬化涂层的厚度总和小于或等于20μm，所有所述透明层的厚度总和小于或等于80μm。
5.如权利要求1所述的柔性保护盖板，其特征在于，每一层所述硬化涂层的厚度均相同，并且，每一层所述透明层的厚度均相同。
6.如权利要求1所述的柔性保护盖板，其特征在于，夹设在相邻两层所述透明层之间的所述硬化层的材料为氮化硅、氧化硅、氮化硅掺杂有机材料、氧化硅掺杂有机材料中任一种。
7.如权利要求1所述的柔性保护盖板，其特征在于，所述透明层的材料为透明聚酰亚胺、聚对苯二甲酸乙二醇酯、聚萘二甲酸乙二醇酯、聚甲基丙烯酸甲酯中的任一种。
8.一种显示装置，包括一显示面板和权利要求1至7中任一项所述的柔性保护盖板，其中，所述柔性保护盖板设置于所述显示面板的一侧面上。
9.如权利要求8所述的显示装置，其特征在于，所述柔性保护盖板的所述硬化涂层覆盖并接触所述显示面板的所述侧面。
10.如权利要求8所述的显示装置，其特征在于，所述显示面板为一柔性显示面板。
CN201910699335.XA 2019-07-31 2019-07-31 柔性保护盖板及显示装置 Pending CN110475006A (zh)