CN110330317A - 一种氧化锆复合氧化铝陶瓷烧结体、其制备方法及应用 - Google Patents
一种氧化锆复合氧化铝陶瓷烧结体、其制备方法及应用 Download PDFInfo
- Publication number
- CN110330317A CN110330317A CN201910670185.XA CN201910670185A CN110330317A CN 110330317 A CN110330317 A CN 110330317A CN 201910670185 A CN201910670185 A CN 201910670185A CN 110330317 A CN110330317 A CN 110330317A
- Authority
- CN
- China
- Prior art keywords
- content
- oxide
- zirconium oxide
- compound
- containing compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (10)